CN105504482B - 一种无卤阻燃线性低密度聚乙烯材料 - Google Patents
一种无卤阻燃线性低密度聚乙烯材料 Download PDFInfo
- Publication number
- CN105504482B CN105504482B CN201610072128.8A CN201610072128A CN105504482B CN 105504482 B CN105504482 B CN 105504482B CN 201610072128 A CN201610072128 A CN 201610072128A CN 105504482 B CN105504482 B CN 105504482B
- Authority
- CN
- China
- Prior art keywords
- halogen
- retardant
- linear low
- density polyethylene
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 | 实施例7 | |
LLDPE | 100kg | 100kg | 100kg | 100kg | 100kg | 100kg | 100kg |
马来酸酐接枝EVA | 15kg | 15kg | 15kg | 15kg | 15kg | 15kg | 15kg |
聚乙烯蜡 | 15kg | 15kg | 15kg | 15kg | 15kg | 15kg | 15kg |
氢氧化镁 | 330kg | 330kg | 330kg | 315kg | 345kg | 315kg | 345kg |
硼酸锌 | 30kg | 30kg | 30kg | 30kg | 30kg | 30kg | 30kg |
微胶囊红磷 | 33kg | 31.5kg | 34.5kg | 33kg | 33kg | 31.5kg | 34.5kg |
测试性能 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 | 实施例7 |
缺口抗冲击强度/kJ·m<sup>-2</sup> | 15.2 | 15.3 | 15.1 | 15.5 | 14.9 | 15.7 | 14.7 |
拉伸强度/MPa | 18.8 | 19.1 | 18.6 | 19.4 | 18.2 | 19.8 | 17.8 |
断裂伸长率/% | 85 | 87 | 82 | 88 | 80 | 90 | 78 |
最大烟密度 | 58 | 67 | 63 | 68 | 64 | 71 | 60 |
极限氧指数/% | 44.5 | 41.8 | 42.6 | 41.1 | 42.7 | 40.6 | 43.8 |
对比例2 | 对比例3 | 对比例4 | 对比例5 | 对比例6 | 对比例7 | 对比例8 | |
LLDPE | 100kg | 100kg | 100kg | 100kg | 100kg | 100kg | 100kg |
马来酸酐接枝EVA | 15kg | 15kg | 15kg | 15kg | 15kg | 15kg | 15kg |
聚乙烯蜡 | 15kg | 15kg | 15kg | 15kg | 15kg | 15kg | 15kg |
氢氧化镁 | 440kg | 220kg | 480kg | 360kg | 300kg | 250kg | 200kg |
硼酸锌 | 40kg | 20kg | 30kg | 30kg | 30kg | 30kg | 30kg |
微胶囊红磷 | 44kg | 22kg | 48kg | 36kg | 30kg | 25kg | 30kg |
测试性能 | 对比例1 | 对比例2 | 对比例3 | 对比例4 | 对比例5 | 对比例6 | 对比例7 | 对比例8 |
缺口抗冲击强度/kJ·m<sup>-2</sup> | 10.0 | 9.4 | 12.6 | 9.1 | 9.8 | 10.4 | 12.2 | 12.4 |
拉伸强度/MPa | 12.1 | 10.5 | 16.8 | 10.1 | 11.8 | 12.6 | 16.4 | 16.6 |
断裂伸长率/% | 58 | 52 | 67 | 50 | 55 | 58 | 63 | 65 |
最大烟密度 | 55 | 52 | 54 | 60 | 62 | 65 | 61 | 62 |
极限氧指数/% | 38.1 | 42.0 | 36.5 | 41.5 | 40.1 | 39.5 | 36.0 | 35.5 |
Claims (1)