CN105086669A - Plant purification interior wall latex paint capable of being scrubbed with hands and preparing method thereof - Google Patents
Plant purification interior wall latex paint capable of being scrubbed with hands and preparing method thereof Download PDFInfo
- Publication number
- CN105086669A CN105086669A CN201510473077.5A CN201510473077A CN105086669A CN 105086669 A CN105086669 A CN 105086669A CN 201510473077 A CN201510473077 A CN 201510473077A CN 105086669 A CN105086669 A CN 105086669A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- latex paint
- paint
- plant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plant purification interior wall latex paint capable of being scrubbed with hands. The plant purification interior wall latex paint is characterized in that the plant purification interior wall latex paint is prepared from, by weight, 9-12 parts of talcum powder, 5-7 parts of hydrophobic fumed silica, 25-33 parts of polyvinyl acetate emulsion, 5-7 parts of lactam, 1-2 parts of sodium hydroxide, 1-2 parts of monopotassium phosphate, 7-9 parts of quartz powder, 10-13 parts of silica powder, 4-6 parts of gelidium jelly, 2-3 parts of galactomannan, 6-8 parts of activated clay, 95-100 parts of water and 7-9 parts of mixed plant sizing agents. According to the plant purification interior wall latex paint, the hydrophobic fumed silica is added, the water resistance is improved, and the prepared latex paint is good in hardness, capable of being scrubbed with hands and not prone to falling off; the activated clay is added, the adsorption effect is achieved, and the purifying effect can be achieved; the mixed plant sizing agents are added, the paint smells fragrant and is safe, environment friendly, free of toxin and resistant to corrosion; the wall is very attractive after being coated with the paint, and the paint is very suitable for being used in public occasions with the requirement for the healthy and safe indoor environments.
Description
Technical field
The present invention relates to a kind of coating and preparation method thereof, plant purification interiro wall latex paint of particularly a kind of available hand scouring and preparation method thereof.
Background technology
Hydrophobicity aerosil chemical reaction is occurred by hydrophilic fumed silica and reactive silane (such as chlorosilane or hexamethyldisilazane) and is obtained.Except the above-mentioned advantage of wetting ability product, the feature of hydrophobicity aerosil product is: even if agent of low hygroscopicity, well dispersiveness also have stream to become regulating power for polar system.Can not be moistening by water institute unlike, hydrophobicity aerosil with hydrophilic silicon oxides.Although hydrophobicity aerosil density is greater than the density of water, on they can be bubbled through the water column.After hydrophobization, the amount of the moisture absorbed significantly can reduce than original wetting ability gas phase SiClx, such as in the air of relative humidity 80%, AEROSILR972 only adsorbs the water of 0.5%, and there is the hydrophilic fumed silica AEROSIL200 of identical specific surface area, its water regain can improve more than 10 times.
China is coating material production and consumption big country, but current domestic coating ubiquity the deficiency of aspect of performance, and such as suspension stability is poor, thixotropy is poor, weathering resistance is poor, abrasion resistance is poor, causes and needs a large amount of high-quality coating of import every year.Shanghai, Beijing, Hangzhou, some coating production enterprises on the ground such as Ningbo dare to be innovated, successfully achieve the application of aerosil in coating, this nanocomposite coatings changes the deficiency of product in the past, its main performance index is except contrast ratio is constant after testing, all the other all significantly improve, abrasion resistance as exterior coating brings up to more than 10,000 time by original more than 1,000 time, artificial acceleration weathering age and man-made radiation expose digestion time by (efflorescence 1 grade in original 250 hours, variable color 2 grades) bring up to 600 hours (without efflorescence, paint film is without variable color, value of chromatism 4.8), in addition film and body of wall bonding strength significantly improve, hardness of film significantly increases, clean surfaces ability is also improved.
Along with the development with emulsion paint technology that improves constantly of living standards of the people, healthy particularly important to people of indoor environment, especially the environment of public place enjoys people to pay close attention to, movement of population and the intensive places such as picture hospital, school, hotel, will regularly carry out disinfection in multicell, reduce bacteria breed, thus ensure that the air of people is healthy pure and fresh.
The present invention attempts to start with from emulsion paint, invent a kind of interiro wall latex paint, natural vegetable powder is made slurry and be combined with hydrophobicity aerosil, emulsion paint, not only there is fabulous hydrophobic performance, can scrubbing resistance, and smell pure and fresh, there is certain sterilization and health-care effect, be applicable to the place such as medical institutions, gymnasium use, and emulsion paint add plant constituent, there is natural pigment, not only healthy nontoxic, and color is simple and elegant, attractive in appearance.
