CN105249677B - Hair rotary broom and preparation method thereof in one kind - Google Patents

Hair rotary broom and preparation method thereof in one kind Download PDF

Info

Publication number
CN105249677B
CN105249677B CN201510651949.2A CN201510651949A CN105249677B CN 105249677 B CN105249677 B CN 105249677B CN 201510651949 A CN201510651949 A CN 201510651949A CN 105249677 B CN105249677 B CN 105249677B
Authority
CN
China
Prior art keywords
parts
rotary broom
slag
hair
inner tube
Prior art date
Application number
CN201510651949.2A
Other languages
Chinese (zh)
Other versions
CN105249677A (en
Inventor
杨传长
Original Assignee
安徽创业机电设备有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 安徽创业机电设备有限公司 filed Critical 安徽创业机电设备有限公司
Priority to CN201510651949.2A priority Critical patent/CN105249677B/en
Publication of CN105249677A publication Critical patent/CN105249677A/en
Application granted granted Critical
Publication of CN105249677B publication Critical patent/CN105249677B/en

Abstract

Field is produced and processed the present invention relates to rotary broom, more specifically to hair rotary broom and preparation method thereof in one kind, including inner tube and bristle, it is characterised in that described inner tube is made up of Treated By Modified Slag, described bristle includes the component of following parts by weight:90 100 parts of composite fibre, 0.5 1 parts of zinc stearate micro mists, 11 15 parts of phenolic resin, 12 parts of synthctic fat acid resins, 0.1 0.8 parts of zinc oxide ultra_fine powderses, 0.9 1.5 parts of antiagers, 12 parts of pigment, the present invention uses slag for raw material, solve the intractable problem of slag, ample resources is saved, using composite fibre so that obtained middle hairbrush capillary is small, neither too hard, nor too soft and excellent adsorption, lacquer painting texture is small after brushing, more uniformly, smoothly.

Description

Hair rotary broom and preparation method thereof in one kind

Technical field:

Field is produced and processed the present invention relates to rotary broom, more specifically to hair rotary broom and its preparation side in one kind Method.

Background technology:

Rotary broom, because rolling face scope is wide, so being most laborsaving, timesaving brushing tool, is especially connected after extension rod, can be light Metope eminence or ceiling are easily painted, but has the disadvantage the situation that easily produces paint vehicle splash, so the hair of rotary broom is not too short, But must be thin, so brushing out the paint film come just can feel exquisiteness;Rotary broom point becomes mildewed, three kinds of middle hair, undercoat, and it shows as rolling The length of cylinder bristle, rather than the thickness and length of roller in itself, bristle are generally divided into two kinds of wool and chemical fibre class.Different rollings Cylinder brush can brush different effects, and the roller that becomes mildewed can brush some tiny textures, there is concave-convex sense, be imitated similar to skin texture Really.Lacquer painting is than more uniform after undercoat Cylinder coating brush, and smoothly, without concave-convex sense, middle hair falls between.Rotary broom is to use mostly Wool, foamed plastics are made, and can be divided into paint cylinder brush, plucking rotary broom, terrace paint roller brush, flat painting rotary broom etc., mainly Large area paint rolling applying for building decoration engineering.And available for the various mixed paint of rolling are applied, such as:It is emulsion paint, antirust paint, inside and outside Wall coating, wallpaper paper glue etc..

The content of the invention:

The technical problems to be solved by the invention be to overcome existing technological deficiency provide it is a kind of in hair rotary broom and its Preparation method.

The technical problems to be solved by the invention are realized using following technical scheme:

Hair rotary broom in one kind, including inner tube and bristle, it is characterised in that described inner tube is made up of Treated By Modified Slag, described Bristle include the component of following parts by weight:90-100 parts of composite fibre, 0.5-1 parts of zinc stearate micro mists, 11-15 parts of phenolic aldehyde trees Fat, 1-2 parts of synthctic fat acid resins, 0.1-0.8 parts of zinc oxide ultra_fine powderses, 0.9-1.5 parts of antiagers, 1-2 parts of pigment.

Further, described Treated By Modified Slag is made up of the raw material of following parts by weight:80-90 parts of slags, 5-8 parts of hydroxides Sodium, 2-4 part potassium polyphposphate, 10-15 parts of polyacrylamides, 6-8 parts of polyether Glycols, 3-5 parts of castor oil, 6-8 parts of bentonites, 0.5-2 parts of iron oxide, 2-3 parts of zinc oxide, 1-2 parts of crosslinking agents.

