CN105247596B - A kind of method using synthetic resin film production brand mark and commecial label - Google Patents

A kind of method using synthetic resin film production brand mark and commecial label Download PDF

Info

Publication number
CN105247596B
CN105247596B CN201480011305.0A CN201480011305A CN105247596B CN 105247596 B CN105247596 B CN 105247596B CN 201480011305 A CN201480011305 A CN 201480011305A CN 105247596 B CN105247596 B CN 105247596B
Authority
CN
China
Prior art keywords
mentioned
synthetic resin
resin film
pattern
color
Prior art date
Application number
CN201480011305.0A
Other languages
Chinese (zh)
Other versions
CN105247596A (en
Inventor
朴世斗
Original Assignee
株式会社爱睦全球
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to KR10-2013-0109055 priority Critical
Priority to KR1020130109055A priority patent/KR101354577B1/en
Application filed by 株式会社爱睦全球 filed Critical 株式会社爱睦全球
Priority to PCT/KR2014/008252 priority patent/WO2015037866A1/en
Publication of CN105247596A publication Critical patent/CN105247596A/en
Application granted granted Critical
Publication of CN105247596B publication Critical patent/CN105247596B/en

Abstract

The present invention relates to a kind of method using synthetic resin film production brand mark and commecial label, it includes:Preparation has figure or the electroforming mould of pattern or the first step of mantle;Coat the second step of UV resins;Lay the third step for the lucite film that arrangement light can project;With pressure roller overlay the four steps of processing;Irradiate ultraviolet and harden the 5th step of UV resins;Peel off synthetic resin film and produce the 6th step of the film for possessing figure or pattern;The 7th step of metal coating is formed at the synthetic resin film back side;Formed for protecting metal coating and playing the 8th step of the function while the printing layer embodied for first time color that prevent light projection;Carry out laser marking and partly remove the printing layer and metal coating for being located at the synthetic resin film back side, so as to only expose the 9th step of the part for wanting second of color to embody;Carry out electron beam evaporation plating or printed using silk screen print method and form the tenth step of second of color embodied layers;Adhere to pressure sensitive adhesive double coated or spraying bonding bottoming agent the 11st step;It is cut by laser and exposes the 12nd step of brand mark and commecial label.

