CN105018729A - 净化脱除硫酸锌溶液中硒和碲的复合添加剂及使用方法 - Google Patents

净化脱除硫酸锌溶液中硒和碲的复合添加剂及使用方法 Download PDF

Info

Publication number
CN105018729A
CN105018729A CN201510507680.0A CN201510507680A CN105018729A CN 105018729 A CN105018729 A CN 105018729A CN 201510507680 A CN201510507680 A CN 201510507680A CN 105018729 A CN105018729 A CN 105018729A
Authority
CN
China
Prior art keywords
solution
zinc sulfate
composite additive
tellurium
selenium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510507680.0A
Other languages
English (en)
Other versions
CN105018729B (zh
Inventor
罗永光
孙成余
曲洪涛
孙斯景
马云川
谢庭芳
王瑞山
罗凌燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yunnan Chihong Zinc and Germanium Co Ltd
Original Assignee
Yunnan Chihong Zinc and Germanium Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yunnan Chihong Zinc and Germanium Co Ltd filed Critical Yunnan Chihong Zinc and Germanium Co Ltd
Priority to CN201510507680.0A priority Critical patent/CN105018729B/zh
Publication of CN105018729A publication Critical patent/CN105018729A/zh
Application granted granted Critical
Publication of CN105018729B publication Critical patent/CN105018729B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及净化脱除硫酸锌溶液中硒和碲的复合添加剂及使用方法,属于冶金领域,其复合添加剂包括Al(OH)3、Al2O3、Fe(OH)3、KAl(SO4)2四种化合物;复合添加剂的使用方法为:用50-95℃、pH为1.2-3.5的酸性水溶液将复合添加剂进行溶解,将稀释后的溶液加入到硫酸锌溶液中,控制搅拌机转速70-160转/分钟进行搅拌,完成净化过程的硫酸锌溶液经过压滤装置进行过滤,得到合格的滤液,送下一步工序处理,滤渣另行处理。本发明通过向酸性硫酸锌溶液中加入复合添加剂,使复合添加剂中的氢氧化铝胶体和氢氧化铁胶体对溶液中硒和碲的酸根离子吸附,从而实现硫酸锌溶液中硒和碲的脱除,克服了目前湿法锌冶金过程中硒和碲尚无法深度净化的难题。