Further, the preparation method of described Treated By Modified Slag is:First slag is worn into it is powdered, in drying nitrogen protection Under, slag powders, sodium hydroxide, polyphosphoric acid are put into the closed reactor equipped with thermometer, agitating device and reflux condenser Potassium, adds a certain amount of ethanol solution, is warming up to 70-80 DEG C of reaction half an hour, is cooled to 50-60 DEG C, adds polyacrylamide Amine is reacted 10 minutes, adds polyether Glycols and castor oil, reacts about 1.5 hours, and further reduction temperature is added to 45 DEG C Bentonite, iron oxide and zinc oxide, continue one hour of insulation reaction, are cooled to normal temperature, are eventually adding crosslinking agent and then filtering It is drying to obtain Treated By Modified Slag.

Further, described composite fibre includes 50-60 parts of cotton fibers, 5-6 parts of cocoanut fibers, 12-16 parts of chrysotiles Fiber, 20-30 part acetate fiber, 1-3 parts of regenerated celulose fibres.

A kind of preparation method of middle hair rotary broom, it is characterised in that comprise the following steps:

(1) Treated By Modified Slag is put into industrial furnace, melting is subsequently poured into mould, is reprocessed into inner tube pattern;

(2) by phenolic resin, synthetic fatty acid resin melting, surplus stock and composite fibre uniform stirring are added, so Reeled off raw silk from cocoons afterwards, hairbrush hair in being then made;

(3) middle hairbrush hair and inner tube are subjected to gluing connection using adhesive.

The present invention uses slag for raw material, solves the intractable problem of slag, has saved ample resources, fine using mixing Dimension causes obtained middle hairbrush capillary small, neither too hard, nor too soft and excellent adsorption, and lacquer painting texture is small after brushing, more uniformly, smoothly.

Embodiment:

In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below Specific embodiment is closed, the present invention is expanded on further.

Embodiment 1:Hair rotary broom in one kind, including inner tube and bristle, it is characterised in that described inner tube is by Treated By Modified Slag It is made, described bristle includes the component of following parts by weight:90 parts of composite fibre, 0.5 part of zinc stearate micro mist, 11 parts of phenolic aldehyde trees Fat, 1 part of synthctic fat acid resin, 0.1 part of zinc oxide ultra_fine powders, 0.9-1.5 parts of antiagers, 1 part of pigment.

Treated By Modified Slag is made up of the raw material of following parts by weight:80 parts of slags, 5 parts of sodium hydroxides, 2 parts of potassium polyphposphates, 10 parts Polyacrylamide, 6 parts of polyether Glycols, 3 parts of castor oil, 6 parts of bentonites, 0.5 part of iron oxide, 2 parts of zinc oxide, 1 part of crosslinking agent.

The preparation method of Treated By Modified Slag is:First slag is worn into it is powdered, under the protection of dry nitrogen, to equipped with temperature Input slag powders, sodium hydroxide, potassium polyphposphate, are added a certain amount of in the closed reactor of meter, agitating device and reflux condenser Ethanol solution, be warming up to 70 DEG C of reaction half an hours, be cooled to 50 DEG C, add polyacrylamide and react 10 minutes, add Polyether Glycols and castor oil, react about 1.5 hours, and further reduction temperature adds bentonite, iron oxide and oxidation to 45 DEG C Zinc, continues one hour of insulation reaction, is cooled to normal temperature, is eventually adding crosslinking agent and then filtration drying produces Treated By Modified Slag.

Composite fibre include 50 parts of cotton fibers, 5 parts of cocoanut fibers, 12 parts of chrysotile asbestos fibres, 20 parts of acetate fibers, 1 part again Raw cellulose fibre.

Embodiment 2:Hair rotary broom in one kind, including inner tube and bristle, it is characterised in that described inner tube is by Treated By Modified Slag It is made, described bristle includes the component of following parts by weight:100 parts of composite fibre, 1 part of zinc stearate micro mist, 15 parts of phenolic aldehyde trees Fat, 2 parts of synthctic fat acid resins, 0.8 part of zinc oxide ultra_fine powders, 1.5 parts of antiagers, 2 parts of pigment.

Treated By Modified Slag is made up of the raw material of following parts by weight:90 parts of slags, 8 parts of sodium hydroxides, 4 parts of potassium polyphposphates, 15 parts Polyacrylamide, 8 parts of polyether Glycols, 5 parts of castor oil, 8 parts of bentonites, 2 parts of iron oxide, 3 parts of zinc oxide, 2 parts of crosslinking agents.

