CN105086272A - PVC wood-plastic plate with termite-resisting function and for wall decoration - Google Patents

PVC wood-plastic plate with termite-resisting function and for wall decoration Download PDF

Info

Publication number
CN105086272A
CN105086272A CN201510530473.7A CN201510530473A CN105086272A CN 105086272 A CN105086272 A CN 105086272A CN 201510530473 A CN201510530473 A CN 201510530473A CN 105086272 A CN105086272 A CN 105086272A
Authority
CN
China
Prior art keywords
temperature
parts
wood
powder
termite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510530473.7A
Other languages
Chinese (zh)
Inventor
陈篯
孙维乐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Bei Ma Technology Co Ltd
Original Assignee
Anhui Bei Ma Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Bei Ma Technology Co Ltd filed Critical Anhui Bei Ma Technology Co Ltd
Priority to CN201510530473.7A priority Critical patent/CN105086272A/en
Publication of CN105086272A publication Critical patent/CN105086272A/en
Pending legal-status Critical Current

Abstract

The invention belongs to a PVC wood-plastic plate with a termite-resisting function and for wall decoration. The PVC wood-plastic plate is manufactured by, by weight, 30-40 parts of wood powder, 10-20 parts of butyl acrylate, 0.02-0.03 part of benzoyl peroxide, 0.01-0.02 part of N,N-dimethylaniline, 3-4 parts of polyethylene wax, 1-1.2 parts of dilauryl thiodipropionate, 1.5-2 parts of calcium stearate, 95-100 parts of polyvinyl chloride, 2-3 parts of AC foamer, 1-2 parts of cell regulator ACR530, 6-8 parts of chlorinated polyethylene, 0.5-0.7 part of pyrethrin, 3-4 parts of nano boehmite, 2-3 parts of high-boron calcium borate, 0.4-0.6 part of nano silver powder and 0.2-0.3 part of silane coupling agent kh570. The PVC wood-plastic plate is simple to manufacture, low in production cost, high in termite resistance and flame resistance, good in market prospect, long in service life and suitable for popularization and application in the field of building decoration.