Description

A kind of method using synthetic resin film production brand mark and commecial label
Technical field
The present invention relates to a kind of brand mark and trade mark mark for being used to be attached on the electronic products such as mobile phone or household electrical appliance The preparation method of label, more particularly to one kind utilize synthetic resin film, and additional UV coatings, evaporation and laser processing technology etc., and The texture or pattern of metal can be embodied, and diversified color can be embodied, while can also be realized a variety of more The method using synthetic resin film production brand mark and commecial label of sample quality.
Background technology
Generally, on the various electronic products such as mobile phone or household electrical appliance, in order to represent producer and product, or in order to its He distinguishes product, and adheres to brand mark or commecial label etc..
Recently, widely use and rich and varied, graceful vivid metal sticker is embodied by metallicity texture, and greatly It is more to be made using electro-deposition modes such as plating or electroforming.
Also, it is directed to printing mark, trade mark or pattern etc. in metal sticker surface color, and further deepens to production Product or the vivid effort of producer.
It is difficult to embody so as to exist however, mainly having used steel plate as raw material when making metal sticker in the past Diversified color and the problem of varied product can not be mass produced.
It additionally, there are when being printed on the metal materials such as steel plate, it is impossible to which smooth print color is printed on metal material On the bad grade of color state and product quality decline the problem of.
And then if using common paster, then it is difficult to metal-like or pattern are embodied, it is a variety of more so as to want to embody The quality and product of sample will have sizable limitation.
On the other hand, as former first technology, there is Korean granted patent the 10-0930174th special with Korean granted Sharp No. 10-0669482 and many technologies of Korean granted patent 10-0900929 grades, but these will all propose with following The present invention had differences on engineering mode and application technology.
【Citation】
Korean granted patent announces No. 10-0930174
Korean granted patent announces No. 10-0669482
Korean granted patent announces No. 10-0900929
The content of the invention
The present invention be for solve the problems, such as it is above-mentioned before etc., and consider this point and work out, its object is to provide One kind utilize synthetic resin film, and additional UV coatings, is deposited and laser processing technology etc., and can embody metal texture or Pattern, and diversified color can be embodied while the utilization synthetic resin film system of varied quality can also be realized Make the method for brand mark and commecial label.
To achieve the above object it is a feature of the present invention that including:First step, prepare to have selected from rotated shape, ripple Any one in line, hologram, mark, grain pattern or the electroforming mould or soft of the two or more figures formed of combination or pattern Film;Second step, UV resins are coated above electroforming mould or mantle with above-mentioned figure or pattern;Third step, upper State above electroforming mould or mantle in the state of coating UV resins, the transparent synthesis tree that arrangement light can project is laid on mould Adipose membrane;Four steps, in the state of the above-mentioned synthetic resin film of placement arrangement above electroforming mould or mantle, pressed with pressure roller Patch processing;5th step, irradiate ultraviolet on the semi-finished product Jing Guo above-mentioned four steps and harden UV resins;6th step, Synthetic resin film is peeled off on above-mentioned electroforming mould or mantle, and produces on synthetic resin film to possess and is formed by UV resins Figure or pattern film;7th step, in the synthetic resin film for possessing the figure formed by above-mentioned UV resins or pattern The back side, form metal coating;8th step, printed below the semi-finished product provided with above-mentioned metal coating, and formed and be used for Protection metal coating simultaneously plays the function of preventing light projection while the printing layer embodied for first time color;9th step is right Possess the semi-finished product of above-mentioned printing layer, in order to which second of color embodies and is used as pre-treatment step progress laser marking, and part The printing layer and metal coating for being located at the synthetic resin film back side are removed, so as to only expose the part for wanting second of color to embody; Tenth step, to the semi-finished product Jing Guo above-mentioned 9th step, carry out electron beam evaporation plating at the synthetic resin film back side or utilize silk screen Print process is printed, and forms second of color embodied layers;11st step, to the semi-finished product Jing Guo above-mentioned tenth step, At the back side provided with second of color embodied layers, attachment is pressure sensitive adhesive double coated or spraying bonds bottoming agent;12nd step, to by above-mentioned The semi-finished product of tenth step, it is cut by laser and exposes brand mark and commecial label.
