CN105110693A - 一种液体混凝土泵送膨胀剂 - Google Patents
一种液体混凝土泵送膨胀剂 Download PDFInfo
- Publication number
- CN105110693A CN105110693A CN201510474937.7A CN201510474937A CN105110693A CN 105110693 A CN105110693 A CN 105110693A CN 201510474937 A CN201510474937 A CN 201510474937A CN 105110693 A CN105110693 A CN 105110693A
- Authority
- CN
- China
- Prior art keywords
- component
- concrete
- pumping
- percent
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及了一种液体混凝土泵送膨胀剂,包括膨胀组份、溶胀组份、减缩组份、保水组份、泵送组份和功能组份;所述膨胀组份材料为无水硫酸铝、溶胀组份材料为聚乙烯醇、减缩组份材料为聚醚、保水组份材料为羟丙基纤维素醚、泵送组份材料为聚羧酸盐减水剂和功能组份材料为葡萄糖酸钠;所述组份百分含量比为:无水硫酸铝0.10%~0.18%、聚乙烯醇0.05%~0.10%、聚醚0.20%~0.60%、羟丙基纤维素醚0.08%~0.15%、聚羧酸盐减水剂0.40%~0.60%和葡萄糖酸钠0.04%~0.07%。该膨胀剂掺入混凝土中能有效增加混凝土的体积膨胀,减小混凝土体积收缩,从而提高混凝土的抗裂抗渗能力。
Description
技术领域
本发明涉及混凝土膨胀剂制作技术领域,具体为一种液体混凝土泵送膨胀剂。
背景技术
膨胀剂是一种化学外加剂,加在水泥中,当水泥凝结硬化时,随之体积膨胀,起补偿收缩和张拉钢筋产生预应力以及充分填充水泥间隙的作用;该膨胀剂在地下建筑物:如地铁、地下停车场、地下仓库、隧道、矿井、人防工程、基坑等、搅拌站等等;水池、游泳池、水塔、储罐、大型容器、粮仓、油罐、山洞内仓库等建筑时应用极为广泛;
目前,市场上使用的膨胀剂基本上都呈粉状,掺量一般都在8.0%以上,使用时往往需要人工计量和添加,在混凝土生产量较大时,由于每盘混凝土的搅拌时间较短,两盘之间的间隔时间最多只有约5分钟,而每盘混凝土的膨胀剂使用量在100kg以上,要在这么短的时间内,靠人工投入,要消耗很大的体力,既不能保证准确计量,也不能持续很长时间,所以,很不利于生产和推广使用,且市场上销售的粉状膨胀剂一般效果不佳,对于减小混凝土体积收缩效果不明显。
发明内容
本发明的目的在于提供一种液体混凝土泵送膨胀剂,它增加混凝土的体积膨胀,减小混凝土体积收缩,对于混凝土的抗裂抗渗能力提高具有显著效果。
为实现上述目的,本发明提供如下技术方案:一种液体混凝土泵送膨胀剂,包括膨胀组份、溶胀组份、减缩组份、保水组份、泵送组份和功能组份;所述膨胀组份材料为无水硫酸铝、溶胀组份材料为聚乙烯醇、减缩组份材料为聚醚、保水组份材料为羟丙基纤维素醚、泵送组份材料为聚羧酸盐减水剂和功能组份材料主要为葡萄糖酸钠等;所述组份百分含量比为:无水硫酸铝0.10%~0.18%、聚乙烯醇0.05%~0.10%、聚醚0.20%~0.60%、羟丙基纤维素醚0.08%~0.15%、聚羧酸盐减水剂0.40%~0.60%和葡萄糖酸钠0.04%~0.07%。
进一步,所述无水硫酸铝百分含量比优选为0.15%、聚乙烯醇0.07%、聚醚0.40%、羟丙基纤维素醚0.11%、聚羧酸盐减水剂0.50%和葡萄糖酸钠0.05%。
与现有技术相比,本发明的有益效果是:该膨胀剂掺入混凝土中能有效增加混凝土的体积膨胀,减小混凝土体积收缩,从而提高混凝土的抗裂抗渗能力。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
本发明提供一种技术方案:一种液体混凝土泵送膨胀剂,包括膨胀组份、溶胀组份、减缩组份、保水组份、泵送组份和功能组份;所述膨胀组份材料为无水硫酸铝、溶胀组份材料为聚乙烯醇、减缩组份材料为聚醚、保水组份材料为羟丙基纤维素醚、泵送组份材料为聚羧酸盐减水剂和功能组份材料为葡萄糖酸钠;所述组份百分含量比为:无水硫酸铝0.10%~0.18%、聚乙烯醇0.05%~0.10%、聚醚0.20%~0.60%、羟丙基纤维素醚0.08%~0.15%、聚羧酸盐减水剂0.40%~0.60%和葡萄糖酸钠0.04%~0.07%。