Description

A kind of wall decoration pvc Wood plastic boards with termite-resisting function
Technical field
The present invention relates to Wood-plastic material technical field, particularly relate to a kind of wall decoration pvc Wood plastic boards with termite-resisting function.
Background technology
China is the country that a timber does not enrich, and underproducely causes the demand that can not meet market.Enhancing along with environmental consciousness and the protection to trees, wood plastic composite swarms into the visual field of people gradually, and Wood-plastic material is that one wood powder, xylon or other vegetable fibre fill thermoplastic polymer composite material, has the advantage of timber and plastics concurrently.According to the kind of thermoplastics used, can be divided into that PVC foam wood/plastic, ABS foaming wood-plastic, PS foaming wood-plastic, PE wood are moulded, PP wood is moulded, Wood-plastic material is because of advantages such as its environmental protection, shaping efficiency are high, the friendly of waterproof, good weatherability, environment, and development in recent years more and more sooner and be applied in each field widely.Although wood plastic composite has a good application prospect, due to more crisp, low impact property, there is higher density compared with natural timber and cause it to be restricted in application.In Wood-plastic material formula; add whipping agent and can prepare foaming wood-plastic goods with abscess; foaming wood-plastic goods are except possessing the feature of traditional wood plastic product; also there is the superperformances such as light weight, heat insulation, noise reduction; but mould formula carry out foaming as whipping agent directly added wood; wood-plastic products often can be uneven because of whipping agent dispersion, causes the problems such as cell size is uneven, product processes is unstable, greatly affect the application performance of goods.
Summary of the invention
The object of the invention is exactly the defect in order to make up prior art, provides a kind of wall decoration pvc Wood plastic boards with termite-resisting function.
The present invention is achieved by the following technical solutions:
A kind of wall decoration pvc Wood plastic boards with termite-resisting function, be made up of the raw material of following weight part: wood powder 30-40, butyl acrylate 10-20, benzoyl peroxide 0.02-0.03, N, accelerine 0.01-0.02, polyethylene wax 3-4, thiodipropionic acid dilauryl cinnamic acid ester 1-1.2, calcium stearate 1.5-2, polyvinyl chloride 95-100, AC whipping agent 2-3, cell modifiers ACR5301-2, chlorinatedpolyethylene 6-8, pyrethrin 0.5-0.7, nm boehmite 3-4, high boron lime borate 2-3, nano-silver powder 0.4-0.6, silane coupling agent kh5700.2-0.3,
Described a kind of wall decoration pvc Wood plastic boards with termite-resisting function, be made up of following concrete step:
(1) pyrethrin, nm boehmite, high boron lime borate and nano-silver powder are mixed, add silane coupling agent kh570 grinding distribution and evenly obtain mixed powder, again polyethylene wax is heated to melting, add Antioxidant DLTP, calcium stearate stirs, be coated on mixed powder surface, made particle for subsequent use;
(2) by wood powder the temperature range of 190-230 ° C in the heat treated of granularity between 20-60 order, by moisture controlled below 3%, being added to by dried wood powder has in the container of stirring rod, by butyl acrylate, benzoyl peroxide, N, accelerine mixes and is added in wood powder, control temperature is at 85-90 ° of C, and polyreaction 1-1.5h makes it homogenization, for subsequent use after cooling;
(3) polyvinyl chloride and chlorinatedpolyethylene are placed in the heating of acceleration mixing machine to mix, reduce temperature to the product adding step (1) during 110-115 ° of C and prepare, continue mixing and stirring, AC whipping agent is added and cell modifiers ACR530 is mixed to evenly when adjusting the temperature to 60-65 ° of C, add modified wood powder prepared by step (2) again to stir, temperature is controlled stop when 40-45 ° of C stirring to be dry blend;
(4) dry blend step (3) obtained is sent in forcing machine, wherein expressing technique is: district's temperature is 160-165 ° of C, two district's temperature are 175-185 ° of C, three district's temperature are 195-200 ° of C, four district's temperature are 190-195 ° of C, head temperature is 180-185 ° of C, and rotor speed is 35-40r/pm, and extrusion moulding can obtain wood plastic composite.
Advantage of the present invention is: the present invention adopts lubricant to carry out coated to blending ingredients, polyvinyl chloride is made to add minimizing generation in man-hour heat of friction, improve the stability of product and qualitative, and adopt calcium stearate to replace Pb stabilizer, can not only absorbing hydrogen chloride, add and play auxiliary stable effect man-hour, complexing can also be produced with polyvinyl chloride, produce the effect of lubrication, wood powder is also carried out dip treating by the present invention, solve vegetable fibre and pvc resin boundary surface compatibility problem, modified wood powder and resin boundary surface wettability, interfacial adhesion effect is better, improve the physical strength of matrix material, the pyrethrin added, nm boehmite, high boron lime borate and nano-silver powder cooperatively interact, great raising is to the defense reaction of termite, and have fire-retardant, the effects such as sterilization, preparation method of the present invention is simple, production cost is low, termite-proof property and good flame resistance, market outlook are good, long service life, be suitable for applying in building decoration field.
Embodiment
A kind of wall decoration pvc Wood plastic boards with termite-resisting function, be made up of the raw material of following weight part (kilogram): wood powder 30, butyl acrylate 10, benzoyl peroxide 0.02, N, N xylidine 0.01, polyethylene wax 3, thiodipropionic acid dilauryl cinnamic acid ester 1, calcium stearate 1.5, polyvinyl chloride 95, AC whipping agent 2, cell modifiers ACR5301, chlorinatedpolyethylene 6, pyrethrin 0.5, nm boehmite 3, high boron lime borate 2, nano-silver powder 0.4, silane coupling agent kh5700.2;
Described a kind of wall decoration pvc Wood plastic boards with termite-resisting function, be made up of following concrete step:
(1) pyrethrin, nm boehmite, high boron lime borate and nano-silver powder are mixed, add silane coupling agent kh570 grinding distribution and evenly obtain mixed powder, again polyethylene wax is heated to melting, add Antioxidant DLTP, calcium stearate stirs, be coated on mixed powder surface, made particle for subsequent use;
(2) by wood powder the temperature range of 190 ° Cs in the heat treated of granularity between 20 orders, by moisture controlled below 3%, being added to by dried wood powder has in the container of stirring rod, by butyl acrylate, benzoyl peroxide, N, N xylidine mixes and is added in wood powder, control temperature is at 85 ° of C, and polyreaction 1h makes it homogenization, for subsequent use after cooling;
(3) polyvinyl chloride and chlorinatedpolyethylene are placed in the heating of acceleration mixing machine to mix, product prepared by step (1) is added when reducing temperature to 110 ° C, continue mixing and stirring, AC whipping agent is added and cell modifiers ACR530 is mixed to evenly when adjusting the temperature to 60 ° of C, add modified wood powder prepared by step (2) again to stir, temperature is controlled stop when 40 ° of C stirring to be dry blend;
(4) dry blend step (3) obtained is sent in forcing machine, wherein expressing technique is: district's temperature is 160 ° of C, two district's temperature are 175 ° of C, three district's temperature are 195 ° of C, four district's temperature are 190 ° of C, head temperature is 180 ° of C, and rotor speed is 35r/pm, and extrusion moulding can obtain wood plastic composite.
According to wood plastic composite prepared by embodiment, carry out performance test to it, result is as follows:
Tensile strength is 33.45MPa, and shock strength is 7.19KJ/m2, and elongation at break is 3.46%, and flexural strength is at 16.9MPa, and water-intake rate is 0.64%, and percent thermal shrinkage is 0.59%.

