CN105133808A - Production method for fireproof and scrape-proof noctilucence wallpaper - Google Patents
Production method for fireproof and scrape-proof noctilucence wallpaper Download PDFInfo
- Publication number
- CN105133808A CN105133808A CN201510530591.8A CN201510530591A CN105133808A CN 105133808 A CN105133808 A CN 105133808A CN 201510530591 A CN201510530591 A CN 201510530591A CN 105133808 A CN105133808 A CN 105133808A
- Authority
- CN
- China
- Prior art keywords
- wallpaper
- coating
- noctilucence
- scratch resistant
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production method for fireproof and scrape-proof noctilucence wallpaper. The method comprises the following steps that firstly, a wallpaper base material is unwound and fed into a coating machine, noctilucence coating coats the base material, and cooling is performed after hot blast drying is performed; secondly, the base material is fed into a printing device for color and pattern printing, and cooling is performed after hot blast drying is performed; thirdly, heating is performed to soften the base material, an embossing wheel is used for pressing the fabric, and cooling is performed; fourthly, flame-retardant coating coats the material, and cooling is performed after hot blast drying is performed; fifthly, scrape-proof coating coats the material, and hot blast drying and cooling are performed to obtain the fireproof and scrape-proof noctilucence wallpaper. Compared with the prior art, the method is easy to implement and low in cost, the wallpaper produced through the method has the fireproof and scrape-proof functions while the appearance in the daytime and at night is ensured, and the service life of the wallpaper is greatly prolonged; the noctilucence coating can emit light at night or in dark environment, patterns and figures on the wallpaper can be seen at night, and the wallpaper is more attractive due to the fluorescent effect.
Description
Technical field
The present invention relates to wallpaper field, particularly relate to a kind of production method of scratch resistant noctilucence wallpaper of preventing fires.
Background technology
Wallpaper, also referred to as wallpaper, it is a kind of application house decorative material quite widely.The feature that other house decorative materials multiple such as color is various, pattern enriches because wallpaper has, luxurious style, safety and environmental protection, easy construction, affordable are incomparable, therefore obtain the universal of certain degree at developed countries and regions such as America and Europe, Southeast Asia, Japan.
In recent years, China's indoor decorating is persistently overheating, the wallpaper be once given the cold shoulder has come into parlor, bedroom, hotel, conference room etc. again with its gorgeous new attitude, and it, with himself attractive in appearance, fashion, individual character, generous, more and more becomes the favorite in current house ornament.
In the past, wallpaper comes into the life of people as just a kind of decorative material, people to its require many ornamental with aesthetic property above, but along with the raising of people's living standard, people need to want the wallpaper of high-quality to decorate the life of oneself, people's other Functional Requirement to wallpaper also gets more and more, such as: the aesthetic property of application life of wallpaper, fire resistance, night-environment.
Wallpaper is in the extensive use of the public place such as megastore, hotel, and the application in these places will inevitably cause the friction with other objects, can affect the attractive in appearance of wallpaper and life-span in friction process; Wallpaper is a kind of wall decorative material that base is made after printing, the base material of wallpaper is generally body paper, non-woven paper, non-woven fabrics, statecraft cloth, gauze or cotton, and these materials all have stronger inflammability, also bring certain potential safety hazard to user when practical application; Wallpaper is mainly used in room for human habitation, and the room user of being attractive in appearance does one's utmost to pursue, and common wallpaper cannot be viewed and admired in dark surrounds.
Summary of the invention
Object of the present invention is intended to overcome above-mentioned deficiency of the prior art, provides a kind of and produces production method that is simple, durable in use, the scratch resistant noctilucence wallpaper of charming fire prevention more attractive in appearance at night.
For solving above-mentioned technical problem, the present invention by the following technical solutions:
Prevent fires the production method of scratch resistant noctilucence wallpaper, it comprises the following steps:
A, wallpaper base material to be unreeled on the printer, send into coating machine, utilize coating machine luminescent coating to be coated on the surface of described wallpaper basic unit, then by hot-air seasoning, then cool, namely obtain coating semiproduct;
B, described coating semiproduct to be unreeled, send into printing equipment, the half-finished surface of described coating is carried out to the printing of design and color, and by hot-air seasoning, then cool, namely obtain printing semiproduct;
C, described printing semiproduct are carried out to heating and make it soften, after fabric is softening, utilizes embossed wheel to oppress fabric, produce corresponding embossing effect, then cool, namely obtain embossing semiproduct;
D, described embossing semiproduct are sent into second coating machine, anti-flaming dope is coated on the half-finished surface of described embossing, and by hot-air seasoning, then cool, namely obtain wallpaper semiproduct;
E, described wallpaper semiproduct are sent into the 3rd coating machine, by scratch resistant coatings on its surface, and by hot-air seasoning, then cool, namely obtain the scratch resistant noctilucence wallpaper of described fire prevention.
