CN105315534A - Plastic pallet beneficial to product storage and transportation - Google Patents

Plastic pallet beneficial to product storage and transportation Download PDF

Info

Publication number
CN105315534A
CN105315534A CN201510689585.7A CN201510689585A CN105315534A CN 105315534 A CN105315534 A CN 105315534A CN 201510689585 A CN201510689585 A CN 201510689585A CN 105315534 A CN105315534 A CN 105315534A
Authority
CN
China
Prior art keywords
parts
powder
plastic pallet
weight
transport
Prior art date
Application number
CN201510689585.7A
Other languages
Chinese (zh)
Inventor
黄庆洪
Original Assignee
安徽冠泓塑业有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 安徽冠泓塑业有限公司 filed Critical 安徽冠泓塑业有限公司
Priority to CN201510689585.7A priority Critical patent/CN105315534A/en
Publication of CN105315534A publication Critical patent/CN105315534A/en

Abstract

The invention discloses a plastic pallet beneficial to product storage and transportation, and relates to the technical field of plastic product production. The plastic pallet is prepared from, by weight, 70-80 parts of high-density polyethylene, 35-40 parts of polypropylene, 15-20 parts of methyl methacrylate-butadiene-styrene copolymers, 5-8 parts of nanometer silicon carbide, 13-17 parts of organically modified montmorillonite, 12-15 parts of vermiculite powder, 10-13 parts of glycerinum, 8-12 parts of bone meal, 6-10 parts of mildew preventive, 6-10 parts of spermol, 5-8 parts of diisopropyl cyclohexane-1,2-dicarboxylate, 5-8 parts of dilauryl thiodipropionate, 4-6 parts of octadecanamide and 3-6 parts of di-n-octyltin. High-density polyethylene and polypropylene serve as the main raw materials, and with the aid of various functional auxiliaries, the prepared plastic pallet has excellent moisture resistance, corrosion resistance, pressure resistance, abrasive resistance and the like and is light in weight and suitable for storing, loading, unloading and transporting various products.

