CN105483757A - Machining technology for carbon electrolysis plate and carbon electrolysis plate using machining technology - Google Patents
Machining technology for carbon electrolysis plate and carbon electrolysis plate using machining technology Download PDFInfo
- Publication number
- CN105483757A CN105483757A CN201510876640.3A CN201510876640A CN105483757A CN 105483757 A CN105483757 A CN 105483757A CN 201510876640 A CN201510876640 A CN 201510876640A CN 105483757 A CN105483757 A CN 105483757A
- Authority
- CN
- China
- Prior art keywords
- electrode
- steel sheet
- coated steel
- electrolytic zinc
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a machining technology for a carbon electrolysis plate and the carbon electrolysis plate using the machining technology. The carbon electrolysis plate is machined through the steps of fixing, positioning, drilling, tapping, cleaning, electrode assembling and electrode installing. The carbon electrolysis plate comprises an electrolysis plate body. Electrode holes are formed in the electrolysis plate body in a central symmetry manner. Inner threads are arranged on the inner walls of the electrode holes. The electrode holes are connected with electrodes through the threads. Connecting pieces are arranged at the upper ends of the electrodes. Elastic gaskets are arranged at the lower portions of the connecting pieces. Outer threads are arranged on the outer side walls of the upper ends of the connecting pieces. The machining technology has the advantages that the technology is simple, the trepanning effect is good, the machining efficiency is high, the trepanning integrity rate is high, and electrode connection is firm.
Description
Technical field
The invention belongs to electrolytic zinc-coated steel sheet technical field, be specifically related to a kind of complete processing of carbon element electrolytic zinc-coated steel sheet and use the carbon element electrolytic zinc-coated steel sheet of this technique.
Background technology
Carbon element electrolytic zinc-coated steel sheet is use very extensive in modern production, but existing carbon element electrolytic zinc-coated steel sheet also exists many problems, great inconvenience is caused to the production of electrolytic zinc-coated steel sheet and use, existing carbon element electrolytic zinc-coated steel sheet is all small volumes, the electrolytic zinc-coated steel sheet that drilling depth is more shallow, bore process compare simple, but it is larger for its volume of the electrolytic zinc-coated steel sheet used in nuclear power industry, drilling depth is darker, higher for processing requirement, carbon element electrolytic zinc-coated steel sheet belongs to hard brittle material, carrying out in deep and long hole boring, easy appearance cracking, in addition, after the electrode installation of carbon element electrolytic zinc-coated steel sheet, easily contact is bad, the impact of factor such as to be easily given a shock.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art and the complete processing of the carbon element electrolytic zinc-coated steel sheet that a kind of technique is simple, perforate is effective, working (machining) efficiency is high, perforate percentage of head rice is high, Electrode connection is firm be provided and use the carbon element electrolytic zinc-coated steel sheet of this technique.
Technical scheme of the present invention is a kind of complete processing of carbon element electrolytic zinc-coated steel sheet, and described preparation technology is as follows:
Step 1: fixing: to get 300*600*80mm carbon materials and be placed in hole drilling die;
Step 2: location: prevent on drilling machine by the hole drilling die being placed with carbon materials, regulates the position of hole drilling die;
Step 3: boring: the carbon materials be fixed in step 2 in hole drilling die is placed on drilling machine, and keyhole degree of depth 470mm;
Step 4: tapping: the carbon materials after step 3 being holed is placed on tapping on tapping machine;
Step 5: cleaning: the carbon materials obtained after tapping is carried out clean the Graphite Powder 99 in boring;
Step 6: electrode assembling: elastomeric pad is set with live and extremely goes up;
Step 7: installing electrodes: the electrode with elastomeric pad is screwed on carbon materials that step 5 obtains.
In described step 4, the nominal diameter of the screw thread of tapping is 20mm.
During described boring, the rotating speed of drill bit controls at 1500-2000r/min, and the drill bit of boring adopts diamond head.
A kind of carbon element electrolytic zinc-coated steel sheet, it comprises electrolytic zinc-coated steel sheet body, it is characterized in that: the centrosymmetry of described electrolytic zinc-coated steel sheet body is provided with electrode hole, the inwall of described electrode hole is provided with internal thread, electrode hole has been threaded connection electrode, the upper end of described electrode arranges web member, and the bottom of described web member is provided with elastomeric pad, and the outer side wall of the upper end of web member is provided with outside screw.