Be preferably, above-mentioned metal coating can be using physical vaporous deposition (PVD), chemical vapour deposition technique (CVD), What any one in the dry process engineering such as metallikon formed.
Be preferably, above-mentioned synthetic resin film can be selected from PET (PET), makrolon (PC), It is any one in polymethyl methacrylate (PMMA), cyclic olefine copolymer (COC), polyvinyl chloride (PVC), polyimides (PI) Kind.
According to the present invention, using synthetic resin film, and UV coatings, evaporation and laser processing technology etc. are added, it becomes possible to body Reveal the texture and/or pattern of metal, and the product of varied quality can be made by embodying diversified color Board mark and commecial label, so as to which beneficial effect can be realized.
Even if the present invention reflects metal-like without using metal material, so as to embody the style of elegance, and can Image or pattern are embodied simultaneously on brand mark or commecial label, so as to increase graceful and aesthetic feeling, can be made varied The product of quality, large-scale production efficiency is also improved, so as to which beneficial effect can be realized.
Brief description of the drawings
Fig. 1 is to illustrate according to embodiments of the present invention to utilize synthetic resin film production brand mark and commecial label Method and the block flow diagram illustrated.
Fig. 2 a to Fig. 2 k are to illustrate utilization synthetic resin film production brand mark and business according to embodiments of the present invention The process chart marked the method for label and illustrated.
Fig. 3 is the figure for the engineering example for illustrating another embodiment of the present invention.
Reference
1:Mould 2:UV resins
3:Synthetic resin film 4:Pressure roller
5:Metal coating 6:Printing layer
7:Second of color embodied layers 100:Brand mark and commecial label
Embodiment
It is as follows to be described with reference to the preferred embodiments of the present invention, by being described in detail as follows, it will definitely manage Solve the purpose of the present invention and structure and its feature.
Reference picture 1, Fig. 2 a to Fig. 2 k, illustrate it is according to embodiments of the present invention using synthetic resin film production brand mark and The method of commecial label is as follows.
As shown in Figure 2 a, prepare to have such as rotated shape (Cyclotron) or ripple (ripples shape) or hologram (interference bar Line) etc. various patterns or figure needed for client mould 1- steps S1.
Now, it is the precision and fineness that improve pattern in above-mentioned mould 1, using passing through electroforming (electro Forming) the electroforming mould of processing and fabricating is preferred, and for the pressure of thrifty manufacturing cost, it is figuratum to may be used at tool Surface carries out the mantle of waterproof coating (silicon coating).
Here, the pattern formed on above-mentioned mould 1, is mostly used for improving visually beautiful and aesthetic feeling, and can using The moon is carved or Yang Ke or its combination, sometimes can also be without using pattern, and uses the figures such as mark or grain pattern.
Also, the patterns such as rotated shape, ripple, hologram, mark, grain pattern or figure, one kind of or group can be used Close two or more.
As shown in Figure 2 b, in the top for the mould 1 for possessing above-mentioned pattern, coating has ultraviolet (Ultra Violet) anti- Answer the UV resin 2- steps S2 of performance.
Now, transparent acrylic compounds or silicone-based materials can be used in above-mentioned UV resins, can be according to following synthetic resin The species of film is selectively applied.
As shown in Figure 2 c, in the state of coating UV resins above the mould 1 with above-mentioned pattern, pacify on mould 1 Put and arrange synthetic resin film 3- steps S3.
Now, the material that above-mentioned synthetic resin film 3 can preferentially be projected using transparent and light, it can be used and be selected from poly- terephthaldehyde Sour second diester (Poly Ethylene Terephthalate), makrolon (Poly Carbonate), poly-methyl methacrylate Ester (Poly Methyl Methacrylate), cyclic olefine copolymer (cyclone Olenfin Copolymer), polyvinyl chloride Any one in (Poly vinyl chloride), polyimides (Poly Imide).