Description

A kind of plastic pallet being convenient to product stock and transport
Technical field:
The present invention relates to plastics production technical field, be specifically related to a kind of plastic pallet being convenient to product stock and transport.
Background technology:
Plastic pallet is also known as (plastic pallet, plastics clamp, Forklift plate etc.) multiple call.The proper use of of pallet should accomplish that packaged combination is piled up the goods on pallet and adds suitable tying up and wrap up in bag, is convenient to mechanical handling and transport, thus the requirement meeting handling, transport and store.Generally select PE, PP plastics raw material to make, there is the advantage of environmental protection, protection against the tide, anticorrosion, Portable durable, be widely used in the industries such as storage, logistics, supermarket, loading and discharging.At present, although the plastic pallet that most of factory uses can meet basic product stock and movement requirement, its work-ing life is shorter.In use for some time, easily there is the phenomenon of wearing and tearing and depression in its surface.In order to ensure the security of product stock and transport, needing to change in time, to avoid security incident.
Summary of the invention:
Technical problem to be solved by this invention is to provide a kind of protection against the tide, anticorrosion, withstand voltage, the wear-resisting and light plastic pallet being convenient to product stock and transport.
Technical problem to be solved by this invention adopts following technical scheme to realize:
Be convenient to a plastic pallet for product stock and transport, be made up of the raw material of following parts by weight:
High density polyethylene(HDPE) 70-80 part, polypropylene 35-40 part, MBS 15-20 part, nanometer silicon carbide 5-8 part, modified montmorillonoid 13-17 part, vermiculite power 12-15 part, glycerine 10-13 part, bone meal 8-12 part, mould inhibitor 6-10 part, hexadecanol 6-10 part, 1,2-hexanaphthene-dicaxboxylate 5-8 part, Tyox B 5-8 part, stearic amide 4-6 part, dioctyltin 3-6 part.
Described modified montmorillonoid is made up of the raw material of following parts by weight: polynite 90-100 part, gluten powder 12-15 part, cetrimonium bromide 10-13 part, palmitinic acid 7-10 part, nanmeter antimong trioxide 5-8 part, water 150-200 part, its preparation method is: first polynite be scattered in water and soak 3-5h, add cetrimonium bromide and nanmeter antimong trioxide again, in microwave frequency 2450MHz after mixing, microwave treatment 15-20min under power 600W, gluten powder and palmitinic acid is added after being cooled to 35-40 DEG C, then in ultrasonic frequency 40kHz, supersound process 25-30min under power 100W, filter, powder is ground into after filter residue drying.Polynite, through modification, enhances its carrier performance, is conducive to the mechanical property improving this plastic pallet.
Described mould inhibitor is made up of the raw material of following parts by weight: hardship is remonstrated with skin 25-30 part, camphor leaf 20-25 part, stone-like omphalia 15-20 part, Wu Chia Pee 6-10 part, balsam pear 6-10 part, leek 4-7 part, zanthoxylum powder 2-3 part, chilli seed powder 1-2 part, Xylo-Mucine 12-15 part, saltcake 3-5 part, potassium permanganate 2-3 part, nanometer silver 1-2 part, sulphur 1-2 part, its preparation method is: skin of hardship being remonstrated with, camphor leaf, stone-like omphalia and Wu Chia Pee add in 3-5 times of water gaging, in microwave frequency 2450MHz after immersion 3-5h, microwave treatment 20-30min under power 600W, balsam pear and leek is added after being cooled to room temperature, then in ultrasonic frequency 40kHz, supersound process 30-45min under power 100W, filter, filtrate is condensed into solid content 70-80% lotion, add Xylo-Mucine again, after drying, powder is ground into after mixing, finally add zanthoxylum powder, chilli seed powder, saltcake, potassium permanganate, nanometer silver and sulphur, fully mix.This mould inhibitor is mixed with having the Chinese medical extract of excellent anti-mold effect, fruit and chemical substance, composite effective, substantially increases the mildew resistance of this plastic pallet.
The invention has the beneficial effects as follows: the present invention with high density polyethylene(HDPE) and polypropylene for main raw material, be aided with several functions auxiliary agent, obtained plastic pallet has excellent moistureproofness, preservative property, resistance to pressure and wear resistance etc., and light weight, be applicable to the storage of multiple product, handling and transport.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
Be convenient to a plastic pallet for product stock and transport, be made up of the raw material of following parts by weight:
High density polyethylene(HDPE) 72 parts, polypropylene 38 parts, MBS 16 parts, nanometer silicon carbide 6 parts, modified montmorillonoid 14 parts, vermiculite power 13 parts, glycerine 12 parts, bone meal 10 parts, mould inhibitor 8 parts, hexadecanol 7 parts, 1,2-hexanaphthene-dicaxboxylate 6 parts, Tyox B 6 parts, stearic amide 5 parts, dioctyltin 4 parts.
Above-mentioned raw materials fully being mixed, then adds in single screw extrusion machine, through melt extruding, blowing, making plastic pallet after cooling and shaping.Wherein, the barrel temperature of single screw extrusion machine is: 140-144 DEG C, I district, 145-149 DEG C, II district, 150-154 DEG C, III district, 155-159 DEG C, IV district, 160-164 DEG C, V district, 165-169 DEG C, VI district, die head temperature 162-165 DEG C.
The preparation of modified montmorillonoid: first 95 parts of polynites are scattered in 180 parts of water and soak 5h, add 10 parts of cetrimonium bromides and 6 parts of nanmeter antimong trioxides again, after mixing under microwave frequency 2450MHz, power 600W microwave treatment 15min, 13 parts of gluten powders and 8 parts of palmitinic acids are added after being cooled to 35-40 DEG C, then supersound process 30min under ultrasonic frequency 40kHz, power 100W, filter, after filter residue drying, be ground into powder.
The preparation of mould inhibitor: skin that 25 parts of hardships are remonstrated with, 22 parts of camphor leaves, 16 parts of stone-like omphalias and 7 parts of Wu Chia Pee add in 3 times of water gagings, in microwave frequency 2450MHz after immersion 5h, microwave treatment 20min under power 600W, 7 portions of balsam pears and 5 portions of leek are added after being cooled to room temperature, then in ultrasonic frequency 40kHz, supersound process 30min under power 100W, filter, filtrate is condensed into solid content 70-80% lotion, add 13 parts of Xylo-Mucines again, after drying, powder is ground into after mixing, finally add 2 parts of zanthoxylum powders, 1 part of chilli seed powder, 3 parts of saltcake, 2 parts of potassium permanganate, 1 part of nanometer silver and 1 part of sulphur, fully mix.
Embodiment 2
Be convenient to a plastic pallet for product stock and transport, be made up of the raw material of following parts by weight:
High density polyethylene(HDPE) 80 parts, polypropylene 38 parts, MBS 19 parts, nanometer silicon carbide 7 parts, modified montmorillonoid 15 parts, vermiculite power 14 parts, glycerine 12 parts, bone meal 11 parts, mould inhibitor 9 parts, hexadecanol 8 parts, 1,2-hexanaphthene-dicaxboxylate 7 parts, Tyox B 8 parts, stearic amide 5 parts, dioctyltin 5 parts.
Above-mentioned raw materials fully being mixed, then adds in single screw extrusion machine, through melt extruding, blowing, making plastic pallet after cooling and shaping.Wherein, the barrel temperature of single screw extrusion machine is: 140-144 DEG C, I district, 145-149 DEG C, II district, 150-154 DEG C, III district, 155-159 DEG C, IV district, 160-164 DEG C, V district, 165-169 DEG C, VI district, die head temperature 162-165 DEG C.
The preparation of modified montmorillonoid: first 100 parts of polynites are scattered in 200 parts of water and soak 5h, add 12 parts of cetrimonium bromides and 7 parts of nanmeter antimong trioxides again, after mixing under microwave frequency 2450MHz, power 600W microwave treatment 15min, 15 parts of gluten powders and 9 parts of palmitinic acids are added after being cooled to 35-40 DEG C, then supersound process 30min under ultrasonic frequency 40kHz, power 100W, filter, after filter residue drying, be ground into powder.
The preparation of mould inhibitor: skin that 30 parts of hardships are remonstrated with, 25 parts of camphor leaves, 18 parts of stone-like omphalias and 10 parts of Wu Chia Pee add in 3 times of water gagings, in microwave frequency 2450MHz after immersion 5h, microwave treatment 20min under power 600W, 10 portions of balsam pears and 6 portions of leek are added after being cooled to room temperature, then in ultrasonic frequency 40kHz, supersound process 30min under power 100W, filter, filtrate is condensed into solid content 70-80% lotion, add 15 parts of Xylo-Mucines again, after drying, powder is ground into after mixing, finally add 3 parts of zanthoxylum powders, 2 parts of chilli seed powder, 4 parts of saltcake, 2 parts of potassium permanganate, 2 parts of nanometer silvers and 1 part of sulphur, fully mix.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.

