CN105295769A - 含烯烃基桥联剂的反应型橡胶防水密封膏及其制备方法 - Google Patents

含烯烃基桥联剂的反应型橡胶防水密封膏及其制备方法 Download PDF

Info

Publication number
CN105295769A
CN105295769A CN201410330422.5A CN201410330422A CN105295769A CN 105295769 A CN105295769 A CN 105295769A CN 201410330422 A CN201410330422 A CN 201410330422A CN 105295769 A CN105295769 A CN 105295769A
Authority
CN
China
Prior art keywords
thickening
waterproof sealing
bridging agent
sealing compound
rubber latex
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410330422.5A
Other languages
English (en)
Inventor
卢桂才
朱方伍
伍盛江
郭文雄
周为为
赵晓岚
Original Assignee
卢桂才
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 卢桂才 filed Critical 卢桂才
Priority to CN201410330422.5A priority Critical patent/CN105295769A/zh
Publication of CN105295769A publication Critical patent/CN105295769A/zh
Pending legal-status Critical Current

Abstract

本发明旨在提供一种含烯烃基桥联剂的反应型橡胶防水密封膏及其制备方法,该防水密封膏包括合成橡胶胶乳、桥联剂。本发明的配方体系中加入了桥联剂,通过该桥联剂,防水密封膏中的橡胶能够与未固化的水泥或混凝土形成化学交联和物理卯榫协同粘结作用,将密封膏和水泥紧密地联结为一体,相关部位存在化学键作用,固化后起到不可逆的粘结作用,防水密封膏在水泥凝固的过程中可蠕动渗入到水泥凝胶和混凝土毛细孔内,达到结合紧密、牢固、不可逆的骨肉相连粘结效果。

Description

含婦炫基桥联剂的反应型橡胶防水密封實及其制备方法
技术领域
[0001] 本发明涉及一种密封防水领域,尤其涉及一种含帰姪基桥联剂的反应型橡胶防水 密封膏及其制备方法。
背景技术
[0002] 目前,在楼房厨卫间穿越楼板部位的PPR或PVC给排水管与混凝±楼板的线膨胀 系数相差很大,常温下混凝±为1*10 ,PPR或PVC管材为化~7) *10 ,经过几次 季节性冷热冻融循环后,给排水管与混凝±楼板连接处很容易出现缝隙,因此,楼房厨卫 间给排水管道施工时,穿越楼板部位PPR或PVC给排水管施工时,需要进行密封防水处理。 现有的密封防水处理技术有W下的几种方式:
[0003] 改性渐青密封处理,采用改性渐青在适宜温度下热烙之后进行德筑,该工艺施工 时操作复杂,温度控制与涂布工艺非常关键。首先,热烙渐青的时候温度控制要恰到好处, 如果温度太高,渐青流动性过好,会使得渐青无法粘附与PH?或PVC管材上,无法实现密封, 而且当温度超过IOOC时,容易损坏;如果温度太低,渐青与PPR或PVC管材、W及混凝±的 粘附性能都会达不到要求。第二是施工时手法要非常注意,涂布要非常均匀,往往要进行 数次W上的反复涂布,送是因为改性渐青与PH?或PVC管材、W及混凝±的粘附效果不够理 想,只有通过施工手法来进行弥补。
