CN105155744A - High-strength curtain wall - Google Patents
High-strength curtain wall Download PDFInfo
- Publication number
- CN105155744A CN105155744A CN201510643654.0A CN201510643654A CN105155744A CN 105155744 A CN105155744 A CN 105155744A CN 201510643654 A CN201510643654 A CN 201510643654A CN 105155744 A CN105155744 A CN 105155744A
- Authority
- CN
- China
- Prior art keywords
- parts
- curtain wall
- casting mold
- high strength
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-strength curtain wall, which sequentially comprises a base layer, a heat insulation layer, a reinforcing layer and a surface layer. The high-strength curtain wall has the advantages that a product can be enabled to have certain mechanical property through the base layer; the heat insulation performance of the curtain wall can be improved through the heat insulation layer; and meanwhile, the weight of the curtain wall can be reduced.
Description
Technical field
The present invention relates to a kind of high strength curtain wall, belongs to external wall field.
Background technology
In modern architecture, the ornamental exterior walls such as curtain wall, stone curtain wall, metal curtain wall define idiosyncrasy.Along with popularizing of this style, the favor of people to brick exterior wall is also day by day gone up, to make curtain wall and brick wall form rational collocation, avoids single vision.Curtain wall brick (being also clear water brick) arises at the historic moment in this case.Its outward appearance and material completely based on traditional brick, but are hollow structure, lightweight, pave rear outward appearance truly, not aging.Its producer produced increases increasingly.
Summary of the invention
A kind of high strength curtain wall, described curtain wall comprises basic unit successively, insulation layer, enhancement layer, surface layer,
Basic unit is cement 30-40 part, flyash 20-30 part, fine sand 20-30 part, hydrophobically modified hydroxyethyl guar gum 4-5 part, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms
Insulation layer is cement 50-60 part, silica 10-20 part, expanded perlite 15 parts, 10 parts, zeolite, 10 parts, kieselguhr, zirconium carbonate 5 parts, acetylacetone,2,4-pentanedione zirconium 3 parts, polyvinyl alcohol 1 part, after the mixing of 20 parts, water, basic unit carries out casting mold,
Enhancement layer is magnesium chloride 50-60 part, magnesia 30-40 part, Fluorspar Powder 10-20 part, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold,
Surface layer is epoxy resin 30-40 part, illite 10-20 part, vermiculite 10-20 part, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.
Described a kind of high strength curtain wall, basic unit is cement 30 parts, 20 parts, flyash, fine sand 20 parts, hydrophobically modified hydroxyethyl guar gum 4 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms.
Described a kind of high strength curtain wall, basic unit is cement 40 parts, 30 parts, flyash, fine sand 30 parts, hydrophobically modified hydroxyethyl guar gum 4-5 part, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms.
Described a kind of high strength curtain wall, basic unit is cement 35 parts, 25 parts, flyash, fine sand 25 parts, hydrophobically modified hydroxyethyl guar gum 4.5 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms.
Described a kind of high strength curtain wall, enhancement layer is 50 parts, magnesium chloride, 30 parts, magnesia, Fluorspar Powder 10 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold.
Described a kind of high strength curtain wall, enhancement layer is 60 parts, magnesium chloride, 40 parts, magnesia, Fluorspar Powder 20 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold.
Described a kind of high strength curtain wall, enhancement layer is 55 parts, magnesium chloride, 35 parts, magnesia, Fluorspar Powder 15 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold.
Described a kind of high strength curtain wall, surface layer is epoxy resin 30 parts, illite 10 parts, vermiculite 10 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.
Described a kind of high strength curtain wall, surface layer is epoxy resin 40 parts, illite 20 parts, vermiculite 20 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.
Described a kind of high strength curtain wall, surface layer is epoxy resin 35 parts, illite 15 parts, vermiculite 15 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.
A manufacture method for high strength curtain wall, described curtain wall comprises basic unit successively, insulation layer, enhancement layer, surface layer,
Basic unit is cement 30-40 part, flyash 20-30 part, fine sand 20-30 part, hydrophobically modified hydroxyethyl guar gum 4-5 part, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms
Insulation layer is cement 50-60 part, silica 10-20 part, expanded perlite 15 parts, 10 parts, zeolite, 10 parts, kieselguhr, zirconium carbonate 5 parts, acetylacetone,2,4-pentanedione zirconium 3 parts, polyvinyl alcohol 1 part, after the mixing of 20 parts, water, basic unit carries out casting mold,
Enhancement layer is magnesium chloride 50-60 part, magnesia 30-40 part, Fluorspar Powder 10-20 part, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold,
Surface layer is epoxy resin 30-40 part, illite 10-20 part, vermiculite 10-20 part, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.