Description

净化脱除硫酸锌溶液中砸和碲的复合添加剂及使用方法
技术领域
[0001] 本发明属于冶金领域,具体地说,涉及净化脱除硫酸锌溶液中砸和碲的复合添加剂及使用方法。
背景技术
[0002] 在湿法锌冶炼中,硫酸锌溶液的pH为3.8-5.4条件,溶液中的砸和碲以酸根离子存在,采用常规现有的锌粉(金属锌粉、电炉锌粉、不含铝的合金锌粉)置换法不能将其除去,其他净化成本较高,在工业生产中不经济。
发明内容
[0003] 为了克服上述现有技术的不足,本发明提供了净化脱除硫酸锌溶液中砸和碲的复合添加剂及使用方法,能高效的去除酸性条件下硫酸锌溶液中的砸和碲,且生产成本低。
[0004] 为实现上述目的,本发明是通过如下技术方案实现的:
[0005] 净化脱除硫酸锌溶液中砸和碲的复合添加剂,复合添加剂的成分包括Al (0H)3、A1203、Fe (0H)3、KAl (SO4)2四种化合物,其中,Al的总含量为2.5-10%, Fe的总含量为10-20 %,其余成分为S、0、H。
[0006] 净化脱除硫酸锌溶液中砸和碲的复合添加剂的使用方法,具体步骤为:
[0007] I)用50_95°C、pH为L 2-3.5的酸性水溶液将复合添加剂进行溶解;
[0008] 2)按每m3硫酸锌溶液加入40-200L的加入量,将稀释后的复合添加剂溶液加入到硫酸锌溶液中,控制搅拌机转速70-160转/分钟,对溶液搅拌30-60分钟;
[0009] 3)完成净化过程的硫酸锌溶液经过压滤装置进行过滤,得到合格的滤液,送下一步工序处理,滤渣另行处理。
[0010] 作为优选,步骤2)中,硫酸锌溶液的pH值为2.5-5.4,含砸1.5_8mg/L,含碲4-15mg/L。
[0011 ] 作为优选,步骤2)中,控制溶液反应温度为55_92°C。
[0012] 本发明的有益效果:本发明通过向酸性硫酸锌溶液中加入复合添加剂,使铝、铁的化合物中的氢氧化铝胶体和氢氧化铁胶体对溶液中砸和碲的酸根离子吸附,从而实现硫酸锌溶液中砸和碲的脱除,克服了目前湿法锌冶金过程中砸和碲尚无法深度净化的难题,具有净化效果好,脱除率高,生产成本低的优点。
附图说明
[0013] 图1为本发明使用方法的工艺流程图。
具体实施方式
[0014] 下面将结合本发明实施例和附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。
[0015] 净化脱除硫酸锌溶液中砸和碲的复合添加剂,复合添加剂的成分包括Al (0H)3、A1203、Fe (0H)3、KAl (SO4)2四种化合物,其中,Al的总含量为2.5-10%, Fe的总含量为10-20 %,其余成分为S、0、H。
[0016] 如图1所示,净化脱除硫酸锌溶液中砸和碲的复合添加剂的使用方法,具体步骤为:
[0017] I)用50_95°C、pH为1.2-3.5的酸性水溶液将复合添加剂进行溶解;
[0018] 2)按每m3硫酸锌溶液(pH值为2.5-5.4,含砸1.5_8mg/L,含碲4_15mg/L)加入40-200L的加入量,将稀释后的复合添加剂溶液加入到硫酸锌溶液中,控制溶液反应温度为55-920C,控制搅拌机转速70-160转/分钟,对溶液搅拌30-60分钟;
[0019] 3)完成净化过程的硫酸锌溶液经过压滤装置进行过滤,得到合格的滤液,送下一步工序处理,滤渣另行处理。
[0020] 本发明通过向酸性硫酸锌溶液中加入复合添加剂,使复合添加剂中的氢氧化铝胶体和氢氧化铁胶体对溶液中砸和碲的酸根离子吸附,从而实现硫酸锌溶液中砸和碲的脱除。其化学式为:
[0021] mSe032 +nAl (H0)3Z+— nzAl (HO) 3+.m SeO32 I
[0022] m TeO32 +nAl (HO) 3Z+— nzAl (HO) 3+.m TeO32 I
[0023] mSe032 +nFe (HO) 3Z+—nzFe (HO) 3+.m SeO32 I
[0024] m TeO32 +nFe (HO) 3Z+— nzFe (HO) 3+.m TeO32 I
[0025] 实施例1
[0026] 焙烧矿中性浸出的硫酸锌溶液(pH:5.0、Se3.65mg/L、Te4.82mg/L)取1000ml置于2000ml的烧杯中,将稀释后浓度为5g/L的复合添加剂溶液200mL加入到硫酸锌溶液中,控制溶液温度为55-65°C、控制搅拌机转速70-160转/分钟,搅拌时间30分钟。得到溶液成分为:Sel.47mg/L、Te3.925mg/L。
[0027] 实施例2
[0028] 湿法锌冶炼酸性硫酸锌浸出溶液(pH:4.0、Se4.24mg/L、Te5.78mg/L) 1000ml置于2000ml的烧杯中,将稀释后浓度为10g/L的复合添加剂溶液120mL加入到硫酸锌溶液中,控制溶液温度为75-85°C,控制搅拌机转速70-160转/分钟,搅拌时间60分钟,得到溶液成分为:Sel.64mg/L、Te3.38mg/L。
[0029] 实施例3
[0030] 湿法锌冶炼二段净化后硫酸锌溶液(pH:5.0、Se5.62mg/L、Te6.23mg/L) 1000ml置于2000ml的烧杯中,将稀释后浓度为30g/L的复合添加剂溶液40mL加入到硫酸锌溶液中。控制溶液温度为80-85°C,控制搅拌机转速70-160转/分钟,搅拌时间60分钟,得到溶液成分为:Se0.92mg/L、Tel.24mg/L。
[0031 ] 本发明通过向酸性硫酸锌溶液中加入复合添加剂,使铝、铁的化合物中的氢氧化铝胶体和氢氧化铁胶体对溶液中砸和碲的酸根离子吸附,从而实现硫酸锌溶液中砸和碲的脱除,克服了目前湿法锌冶金过程中砸和碲尚无法深度净化的难题,具有净化效果好,脱除率高,生产成本低的优点。
[0032] 最后说明的是,以上优选实施例及附图仅用以说明本发明的技术方案而非限制,尽管通过上述优选实施例已经对本发明进行了详细的描述,但本领域技术人员应当理解,可以在形式上和细节上对其作出各种各样的改变,而不偏离本发明权利要求书所限定的范围。

Claims (4)

1.净化脱除硫酸锌溶液中砸和碲的复合添加剂,其特征在于:所述的净化脱除硫酸锌溶液中砸和碲的复合添加剂的成分包括Al (OH) 3、A1203、Fe (OH)3, KAl (SO4)2四种化合物,其中,Al的总含量为2.5-10%,Fe的总含量为10-20%,其余成分为S、0、H。
2.净化脱除硫酸锌溶液中砸和碲的复合添加剂的使用方法,其特征在于,具体步骤为: 1)用50-95°C、pH为1.2-3.5的酸性水溶液将复合添加剂进行溶解; 2)按每m3硫酸锌溶液加入40-200L的加入量,将稀释后的复合添加剂溶液加入到硫酸锌溶液中,控制搅拌机转速70-160转/分钟,对溶液搅拌30-60分钟; 3)完成净化过程的硫酸锌溶液经过压滤装置进行过滤,得到合格的滤液,送下一步工序处理,滤渣另行处理。
3.根据权利要求2所述的净化脱除硫酸锌溶液中砸和碲的复合添加剂的使用方法,其特征在于:步骤2)中,硫酸锌溶液的pH值为2.5-5.4,含砸1.5_8mg/L,含碲4_15mg/L。
4.根据权利要求2所述的净化脱除硫酸锌溶液中砸和碲的复合添加剂的使用方法,其特征在于:步骤2)中,控制溶液反应温度为55-92 °C。
CN201510507680.0A 2015-08-18 2015-08-18 净化脱除硫酸锌溶液中硒和碲的复合添加剂及使用方法 Active CN105018729B (zh)