CN104986981A - 一种聚苯乙烯泡沫颗粒轻质骨料及其制备方法 - Google Patents
一种聚苯乙烯泡沫颗粒轻质骨料及其制备方法 Download PDFInfo
- Publication number
- CN104986981A CN104986981A CN201510369359.0A CN201510369359A CN104986981A CN 104986981 A CN104986981 A CN 104986981A CN 201510369359 A CN201510369359 A CN 201510369359A CN 104986981 A CN104986981 A CN 104986981A
- Authority
- CN
- China
- Prior art keywords
- polystyrene foam
- epoxy resin
- foam particles
- acetone
- dibutylester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚苯乙烯泡沫颗粒轻质骨料及其制备方法,由以下原料制备而成:聚苯乙烯泡沫颗粒、E44环氧树脂、T31、二丁酯及丙酮;制备方法为,将聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯按照质量比例1:2.5~3:2~3:0.25~0.3:0.25~0.3称取备用;在E44环氧树脂中依次加入T31、丙酮、二丁酯,制备环氧树脂胶,然后将制备而成的环氧树脂胶倒入聚苯乙烯泡沫颗粒中搅拌均匀,即成。本发明制备的骨料具有轻质的特点,还克服了聚苯乙烯泡沫颗粒与胶凝材料表面粘结力较差的缺点;制备的骨料的吸水率极小,耐久性较好;有利于废弃聚苯乙烯泡沫的回收和利用。
Description
技术领域
本发明属于建筑材料领域,具体为一种聚苯乙烯泡沫颗粒轻质骨料及其制备方法。
背景技术
近年来,聚苯乙烯泡沫得到了快速发展,年产量已超过50吨。聚苯乙烯泡沫的不能重复利用性的缺点,而且无法自行降解,致使每年有近千万立方的废弃聚苯乙烯因得不到处理及降解而成为白色污染物。现有技术,主要采用人工降解来处理废弃的聚苯乙烯泡沫,耗资较大。如果这些废弃的聚苯泡沫得到充分的利用,不仅可以解决白色污染问题,促进聚苯泡沫的发展,同时还可以大量因处理废弃物而产生的资金开销。为解决聚苯乙烯的回收和利用难题,现有技术中,直接利用聚苯乙烯泡沫颗粒作为胶凝材料的填充骨料,或者对其表面进行改性后作为胶凝材料的填充骨料,将其轻质、隔声、隔热、耐久等优良特性带到建筑行业中,充分的利用废弃聚苯泡沫,解决白色污染问题,促进聚苯泡沫的发展,节约大量因处理废弃物而产生的资金开销。
现有技术在利用聚苯乙烯泡沫颗粒作为胶凝材料的填充骨料时,颗粒与胶凝材料的粘结力差;同时,表面改性改变了聚苯乙烯泡沫颗粒不吸水的优点,会增大聚苯乙烯泡沫颗粒的吸水率,降低复合材料的耐久性。因此,有必要提供一种聚苯乙烯泡沫颗粒轻质骨料,克服上述缺陷。
发明内容
本发明的目的在于提供一种聚苯乙烯泡沫颗粒轻质骨料及其制备方法,以解决上述技术问题。
为实现上述目的本发明采用以下技术方案:
一种聚苯乙烯泡沫颗粒轻质骨料,由以下原料制备而成:聚苯乙烯泡沫颗粒、环氧树脂、固化剂、增塑剂及稀释剂;所述聚苯乙烯泡沫颗粒为废弃聚苯泡沫破碎而成,直径为3-5mm;所述环氧树脂采用E44环氧树脂,所述固化剂采用T31,所述增塑剂采用二丁酯,所述稀释剂采用丙酮。
所述聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯的质量比为1:2.5~3:2~3:0.25~0.3:0.25~0.3。
一种聚苯乙烯泡沫颗粒轻质骨料的制备方法,包括如下步骤:将聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯按照质量比例1:2.5~3:2~3:0.25~0.3:0.25~0.3称取备用;在E44环氧树脂中依次加入T31、丙酮、二丁酯,搅拌1~2min,制备环氧树脂胶,然后将制备而成的环氧树脂胶倒入聚苯乙烯泡沫颗粒中搅拌均匀,使环氧树脂胶均匀的覆盖在聚苯乙烯泡沫颗粒的表面,在15℃~25℃下摊开放置2~3min,使表面的环氧树脂具有一定的强度,即成。
本发明有益效果:本发明制备的骨料不仅具有轻质的特点,同时还克服了聚苯乙烯泡沫颗粒与胶凝材料表面粘结力较差的缺点;而且由于聚苯乙烯泡沫颗粒溶于有机溶剂,所以颗粒表面与环氧树脂外壳的粘结力较强,整体效果较好;由于环氧树脂不溶于水,所以所制备的骨料的吸水率极小,耐久性较好;由于聚苯乙烯爬模颗粒外表面有环氧外壳,所以在振捣的过程中,可以减少骨料的上浮;有利于废弃聚苯乙烯泡沫的回收和利用。
具体实施方式
下面结合具体实施例对本发明作进一步阐述。
实施例1