Described web member and electrode one-body molded, and the copper that the material of web member and electrode all adopts.
The diameter of described electrode is less than the diameter of web member.
Described externally threaded nominal diameter 20mm.
The invention has the beneficial effects as follows: the difficult problem that the invention solves carbon materials deep and long hole handling ease cracking, and tapping operation is carried out to electrode hole, effectively add the combination of electrode and carbon element plate, avoid loose contact phenomenon, it is more tight that the mode of this connection makes electrode be connected with electrolytic zinc-coated steel sheet body, the web member simultaneously arranged in electrode upper end is arranged with elastomeric pad, effectively can prevent the motion of electrode in vibrating, the upper end of this external web member is provided with outside screw, be convenient to the connection with outer lead, conductive effect is better, it is simple that the present invention has technique, perforate is effective, working (machining) efficiency is high, perforate percentage of head rice is high, the advantage that Electrode connection is firm.
Accompanying drawing explanation
Fig. 1 is the structural representation of a kind of carbon element electrolytic zinc-coated steel sheet of the present invention.
In figure: 1, electrolytic zinc-coated steel sheet body 2, electrode hole 3, internal thread 4, electrode 5, web member 6, elastomeric pad 7, outside screw.
Specific embodiment
Below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1
A complete processing for carbon element electrolytic zinc-coated steel sheet, described preparation technology is as follows:
Step 1: fixing: to get 300*600*80mm carbon materials and be placed in hole drilling die;
Step 2: location: prevent on drilling machine by the hole drilling die being placed with carbon materials, regulates the position of hole drilling die;
Step 3: boring: the carbon materials be fixed in step 2 in hole drilling die is placed on drilling machine, and keyhole degree of depth 470mm;
Step 4: tapping: the carbon materials after step 3 being holed is placed on tapping on tapping machine;
Step 5: cleaning: the carbon materials obtained after tapping is carried out clean the Graphite Powder 99 in boring;
Step 6: electrode assembling: elastomeric pad is set with live and extremely goes up;
Step 7: installing electrodes: the electrode with elastomeric pad is screwed on carbon materials that step 5 obtains.
A kind of carbon element electrolytic zinc-coated steel sheet, it comprises electrolytic zinc-coated steel sheet body 1, the centrosymmetry of described electrolytic zinc-coated steel sheet body 1 is provided with electrode hole 2, the inwall of described electrode hole 2 is provided with internal thread 3, electrode hole 2 has been threaded connection electrode 4, the upper end of described electrode 4 arranges web member 5, and the bottom of described web member 5 is provided with elastomeric pad 6, and the outer side wall of the upper end of web member 5 is provided with outside screw 7.
The invention solves a difficult problem for carbon materials deep and long hole handling ease cracking, and tapping operation is carried out to electrode hole, effectively add the combination of electrode and carbon element plate, avoid loose contact phenomenon, it is more tight that the mode of this connection makes electrode be connected with electrolytic zinc-coated steel sheet body, the web member simultaneously arranged in electrode upper end is arranged with elastomeric pad, effectively can prevent the motion of electrode in vibrating, the upper end of this external web member is provided with outside screw, be convenient to the connection with outer lead, conductive effect is better, it is simple that the present invention has technique, perforate is effective, working (machining) efficiency is high, perforate percentage of head rice is high, the advantage that Electrode connection is firm.
Embodiment 2
A complete processing for carbon element electrolytic zinc-coated steel sheet, described preparation technology is as follows:
Step 1: fixing: to get 300*600*80mm carbon materials and be placed in hole drilling die;
Step 2: location: prevent on drilling machine by the hole drilling die being placed with carbon materials, regulates the position of hole drilling die;
Step 3: boring: the carbon materials be fixed in step 2 in hole drilling die is placed on drilling machine, and keyhole degree of depth 470mm;
Step 4: tapping: the carbon materials after step 3 being holed is placed on tapping on tapping machine;
Step 5: cleaning: the carbon materials obtained after tapping is carried out clean the Graphite Powder 99 in boring;
Step 6: electrode assembling: elastomeric pad is set with live and extremely goes up;
Step 7: installing electrodes: the electrode with elastomeric pad is screwed on carbon materials that step 5 obtains.