Claims (3)

1. be convenient to a plastic pallet for product stock and transport, it is characterized in that, be made up of the raw material of following parts by weight:
High density polyethylene(HDPE) 70-80 part, polypropylene 35-40 part, MBS 15-20 part, nanometer silicon carbide 5-8 part, modified montmorillonoid 13-17 part, vermiculite power 12-15 part, glycerine 10-13 part, bone meal 8-12 part, mould inhibitor 6-10 part, hexadecanol 6-10 part, 1,2-hexanaphthene-dicaxboxylate 5-8 part, Tyox B 5-8 part, stearic amide 4-6 part, dioctyltin 3-6 part.
2. the plastic pallet being convenient to product stock and transport according to claim 1, it is characterized in that, described modified montmorillonoid is made up of the raw material of following parts by weight: polynite 90-100 part, gluten powder 12-15 part, cetrimonium bromide 10-13 part, palmitinic acid 7-10 part, nanmeter antimong trioxide 5-8 part, water 150-200 part, its preparation method is: first polynite be scattered in water and soak 3-5h, add cetrimonium bromide and nanmeter antimong trioxide again, in microwave frequency 2450MHz after mixing, microwave treatment 15-20min under power 600W, gluten powder and palmitinic acid is added after being cooled to 35-40 DEG C, then in ultrasonic frequency 40kHz, supersound process 25-30min under power 100W, filter, powder is ground into after filter residue drying.
3. the plastic pallet being convenient to product stock and transport according to claim 1, is characterized in that, described mould inhibitor is made up of the raw material of following parts by weight: hardship is remonstrated with skin 25-30 part, camphor leaf 20-25 part, stone-like omphalia 15-20 part, Wu Chia Pee 6-10 part, balsam pear 6-10 part, leek 4-7 part, zanthoxylum powder 2-3 part, chilli seed powder 1-2 part, Xylo-Mucine 12-15 part, saltcake 3-5 part, potassium permanganate 2-3 part, nanometer silver 1-2 part, sulphur 1-2 part, its preparation method is: skin of hardship being remonstrated with, camphor leaf, stone-like omphalia and Wu Chia Pee add in 3-5 times of water gaging, in microwave frequency 2450MHz after immersion 3-5h, microwave treatment 20-30min under power 600W, adds balsam pear and leek, then in ultrasonic frequency 40kHz after being cooled to room temperature, supersound process 30-45min under power 100W, filters, filtrate is condensed into solid content 70-80% lotion, then adds Xylo-Mucine, is ground into powder, finally adds zanthoxylum powder after mixing after drying, chilli seed powder, saltcake, potassium permanganate, nanometer silver and sulphur, fully mix.
CN201510689585.7A 2015-10-22 2015-10-22 Plastic pallet beneficial to product storage and transportation CN105315534A (en)