CN105040214B - The preparation technology of lousiness heavy twist anti-wrinkle fabric - Google Patents

The preparation technology of lousiness heavy twist anti-wrinkle fabric Download PDF

Info

Publication number
CN105040214B
CN105040214B CN201510524860.XA CN201510524860A CN105040214B CN 105040214 B CN105040214 B CN 105040214B CN 201510524860 A CN201510524860 A CN 201510524860A CN 105040214 B CN105040214 B CN 105040214B
Authority
CN
China
Prior art keywords
wool
dyeing
fabric
yarn
australian
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510524860.XA
Other languages
Chinese (zh)
Other versions
CN105040214A (en
Inventor
顾士清
倪成良
倪红明
葛立平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU NIJIAXIANG GROUP WORSTED TEXTILE Co.,Ltd.
Original Assignee
JIANGSU NIJIAXIANG GROUP WORSTED TEXTILE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU NIJIAXIANG GROUP WORSTED TEXTILE CO Ltd filed Critical JIANGSU NIJIAXIANG GROUP WORSTED TEXTILE CO Ltd
Priority to CN201510524860.XA priority Critical patent/CN105040214B/en
Publication of CN105040214A publication Critical patent/CN105040214A/en
Application granted granted Critical
Publication of CN105040214B publication Critical patent/CN105040214B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of preparation technology of lousiness heavy twist anti-wrinkle fabric, it is characterized in that, comprise the following steps that:(1)Australian high-n wool and mulberry silk are dyed respectively, silver mixing is carried out after dyeing, wool top is made;The dyeing of the Australian high-n wool uses lanasol dye, adds wool protective agent;The dyeing of the mulberry silk uses the grand dyestuff of vapour Bark, and part flushing is filled after dyeing, cleans the glauber salt of residual;(2)Wool top is made yarn, the number of yarn is 90S, the twist 1300;Again by yarn weaving into fabric;(3)Obtained fabric through dry, singly boil, bristle, cropping, dewing, high pressure steaming are handled, obtain described anti-wrinkle fabric.The present invention is formed using Australian high-n wool and mulberry silk blended union, and obtained fabric feel is smooth, and excellent spring, drapability is good, and wearability is good, has reached the requirement of easy nursing.

Description

The preparation technology of lousiness heavy twist anti-wrinkle fabric
Technical field
The present invention relates to a kind of anti-wrinkle fabric, especially a kind of preparation technology of lousiness heavy twist anti-wrinkle fabric, belong to weaving Fabric technical field.
Background technology
With the increasingly raising of people's living standard, diversified trend is also presented in consumption demand, and consumer is special to textile It is not that more and more higher is required to the quality of new textile, function etc..Now, people more advocate natural, comfortable, green ring The weaving face fabric of guarantor, therefore textile increasingly focuses on the use of raw material and the scientific and technological content of technique, traditional textile leads to Cross new technology processing and reach its brand-new vision and haptic effect.
The content of the invention
The purpose of the present invention is to overcome the deficiencies in the prior art, there is provided a kind of preparation of lousiness heavy twist anti-wrinkle fabric Technique, obtained fabric feel is smooth, and excellent spring, drapability is waitd upon, and wearability is good, has reached the requirement of easy nursing.