The pattern being located on mould 1 is transferred here, above-mentioned synthetic resin film 3 mainly plays together with UV resins 2 Function.
As shown in Figure 2 d, in the state of laying above the mould 1 and arranging above-mentioned synthetic resin film 3, carried out by pressure roller 4 Overlay-step S4.
Equably transferred here, carrying out overlaying the pattern that can make to be located on mould 1 by pressure roller 4, and to make product more It is flat and carry out grade processing, also play the function that UV resins 2 and synthetic resin film 3 be combined with each other.
As shown in Figure 2 e, to progress above-mentioned steps S4 semi-finished product, irradiation ultraviolet is so that UV resins 2 harden-step S5.
As shown in figure 2f, synthetic resin film 3 is peeled off on above-mentioned mould 1, and is produced in synthetic resin film 3 above in conjunction with UV Resin 2 and formed possess figure or pattern pattern film-step S6.
Now, the pattern or figure being located on synthetic resin film 3, cloudy quarter is carried out according to the shape of pattern on mould 1, sun is carved Or it combines and formed.
As shown in Figure 2 g, in the back side entire surface of synthetic resin film 3 with the pattern formed by above-mentioned UV resins 2, Form metal coating 5- steps S7.
Now, above-mentioned metal coating 5 is preferentially using physical vaporous deposition (PVD), chemical vapour deposition technique (CVD), spray The dry process engineering such as plating method.
The diversified metal material such as gold, silver, chromium, nickel, copper can be used in above-mentioned metal coating 5, for being added to product Metal-like.
As shown in fig. 2h, printed, and formed for protecting metal below the semi-finished product provided with above-mentioned metal coating 5 Plated film and the printing layer 6- steps S8 for playing the function of preventing light projection.
Now, printing layer 6 prevents the function of light projection to play, preferentially using opaque materials such as black or whites, It is responsible for the function of improving the outside resolution of pattern, is additionally operable to the embodiment of first time color.
As shown in fig. 2i, to possessing on the semi-finished product of above-mentioned printing layer 6, in order to which second of color embodies and is used as pretreatment Step carries out laser marking, and part removes the printing layer 6 and metal coating 5 for being located at the back side of synthetic resin film 3, and only exposes Part-step the S9 for wanting second of color to embody.
Now, the UV resins 2 being located at before synthetic resin film 3 also can partly be removed.
Here, above-mentioned 9th step S9 is as shown in figure 3, can be without using laser marking, and carried out using silk screen print method Printing, etching, and part removes the printing layer 6 and metal coating 5 for being located at the back side of synthetic resin film 3, and only expose and want second The part that secondary color embodies.
As shown in figure 2j, to the semi-finished product by above-mentioned 9th step S9, the vacuum evaporations such as electron beam evaporation plating are utilized (vacuum evaporation) mode, is deposited at the back side of synthetic resin film 3 or is printed using silk screen print method, and Form second of color embodied layers 7- steps S10.
Now, above-mentioned second of color embodied layers 7 can form silver color, gold, black according to the demand of client by film shape Other diversified colors such as color, white.
Then, to the semi-finished product by above-mentioned tenth step S10, at the back side provided with second of color embodied layers 7, in order to Increase viscosity, and adhere to pressure sensitive adhesive double coated or spraying bonding bottoming agent-step S11.
Now, if spraying bonds bottoming agent, to protect its viscosity to adhere to inner membrance.
Finally, to being cut by laser by above-mentioned 11st step S11 semi-finished product, and brand is exposed as shown in Fig. 2 k Mark and commecial label and complete-step S12.
Here, above-mentioned brand mark and commecial label 100 can individually expose, the side that can also expose together as shown in the figure Formula forms.
Embodiment described above is the preferred embodiments of the present invention, and the present invention is not limited to these embodiments, according to Situation can carry out technical deformation, replacement or modification etc. in the technological thought and Claims scope of the present invention, these It should be considered to be encompassed in the range of the technology of the present invention.
The present invention reflects metal-like and/or pattern, and by diversified color, makes varied quality Brand mark and commecial label, the brand mark and commecial label made accordingly be applicable to the electronics such as mobile phone or household electrical appliance On product, and there is industrial application possibility.