[0004] 渐青混合物密封膏处理,利用纯渐青、纤维物和溶剂的混合制备成密封膏,该密封 膏具有常温下成粘稠液体状态的性质,可W直接用于水泥和管道连接处的封涂,比如美国 亨利公司的班8®-WetPatch™牌子的屋面渗漏维修产品。该类密封膏,但是该类密封膏运 用了低挥发性的有机溶剂作为溶剂,干燥时间慢,往往需要两个星期W上的时间才能干燥, 而且在基面潮湿的情况下,因为无法与基面粘附,而不能施工;而且因为主要成分为渐青和 纤维物组成,干燥之后密封层没有弹性,强度较差,不够持久耐用。
[0005] 聚氨醋密封膏,W聚氨醋为主要成分,可在常温下直接使用,缺点是与PPR或PVC管材、W及混凝±的粘附效果不够理想,并且在基面潮湿时无法施工。
[0006] 娃丽密封胶,W娃酸钢和有机娃、娃丽结构聚合物等材料为主要成分,与PPR或PVC管材、W及混凝±的粘附效果较好,但是其稳定性差,在阳光照射或者潮湿状态下不能 持久,容易脱落,强度也较差,不能满足施工要求。
[0007] 聚丙帰酸树脂密封膏,W丙帰酸树脂类为主要成分,其制备工艺比较复杂,需要进 行高要求的改性,制备成水性丙帰酸树脂,然后制备成乳液。聚丙帰酸树脂密封膏可在潮湿 基面上施工,但是其与PPR或PVC管材、W及混凝±的粘附效果较差。
[0008] 综上所述,现有技术在穿越楼板部位的PPR或PVC给排水管施工时的密封处理技 术还存在诸多不足,急需找到一种制备工艺简单,施工方便,密封防水性能好,强度高,经久 耐用的新型防水密封产品。
发明内容
[0009] 本发明旨在提供一种含帰姪基桥联剂的反应型橡胶防水密封膏及其制备方法,该 防水密封膏制备工艺简单,施工方便,密封防水性能好,强度高,经久耐用。
[0010] 所述的防水密封膏,是由包括W下重量份数的原料制备而成的:
[0011] 合成橡胶胶乳 10~180 ;
[001引桥联剂 0.1~5;
[001引 增稠剂 0. 1~3 ;
[0014] 所述的桥联剂为帰基娃焼,帰姪基娃焼的一端与橡胶的不饱和C=C双键结合,另 一端与水泥水化后产生的酸根结合,架起一座防水材料的防水桥梁;
[0015] 其通式如下:
Figure CN105295769AD00051
[0016]
[0017]其中,
[001 引X为Cl、-0CnH2n4 或邸3;
[0019] n为0-10之间的自然数值。
[0020] 所述的合成橡胶胶乳的固含量为20% -80%。
[0021] 所述的合成橡胶胶乳为了苯橡胶胶乳、氯了橡胶胶乳、SBS橡胶胶乳、聚丙帰酸醋 类中的任一种或一种W上的混合物。
[0022] 建筑防水领域采用的橡胶,多为混合物的形式存在,因此,上述橡胶胶乳可W任何 比例进行混合运用。
[0023] 所述的桥联剂与混凝±的反应机理均一致,并且各桥联剂之间其化学性质也相 似,因此可W任何比例混合使用。
[0024] 所述的增稠剂是纤维素離及其衍生物、碱溶胀型增稠剂、聚氨醋增稠剂、疏水改性 非聚氨醋增稠剂、无机增稠剂、络合型有机金属化合物类增稠剂、聚丙帰醜胺、聚丙帰酸钢、 駿甲基纤维素钢、海藻酸钢中的一种或者一种W上的混合物。
[00巧]所述的纤维素離及其衍生物包括居己基纤维素、甲基居己基纤维素、己基居己基 纤维素、甲基居丙基纤维素、甲基纤维素、疏水改性纤维素、黄原胶、瓜尔胶。
[0026] 所述的碱溶胀型增稠剂包括非缔合型聚丙帰酸盐碱溶胀型乳液、缔合型聚丙帰酸 盐碱溶胀型乳液。
[0027] 所述的聚氨醋增稠剂和疏水改性非聚氨醋增稠剂包括阴离子型缔合聚氨醋增稠 剂、阳离子型缔合聚氨醋增稠剂、非离子型缔合聚氨醋增稠剂、疏水改性氨基增稠剂、疏水 改性聚離增稠剂、疏水改性聚脈增稠剂。
[0028] 所述的无机增稠剂包括膨润±、凹凸棒±、气相二氧化娃。