According to technical scheme provided by the invention, the preparation technology of the lousiness heavy twist anti-wrinkle fabric, it is characterized in that, including Following processing step:
(1)Australian high-n wool and mulberry silk are dyed respectively, it is after dyeing that 60%~75% Australia is high Branch wool and 25%~40% mulberry silk carry out silver mixing;Ribbon is made through gill box after silver mixing;Ribbon removes on combing machine Kink grain in relatively chopped fiber and fiber, the yarn of even thickness is made;Wool top is made in yarn after gill box again;
The dyeing of the Australian high-n wool is:0.1~6%o.w.f of lanasol dye, hair levelling agent 0.5 1~2%o.w.f of~2%o.w.f and wool protective agent, adjust Value in Dyeing Process 3~6, bath raio 1:10~20, dyeing temperature 40~60 DEG C processing 70~120 minutes;Fixation is carried out after dyeing, technique for fixing uses 0.6~20g/L alkaline agents, and pH value is 8~11, temperature For 20~50 DEG C, the time is 20~40 minutes;Neutralized after fixation with acid;
The dyeing of the mulberry silk is:Silk ball starts to dye in 25~30 DEG C of neutral environment, the grand dye of vapour Bark Material and glauber salt are gradually heating to 98 DEG C in 20~30min, are incubated 10~20min, are down to less than 80 DEG C and slowly add at twice Enter to add acetic acid, be to slowly warm up to 98 DEG C, part flushing is filled after insulation, clean the glauber salt of residual;
(2)By step(1)Obtained wool top is made yarn, and the number of yarn is 90S, the twist 1300;Yarn is knitted again Cause fabric;
(3)For obtained fabric through 100~105 DEG C of bakings, speed is 30~40m/min;Singly boil 10 at 80~90 DEG C again~ 20min;Cropping is carried out after carrying out the bristle of two forward one-reverses on brushing machine again;
(4)Fabric after cropping makes regain reach 8~10% through dewing;Enter horizontal high voltage steaming processing again, obtain described Anti-wrinkle fabric.
Further, the average fineness of the Australian high-n wool is 15~16 μm.
Further, the thread count of the fabric is 400 × 345/10cm, and grammes per square metre is 170~195 grams/m2
Further, the dry fracture strength of the mulberry silk is 3.0~3.5cN/dtex, wet breaking strength is 1.85~ 2.46cN/dtex, elastic restoration ratio are 50%~55%, 20 DEG C, hydroscopicity is 9~10% under conditions of relative humidity 65%.
Lousiness heavy twist anti-wrinkle fabric of the present invention is formed using Australian high-n wool and mulberry silk blended union, is adopted With the crease-resistant face design method of the easily nursing of innovation and postfinishing process, fabric feel is smooth, and excellent spring, drapability is good, takes Performance is good, has reached the requirement of easy nursing, is especially suitable for making high-grade linerless or half lining Business Casual western-style clothes.
Embodiment
With reference to specific embodiment, the invention will be further described.
Wool protective agent of the present invention can use the wool protective agent WSH of Ciba.
Embodiment one:A kind of preparation technology of lousiness heavy twist anti-wrinkle fabric, is comprised the following steps that:
(1)Australian high-n wool and mulberry silk that average fineness is 15 μm are dyed respectively, mulberry silk is done Fracture strength is 3.0cN/dtex, wet breaking strength 1.85cN/dtex, elastic restoration ratio 50%%, 20 DEG C, relative humidity Hydroscopicity is 9% under conditions of 65%;60% Australian high-n wool and 40% mulberry silk are subjected to silver mixing after dyeing;Passed through after silver mixing Ribbon is made in gill box;Ribbon removes the kink grain in relatively chopped fiber and fiber on combing machine, and even thickness is made Yarn;Wool top is made in yarn after gill box again;
The dyeing of the Australian high-n wool is:Lanasol dye 0.1%o.w.f, hair levelling agent 0.5% O.w.f and wool protective agent 1%o.w.f, adjust Value in Dyeing Process 3, bath raio 1:10,40 DEG C of dyeing temperature is handled 120 minutes;Dyeing After carry out fixation, technique for fixing uses 0.6g/L alkaline agents, pH value 8, and temperature is 20 DEG C, and the time is 40 minutes;With acid after fixation Neutralize;
The dyeing of the mulberry silk is:Silk ball starts to dye in 25 DEG C of neutral environment, the grand dyestuff of vapour Bark and Glauber salt is gradually heating to 98 DEG C in 20min, is incubated 10min, is down to less than 80 DEG C and is slowly added into addition acetic acid at twice, delays Slowly 98 DEG C are warming up to, part flushing is filled after insulation, clean the glauber salt of residual;
(2)By step(1)Obtained wool top is made yarn, and the number of yarn is 90S, the twist 1300;Yarn is knitted again Cause fabric;The thread count of the fabric is 400 × 345/10cm, and grammes per square metre is 170 grams/m2
(3)Obtained fabric is through 100 DEG C of bakings, speed 30m/min;Again 20min is singly boiled at 80 DEG C;Again on brushing machine Cropping is carried out after carrying out the bristle of two forward one-reverses;
(4)Fabric after cropping makes regain reach 8% through dewing;Enter horizontal high voltage steaming processing again, obtain described crease-resistant Fabric.
