CN105297254A - 一种防辐射抗菌面料 - Google Patents

一种防辐射抗菌面料 Download PDF

Info

Publication number
CN105297254A
CN105297254A CN201510610156.6A CN201510610156A CN105297254A CN 105297254 A CN105297254 A CN 105297254A CN 201510610156 A CN201510610156 A CN 201510610156A CN 105297254 A CN105297254 A CN 105297254A
Authority
CN
China
Prior art keywords
parts
radiation
radiation proof
facing material
antibiotic facing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510610156.6A
Other languages
English (en)
Inventor
于中建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jieshou Bofeite Garment Co Ltd
Original Assignee
Jieshou Bofeite Garment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jieshou Bofeite Garment Co Ltd filed Critical Jieshou Bofeite Garment Co Ltd
Priority to CN201510610156.6A priority Critical patent/CN105297254A/zh
Publication of CN105297254A publication Critical patent/CN105297254A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防辐射抗菌面料，由如下重量份的物质制成：8~10份金属微丝、25~30份竹纤维、10~15份草珊瑚纤维、50~60份苎麻纤维。本发明所用成分安全环保，取材广泛易得，制作方法简单方便，不仅具有较强的抗菌、防辐射效果，可将辐射剂量由2SV减少至100mSV以下，对金黄色葡萄球菌、大肠杆菌、白色念球菌等的抑菌率均在98%以上，又有较好的吸湿透气、除臭耐磨性能，可用作不同服饰的制作，使用范围广泛。

Description

一种防辐射抗菌面料
技术领域
本发明涉及一种面料，尤其涉及一种防辐射抗菌面料。
背景技术
随着生活水平的日益提高，现代人对身体健康越来越注重，在选择衣物时除了考虑其颜色和款式外，还会考虑衣物的安全性，环保性和功能性。在衣物基本功能不变的基础上，人们越来越多的注重衣物对身体的保健作用，不断的研发衣物面料，利用新工艺将不同性能的材料混纺到衣料面料中或通过浸染、溅镀、表面改性等方式，提高衣物面料的功能性。
目前人们日常生活中离不开电子产品的存在，无论办公还是休闲娱乐，几乎时时刻刻都在与电脑、手机等产品打交道，而这些物品对会对人体产生辐射，长期的接触会对人体产生不良的危害，尤其是孕妇和病患者。市面上也充斥着各种防辐射功能面料，但不少在选材或制备方法上的差异和缺陷，使其所制备的面料的综合性能参差不齐，并待提高和完善。
发明内容
为了解决上述问题，本发明提供了一种防辐射抗菌面料，材料易得、方法简单，不仅具有良好的透气、吸湿性能，又有很好的抗菌、防辐射效果。
本发明通过如下技术方案来实现：
一种防辐射抗菌面料，由如下重量份的物质制成：
8~10份金属微丝、25~30份竹纤维、10~15份草珊瑚纤维、50~60份苎麻纤维。
一种防辐射抗菌面料，由如下重量份的物质制成：
10份金属微丝、30份竹纤维、15份草珊瑚纤维、55份苎麻纤维。
进一步的，所述金属微丝为银丝，直径为0.035~0.050mm。
一种防辐射抗菌面料的制备方法，包括如下步骤：
（1）将8~10份金属微丝和25~30份竹纤维进行并捻合股后得纬纱备用；
（2）将10~15份草珊瑚纤维和50~60份苎麻纤维进行并捻合股后得经纱备用；
（3）将上述经纱、纬纱进行混纺后得布匹备用；
（4）将所制布匹放于混合水溶液中浸渍20~30min，期间控制水温为40~45℃，再将其取出置于室温流水中冲洗15~20min，最后再对其进行定型烘烤即可。
进一步的，所述金属微丝为银丝，直径为0.035~0.050mm。
进一步的，步骤（1）所述纬纱的捻度为300~320捻/m。
进一步的，步骤（2）所述经纱的捻度为280~300捻/m。
进一步的，步骤（4）所述混合水溶液是质量分数为1~1.5%的净洗剂和质量分数为1~2%的柔软剂以体积比1:1混合而成，浸渍时布匹与混合水溶液的浴比为1:25。
本发明具有如下有益效果：利用金属微丝的金属屏蔽作用来起到防辐射效果，将其与竹纤维进行并捻后用作纬纱可提高织物的紧密性、光滑性和强度，而竹纤维内部的特殊超细微孔结构又具有较强的吸附能力，可以消除不良异味，此外还具有一定的抗菌、防辐射作用；草珊瑚纤维具有较强的抗菌功能，对金黄色葡萄球菌、大肠杆菌、白色念球菌等具有很好的抑制作用。本发明所用成分安全环保，取材广泛易得，制作方法简单方便，不仅具有较强的抗菌、防辐射效果，可将辐射剂量由2SV减少至100mSV以下，对金黄色葡萄球菌、大肠杆菌、白色念球菌等的抑菌率均在98%以上，又有较好的吸湿透气、除臭耐磨性能，可用作不同服饰的制作，使用范围广泛。
具体实施方式
实施例1
一种防辐射抗菌面料，由如下重量份的物质制成：
10份金属微丝、30份竹纤维、15份草珊瑚纤维、55份苎麻纤维。
一种防辐射抗菌面料的制备方法，包括如下步骤：
（1）将10份金属微丝和30份竹纤维进行并捻合股后得纬纱备用；
（2）将15份草珊瑚纤维和55份苎麻纤维进行并捻合股后得经纱备用；
（3）将上述经纱、纬纱进行混纺后得布匹备用；
（4）将所制布匹放于混合水溶液中浸渍25min，期间控制水温为40~45℃，再将其取出置于室温流水中冲洗18min，最后再对其进行定型烘烤即可。
进一步的，所述金属微丝为0.035mm。
进一步的，步骤（1）所述纬纱的捻度为310捻/m。
进一步的，步骤（2）所述经纱的捻度为280捻/m。
进一步的，步骤（4）所述混合水溶液是质量分数为1%的净洗剂和质量分数为1.5%的柔软剂以体积比1:1混合而成，浸渍时布匹与混合水溶液的浴比为1:25。
实施例2
一种防辐射抗菌面料，由如下重量份的物质制成：
8份金属微丝、26份竹纤维、10份草珊瑚纤维、60份苎麻纤维。
一种防辐射抗菌面料的制备方法，包括如下步骤：
（1）将8份金属微丝和26份竹纤维进行并捻合股后得纬纱备用；
（2）将10份草珊瑚纤维和60份苎麻纤维进行并捻合股后得经纱备用；
（3）将上述经纱、纬纱进行混纺后得布匹备用；
（4）将所制布匹放于混合水溶液中浸渍30min，期间控制水温为40~45℃，再将其取出置于室温流水中冲洗20min，最后再对其进行定型烘烤即可。
进一步的，所述金属微丝为0.050mm。
进一步的，步骤（1）所述纬纱的捻度为320捻/m。
进一步的，步骤（2）所述经纱的捻度为280捻/m。
进一步的，步骤（4）所述混合水溶液是质量分数为1.5%的净洗剂和质量分数为2%的柔软剂以体积比1:1混合而成，浸渍时布匹与混合水溶液的浴比为1:25。
将上述实施例所制面料采用国际标准ISO20743进行抗菌检测，结果显示如下：
实施例1产品对金黄葡萄球菌抑菌率99.2%，对大肠杆菌、白色念球菌抑菌率99.2%。
实施例2产品对金黄葡萄球菌抑菌率99.4%，对大肠杆菌、白色念球菌抑菌率99.3%。

