CN105464266A - Iron sheet floor plate and preparation method of iron sheet floor plate - Google Patents

Iron sheet floor plate and preparation method of iron sheet floor plate Download PDF

Info

Publication number
CN105464266A
CN105464266A CN201510877605.3A CN201510877605A CN105464266A CN 105464266 A CN105464266 A CN 105464266A CN 201510877605 A CN201510877605 A CN 201510877605A CN 105464266 A CN105464266 A CN 105464266A
Authority
CN
China
Prior art keywords
iron sheet
floor plates
parts
fiber
floor
Prior art date
Application number
CN201510877605.3A
Other languages
Chinese (zh)
Inventor
彭庆付
Original Assignee
安徽省中坤元新型建材有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 安徽省中坤元新型建材有限公司 filed Critical 安徽省中坤元新型建材有限公司
Priority to CN201510877605.3A priority Critical patent/CN105464266A/en
Publication of CN105464266A publication Critical patent/CN105464266A/en

Abstract

The invention discloses an iron sheet floor plate, which is used as a floor plate or a roof plate. The iron sheet floor plate is prepared by the following steps of coating unsaturated or saturated resin glue on at least one side of a floor base plate; bonding a layer of iron sheet; and performing compact pressing and natural drying in the air. The floor base plate is prepared from the following ingredients in parts by weight: 38 to 45 parts of magnesium oxide, 20 to 35 parts of brine, 15 to 25 parts of fiber, 5 to 8 parts of fly ash, 5 to 8 parts of talcum powder, 6 to 10 parts of mineral waste residue, 2 to 4 parts of modifying agents, 0.1 to 0.5 part of recurrent halogen agents, 1 to 3 parts of alkali-resistant glass fiber gridding cloth and 1 to 3 parts of non-woven fabrics. The invention also discloses concrete preparation steps. Through the floor base plate proportioning, the iron sheet and the production process, high strength can be ensured; high toughness can also be realized; the nail absorption force of a produced finished product is high; the practicability is high; the effects of stage-A fireproof performance, energy-saving effect, sound-isolation function, heat-insulation performance, long service life, light weight and green and environment protection effects are achieved; and any toxic or harmful gas is not released into a room.

Description

A kind of iron sheet floor plates and preparation method thereof

Technical field

The present invention relates to a kind of iron sheet floor plates and preparation method thereof, belong to building material technical field.

Background technology

Floor plates is by traditional floor through researching and developing a kind of building board of progressively developing, is raw material as main with steel, the on-the-spot floor plates by being welded to connect; Take steel concrete as the floor plates of raw material, when package is installed between floors, use that later stage fluting buries, the method for cast-in-site, site operation; With the floor plates that wooden splint, woodwork plate are raw material.

All there is self defect in above-mentioned floor plates, although as wooden splint woodwork plate can easily movement, conveniently combinationally use, its insufficient strength, fireproof performance is poor, and lumber consumption is large; With the floor plates of welded steel, price is high enough, and construction is complicated; The floor plates that one steel concrete manufactures, waste of raw materials is serious, and building waste is many, time-consuming, and speed is slow, and energy consumption is high, and quality is uncontrollable, and therefore, these floor plates all do not meet requirement and the developing direction of the environmental protection and energy saving policy of country.

The development need of floor plates should have some strength, toughness, there is very strong suction nail power again, and there is the fire prevention of A level, energy-conservation, sound insulation, insulation, long-life, more lightweight, and green, environmental protection, not to any toxic and harmful of indoor discharge, existing floor plates all can not accomplish to have above-mentioned all features simultaneously.

Summary of the invention

In order to solve the deficiencies in the prior art, the object of the present invention is to provide a kind of intensity, toughness high, it is strong to inhale nail power, has the fire prevention of A level, energy-conservation, sound insulation, insulation, long-life, more lightweight, and green, environmental protection, not to the iron sheet floor plates of any toxic and harmful of indoor discharge.

For achieving the above object, the technology used in the present invention means are: a kind of iron sheet floor plates, and as floor plates or roof panel, at least simultaneously coat unsaturated or saturated resin glue by floor substrate, paste one deck iron sheet, compacting is naturally dried and formed.

Further, described floor substrate is made up of the raw material of following weight portion: magnesia 38 ~ 45, bittern 20 ~ 35, fiber 15 ~ 25, flyash 5 ~ 8, French chalk 5 ~ 8, slag 6 ~ 10, modifier 2 ~ 4, anti-halogen agent 0.1 ~ 0.5, alkali-proof glass screen grid cloth 1 ~ 3, non-woven fabrics 1 ~ 3.

Further, described fiber is the one or more combination of organic fiber, inorfil, string or string and sawdust mixture.