进一步,所述无水硫酸铝百分含量比优选为无水硫酸铝0.15%、聚乙烯醇0.07%、聚醚0.40%、羟丙基纤维素醚0.11%、聚羧酸盐减水剂0.50%和葡萄糖酸钠0.05%。
实施例一:
以制作100g液体混凝土泵送膨胀剂为例,
原料采用为:无水硫酸铝0.15g聚乙烯醇0.07g聚醚0.40g
羟丙基纤维素醚0.11g聚羧酸盐减水剂0.50g
葡萄糖酸钠0.05g和其他。
实施例二:
以制作100g液体混凝土泵送膨胀剂为例,
原料采用为:无水硫酸铝0.1g聚乙烯醇0.05g聚醚0.20g
羟丙基纤维素醚0.08g聚羧酸盐减水剂0.40g
葡萄糖酸钠0.04g和其他。
实施例三:
以制作100g液体混凝土泵送膨胀剂为例,
原料采用为:无水硫酸铝0.18g聚乙烯醇0.10g聚醚0.60g
羟丙基纤维素醚0.15g聚羧酸盐减水剂0.60g
葡萄糖酸钠0.07g和其他。
本发明实施例中:
无水硫酸铝:
硫酸铝(化学式Al2(SO4)3,式量342.15),白色斜方晶系结晶粉末,密度1.69g/cm3(25℃)。在造纸工业中作为松香胶、蜡乳液等胶料的沉淀剂,水处理中作絮凝剂,还可作泡沫灭火器的内留剂,制造明矾、铝白的原料,石油脱色、脱臭剂、某些药物的原料等。还可制造人造宝石及高级铵明矾。
第一大用途是用于造纸,第二大用途是在饮用水、工业用水和工业废水处理中做絮凝剂,大约占硫酸铝总产量40%。当向这类水中加入硫酸铝后,可以生成胶状的、能吸附和沉淀出细菌、胶体和其他悬浮物的氢氧化铝絮片。
聚乙烯醇:聚乙烯醇,有机化合物,白色片状、絮状或粉末状固体,无味。溶于水,不溶于汽油、煤油、植物油、苯、甲苯、二氯乙烷、四氯化碳、丙酮、醋酸乙酯、甲醇、乙二醇等。微溶于二甲基亚砜。聚乙烯醇是重要的化工原料,用于制造聚乙烯醇缩醛、耐汽油管道和维尼纶合成纤维、织物处理剂、乳化剂、纸张涂层、粘合剂、胶水等。
聚醚:聚醚又称聚乙二醇醚,是目前销售量最大的一种合成油。它是以环氧乙烷、环氧丙烷、环氧丁烷等为原料,在催化剂作用下开环均聚或共聚制得的线型聚合物。
羟丙基纤维素醚:羟丙基甲基纤维素,又名羟丙甲纤维素、纤维素羟丙基甲基醚,是选用高度纯净的棉纤维素作为原料,在碱性条件下经专门醚化而制得。在建筑上,作为水泥砂浆的保水剂、缓凝剂使砂浆具有泵送性。在抹灰浆、石膏料、腻子粉或其他的建材作为黏合剂,提高涂抹性和延长可操作时间。用作粘贴瓷砖、大理石、塑料装饰,粘贴增强剂,还可以减少水泥用量。HPMC的保水性能使浆料在涂抹后不会因干得太快而龟裂,增强硬化后强度。
聚羧酸盐减水剂:聚羧酸(盐)减水剂的分子是通过“分子设计”人为形成的“梳状”或“树枝状”结构,及在分子主链上接有许多个有一定长度和刚度的支链(侧链)。在主链上也有能使水泥颗粒带电的磺酸盐或其它基团,可以起到传统减水剂的作用,更重要的是一旦主链吸附在水泥颗粒表面后,支链与其它颗粒表面的支链形成立体交叉,阻碍了颗粒相互接近,从而达到分散(即减水)作用。这种空间位阻作用不以时间延长而弱化,因此,聚羧酸减水剂的分散作用更为持久。
葡萄糖酸钠:葡萄糖酸钠在工业上用途十分广泛,葡萄糖酸钠可以在建筑、纺织印染和金属表面处理以及水处理等行业作高效螯合剂,钢铁表面清洗剂,玻瓶清洗剂,电镀工业铝氧着色,在混凝土行业用作高效缓凝剂、高效减水剂等。
尽管已经示出和描述了本发明的实施例,对于本领域的普通技术人员而言,可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由所附权利要求及其等同物限定。
Claims (2)
1.一种液体混凝土泵送膨胀剂,包括膨胀组份、溶胀组份、减缩组份、保水组份、泵送组份和功能组份;其特征在于:所述膨胀组份材料为无水硫酸铝、溶胀组份材料为聚乙烯醇、减缩组份材料为聚醚、保水组份材料为羟丙基纤维素醚、泵送组份材料为聚羧酸盐减水剂和功能组份材料为葡萄糖酸钠;所述组份百分含量比为:无水硫酸铝0.10%~0.18%、聚乙烯醇0.05%~0.10%、聚醚0.20%~0.60%、羟丙基纤维素醚0.08%~0.15%、聚羧酸盐减水剂0.40%~0.60%和葡萄糖酸钠0.04%~0.07%。
2.根据权利要求1所述的一种液体混凝土泵送膨胀剂,其特征在于:所述无水硫酸铝百分含量比优选为0.15%、聚乙烯醇0.07%、聚醚0.40%、羟丙基纤维素醚0.11%、聚羧酸盐减水剂0.50%和葡萄糖酸钠0.05%。