Claims (7)

1.一种防辐射抗菌面料，其特征在于，由如下重量份的物质制成：
8~10份金属微丝、25~30份竹纤维、10~15份草珊瑚纤维、50~60份苎麻纤维。
2.一种防辐射抗菌面料，其特征在于，由如下重量份的物质制成：
10份金属微丝、30份竹纤维、15份草珊瑚纤维、55份苎麻纤维。
3.根据权利要求1所述的一种防辐射抗菌面料，其特征在于，所述金属微丝为银丝，直径为0.035~0.050mm。
4.一种如权利要求1所述的防辐射抗菌面料的制备方法，其特征在于，包括如下步骤：
（1）将8~10份金属微丝和25~30份竹纤维进行并捻合股后得纬纱备用；
（2）将10~15份草珊瑚纤维和50~60份苎麻纤维进行并捻合股后得经纱备用；
（3）将上述经纱、纬纱进行混纺后得布匹备用；
（4）将所制布匹放于混合水溶液中浸渍20~30min，期间控制水温为40~45℃，再将其取出置于室温流水中冲洗15~20min，最后再对其进行定型烘烤即可。
5.根据权利要求4所述的一种防辐射抗菌面料的制备方法，其特征在于，步骤（1）所述纬纱的捻度为300~320捻/m。
6.根据权利要求4所述的一种防辐射抗菌面料的制备方法，其特征在于，步骤（2）所述经纱的捻度为280~300捻/m。
7.根据权利要求4所述的一种防辐射抗菌面料的制备方法，其特征在于，步骤（4）所述混合水溶液是质量分数为1~1.5%的净洗剂和质量分数为1~2%的柔软剂以体积比1:1混合而成，浸渍时布匹与混合水溶液的浴比为1:25。
CN201510610156.6A 2015-09-23 2015-09-23 一种防辐射抗菌面料 Pending CN105297254A (zh)