Further, the preparation process of described iron sheet floor plates is as follows:

One, mold oil is sprayed uniformly by production template, in template, then spread alkali-proof glass screen grid cloth or alkali-proof glass screen grid cloth and non-woven fabrics, now according under demand or fabric of not going to the bottom, add the compound of magnesia, bittern, fiber, flyash, French chalk, slag, modifier, anti-halogen agent, in the middle of compound, insert one or more layers simultaneously or do not insert alkali-proof glass screen grid cloth, add or do not add fabric according to design requirement, by roller bearing rolling machine roller-compaction;

Two, enter after roller-compaction between solidification, fast steam-cured, solidification or spontaneous curing;

Three, the floor plates demoulding will be cured, sends into maintenance between maintenance;

Four, by unsaturated for floor plates even application good for maintenance or saturated resin glue, paste iron sheet, compacting is dried naturally, can send into the finished product that saw room cuts into required length and width size.

Further, described bottom surface material or fabric are the part mixing of the magnesia got in raw material, bittern, modifier, and the appropriate brightening agent that adds is made.

Further, the thickness of described iron sheet is 1 ~ 10mm.

Further, between described solidification fast steam-cured, solidification time temperature set between 35 DEG C ~ 65 DEG C, be room temperature during spontaneous curing.

Further, between described maintenance, temperature sets between 0 DEG C ~ 35 DEG C.

The invention has the beneficial effects as follows: by the batching of floor substrate and attachment iron sheet and production technology, high strength can be ensured, high tenacity can be realized again, the one-tenth smoking nail power produced is strong, Practical Performance is good, there is the fire prevention of A level, energy-conservation, sound insulation, insulation, long-life, more lightweight, and green, environmental protection, not to any toxic and harmful of indoor discharge.

Detailed description of the invention

embodiment 1

A kind of iron sheet floor plates, as floor plates or dividing plate, at least simultaneously coat unsaturated-resin glue by floor substrate, paste one deck iron sheet, compacting is naturally dried and is formed.Described floor substrate is made up of the raw material of following weight portion: magnesia 38, bittern 20, fiber 15, flyash 5, French chalk 5, slag 6, modifier 2, anti-halogen agent 0.1, alkali-proof glass screen grid cloth 1, non-woven fabrics 1.

Described fiber is the one or more combination of organic fiber, inorfil, string or string and sawdust mixture.

The preparation process of described iron sheet floor plates is as follows:

One, mold oil is sprayed uniformly by production template, in template, then spread alkali-proof glass screen grid cloth or alkali-proof glass screen grid cloth and non-woven fabrics, now according under demand or fabric of not going to the bottom, add the compound of magnesia, bittern, fiber, flyash, French chalk, slag, modifier, anti-halogen agent, in the middle of compound, insert one or more layers simultaneously or do not insert alkali-proof glass screen grid cloth, add or do not add fabric according to design requirement, by roller bearing rolling machine roller-compaction;

Two, enter after roller-compaction between solidification, fast steam-cured, solidification or spontaneous curing;

Three, the floor plates demoulding will be cured, sends into maintenance between maintenance;

Four, by floor plates even application unsaturated-resin glue good for maintenance, paste iron sheet, compacting is dried naturally, can send into the finished product that saw room cuts into required length and width size.

Temperature between described solidification sets between 35 DEG C ~ 65 DEG C, and between maintenance, temperature sets between 0 DEG C ~ 35 DEG C.

embodiment 2

A kind of iron sheet floor plates, as floor plates or dividing plate, at least simultaneously coat unsaturated-resin glue by floor substrate, paste one deck iron sheet, compacting is naturally dried and is formed.Described floor substrate is made up of the raw material of following weight portion: magnesia 45, bittern 35, fiber 25, flyash 8, French chalk 8, slag 10, modifier 4, anti-halogen agent 0.5, alkali-proof glass screen grid cloth 3, non-woven fabrics 3.

Described bottom surface material or fabric are the part mixing of the magnesia got in raw material, bittern, modifier, and the appropriate brightening agent that adds is made.Preparation process one, spray mold oil uniformly by production template, in template, then spread alkali-proof glass screen grid cloth or alkali-proof glass screen grid cloth and non-woven fabrics, to go to the bottom fabric, add the compound of magnesia, bittern, fiber, flyash, French chalk, slag, modifier, anti-halogen agent, in the middle of compound, insert one deck alkali-proof glass screen grid cloth simultaneously, add fabric, by roller bearing rolling machine roller-compaction; The thickness of described iron sheet is 1 ~ 10mm.Room temperature spontaneous curing.Between maintenance, temperature sets between 0 DEG C ~ 35 DEG C.Described fiber is organic fiber.

embodiment 3

A kind of iron sheet floor plates, as floor plates or dividing plate, at least simultaneously coat unsaturated-resin glue by floor substrate, paste one deck iron sheet, compacting is naturally dried and is formed.Described floor substrate is made up of the raw material of following weight portion: magnesia 39, bittern 32, fiber 17, flyash 6, French chalk 6, slag 7, modifier 3, anti-halogen agent 0.3, alkali-proof glass screen grid cloth 2, non-woven fabrics 2.Described fiber is string and sawdust mixture.

