CN105002652A - Antimicrobial mildew-proof down composite warmth retention material and preparation method thereof - Google Patents
Antimicrobial mildew-proof down composite warmth retention material and preparation method thereof Download PDFInfo
- Publication number
- CN105002652A CN105002652A CN201510349583.3A CN201510349583A CN105002652A CN 105002652 A CN105002652 A CN 105002652A CN 201510349583 A CN201510349583 A CN 201510349583A CN 105002652 A CN105002652 A CN 105002652A
- Authority
- CN
- China
- Prior art keywords
- parts
- warmth retention
- down composite
- heat insulation
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antimicrobial mildew-proof down composite warmth retention material. The down composite warmth retention material is characterized in that the down composite warmth retention material is prepared from raw materials comprising, by weight, 30-40 parts of eider, 3-5 parts of soybean fibers, 10-15 parts of bamboo fibers, 10-20 parts of polylactic acid composite fibers, 5-10 parts of polyethelene alcohol fibers, 0.2-0.4 parts of glycerol monolaurate, 0.5-1 parts of polyvinylpyrrolidone, 1-2 parts of coconut oil, 0.1-0.2 parts of nanometer silica, and 10-15 parts of water. The down composite warmth retention material has excellent warmth retention performance, is high in air permeability, hygroscopicity, resilience and strength, has good antimicrobial mildew-proof performance and using performance, and facilitates the hygiene of products and human health.
Description
Technical field
The present invention relates to heat insulating material formed field, be specifically related to a kind of antibacterial and mouldproof eider down composite heat insulation material and preparation method thereof.
Background technology
Eider down is a kind of natural protein fibre material, due to its excellent elasticity, moisture permeability and being used in a large number as textile material, cotton, wool, silk and eider down four large natural heat insulating material formed in, the thermal property of eider down is best.The most traditional purposes of eider down is as stuffing for various warm-keeping product, mainly clothes and bedding, its goods have softness, fluffy, there is the advantages such as elasticity, warmth retention property be good, welcome widely.But eider down intensity is poor, frangibility after Long-Time Service, durability is low; After moisture absorption, warming effect declines, and source nervous, expensive, easily damage by worms, easy breed bacteria, a large amount of popularization and application cannot be obtained.Therefore, along with the development of textile industry, compoundly heat insulating material formedly day by day to come into one's own.By to the adjustment of raw material and technique and improvement, the compound heat insulating material formed deficiency that can overcome single type material, reduces costs, keeps excellent thermal property and serviceability, has wide market prospects and higher researching value.
Summary of the invention
The object of this invention is to provide a kind of antibacterial and mouldproof eider down composite heat insulation material, have good mechanical property and thermal property concurrently.
The present invention is achieved by the following technical solutions:
A kind of antibacterial and mouldproof eider down composite heat insulation material, it is obtained by the raw material of following weight parts:
Duck's down 30-40, fibre and soya 3-5, bamboo fibre 10-15, PLA Composite Fiber 10-20, vinal 5-10, lauric monoglyceride 0.2-0.4, polyvinylpyrrolidone 0.5-1, coconut oil 1-2, nano silicon 0.1-0.2, water 10-15;
Described PLA Composite Fiber is obtained by the raw material of following weight parts: PLA 40-50, oyster shell whiting 4-6, glycerine 4-8, silane resin acceptor kh-550 0.3-0.5; Oyster shell whiting is mixed latter 100-120 DEG C to process 1-2h by the preparation method of described PLA Composite Fiber with silane resin acceptor kh-550, mix with all the other raw materials after cooling, normal temperature makes material with double screw extruder after placing 3-5h under 160-180 DEG C of condition, again with the spinning of conventional melt spin processes, to obtain final product.
A preparation method for antibacterial and mouldproof eider down composite heat insulation material, comprises the following steps:
(1) by fibre and soya, bamboo fibre, PLA Composite Fiber, vinal weaving opener respectively shredding, fully after mixing, then mix with duck's down, removal of impurities, obtain blended fiber;
(2) nano silicon and polyvinylpyrrolidone are added to the water stir after ultrasonic disperse 5-10min, add lauric monoglyceride 70-80 DEG C again, 600-800r/min stirs 10-15min, stir 20-30min under finally adding all the other raw material similarity conditions, obtain multiple emulsion;
(3) multiple emulsion in (2) to be evenly sprayed onto in the blended fiber in (1) and to be uniformly mixed 2-4h in 60-80 DEG C, again carry out shredding mixing, then carry out combing, random web-laying equipment becomes net, finally in 120 DEG C of-140 DEG C of hot melt adhesives, obtain eider down composite heat insulation material.