[0029] 所述的桥联剂优选为己帰基H甲氧基娃焼、己帰基H(目-甲氧基己氧基)娃焼、 己帰基二氯娃焼、己帰基二己氧基娃焼、己帰基二己酸基娃焼、二叔了氧基己帰基娃焼、己 帰基H叔了基过氧娃焼、帰丙基H甲氧基娃焼、帰丙基H己氧基娃焼、帰丙基H氯娃焼。
[0030] 所所述的防水密封膏,其生产方法包括W下步骤:将合成橡胶胶乳、桥联剂注入蓋 内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均匀。
[0031] 本发明的配方体系中加入了桥联剂,送一成分对于提升密封膏体系对混凝±的粘 接力起到了至关重要的作用,是本发明中核必技术之一,发明人经过了大量的筛选实验确 定了送些桥联剂成分。其原理如下:桥联剂中的帰基在反应蓋配料过程中,一定温度条件下 与橡胶中不饱和C=C双键发生反应,形成交联的网络连接结构,使橡胶分子间空间网络结 构更加牢靠稳固;同时由于混凝±是有石料与水泥共混固化而成,水泥水化后生成水化娃 酸巧(C-S-H凝胶)和氨氧化巧,表面含有大量的活性Si-OH基团及带负电的含氧无机化合 物。本发明正是通过该桥联剂,将水泥和橡胶组成的密封膏桥联起来,形成牢固的密封防水 体系,从而获得了优异的防水效果。
[0032] 其反应机理如下:
[003引 1、与橡胶反应
Figure CN105295769AD00061
[00对其中
[0036]
Figure CN105295769AD00062
代表橡胶中的不饱和姪类。
[0037] 2、与混凝±反应
[0038]W娃酸盐水泥为例:
[0039] ①常温下水泥发生水化反应生成水化娃酸巧(C-S-H凝胶)和化(OH)2,C甜凝胶 中存在Si-OH基团,反应式;3Ca0 • Si〇2+nH2〇=xCa•Si〇2•yH2〇+(3-x)Ca(OH)2
[0040] ②胶层中的活性基团遇水水解:
Figure CN105295769AD00063
[0042] ⑨水解生成Si-OH基团与C甜凝胶中Si-OH基团反应生成離键,使水化娃酸巧凝 胶与卷材表面生成化学键而牢固粘结。反应如下:
Figure CN105295769AD00064
[0044] 所述的帰姪基娃焼的一端与铅酸水泥、硫铅酸水泥或铁铅酸水泥反应的机理也是 一样的。所述帰姪基娃焼的一端与橡胶的不饱和C=C双键结合,另一端与水泥水化后产 生的酸根结合。所述的水泥水化后产生的酸根是娃酸根、铅酸根、硫铅酸根或铁铅酸根。也 就是说,W上所述的帰姪基娃焼防水桥联剂,该桥联剂的结构式一端的帰基能够与橡胶的 不饱和C=C双键连接起来,形成较好的化学亲和力,而娃焼的另一端在加入水和水泥的混 凝±中,产生水化的化学键,与混凝±进行化学交联和物理卯釋协同粘结,将橡胶和水泥紧 密地联结为一体,相关部位存在化学键作用,固化后起到不可逆的粘结作用,可W做成防水 密封膏,其耐油性和耐屈挽性突出,且无毒,安全环保、无污染,在水泥、混凝±凝固的过程 中可蠕动渗入到水泥凝胶和混凝±毛细孔内,达到结合紧密、牢固、不可逆的骨肉相连粘结 效果。要想取走或剥离防水层,是很难做到的。
[0045] 本发明的帰姪基娃焼桥联剂在与水泥凝胶中的居基、離键与二氧化娃的偶联化合 物,不会造成对钢筋的损害。
[0046] 本发明运用了同时能够与橡胶和混凝±发生反应的桥联剂,制成的密封膏相比传 统产品,具有更好的混凝±粘结强度和抗剥离强度。
[0047] 本发明的配方体系可中采用较大量的增稠剂,运用增稠剂的主要目的是为了调整 产品粘稠度,使得反应型橡胶防水密封膏能够用于管根、立墙而不出现下滑、流挂等现象, 实现对PPR或PVC给排水管与混凝±楼板连接处良好的密封。
具体实施方式[004引 实施例1
[0049] 合成橡胶胶乳 IOkg;
[0050] 桥联剂 0. 3kg;
[00川增稠剂 0.化g;
[0052] 所述的合成橡胶胶乳为了苯橡胶胶乳;
[0053] 所述的桥联剂是己帰基二甲氧基娃焼。