As a kind of preferred embodiment of the present invention, in step, described wallpaper base material is body paper, non-woven paper, non-woven fabrics, gauze or cotton dry again after fire retardant soaks.
As another kind of preferred embodiment of the present invention, in step, described luminescent coating is formed by luminescent powder and adhesive coating Homogeneous phase mixing, and the thickness of its coating is 0.1-0.3mm.
As another kind of preferred embodiment of the present invention, in step, described adhesive coating is 56: 24: 6: 6: 1 by weight ratio polyvinyl chloride, plasticizing agent, thinner, external lubricant and stabilizing agent Homogeneous phase mixing form.
As another kind of preferred embodiment of the present invention, in step C, thermoplastic temperature is 165-185 DEG C.
As another kind of preferred embodiment of the present invention, in step D, described anti-flaming dope is made up of magnalium hydrotalcite colloid.
As another kind of preferred embodiment of the present invention, in step D, the thickness of described anti-flaming dope coating is 0.1-0.2mm.
As another kind of preferred embodiment of the present invention, in step e, described anti-spread coated paint is that polyvinyl chloride, plasticizing agent, thinner, external lubricant and the stabilizing agent Homogeneous phase mixing being 56: 24: 6: 6: 1 by weight ratio forms, and thickness of its coating is 0.1-0.3mm.
As another kind of preferred embodiment of the present invention, in steps A, B, C, E, the temperature of hot-air seasoning is 170-180 DEG C.
As another kind of preferred embodiment of the present invention, in steps A, B, C, D, E, be all utilize recirculated water to cool, until return to normal temperature state.
Compared with prior art, the invention has the beneficial effects as follows:
The inventive method is simple to operate, cost is low, and the wallpaper utilizing it to produce in guarantee in the daytime, while night aesthetic property, also have the function that fire prevention is scratch resistant, substantially prolongs the application life of wallpaper; Luminescent coating is after being subject to the irradiations such as natural light, daylight light, ultraviolet light, luminous energy is stored, after stopping illumination penetrating, discharge in the mode of fluorescence lentamente again, still can be luminous in night or dark surrounds, duration reaches several little of tens hours, also can see the pattern on wallpaper and decorative pattern so at night, and add that fluorescent effect makes wallpaper more attractive in appearance.
The base material of wallpaper described in the present invention adopts body paper dry again after fire retardant soaks, non-woven paper, non-woven fabrics, gauze or cotton, can better play fireproof effect.
Have employed plasticizing agent and external lubricant in anti-spread coated paint in the present invention, make the wallpaper of final gained effectively can cushion external force under external force and play scratch resistant effect, and still keep original attractive in appearance after running into external force friction.
Detailed description of the invention
Be described principle of the present invention and feature below, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Embodiment 1
Prevent fires the production method of scratch resistant noctilucence wallpaper, it comprises the following steps:
A, by body paper dry again after fire retardant soaks, non-woven paper, non-woven fabrics, gauze or cotton unreel on the printer, send into coating machine, utilize coating machine that the luminescent coating by luminescent powder and adhesive coating Homogeneous phase mixing is coated on the surface of described wallpaper basic unit, the thickness of coating is 0.2mm, described adhesive coating is the polyvinyl chloride of 56: 24: 6: 6: 1 by weight ratio, plasticizing agent, thinner, external lubricant and stabilizing agent Homogeneous phase mixing form, again by the hot-air seasoning of 175 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely coating semiproduct are obtained,
B, described coating semiproduct to be unreeled, send into printing equipment, the half-finished surface of described coating is carried out to the printing of design and color, and pass through the hot-air seasoning of 175 DEG C, then utilize recirculated water to cool, until return to normal temperature state, namely obtain printing semiproduct;
C, be carry out heating to described printing semiproduct under the condition of 175 DEG C to make it soften in temperature, after fabric is softening, utilize embossed wheel to oppress fabric, produce corresponding embossing effect, then utilize recirculated water to cool, until return to normal temperature state, namely obtain embossing semiproduct;
D, described embossing semiproduct are sent into second coating machine, the anti-flaming dope be made up of magnalium hydrotalcite colloid is coated on the half-finished surface of described embossing, the thickness of coating is 0.15mm, and pass through the hot-air seasoning of 175 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely obtain wallpaper semiproduct;
E, described wallpaper semiproduct are sent into the 3rd coating machine, by by weight ratio be 56: 24: 6: 6: 1 polyvinyl chloride, plasticizing agent, thinner, external lubricant and stabilizing agent Homogeneous phase mixing scratch resistant coatings on its surface, the thickness of coating is 0.2mm, and pass through the hot-air seasoning of 175 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely obtain the scratch resistant noctilucence wallpaper of described fire prevention.