Claims (2)

1. one kind has the wall decoration pvc Wood plastic boards of termite-resisting function, it is characterized in that, be made up of the raw material of following weight part: wood powder 30-40, butyl acrylate 10-20, benzoyl peroxide 0.02-0.03, N, accelerine 0.01-0.02, polyethylene wax 3-4, thiodipropionic acid dilauryl cinnamic acid ester 1-1.2, calcium stearate 1.5-2, polyvinyl chloride 95-100, AC whipping agent 2-3, cell modifiers ACR5301-2, chlorinatedpolyethylene 6-8, pyrethrin 0.5-0.7, nm boehmite 3-4, high boron lime borate 2-3, nano-silver powder 0.4-0.6, silane coupling agent kh5700.2-0.3.
2. a kind of wall decoration pvc Wood plastic boards with termite-resisting function according to claim 1, is characterized in that, be made up of following concrete step:
(1) pyrethrin, nm boehmite, high boron lime borate and nano-silver powder are mixed, add silane coupling agent kh570 grinding distribution and evenly obtain mixed powder, again polyethylene wax is heated to melting, add Antioxidant DLTP, calcium stearate stirs, be coated on mixed powder surface, made particle for subsequent use;
(2) by wood powder the temperature range of 190-230 ° C in the heat treated of granularity between 20-60 order, by moisture controlled below 3%, being added to by dried wood powder has in the container of stirring rod, by butyl acrylate, benzoyl peroxide, N, accelerine mixes and is added in wood powder, control temperature is at 85-90 ° of C, and polyreaction 1-1.5h makes it homogenization, for subsequent use after cooling;
(3) polyvinyl chloride and chlorinatedpolyethylene are placed in the heating of acceleration mixing machine to mix, reduce temperature to the product adding step (1) during 110-115 ° of C and prepare, continue mixing and stirring, AC whipping agent is added and cell modifiers ACR530 is mixed to evenly when adjusting the temperature to 60-65 ° of C, add modified wood powder prepared by step (2) again to stir, temperature is controlled stop when 40-45 ° of C stirring to be dry blend;
(4) dry blend step (3) obtained is sent in forcing machine, wherein expressing technique is: district's temperature is 160-165 ° of C, two district's temperature are 175-185 ° of C, three district's temperature are 195-200 ° of C, four district's temperature are 190-195 ° of C, head temperature is 180-185 ° of C, and rotor speed is 35-40r/pm, and extrusion moulding can obtain wood plastic composite.
CN201510530473.7A 2015-08-26 2015-08-26 PVC wood-plastic plate with termite-resisting function and for wall decoration Pending CN105086272A (en)