[0054] 所述的增稠剂是纤维素離及其衍生物,具体为甲基居丙基纤维素;
[0055] 所述的合成橡胶胶乳的固含量为60% ;
[0056] 将合成橡胶胶乳、桥联剂注入反应蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽 拌均匀。
[0057] 实施例2
[0058] 合成橡胶胶乳 180kg;
[00则桥联剂 1.Okg;
[0060] 增稠剂 1. 4kg;
[0061] 所述的合成橡胶胶乳为SBS橡胶胶乳;
[0062] 所述的桥联剂是二叔了氧基己帰基娃焼;
[0063] 所述的增稠剂是聚氨醋增稠剂,具体为阳离子型缔合聚氨醋增稠剂;
[0064] 所述的合成橡胶胶乳的固含量为20% ;
[0065] 将合成橡胶胶乳、桥联剂注入反应蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽 拌均匀。
[0066] 实施例3
[0067] 合成橡胶胶乳 40kg;
[006引桥联剂 1.化邑;
[006引增稠剂 0. 3kg;
[0070] 所述的合成橡胶胶乳为氯了橡胶胶乳;
[0071] 所述的桥联剂是帰丙基H甲氧基娃焼;
[0072] 所述的增稠剂是碱溶胀型增稠剂,具体为非缔合型聚丙帰酸盐碱溶胀型乳液;
[0073] 所述的合成橡胶胶乳的固含量为30% ;
[0074] 将合成橡胶胶乳、桥联剂注入反应蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽 拌均匀。
[00巧]实施例4
[0076] 合成橡胶胶乳 70kg;
[0077] 桥联剂 1.化g ;
[007引增稠剂 0.化g ;
[0079] 所述的合成橡胶胶乳为了苯橡胶胶乳、氯了橡胶胶乳的混合物;
[0080] 所述的桥联剂是帰丙基H己氧基娃焼;
[0081] 所述的增稠剂是纤维素離及其衍生物,具体为居己基纤维素;
[0082] 所述的合成橡胶胶乳的固含量为40% ;
[0083] 将合成橡胶胶乳、桥联剂注入蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均 匀。
[0084] 实施例5
[0085] 合成橡胶胶乳 48kg;
[008引桥联剂 1. 9kg ;
[0087] 增稠剂 0. 8kg ;
[0088] 所述的合成橡胶胶乳聚丙帰酸醋胶乳;
[0089] 所述的桥联剂是帰丙基H氯娃焼;
[0090] 所述的增稠剂是纤维素離及其衍生物,具体为己基居己基纤维素与瓜尔胶的混合 物。
[0091] 所述的合成橡胶胶乳的固含量为50% ;
[0092] 将合成橡胶胶乳、桥联剂注入蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均 匀。
[0093] 实施例6
[0094] 合成橡胶胶乳 146kg ;
[009引桥联剂 3kg;
[009引增稠剂 1.化g;
[0097] 所述的合成橡胶胶乳为了苯橡胶和SBS橡胶胶乳的混合物;
[009引所述的桥联剂己帰基二甲氧基娃焼、己帰基二(目-甲氧基己氧基)娃焼、己帰基H氯娃焼、己帰基H己氧基娃焼的混合物;
[0099] 所述的增稠剂是碱溶胀型增稠剂,具体为非缔合型聚丙帰酸盐碱溶胀型乳液和缔 合型聚丙帰酸盐碱溶胀型乳液的混合物;
[0100] 所述的合成橡胶胶乳的固含量为60% ;
[0101] 将合成橡胶胶乳、桥联剂注入蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均 匀。
[0102] 实施例7
[0103] 合成橡胶胶乳 112kg;
[0104] 桥联剂 1.8kg;
[0105] 增稠剂 LOkg;
[0106] 所述的合成橡胶胶乳为聚丙帰酸醋胶乳;