Advantage of the present invention is:
PLA and the blended rear melt spinning of oyster shell whiting are obtained PLA Composite Fiber, utilizes the loose structure of oyster shell whiting itself and the performance such as toughness reinforcing, improve mechanical property and the moisture permeability of PLA Composite Fiber; By the PLA Composite Fiber that obtains and eider down and cofibre material blended, combining nano silica carries out surface treatment to blended fiber material, be conducive to improving its intensity, stability and ageing resistace, pass through the composite of all the other raw materials, make the eider down composite heat insulation material obtained not only have excellent thermal property, ventilative and hygroscopicity, resilience are good simultaneously, intensity is high, and there is good antibacterial and mouldproof performance, be conducive to the wholesomeness and the health that keep goods, serviceability is good.
Detailed description of the invention
Non-limiting examples of the present invention is as follows:
A kind of antibacterial and mouldproof eider down composite heat insulation material, is prepared from by the component raw material of following weight (kg):
Duck's down 35, fibre and soya 4, bamboo fibre 12, PLA Composite Fiber 15, vinal 8, lauric monoglyceride 0.3, polyvinylpyrrolidone 0.8, coconut oil 1.5, nano silicon 0.15, water 12;
Described PLA Composite Fiber is obtained by the raw material of following weight parts: PLA 45, oyster shell whiting 5, glycerine 6, silane resin acceptor kh-550 0.4; Oyster shell whiting is mixed latter 100 DEG C to process 1h by the preparation method of described PLA Composite Fiber with silane resin acceptor kh-550, mix with all the other raw materials after cooling, normal temperature makes material with double screw extruder after placing 3h under 160-180 DEG C of condition, then with the spinning of conventional melt spin processes, to obtain final product.
The preparation method of antibacterial and mouldproof eider down composite heat insulation material comprises the following steps:
(1) by fibre and soya, bamboo fibre, PLA Composite Fiber, vinal weaving opener respectively shredding, fully after mixing, then mix with duck's down, removal of impurities, obtain blended fiber;
(2) nano silicon and polyvinylpyrrolidone are added to the water stir after ultrasonic disperse 5min, then add lauric monoglyceride 80 DEG C, 800r/min stirs 10min, stir 20min under finally adding all the other raw material similarity conditions, obtain multiple emulsion;
(3) multiple emulsion in (2) to be evenly sprayed onto in the blended fiber in (1) and to be uniformly mixed 4h in 80 DEG C, again carry out shredding mixing, then carry out combing, random web-laying equipment becomes net, finally in 140 DEG C of hot melt adhesives, obtain eider down composite heat insulation material.
Carry out performance test to above-mentioned obtained eider down composite heat insulation material, result is as follows:
Warming rate: 91.2%;
Compress ional resilience index: 87.3%;
Ultimate strength: longitudinal 8.1N, horizontal 20.4N.
Claims (2)
1. an antibacterial and mouldproof eider down composite heat insulation material, is characterized in that, it is obtained by the raw material of following weight parts:
Duck's down 30-40, fibre and soya 3-5, bamboo fibre 10-15, PLA Composite Fiber 10-20, vinal 5-10, lauric monoglyceride 0.2-0.4, polyvinylpyrrolidone 0.5-1, coconut oil 1-2, nano silicon 0.1-0.2, water 10-15;
Described PLA Composite Fiber is obtained by the raw material of following weight parts: PLA 40-50, oyster shell whiting 4-6, glycerine 4-8, silane resin acceptor kh-550 0.3-0.5; Oyster shell whiting is mixed latter 100-120 DEG C to process 1-2h by the preparation method of described PLA Composite Fiber with silane resin acceptor kh-550, mix with all the other raw materials after cooling, normal temperature makes material with double screw extruder after placing 3-5h under 160-180 DEG C of condition, again with the spinning of conventional melt spin processes, to obtain final product.
2. the preparation method of a kind of antibacterial and mouldproof eider down composite heat insulation material according to claim 1, is characterized in that, comprise the following steps:
(1) by fibre and soya, bamboo fibre, PLA Composite Fiber, vinal weaving opener respectively shredding, fully after mixing, then mix with duck's down, removal of impurities, obtain blended fiber;
(2) nano silicon and polyvinylpyrrolidone are added to the water stir after ultrasonic disperse 5-10min, add lauric monoglyceride 70-80 DEG C again, 600-800r/min stirs 10-15min, stir 20-30min under finally adding all the other raw material similarity conditions, obtain multiple emulsion;
(3) multiple emulsion in (2) to be evenly sprayed onto in the blended fiber in (1) and to be uniformly mixed 2-4h in 60-80 DEG C, again carry out shredding mixing, then carry out combing, random web-laying equipment becomes net, finally in 120 DEG C of-140 DEG C of hot melt adhesives, obtain eider down composite heat insulation material.