Foregoing invention content is relative to the beneficial effect of prior art: 1) basic unit of high strength curtain wall of the present invention can ensure that product has certain mechanical property; 2) insulation layer can improve curtain wall heat-insulating property, can alleviate the quality of curtain wall, 3 simultaneously) enhancement layer effectively can ensure product mechanical strength needs; 4) surface layer be arranged so that curtain wall has good corrosion resistance performance.
Accompanying drawing explanation
Fig. 1 is high strength curtain wall schematic cross-section.
Detailed description of the invention
In order to there be understanding clearly to technical characteristic of the present invention, object and effect, now describe the specific embodiment of the present invention in detail.
A high strength curtain wall as shown in Figure 1, described curtain wall comprises basic unit 1 successively, insulation layer 2, enhancement layer 3, surface layer 4.
Embodiment 1
A kind of high strength curtain wall, described curtain wall comprises basic unit successively, insulation layer, enhancement layer, surface layer,
Basic unit is cement 30 parts, 20 parts, flyash, fine sand 20 parts, hydrophobically modified hydroxyethyl guar gum 4 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, and 16 parts, water mixes, and casting mold forms,
Insulation layer is cement 50 parts, 10 parts, silica, expanded perlite 15 parts, 10 parts, zeolite, 10 parts, kieselguhr, zirconium carbonate 5 parts, acetylacetone,2,4-pentanedione zirconium 3 parts, polyvinyl alcohol 1 part, after the mixing of 20 parts, water, basic unit carries out casting mold,
Enhancement layer is 50 parts, magnesium chloride, 30 parts, magnesia, Fluorspar Powder 10 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, carries out casting mold at insulation layer,
Surface layer is epoxy resin 30 parts, illite 10 parts, vermiculite 10 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, carries out casting mold at enhancement layer.
Embodiment 2
A kind of high strength curtain wall, described curtain wall comprises basic unit successively, insulation layer, enhancement layer, surface layer,
Basic unit is cement 40 parts, 30 parts, flyash, fine sand 30 parts, hydrophobically modified hydroxyethyl guar gum 5 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, and 16 parts, water mixes, and casting mold forms,
Insulation layer is cement 60 parts, 20 parts, silica, expanded perlite 15 parts, 10 parts, zeolite, 10 parts, kieselguhr, zirconium carbonate 5 parts, acetylacetone,2,4-pentanedione zirconium 3 parts, polyvinyl alcohol 1 part, after the mixing of 20 parts, water, basic unit carries out casting mold,
Enhancement layer is 60 parts, magnesium chloride, 40 parts, magnesia, Fluorspar Powder 20 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, carries out casting mold at insulation layer,
Surface layer is epoxy resin 40 parts, illite 20 parts, vermiculite 20 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, carries out casting mold at enhancement layer.
Embodiment 3
A kind of high strength curtain wall, described curtain wall comprises basic unit successively, insulation layer, enhancement layer, surface layer,
Basic unit is cement 35 parts, 25 parts, flyash, fine sand 25 parts, hydrophobically modified hydroxyethyl guar gum 4.5 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, and 16 parts, water mixes, and casting mold forms,
Insulation layer is cement 55 parts, 15 parts, silica, expanded perlite 15 parts, 10 parts, zeolite, 10 parts, kieselguhr, zirconium carbonate 5 parts, acetylacetone,2,4-pentanedione zirconium 3 parts, polyvinyl alcohol 1 part, after the mixing of 20 parts, water, basic unit carries out casting mold,
Enhancement layer is 55 parts, magnesium chloride, 35 parts, magnesia, Fluorspar Powder 15 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, carries out casting mold at insulation layer,
Surface layer is epoxy resin 35 parts, illite 15 parts, vermiculite 15 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, carries out casting mold at enhancement layer.
Embodiment 4
A kind of high strength curtain wall, described curtain wall comprises basic unit successively, insulation layer, enhancement layer, surface layer,
Basic unit is cement 32 parts, 21 parts, flyash, fine sand 23 parts, hydrophobically modified hydroxyethyl guar gum 4.4 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, and 16 parts, water mixes, and casting mold forms,
Insulation layer is cement 53 parts, 13 parts, silica, expanded perlite 15 parts, 10 parts, zeolite, 10 parts, kieselguhr, zirconium carbonate 5 parts, acetylacetone,2,4-pentanedione zirconium 3 parts, polyvinyl alcohol 1 part, after the mixing of 20 parts, water, basic unit carries out casting mold,
Enhancement layer is 51 parts, magnesium chloride, 32 parts, magnesia, Fluorspar Powder 14 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, carries out casting mold at insulation layer,
Surface layer is epoxy resin 34 parts, illite 13 parts, vermiculite 14 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, carries out casting mold at enhancement layer.