If print in step B of the present invention be starry sky pattern with star, the moon time, so under fluorescent effect, appreciate these patterns evening, can give people unusual sensation, make whole room look more attractive in appearance, more charming.
Embodiment 2
Prevent fires the production method of scratch resistant noctilucence wallpaper, it comprises the following steps:
A, by body paper dry again after fire retardant soaks, non-woven paper, non-woven fabrics, gauze or cotton unreel on the printer, send into coating machine, utilize coating machine that the luminescent coating by luminescent powder and adhesive coating Homogeneous phase mixing is coated on the surface of described wallpaper basic unit, the thickness of coating is 0.1mm, described adhesive coating is the polyvinyl chloride of 56: 24: 6: 6: 1 by weight ratio, plasticizing agent, thinner, external lubricant and stabilizing agent Homogeneous phase mixing form, again by the hot-air seasoning of 170 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely coating semiproduct are obtained,
B, described coating semiproduct to be unreeled, send into printing equipment, the half-finished surface of described coating is carried out to the printing of design and color, and pass through the hot-air seasoning of 170 DEG C, then utilize recirculated water to cool, until return to normal temperature state, namely obtain printing semiproduct;
C, be carry out heating to described printing semiproduct under the condition of 165 DEG C to make it soften in temperature, after fabric is softening, utilize embossed wheel to oppress fabric, produce corresponding embossing effect, then utilize recirculated water to cool, until return to normal temperature state, namely obtain embossing semiproduct.
D, described embossing semiproduct are sent into second coating machine, the anti-flaming dope be made up of magnalium hydrotalcite colloid is coated on the half-finished surface of described embossing, the thickness of coating is 0.1mm, and pass through the hot-air seasoning of 170 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely obtain wallpaper semiproduct;
E, described wallpaper semiproduct are sent into the 3rd coating machine, by by weight ratio be 56: 24: 6: 6: 1 polyvinyl chloride, plasticizing agent, thinner, external lubricant and stabilizing agent Homogeneous phase mixing scratch resistant coatings on its surface, the thickness of coating is 0.1mm, and pass through the hot-air seasoning of 170 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely obtain the scratch resistant noctilucence wallpaper of described fire prevention.
If print in step B of the present invention be starry sky pattern with star, the moon time, so under fluorescent effect, appreciate these patterns evening, can give people unusual sensation, make whole room look more attractive in appearance, more charming.
Embodiment 3
Prevent fires the production method of scratch resistant noctilucence wallpaper, it comprises the following steps:
A, by body paper dry again after fire retardant soaks, non-woven paper, non-woven fabrics, gauze or cotton unreel on the printer, send into coating machine, utilize coating machine that the luminescent coating by luminescent powder and adhesive coating Homogeneous phase mixing is coated on the surface of described wallpaper basic unit, the thickness of coating is 0.3mm, described adhesive coating is the polyvinyl chloride of 56: 24: 6: 6: 1 by weight ratio, plasticizing agent, thinner, external lubricant and stabilizing agent Homogeneous phase mixing form, again by the hot-air seasoning of 180 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely coating semiproduct are obtained,
B, described coating semiproduct to be unreeled, send into printing equipment, the half-finished surface of described coating is carried out to the printing of design and color, and pass through the hot-air seasoning of 180 DEG C, then utilize recirculated water to cool, until return to normal temperature state, namely obtain printing semiproduct;
C, be carry out heating to described printing semiproduct under the condition of 185 DEG C to make it soften in temperature, after fabric is softening, utilize embossed wheel to oppress fabric, produce corresponding embossing effect, then utilize recirculated water to cool, until return to normal temperature state, namely obtain embossing semiproduct.