Embodiment two:A kind of preparation technology of lousiness heavy twist anti-wrinkle fabric, is comprised the following steps that:
(1)Australian high-n wool and mulberry silk that average fineness is 16 μm are dyed respectively, mulberry silk is done Fracture strength is 3.5cN/dtex, wet breaking strength 2.46cN/dtex, elastic restoration ratio 55%, 20 DEG C, relative humidity 65% Under conditions of hydroscopicity be 10%;75% Australian high-n wool and 25% mulberry silk are subjected to silver mixing after dyeing;Through pin after silver mixing Ribbon is made in comb;Ribbon removes the kink grain in relatively chopped fiber and fiber on combing machine, and the essence of even thickness is made Sliver;Wool top is made in yarn after gill box again;
The dyeing of the Australian high-n wool is:Lanasol dye 6%o.w.f, hair levelling agent 2%o.w.f With wool protective agent 2%o.w.f, Value in Dyeing Process 6, bath raio 1 are adjusted:20,60 DEG C of dyeing temperature is handled 70 minutes;Carried out after dyeing Fixation, technique for fixing use 20g/L alkaline agents, pH value 11, and temperature is 50 DEG C, and the time is 20 minutes;Neutralized after fixation with acid;
The dyeing of the mulberry silk is:Silk ball starts to dye in 30 DEG C of neutral environment, the grand dyestuff of vapour Bark and Glauber salt is gradually heating to 98 DEG C in 30min, is incubated 20min, is down to less than 80 DEG C and is slowly added into addition acetic acid at twice, delays Slowly 98 DEG C are warming up to, part flushing is filled after insulation, clean the glauber salt of residual;
(2)By step(1)Obtained wool top is made yarn, and the number of yarn is 90S, the twist 1300;Yarn is knitted again Cause fabric;The thread count of the fabric is 400 × 345/10cm, and grammes per square metre is 195 grams/m2
(3)Obtained fabric is through 105 DEG C of bakings, speed 40m/min;Again 10min is singly boiled at 90 DEG C;Again on brushing machine Cropping is carried out after carrying out the bristle of two forward one-reverses;
(4)Fabric after cropping makes regain reach 10% through dewing;Enter horizontal high voltage steaming processing again, obtain described crease-resistant Fabric.
Embodiment three:A kind of preparation technology of lousiness heavy twist anti-wrinkle fabric, is comprised the following steps that:
(1)Australian high-n wool and mulberry silk that average fineness is 15.7 μm are dyed respectively, mulberry silk Dry fracture strength is 3.2cN/dtex, wet breaking strength 2.26cN/dtex, elastic restoration ratio 52%, 20 DEG C, relative humidity Hydroscopicity is 9.5% under conditions of 65%;70% Australian high-n wool and 30% mulberry silk are subjected to silver mixing after dyeing;After silver mixing Ribbon is made through gill box;Ribbon removes the kink grain in relatively chopped fiber and fiber on combing machine, and even thickness is made Yarn;Wool top is made in yarn after gill box again;
The dyeing of the Australian high-n wool is:Lanasol dye 2%o.w.f, hair levelling agent 1%o.w.f With wool protective agent 1.5%o.w.f, Value in Dyeing Process 4, bath raio 1 are adjusted:15,50 DEG C of dyeing temperature is handled 100 minutes;Dye laggard Row fixation, technique for fixing use 10g/L alkaline agents, pH value 10, and temperature is 30 DEG C, and the time is 30 minutes;Neutralized after fixation with acid;
The dyeing of the mulberry silk is:Silk ball starts to dye in 26 DEG C of neutral environment, the grand dyestuff of vapour Bark and Glauber salt is gradually heating to 98 DEG C in 25min, is incubated 15min, is down to less than 80 DEG C and is slowly added into addition acetic acid at twice, delays Slowly 98 DEG C are warming up to, part flushing is filled after insulation, clean the glauber salt of residual;
(2)By step(1)Obtained wool top is made yarn, and the number of yarn is 90S, the twist 1300;Yarn is knitted again Cause fabric;The thread count of the fabric is 400 × 345/10cm, and grammes per square metre is 180 grams/m2
(3)Obtained fabric is through 102 DEG C of bakings, speed 35m/min;Again 15min is singly boiled at 85 DEG C;Again on brushing machine Cropping is carried out after carrying out the bristle of two forward one-reverses;
(4)Fabric after cropping makes regain reach 9% through dewing;Enter horizontal high voltage steaming processing again, obtain described crease-resistant Fabric.