一种聚苯乙烯泡沫颗粒轻质骨料,由以下原料制备而成:聚苯乙烯泡沫颗粒、环氧树脂、固化剂、增塑剂及稀释剂;所述聚苯乙烯泡沫颗粒为废弃聚苯泡沫破碎而成,直径为3-5mm;所述环氧树脂采用E44环氧树脂,所述固化剂采用T31,所述增塑剂采用二丁酯,所述稀释剂采用丙酮,所述聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯的质量比为1:2.5~3:2~3:0.25~0.3:0.25~0.3。
一种聚苯乙烯泡沫颗粒轻质骨料的制备方法,包括如下步骤:将聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯按照质量比例1:3:3:0.3:0.3称取备用;在E44环氧树脂中依次加入T31、丙酮、二丁酯,搅拌1min,制备环氧树脂胶,然后将制备而成的环氧树脂胶倒入聚苯乙烯泡沫颗粒中搅拌均匀,使环氧树脂胶均匀的覆盖在聚苯乙烯泡沫颗粒的表面,在15℃~25℃下摊开放置3min,使表面的环氧树脂具有一定的强度,即成。
实施例2
一种聚苯乙烯泡沫颗粒轻质骨料,由以下原料制备而成:聚苯乙烯泡沫颗粒、环氧树脂、固化剂、增塑剂及稀释剂;所述聚苯乙烯泡沫颗粒为废弃聚苯泡沫破碎而成,直径为3-5mm;所述环氧树脂采用E44环氧树脂,所述固化剂采用T31,所述增塑剂采用二丁酯,所述稀释剂采用丙酮,所述聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯的质量比为1:2.5~3:2~3:0.25~0.3:0.25~0.3。
一种聚苯乙烯泡沫颗粒轻质骨料的制备方法,包括如下步骤:将聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯按照质量比例1:2.5:2.5:0.25:0.25称取备用;在E44环氧树脂中依次加入T31、丙酮、二丁酯,搅拌2min,制备环氧树脂胶,然后将制备而成的环氧树脂胶倒入聚苯乙烯泡沫颗粒中搅拌均匀,使环氧树脂胶均匀的覆盖在聚苯乙烯泡沫颗粒的表面,在15℃~25℃下摊开放置3min,使表面的环氧树脂具有一定的强度,即成。
实施例3
一种聚苯乙烯泡沫颗粒轻质骨料,由以下原料制备而成:聚苯乙烯泡沫颗粒、环氧树脂、固化剂、增塑剂及稀释剂;所述聚苯乙烯泡沫颗粒为废弃聚苯泡沫破碎而成,直径为3-5mm;所述环氧树脂采用E44环氧树脂,所述固化剂采用T31,所述增塑剂采用二丁酯,所述稀释剂采用丙酮,所述聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯的质量比为1:2.5~3:2~3:0.25~0.3:0.25~0.3。
一种聚苯乙烯泡沫颗粒轻质骨料的制备方法,包括如下步骤:将聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯按照质量比例1:3:2:0.25:0.25称取备用;在E44环氧树脂中依次加入T31、丙酮、二丁酯,2min,制备环氧树脂胶,然后将制备而成的环氧树脂胶倒入聚苯乙烯泡沫颗粒中搅拌均匀,使环氧树脂胶均匀的覆盖在聚苯乙烯泡沫颗粒的表面,15℃~25℃下摊开放置2min,使表面的环氧树脂具有一定的强度,即成。
其中,E44环氧树脂起到粘结聚苯乙烯泡沫颗粒的外表面和胶凝材料作用,同时,还还能起到包裹颗粒的作用,隔绝水分的进入;
T31作为环氧树脂的固化剂,起固化作用;
丙酮作为环氧树脂的稀释剂,可以使环氧树脂均匀的包裹在聚苯乙烯泡沫颗粒的表面;
二丁酯作为环氧树脂的增塑剂,可以增加环氧树脂的塑性。
显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
Claims (3)
1.一种聚苯乙烯泡沫颗粒轻质骨料,其特征在于,由以下原料制备而成:聚苯乙烯泡沫颗粒、环氧树脂、固化剂、增塑剂及稀释剂;所述聚苯乙烯泡沫颗粒为废弃聚苯泡沫破碎而成,直径为3-5mm;所述环氧树脂采用E44环氧树脂,所述固化剂采用T31,所述增塑剂采用二丁酯,所述稀释剂采用丙酮。
2.如权利要求1所述的一种聚苯乙烯泡沫颗粒轻质骨料,其特征在于,所述聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯的质量比为1:2.5~3:2~3:0.25~0.3:0.25~0.3。
3.如权利要求1-2任一所述的聚苯乙烯泡沫颗粒轻质骨料的制备方法,其特征在于,包括如下步骤:将聚苯乙烯泡沫颗粒、E44环氧树脂、T31、丙酮、二丁酯按照质量比例1:2.5~3:2~3:0.25~0.3:0.25~0.3称取备用;在E44环氧树脂中依次加入T31、丙酮、二丁酯,搅拌1~2min,制备环氧树脂胶,然后将制备而成的环氧树脂胶倒入聚苯乙烯泡沫颗粒中搅拌均匀,使环氧树脂胶均匀的覆盖在聚苯乙烯泡沫颗粒的表面,在15℃~25℃下摊开放置2~3min,使表面的环氧树脂具有一定的强度,即成。