Claims (4)

1. a kind of method using synthetic resin film production brand mark and commecial label, the brand mark and commecial label are used for It is attached on the electronic product selected from mobile phone or household electrical appliance, it is characterised in that this method includes:
First step, prepare with two kinds of any one in rotated shape, ripple, hologram, mark, grain pattern or combination The figure or the electroforming mould or mantle of pattern formed above;
Second step, UV resins are coated above electroforming mould or mantle with above-mentioned figure or pattern;
Third step, in the state of coating UV resins above above-mentioned electroforming mould or mantle, arrangement light is laid on mould The lucite film that can be projected;
Four steps, in the state of the above-mentioned synthetic resin film of placement arrangement above electroforming mould or mantle, pressed with pressure roller Patch processing;
5th step, irradiate ultraviolet on the semi-finished product Jing Guo above-mentioned four steps and harden UV resins;
6th step, synthetic resin film is peeled off on above-mentioned electroforming mould or mantle, and produce and possess on synthetic resin film The figure or the film of pattern formed by UV resins;
7th step, at the back side for the synthetic resin film for possessing the figure formed by above-mentioned UV resins or pattern, form metal Plated film;
8th step, printed, and formed for protecting metal coating simultaneously below the semi-finished product provided with above-mentioned metal coating Play the function of preventing light projection while the printing layer embodied for first time color;
9th step, to possessing the semi-finished product of above-mentioned printing layer, in order to which second of color embodies and it is used as pre-treatment step to carry out Laser marking, and part removes the printing layer and metal coating for being located at the synthetic resin film back side, will be second so as to only expose The part that color embodies;
Tenth step, to the semi-finished product Jing Guo above-mentioned 9th step, electron beam evaporation plating or utilization are carried out at the synthetic resin film back side Silk screen print method is printed, and forms second of color embodied layers;
11st step, to the semi-finished product Jing Guo above-mentioned tenth step, at the back side provided with second of color embodied layers, attachment two Face glue or spraying bonding bottoming agent;
12nd step, to the semi-finished product Jing Guo above-mentioned 11st step, it is cut by laser and exposes brand mark and trade mark Label.
2. the method according to claim 1 using synthetic resin film production brand mark and commecial label, its feature exists In,
Above-mentioned synthetic resin film is selected from PET (PET), makrolon (PC), polymethyl methacrylate (PMMA), any one in cyclic olefine copolymer (COC), polyvinyl chloride (PVC), polyimides (PI).
3. a kind of method using synthetic resin film production brand mark and commecial label, the brand mark and commecial label are used for It is attached on the electronic product selected from mobile phone or household electrical appliance, it is characterised in that this method includes:
First step, prepare with two kinds of any one in rotated shape, ripple, hologram, mark, grain pattern or combination The figure or the electroforming mould or mantle of pattern formed above;
Second step, UV resins are coated above electroforming mould or mantle with above-mentioned figure or pattern;
Third step, in the state of coating UV resins above above-mentioned electroforming mould or mantle, arrangement light is laid on mould The lucite film that can be projected;
Four steps, in the state of the above-mentioned synthetic resin film of placement arrangement above electroforming mould or mantle, pressed with pressure roller Patch processing;
5th step, irradiate ultraviolet on the semi-finished product Jing Guo above-mentioned four steps and harden UV resins;
6th step, synthetic resin film is peeled off on above-mentioned electroforming mould or mantle, and produce and possess on synthetic resin film The figure or the film of pattern formed by UV resins;
7th step, at the back side for the synthetic resin film for possessing the figure formed by above-mentioned UV resins or pattern, form metal Plated film;
8th step, printed, and formed for protecting metal coating simultaneously below the semi-finished product provided with above-mentioned metal coating Play the function of preventing light projection while the printing layer embodied for first time color;
9th step, to possessing the semi-finished product of above-mentioned printing layer, pass through in order to which second of color embodies and as pre-treatment step Silk screen print method is printed, etched, and part removes the printing layer and metal coating for being located at the synthetic resin film back side, so as to only Only expose the part for wanting second of color to embody;
Tenth step, to the semi-finished product Jing Guo above-mentioned 9th step, electron beam evaporation plating or utilization are carried out at the synthetic resin film back side Silk screen print method is printed, and forms second of color embodied layers;
11st step, to the semi-finished product Jing Guo above-mentioned tenth step, at the back side provided with second of color embodied layers, attachment two Face glue or spraying bonding bottoming agent;
12nd step, to the semi-finished product Jing Guo above-mentioned 11st step, it is cut by laser and exposes brand mark and trade mark Label.
4. the method using synthetic resin film production brand mark and commecial label according to claim 1 or 3, its feature It is,
Above-mentioned metal coating be use selected from physical vaporous deposition (PVD), chemical vapour deposition technique (CVD), metallikon it is dry Any one in formula processing engineering forms.
CN201480011305.0A 2013-09-11 2014-09-03 A kind of method using synthetic resin film production brand mark and commecial label CN105247596B (en)