[0107] 所述的桥联剂是己帰基H(目-甲氧基己氧基)娃焼、己帰基H氯娃焼、己帰基H 己氧基娃焼、己帰基H己酸基娃焼、H叔了氧基己帰基娃焼的混合物。
[010引所述的增稠剂是聚氨醋增稠剂,具体为非离子型缔合聚氨醋增稠剂、疏水改性氨 基增稠剂;
[0109] 所述的合成橡胶胶乳的固含量为70% ;
[0110] 将合成橡胶胶乳、桥联剂注入蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均 匀。
[0111] 实施例8
[0112] 合成橡胶胶乳 16kg;
[0113] 桥联剂 2.0kg;
[0114] 增稠剂 0.化g
[0115] 所述的合成橡胶胶乳为氯了橡胶胶乳和SBR橡胶胶乳的混合物;
[0116] 所述的桥联剂是己帰基H甲氧基娃焼、己帰基H(目-甲氧基己氧基)娃焼、己帰 基二氯娃焼、己帰基二己氧基娃焼、己帰基二己酸基娃焼、二叔了氧基己帰基娃焼的混合 物;
[0117] 所述的增稠剂是疏水改性聚離增稠剂;
[0118] 所述的合成橡胶胶乳的固含量为80% ;
[0119] 将合成橡胶胶乳、桥联剂注入蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均 匀。
[0120] 实施例9
[0121] 合成橡胶胶乳 25kg;
[0122] 桥联剂 1.化g;
[0123] 增稠剂 0.3kg;
[0124] 所述的合成橡胶胶乳为SBS橡胶胶乳和聚丙帰酸醋胶乳的混合物;
[01巧]所述的桥联剂是己帰基H己酸基娃焼、H叔了氧基己帰基娃焼、己帰基H叔了基 过氧娃焼、帰丙基二甲氧基娃焼、帰丙基二己氧基娃焼、帰丙基二氯娃焼的混合物;
[0126] 所述的增稠剂是络合型有机金属化合物类增稠剂;
[0127] 所述的合成橡胶胶乳的固含量为30% ;
[0128] 将合成橡胶胶乳、桥联剂注入蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均 匀。
[0129] 实施例10
[0130] 合成橡胶胶乳 129kg;
[0131] 桥联剂 1.化g;
[0132] 增稠剂 0.化g;
[0133] 所述的合成橡胶胶乳为了苯橡胶胶乳;
[0134] 所述的桥联剂是己帰基H氯娃焼、己帰基H己氧基娃焼的混合物;
[0135] 所述的增稠剂是聚丙帰酸钢;
[0136] 所述的合成橡胶胶乳的固含量为65% ;
[0137] 将合成橡胶胶乳、桥联剂注入蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均 匀。
[013引 实施例11
[0139] 合成橡胶胶乳IOkg;
[0140] 桥联剂 5kg;
[0141] 增稠剂 3kg;
[0142] 所述的合成橡胶胶乳为聚丙帰酸醋胶乳;
[0143] 所述的桥联剂是所述己帰基H己酸基娃焼、H叔了氧基己帰基娃焼、己帰基H叔 了基过氧娃焼的混合物。
[0144] 所述的增稠剂是气态二氧化娃;
[0145] 所述的合成橡胶胶乳的固含量为75% ;
[0146] 将合成橡胶胶乳、桥联剂注入蓋内,揽拌均匀后,将增稠剂加入蓋中,混合揽拌均 匀。
[0147] 实施例12
[014引本发明引入含有两种不同化学活性基团的桥联剂,其中一种基团能与水泥基面发 生化学交联作用,另外一种基团能与橡胶结合形成致密的空间网络结构,最终物理卯釋与 化学交联的协同作用,使防水材料能够与水泥或者混凝±基面紧密结合成统一整体,有效 克服传统二元结构粘结不牢固,冷热交替,干湿循环条件下易与基面剥离的缺陷,显著提高 防水材料的防水性能。同时,本发明的防水密封膏是为水性,因此可W在潮湿的基面施工, 使用方便快捷。
[0149] 产品性能
[0150] 产品由于既能与基面产生物理卯釋又能发生化学交联作用,因此与基面优异的粘 接效果是本产品的性能创新点。对比试验结果见表1 :