Embodiment 5
A kind of high strength curtain wall, described curtain wall comprises basic unit successively, insulation layer, enhancement layer, surface layer,
Basic unit is cement 36 parts, 26 parts, flyash, fine sand 27 parts, hydrophobically modified hydroxyethyl guar gum 4.8 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, and 16 parts, water mixes, and casting mold forms,
Insulation layer is cement 57 parts, 18 parts, silica, expanded perlite 15 parts, 10 parts, zeolite, 10 parts, kieselguhr, zirconium carbonate 5 parts, acetylacetone,2,4-pentanedione zirconium 3 parts, polyvinyl alcohol 1 part, after the mixing of 20 parts, water, basic unit carries out casting mold,
Enhancement layer is 57 parts, magnesium chloride, 39 parts, magnesia, Fluorspar Powder 19 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, carries out casting mold at insulation layer,
Surface layer is epoxy resin 38 parts, illite 19 parts, vermiculite 18 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, carries out casting mold at enhancement layer.
Claims (10)
1. a high strength curtain wall, described curtain wall comprises basic unit successively, insulation layer, enhancement layer, surface layer,
Basic unit is cement 30-40 part, flyash 20-30 part, fine sand 20-30 part, hydrophobically modified hydroxyethyl guar gum 4-5 part, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms
Insulation layer is cement 50-60 part, silica 10-20 part, expanded perlite 15 parts, 10 parts, zeolite, 10 parts, kieselguhr, zirconium carbonate 5 parts, acetylacetone,2,4-pentanedione zirconium 3 parts, polyvinyl alcohol 1 part, after the mixing of 20 parts, water, basic unit carries out casting mold,
Enhancement layer is magnesium chloride 50-60 part, magnesia 30-40 part, Fluorspar Powder 10-20 part, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold,
Surface layer is epoxy resin 30-40 part, illite 10-20 part, vermiculite 10-20 part, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.
2. a kind of high strength curtain wall as claimed in claim 1, basic unit is cement 30 parts, 20 parts, flyash, fine sand 20 parts, hydrophobically modified hydroxyethyl guar gum 4 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms.
3. a kind of high strength curtain wall as claimed in claim 1, basic unit is cement 40 parts, 30 parts, flyash, fine sand 30 parts, hydrophobically modified hydroxyethyl guar gum 4-5 part, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms.
4. a kind of high strength curtain wall as claimed in claim 1, basic unit is cement 35 parts, 25 parts, flyash, fine sand 25 parts, hydrophobically modified hydroxyethyl guar gum 4.5 parts, araboxylan 3 parts, methyl hydroxyethylcellulose 3 parts, citric acid 2 parts, adipic acid 2 parts, calcium thiosulfate 1 part, 16 parts, water mixes, and casting mold forms.
5. a kind of high strength curtain wall as claimed in claim 1, enhancement layer is 50 parts, magnesium chloride, 30 parts, magnesia, Fluorspar Powder 10 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold.
6. a kind of high strength curtain wall as claimed in claim 1, enhancement layer is 60 parts, magnesium chloride, 40 parts, magnesia, Fluorspar Powder 20 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold.
7. a kind of high strength curtain wall as claimed in claim 7, enhancement layer is 55 parts, magnesium chloride, 35 parts, magnesia, Fluorspar Powder 15 parts, montmorillonite powder 5 parts, 5 parts, gypsum, sulfamic acid 3 parts, 2 parts, copper sulphate, prodan 2 parts, after the mixing of 30 parts, water, insulation layer carries out casting mold.
8. a kind of high strength curtain wall as claimed in claim 1, surface layer is epoxy resin 30 parts, illite 10 parts, vermiculite 10 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.
9. a kind of high strength curtain wall as claimed in claim 1, surface layer is epoxy resin 40 parts, illite 20 parts, vermiculite 20 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.
10. a kind of high strength curtain wall as claimed in claim 1, surface layer is epoxy resin 35 parts, illite 15 parts, vermiculite 15 parts, 3 parts, curing compound, sodium dihydrogen phosphate 2 parts, after the mixing of 2 parts, calcium sulfate, calcium nitrite 1 part, enhancement layer carries out casting mold.