Claims (3)

1. a kind of preparation technology of lousiness heavy twist anti-wrinkle fabric, it is characterized in that, comprise the following steps that:
(1)Australian high-n wool and mulberry silk that average fineness is 15 μm are dyed respectively, the dry fracture of mulberry silk Intensity is 3.0cN/dtex, wet breaking strength 1.85cN/dtex, elastic restoration ratio 50%, 20 DEG C, the bar of relative humidity 65% Hydroscopicity is 9% under part;60% Australian high-n wool and 40% mulberry silk are subjected to silver mixing after dyeing;Through gill box after silver mixing Ribbon is made;Ribbon removes the kink grain in relatively chopped fiber and fiber on combing machine, and the yarn of even thickness is made; Wool top is made in yarn after gill box again;
The dyeing of the Australian high-n wool is:Lanasol dye 0.1%o.w.f, hair levelling agent 0.5%o.w.f With wool protective agent 1%o.w.f, Value in Dyeing Process 3, bath raio 1 are adjusted:10,40 DEG C of dyeing temperature is handled 120 minutes;Carried out after dyeing Fixation, technique for fixing use 0.6g/L alkaline agents, pH value 8, and temperature is 20 DEG C, and the time is 40 minutes;Neutralized after fixation with acid;
The dyeing of the mulberry silk is:Silk ball starts to dye in 25 DEG C of neutral environment, and the grand dyestuff of vapour Bark and member are bright Powder is gradually heating to 98 DEG C in 20min, is incubated 10min, is down to less than 80 DEG C and is slowly added into addition acetic acid at twice, slowly rises Temperature fills part flushing to 98 DEG C after insulation, clean the glauber salt of residual;
(2)By step(1)Obtained wool top is made yarn, and the number of yarn is 90S, the twist 1300;Again by yarn weaving into Fabric;The thread count of the fabric is 400 × 345/10cm, and grammes per square metre is 170 grams/m2
(3)Obtained fabric is through 100 DEG C of bakings, speed 30m/min;Again 20min is singly boiled at 80 DEG C;Carried out again on brushing machine Cropping is carried out after the bristle of two forward one-reverses;
(4)Fabric after cropping makes regain reach 8% through dewing;Enter horizontal high voltage steaming processing again, obtain described anti-wrinkle fabric.