In described step 4, the nominal diameter of the screw thread of tapping is 20mm.
During described boring, the rotating speed of drill bit controls at 1500-2000r/min, and the drill bit of boring adopts diamond head.
A kind of electrolytic zinc-coated steel sheet using superhard carbon material, it comprises electrolytic zinc-coated steel sheet body 1, the centrosymmetry of described electrolytic zinc-coated steel sheet body 1 is provided with electrode hole 2, the inwall of described electrode hole 2 is provided with internal thread 3, electrode hole 2 has been threaded connection electrode 4, the upper end of described electrode 4 arranges web member 5, and the bottom of described web member 5 is provided with elastomeric pad 6, and the outer side wall of the upper end of web member 5 is provided with outside screw 7.
Described web member 5 is one-body molded with electrode 4, and the copper that web member 5 all adopts with the material of electrode 4.
The diameter of described electrode 4 is less than the diameter of web member 5.
The nominal diameter 20mm of described outside screw 7.
The invention solves a difficult problem for carbon materials deep and long hole handling ease cracking, and tapping operation is carried out to electrode hole, effectively add the combination of electrode and carbon element plate, avoid loose contact phenomenon, it is more tight that the mode of this connection makes electrode be connected with electrolytic zinc-coated steel sheet body, the web member simultaneously arranged in electrode upper end is arranged with elastomeric pad, effectively can prevent the motion of electrode in vibrating, the upper end of this external web member is provided with outside screw, be convenient to the connection with outer lead, conductive effect is better, it is simple that the present invention has technique, perforate is effective, working (machining) efficiency is high, perforate percentage of head rice is high, the advantage that Electrode connection is firm.
Claims (7)
1. a complete processing for carbon element electrolytic zinc-coated steel sheet, is characterized in that: described preparation technology is as follows:
Step 1: fixing: to get 300*600*80mm carbon materials and be placed in hole drilling die;
Step 2: location: prevent on drilling machine by the hole drilling die being placed with carbon materials, regulates the position of hole drilling die;
Step 3: boring: the carbon materials be fixed in step 2 in hole drilling die is placed on drilling machine, and keyhole degree of depth 470mm;
Step 4: tapping: the carbon materials after step 3 being holed is placed on tapping on tapping machine;
Step 5: cleaning: the carbon materials obtained after tapping is carried out clean the Graphite Powder 99 in boring;
Step 6: electrode assembling: elastomeric pad is set with live and extremely goes up;
Step 7: installing electrodes: the electrode with elastomeric pad is screwed on carbon materials that step 5 obtains.
2. the complete processing of a kind of carbon element electrolytic zinc-coated steel sheet as claimed in claim 1, is characterized in that: in described step 4, the nominal diameter of the screw thread of tapping is 20mm.
3. the complete processing of a kind of carbon element electrolytic zinc-coated steel sheet as claimed in claim 1, is characterized in that: during described boring, the rotating speed of drill bit controls at 1500-2000r/min, and the drill bit of boring adopts diamond head.
4. a carbon element electrolytic zinc-coated steel sheet, it comprises electrolytic zinc-coated steel sheet body, it is characterized in that: the centrosymmetry of described electrolytic zinc-coated steel sheet body is provided with electrode hole, the inwall of described electrode hole is provided with internal thread, electrode hole has been threaded connection electrode, the upper end of described electrode arranges web member, and the bottom of described web member is provided with elastomeric pad, and the outer side wall of the upper end of web member is provided with outside screw.
5. a kind of carbon element electrolytic zinc-coated steel sheet as claimed in claim 4, is characterized in that: described web member and electrode one-body molded, and the copper that the material of web member and electrode all adopts.
6. a kind of carbon element electrolytic zinc-coated steel sheet as claimed in claim 4, is characterized in that: the diameter of described electrode is less than the diameter of web member.
7. a kind of carbon element electrolytic zinc-coated steel sheet as claimed in claim 4, is characterized in that: described externally threaded nominal diameter 20mm.