D, described embossing semiproduct are sent into second coating machine, the anti-flaming dope be made up of magnalium hydrotalcite colloid is coated on the half-finished surface of described embossing, the thickness of coating is 0.2mm, and pass through the hot-air seasoning of 180 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely obtain wallpaper semiproduct;
E, described wallpaper semiproduct are sent into the 3rd coating machine, by by weight ratio be 56: 24: 6: 6: 1 polyvinyl chloride, plasticizing agent, thinner, external lubricant and stabilizing agent Homogeneous phase mixing scratch resistant coatings on its surface, the thickness of coating is 0.3mm, and pass through the hot-air seasoning of 180 DEG C, then recirculated water is utilized to cool, until return to normal temperature state, namely obtain the scratch resistant noctilucence wallpaper of described fire prevention.
If print in step B of the present invention be starry sky pattern with star, the moon time, so under fluorescent effect, appreciate these patterns evening, can give people unusual sensation, make whole room look more attractive in appearance, more charming.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (10)
1. a production method for the scratch resistant noctilucence wallpaper of fire prevention, it is characterized in that, it comprises the following steps:
A, wallpaper base material to be unreeled on the printer, send into coating machine, utilize coating machine luminescent coating to be coated on the surface of described wallpaper basic unit, then by hot-air seasoning, then cool, namely obtain coating semiproduct;
B, described coating semiproduct to be unreeled, send into printing equipment, the half-finished surface of described coating is carried out to the printing of design and color, and by hot-air seasoning, then cool, namely obtain printing semiproduct;
C, described printing semiproduct are carried out to heating and make it soften, after fabric is softening, utilizes embossed wheel to oppress fabric, produce corresponding embossing effect, then cool, namely obtain embossing semiproduct;
D, described embossing semiproduct are sent into second coating machine, anti-flaming dope is coated on the half-finished surface of described embossing, and by hot-air seasoning, then cool, namely obtain wallpaper semiproduct;
E, described wallpaper semiproduct are sent into the 3rd coating machine, by scratch resistant coatings on its surface, and by hot-air seasoning, then cool, namely obtain the scratch resistant noctilucence wallpaper of described fire prevention.
2. the production method of the scratch resistant noctilucence wallpaper of fire prevention according to claim 1, is characterized in that, in step, described wallpaper base material is body paper, non-woven paper, non-woven fabrics, gauze or cotton dry again after fire retardant soaks.
3. the production method of the scratch resistant noctilucence wallpaper of fire prevention according to claim 1, is characterized in that, in step, described luminescent coating is formed by luminescent powder and adhesive coating Homogeneous phase mixing, and the thickness of its coating is 0.1-0.3mm.
4. the production method of the scratch resistant noctilucence wallpaper of fire prevention according to claim 3, it is characterized in that, in step, described adhesive coating is 56: 24: 6: 6: 1 by weight ratio polyvinyl chloride, plasticizing agent, thinner, external lubricant and stabilizing agent Homogeneous phase mixing form.
5. the production method of the scratch resistant noctilucence wallpaper of fire prevention according to claim 1, is characterized in that, in step C, thermoplastic temperature is 165-185 DEG C.
6. the production method of the scratch resistant noctilucence wallpaper of fire prevention according to claim 1, is characterized in that, in step D, described anti-flaming dope is made up of magnalium hydrotalcite colloid.
7. the production method of the scratch resistant noctilucence wallpaper of fire prevention according to claim 6, is characterized in that, in step D, the thickness of described anti-flaming dope coating is 0.1-0.2mm.
8. the production method of the scratch resistant noctilucence wallpaper of fire prevention according to claim 1, it is characterized in that, in step e, described anti-spread coated paint is that polyvinyl chloride, plasticizing agent, thinner, external lubricant and the stabilizing agent Homogeneous phase mixing being 56: 24: 6: 6: 1 by weight ratio forms, and thickness of its coating is 0.1-0.3mm.
9. the production method of the scratch resistant noctilucence wallpaper of the fire prevention according to any one of claim 1-8, is characterized in that, in steps A, B, C, E, the temperature of hot-air seasoning is 170-180 DEG C.
10. the production method of the scratch resistant noctilucence wallpaper of the fire prevention according to any one of claim 1-8, is characterized in that, in steps A, B, C, D, E, is all utilize recirculated water to cool, until return to normal temperature state.