[0151] 表 1
[0152]
Figure CN105295769AD00111
[0153] 实施例13
[0154] 部分桥联剂加入密封膏体系后,具体防水参数对比,结果见表2 :
[0155] 表 2
Figure CN105295769AD00121
[0157] 在同等添加量前提下,在对材料与水泥基面粘结强度的基本一致,表明添加的桥 联剂在粘结方面也有同样的效应。而在不透水性能,低温性能,抗窜水性能方面有所提高, 尤其是在低温柔性及抗窜水性表现比较突出。经实验验证,加入新的桥联剂后能够改善材 料的耐水持久性。因为加入新功能助剂后,密封膏成型后变为结实具有弹性的密封层,并且 密封层内部为橡胶态,能有效阻挡水分子的进入或渗透,并具有憎水性能,因此在不透水W 及抗窜水性能方面比较优异。加入新桥联剂后,密封膏成型W橡胶态为主,橡胶本身在低温 性能方面具有优越性,所W密封膏的低温性能得到改善。

Claims (10)

1. 一种反应型橡胶防水密封膏,其特征在于,是由包括以下重量份数的原料制备而成 的: 合成橡胶胶乳 10~180 ; 桥联剂 0. 1~5 ; 增稠剂 0. 1~3 ; 所述的桥联剂为烯烃基硅烷,烯烃基硅烷的一端与橡胶的不饱和C=C双键结合,另一 端与水泥水化后产生的酸根结合,架起一座防水材料的防水桥梁; 其通式如下: 其中,
Figure CN105295769AC00021
X为Cl、-0CnH2n+1 或CH3; η为0-10之间的自然数值。
2. 根据权利要求1所述的反应型橡胶防水密封膏,其特征在于:所述的合成橡胶胶乳 的固含量为20% -80%。
3. 根据权利要求1所述的反应型橡胶防水密封膏,其特征在于:所述的合成橡胶胶乳 为丁苯橡胶胶乳、氯丁橡胶胶乳、SBS橡胶胶乳、聚丙烯酸酯类中的任一种或一种以上的混 合物。
4. 根据权利要求1所述的反应型橡胶防水密封膏,其特征在于:所述的增稠剂是纤维 素醚及其衍生物、碱溶胀型增稠剂、聚氨酯增稠剂、疏水改性非聚氨酯增稠剂、无机增稠剂、 络合型有机金属化合物类增稠剂、聚丙烯酰胺、聚丙烯酸钠、羧甲基纤维素钠、海藻酸钠中 的一种或者一种以上的混合物。
5. 根据权利要求4所述的反应型橡胶防水密封膏,其特征在于:所述的纤维素醚及其 衍生物包括羟乙基纤维素、甲基羟乙基纤维素、乙基羟乙基纤维素、甲基羟丙基纤维素、甲 基纤维素、疏水改性纤维素、黄原胶、瓜尔胶。
6. 根据权利要求4所述的反应型橡胶防水密封膏,其特征在于:所述的碱溶胀型增稠 剂包括非缔合型聚丙烯酸盐碱溶胀型乳液、缔合型聚丙烯酸盐碱溶胀型乳液。
7. 根据权利要求4所述的反应型橡胶防水密封膏,其特征在于:所述的聚氨酯增稠剂 和疏水改性非聚氨酯增稠剂包括阴离子型缔合聚氨酯增稠剂、阳离子型缔合聚氨酯增稠 剂、非离子型缔合聚氨酯增稠剂、疏水改性氨基增稠剂、疏水改性聚醚增稠剂、疏水改性聚 脲增稠剂。
8. 根据权利要求4所述的反应型橡胶防水密封膏,其特征在于:所述的无机增稠剂包 括膨润土、凹凸棒土、气相二氧化硅。
9. 根据权利要求1所述的反应型橡胶防水密封膏,其特征在于: 所述的桥联剂为乙烯基二甲氧基ϊΐ圭烧、乙烯基二(β_甲氧基乙氧基)ϊΐ圭烧、乙烯基二 氯硅烷、乙烯基三乙氧基硅烷、乙烯基三乙酸基硅烷、三叔丁氧基乙烯基硅烷、乙烯基三叔 丁基过氧5圭烧、稀丙基二甲氧基5圭烧、稀丙基二乙氧基5圭烧、稀丙基二氣5圭烧。
10.根据权利要求1-9任何一项所述的反应型橡胶防水密封膏,其特征在于,其生产方 法包括以下步骤:将合成橡胶胶乳、桥联剂注入釜内,搅拌均匀后,将增稠剂加入釜中,混合 搅拌均匀。
CN201410330422.5A 2014-07-12 2014-07-12 含烯烃基桥联剂的反应型橡胶防水密封膏及其制备方法 Pending CN105295769A (zh)