2. a kind of preparation technology of lousiness heavy twist anti-wrinkle fabric, it is characterized in that, comprise the following steps that:
(1)Australian high-n wool and mulberry silk that average fineness is 16 μm are dyed respectively, the dry fracture of mulberry silk Intensity is 3.5cN/dtex, wet breaking strength 2.46cN/dtex, elastic restoration ratio 55%, 20 DEG C, the bar of relative humidity 65% Hydroscopicity is 10% under part;75% Australian high-n wool and 25% mulberry silk are subjected to silver mixing after dyeing;Through gill box after silver mixing Ribbon is made;Ribbon removes the kink grain in relatively chopped fiber and fiber on combing machine, and the yarn of even thickness is made; Wool top is made in yarn after gill box again;
The dyeing of the Australian high-n wool is:Lanasol dye 6%o.w.f, hair are with levelling agent 2%o.w.f and sheep Hair protective agent 2%o.w.f, adjusts Value in Dyeing Process 6, bath raio 1:20,60 DEG C of dyeing temperature is handled 70 minutes;Consolidated after dyeing Color, technique for fixing use 20g/L alkaline agents, pH value 11, and temperature is 50 DEG C, and the time is 20 minutes;Neutralized after fixation with acid;
The dyeing of the mulberry silk is:Silk ball starts to dye in 30 DEG C of neutral environment, and the grand dyestuff of vapour Bark and member are bright Powder is gradually heating to 98 DEG C in 30min, is incubated 20min, is down to less than 80 DEG C and is slowly added into addition acetic acid at twice, slowly rises Temperature fills part flushing to 98 DEG C after insulation, clean the glauber salt of residual;
(2)By step(1)Obtained wool top is made yarn, and the number of yarn is 90S, the twist 1300;Again by yarn weaving into Fabric;The thread count of the fabric is 400 × 345/10cm, and grammes per square metre is 195 grams/m2
(3)Obtained fabric is through 105 DEG C of bakings, speed 40m/min;Again 10min is singly boiled at 90 DEG C;Carried out again on brushing machine Cropping is carried out after the bristle of two forward one-reverses;
(4)Fabric after cropping makes regain reach 10% through dewing;Enter horizontal high voltage steaming processing again, obtain described crease-resistant face Material.
3. a kind of preparation technology of lousiness heavy twist anti-wrinkle fabric, it is characterized in that, comprise the following steps that:
(1)Australian high-n wool and mulberry silk that average fineness is 15.7 μm are dyed respectively, the dry of mulberry silk is broken Resistance to spalling is 3.2cN/dtex, wet breaking strength 2.26cN/dtex, elastic restoration ratio 52%, 20 DEG C, relative humidity 65% Under the conditions of hydroscopicity be 9.5%;70% Australian high-n wool and 30% mulberry silk are subjected to silver mixing after dyeing;Through pin after silver mixing Ribbon is made in comb;Ribbon removes the kink grain in relatively chopped fiber and fiber on combing machine, and the essence of even thickness is made Sliver;Wool top is made in yarn after gill box again;
The dyeing of the Australian high-n wool is:Lanasol dye 2%o.w.f, hair are with levelling agent 1%o.w.f and sheep Hair protective agent 1.5%o.w.f, adjusts Value in Dyeing Process 4, bath raio 1:15,50 DEG C of dyeing temperature is handled 100 minutes;Consolidated after dyeing Color, technique for fixing use 10g/L alkaline agents, pH value 10, and temperature is 30 DEG C, and the time is 30 minutes;Neutralized after fixation with acid;
The dyeing of the mulberry silk is:Silk ball starts to dye in 26 DEG C of neutral environment, and the grand dyestuff of vapour Bark and member are bright Powder is gradually heating to 98 DEG C in 25min, is incubated 15min, is down to less than 80 DEG C and is slowly added into addition acetic acid at twice, slowly rises Temperature fills part flushing to 98 DEG C after insulation, clean the glauber salt of residual;
(2)By step(1)Obtained wool top is made yarn, and the number of yarn is 90S, the twist 1300;Again by yarn weaving into Fabric;The thread count of the fabric is 400 × 345/10cm, and grammes per square metre is 180 grams/m2
(3)Obtained fabric is through 102 DEG C of bakings, speed 35m/min;Again 15min is singly boiled at 85 DEG C;Carried out again on brushing machine Cropping is carried out after the bristle of two forward one-reverses;
(4)Fabric after cropping makes regain reach 9% through dewing;Enter horizontal high voltage steaming processing again, obtain described anti-wrinkle fabric.
CN201510524860.XA 2015-08-25 2015-08-25 The preparation technology of lousiness heavy twist anti-wrinkle fabric Active CN105040214B (en)