The preparation method of Treated By Modified Slag is:First slag is worn into it is powdered, under the protection of dry nitrogen, to equipped with temperature Input slag powders, sodium hydroxide, potassium polyphposphate, are added a certain amount of in the closed reactor of meter, agitating device and reflux condenser Ethanol solution, be warming up to 80 DEG C of reaction half an hours, be cooled to 60 DEG C, add polyacrylamide and react 10 minutes, add Polyether Glycols and castor oil, react about 1.5 hours, and further reduction temperature adds bentonite, iron oxide and oxidation to 45 DEG C Zinc, continues one hour of insulation reaction, is cooled to normal temperature, is eventually adding crosslinking agent and then filtration drying produces Treated By Modified Slag.

Composite fibre include 60 parts of cotton fibers, 6 parts of cocoanut fibers, 16 parts of chrysotile asbestos fibres, 30 parts of acetate fibers, 3 parts again Raw cellulose fibre.

A kind of preparation method of middle hair rotary broom, it is characterised in that comprise the following steps:

(1) Treated By Modified Slag is put into industrial furnace, melting is subsequently poured into mould, is reprocessed into inner tube pattern;

(2) by phenolic resin, synthetic fatty acid resin melting, surplus stock and composite fibre uniform stirring are added, so Reeled off raw silk from cocoons afterwards, hairbrush hair in being then made;

(3) middle hairbrush hair and inner tube are subjected to gluing connection using adhesive.

The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (4)

1. hair rotary broom in one kind, including inner tube and bristle, it is characterised in that described inner tube is made up of Treated By Modified Slag, described Bristle includes the component of following parts by weight:90-100 parts of composite fibre, 0.5-1 parts of zinc stearate micro mists, 11-15 parts of phenolic aldehyde trees Fat, 1-2 parts of synthctic fat acid resins, 0.1-0.8 parts of zinc oxide ultra_fine powderses, 0.9-1.5 parts of antiagers, 1-2 parts of pigment;
The preparation method of above-mentioned middle hair rotary broom is prepared, is comprised the following steps:
(1) Treated By Modified Slag is put into industrial furnace, melting is subsequently poured into mould, is reprocessed into inner tube pattern;
(2) by phenolic resin, synthetic fatty acid resin melting, surplus stock and composite fibre uniform stirring, Ran Houjin are added Row reels off raw silk from cocoons, hairbrush hair in being then made;
(3) middle hairbrush hair and inner tube are subjected to gluing connection using adhesive.
2. hair rotary broom in one kind according to claim 1, it is characterised in that described Treated By Modified Slag is by following parts by weight Raw material composition:80-90 parts of slags, 5-8 parts of sodium hydroxides, 2-4 parts of potassium polyphposphates, 10-15 parts of polyacrylamides, 6-8 parts gather Ether dihydric alcohol, 3-5 part castor oil, 6-8 parts of bentonites, 0.5-2 parts of iron oxide, 2-3 parts of zinc oxide, 1-2 parts of crosslinking agents.
3. it is according to claim 2 it is a kind of in hair rotary broom, it is characterised in that the preparation method of described Treated By Modified Slag is: First slag is worn into it is powdered, under the protection of dry nitrogen, to closed anti-equipped with thermometer, agitating device and reflux condenser Answer and slag powders, sodium hydroxide, potassium polyphposphate are put into kettle, add a certain amount of ethanol solution, be warming up to 70-80 DEG C and react half Hour, 50-60 DEG C is cooled to, polyacrylamide is added and reacts 10 minutes, polyether Glycols and castor oil, reaction 1.5 are added Hour, further reduction temperature adds bentonite, iron oxide and zinc oxide to 45 DEG C, continues one hour of insulation reaction, cooling To normal temperature, it is eventually adding crosslinking agent and then filtration drying produces Treated By Modified Slag.
4. hair rotary broom in one kind according to claim 1, it is characterised in that described composite fibre includes 50-60 portions of cottons Fiber, 5-6 part cocoanut fiber, 12-16 parts of chrysotile asbestos fibres, 20-30 parts of acetate fibers, 1-3 parts of regenerated celulose fibres.
CN201510651949.2A 2015-10-08 2015-10-08 Hair rotary broom and preparation method thereof in one kind CN105249677B (en)