The preparation process of described iron sheet floor plates is as follows:

One, mold oil is sprayed uniformly by production template, in template, then spread alkali-proof glass screen grid cloth or alkali-proof glass screen grid cloth and non-woven fabrics, to go to the bottom fabric, add the compound of magnesia, bittern, fiber, flyash, French chalk, slag, modifier, anti-halogen agent, in the middle of compound, insert multilayer alkali-proof glass screen grid cloth simultaneously, add fabric, by roller bearing rolling machine roller-compaction;

Two, enter after roller-compaction between solidification, fast steam-cured, solidification; Between described solidification fast steam-cured, solidification time temperature set between 35 DEG C ~ 65 DEG C;

Three, the floor plates demoulding will be cured, sends into maintenance between maintenance; Between described maintenance, temperature sets between 0 DEG C ~ 35 DEG C.

Four, by floor plates even application unsaturated-resin glue good for maintenance, paste iron sheet, compacting is dried naturally, can send into the finished product that saw room cuts into required length and width size.

Described bottom surface material or fabric are the part mixing of the magnesia got in raw material, bittern, modifier, and the appropriate brightening agent that adds is made.

The thickness of described iron sheet is 4mm.The present embodiment is most preferred embodiment, applicant finds, compress by increasing iron sheet, and floor substrate grid cloth and non-woven fabrics and inserts compound, make whole plate have more intensity, owing to adopting the light material such as magnesia cement and string to make plate more lightweight, sound insulation reaches 50 decibels, self-heat conserving better effects if, have the advantages that intensity is high, toughness is high, flexible, and anti-folding, tension, compressive property there is obvious raising; The floor plates own wt produced is light, inhales nail power by force, decreases cost of transportation; Mounting process is convenient and swift, brings facility to construction, and solve the drawback cannot adhering to other article after like product is installed, the floor plates sound insulation of producing, energy-conservation, environmental protection, not to any toxic and harmful of indoor discharge.Production technology is simple and convenient, and production efficiency improves greatly.The step of production technology and the various quality of plate forming all meet industry standard.

The explanation of disclosed embodiment of this invention just to technical scheme of the present invention, can not as the restriction to content of the present invention, and the simple change of those skilled in the art on basis of the present invention, still in protection scope of the present invention.

Claims (9)

1. an iron sheet floor plates, as floor plates or roof panel, at least simultaneously coat unsaturated or saturated resin glue by floor substrate, paste one deck iron sheet, compacting is naturally dried and is formed.
2. iron sheet floor plates according to claim 1, is characterized in that: described floor substrate is made up of the raw material of following weight portion: magnesia 38 ~ 45, bittern 20 ~ 35, fiber 15 ~ 25, flyash 5 ~ 8, French chalk 5 ~ 8, slag 6 ~ 10, modifier 2 ~ 4, anti-halogen agent 0.1 ~ 0.5, alkali-proof glass screen grid cloth 1 ~ 3, non-woven fabrics 1 ~ 3.
3. iron sheet floor plates according to claim 2, is characterized in that: described fiber is the one or more combination of organic fiber, inorfil, string or string and sawdust mixture.
4. the preparation method of iron sheet floor plates as claimed in claim 1, it is characterized in that, preparation process is as follows:
One, mold oil is sprayed uniformly by production template, in template, then spread alkali-proof glass screen grid cloth or alkali-proof glass screen grid cloth and non-woven fabrics, now according under demand or fabric of not going to the bottom, add the compound of magnesia, bittern, fiber, flyash, French chalk, slag, modifier, anti-halogen agent, in the middle of compound, insert one or more layers simultaneously or do not insert alkali-proof glass screen grid cloth, add or do not add fabric according to design requirement, by roller bearing rolling machine roller-compaction;
Two, enter after roller-compaction between solidification, fast steam-cured, solidification or spontaneous curing;
Three, the floor plates demoulding will be cured, sends into maintenance between maintenance;
Four, by unsaturated for floor plates even application good for maintenance or saturated resin glue, paste iron sheet, compacting is dried naturally, can send into the finished product that saw room cuts into required length and width size.
5. the preparation method of iron sheet floor plates according to claim 4, is characterized in that: described bottom surface material or fabric are the part mixing of the magnesia got in raw material, bittern, modifier, and the appropriate brightening agent that adds is made.
6. the preparation method of iron sheet floor plates according to claim 4, is characterized in that: the thickness of described iron sheet is 1 ~ 10mm.
7. the preparation method of iron sheet floor plates according to claim 4, is characterized in that: between described solidification fast steam-cured, solidification time temperature set between 35 DEG C ~ 65 DEG C, be room temperature during spontaneous curing.
8. the preparation method of iron sheet floor plates according to claim 4, is characterized in that:, between described maintenance, temperature sets between 0 DEG C ~ 35 DEG C.
9. iron sheet floor plates according to claim 1, it is characterized in that: described floor substrate is made up of the raw material of following weight portion: magnesia 39, bittern 32, fiber 17, flyash 6, French chalk 6, slag 7, modifier 3, anti-halogen agent 0.3, alkali-proof glass screen grid cloth 2, non-woven fabrics 2, described fiber is string and sawdust mixture.
CN201510877605.3A 2015-12-04 2015-12-04 Iron sheet floor plate and preparation method of iron sheet floor plate CN105464266A (en)