Summary of the invention
The object of this invention is to provide plant purification interiro wall latex paint of a kind of available hand scouring and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
The plant purification interiro wall latex paint that available hand is cleaned, be made up of the raw material of following weight part: talcum powder 9-12, hydrophobicity aerosil 5-7, aqueous polyvinyl acetate emulsion 25-33, with lactan 5-7, sodium hydroxide 1-2, potassium primary phosphate 1-2, silica powder 7-9, silicon powder 10-13, agar-agar 4-6, polygalactomannan 2-3, atlapulgite 6-8, water 95-100, mixed plant slurry 7-9;
Described mixed plant slurry is prepared from by the raw material of following weight part: Stellera chamaejasme L. 2-3, root of Chinese wild ginger 2-3, santal 3-4, whole meal flour 3-5, mulberry leaf 3-5, Rose 1-2, rubber powder 1-2, atlapulgite 1-2, water 45-50; Preparation method is after Stellera chamaejasme L., the root of Chinese wild ginger, santal, mulberry leaf, Rose being cleaned up, and dry 3-5 hour at 60 DEG C-70 DEG C, is then ground into 300-500 object mixed powder; Then whole meal flour, rubber powder are put into water and stirred, be heated to 60 DEG C-80 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
The plant purification interiro wall latex paint that a kind of available hand of the present invention is cleaned, be made up of following concrete steps:
(1) with lactan, silicon powder heating in water bath to 80 DEG C-85 DEG C, 0.5-1 hour will be incubated while stirring, then be cooled to room temperature, slowly add aqueous polyvinyl acetate emulsion, stirring reaction 30-40 minute, stand-by;
(2) talcum powder, silica powder, atlapulgite are put into sand mill, grinding 1.5-2 hour, obtains 600-800 powder material, then adds all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 30-40 minute;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.
The invention has the beneficial effects as follows: the present invention adds hydrophobicity aerosil, improves water tolerance, the emulsion paint hardness made is good, and available hand is cleaned, difficult drop-off; Add atlapulgite, there is the effect of absorption, the effect of purification can be reached; Add mixed plant slurry, smell delicate fragrance, safety and environmental protection is nontoxic, corrosion-resistant, antibacterial, antiviral; Brush this product back wall very attractive in appearance, the public place being applicable to the healthy and safe indoor environment of needs uses.
Specific embodiments
Below by specific examples, the present invention is described in detail.
The plant purification interiro wall latex paint that available hand is cleaned, is made up of the raw material of following weight part (kilogram): talcum powder 9, hydrophobicity aerosil 5, aqueous polyvinyl acetate emulsion 25, with lactan 5, sodium hydroxide 1, potassium primary phosphate 1, silica powder 7, silicon powder 10, agar-agar 4, polygalactomannan 2, atlapulgite 6, water 95, mixed plant slurry 7;
Described mixed plant slurry is prepared from by the raw material of following weight part (kilogram): Stellera chamaejasme L. 2, the root of Chinese wild ginger 2, santal 3, whole meal flour 3, mulberry leaf 3, Rose 1, rubber powder 1, atlapulgite 1, water 45; Preparation method is after Stellera chamaejasme L., the root of Chinese wild ginger, santal, mulberry leaf, Rose being cleaned up, and dry 3-5 hour at 60 DEG C-70 DEG C, is then ground into 300-500 object mixed powder; Then whole meal flour, rubber powder are put into water and stirred, be heated to 60 DEG C-80 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
The plant purification interiro wall latex paint that a kind of available hand of the present invention is cleaned, be made up of following concrete steps:
(1) with lactan, silicon powder heating in water bath to 80 DEG C-85 DEG C, 0.5-1 hour will be incubated while stirring, then be cooled to room temperature, slowly add aqueous polyvinyl acetate emulsion, stirring reaction 30-40 minute, stand-by;
(2) talcum powder, silica powder, atlapulgite are put into sand mill, grinding 1.5-2 hour, obtains 600-800 powder material, then adds all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 30-40 minute;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.
This emulsion paint can adopt the form of construction work of roller coating to construct.The emulsion paint appearance of film obtained according to the method is normal, and be less than 2 hours time of drying, water-fast 96 hours without exception, and alkaline-resisting 48 hours without exception, and abrasion resistance is greater than 2000 times.
Claims (2)
1. the plant purification interiro wall latex paint of an available hand scouring, it is characterized in that, be made up of the raw material of following weight part: talcum powder 9-12, hydrophobicity aerosil 5-7, aqueous polyvinyl acetate emulsion 25-33, with lactan 5-7, sodium hydroxide 1-2, potassium primary phosphate 1-2, silica powder 7-9, silicon powder 10-13, agar-agar 4-6, polygalactomannan 2-3, atlapulgite 6-8, water 95-100, mixed plant slurry 7-9;
Described mixed plant slurry is prepared from by the raw material of following weight part: Stellera chamaejasme L. 2-3, root of Chinese wild ginger 2-3, santal 3-4, whole meal flour 3-5, mulberry leaf 3-5, Rose 1-2, rubber powder 1-2, atlapulgite 1-2, water 45-50; Preparation method is after Stellera chamaejasme L., the root of Chinese wild ginger, santal, mulberry leaf, Rose being cleaned up, and dry 3-5 hour at 60 DEG C-70 DEG C, is then ground into 300-500 object mixed powder; Then whole meal flour, rubber powder are put into water and stirred, be heated to 60 DEG C-80 DEG C, insulation adds all the other remaining components again, 15-20 minute is stirred under 800-1000 rev/min, be cooled to room temperature, finally add mixed powder, grind to form 600-800 order slurry.
2. the plant purification interiro wall latex paint of a kind of available hand scouring according to claim 1, is characterized in that, be made up of following concrete steps:
(1) with lactan, silicon powder heating in water bath to 80 DEG C-85 DEG C, 0.5-1 hour will be incubated while stirring, then be cooled to room temperature, slowly add aqueous polyvinyl acetate emulsion, stirring reaction 30-40 minute, stand-by;
(2) talcum powder, silica powder, atlapulgite are put into sand mill, grinding 1.5-2 hour, obtains 600-800 powder material, then adds all the other remaining components except mixed plant slurry, under 900-1000 rev/min of condition, stir 30-40 minute;
(3) by step (1) material and step (2) mixing of materials, add mixed plant slurry, dispersed with stirring evenly and get final product.