CN104947214A - 一种自动调温纤维面料的制作工艺 - Google Patents
一种自动调温纤维面料的制作工艺 Download PDFInfo
- Publication number
- CN104947214A CN104947214A CN201510409955.7A CN201510409955A CN104947214A CN 104947214 A CN104947214 A CN 104947214A CN 201510409955 A CN201510409955 A CN 201510409955A CN 104947214 A CN104947214 A CN 104947214A
- Authority
- CN
- China
- Prior art keywords
- change material
- phase change
- phase
- temp
- manufacture craft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种自动调温纤维面料的制作工艺,包括以下工艺步骤:(1)选取相变材料,通过纳米技术,制得纳米级含有相变物质的微胶囊,(2)选取竹炭纤维和天然棉纤维配制成纺丝溶液,(3)将上述(1)相变物质的微胶囊,均匀分散在上述纺丝溶液中,得到相变物质混合溶液,(4)对上述相变物质混合溶液进行纺丝,得到可调温纤维面料,(5)对上述可调温纤维面料表面进行环氧树脂处理,得到自动调温纤维面料。通过上述方式,本发明自动调温纤维面料的制作工艺操作简单,制得的面料使用范围广,对冷、热环境能自主调整,且耐水洗,可反复循环使用。
Description
技术领域
本发明涉及水产养殖领域,特别是涉及一种自动调温纤维面料的制作工艺。
背景技术
随着生活水平的提高,功能性纺织品越来越受到人们的青睐,因此,提高纺织品技术含量、研发智能面料、拓展纺织服装产品的功能已成为纺织服装行业的大势所趋,也是我国纺织服装企业在国际市场上取得竞争优势的必要条件。
发明内容
本发明主要解决的技术问题是提供一种对冷、热环境能自主调整,且耐水洗的自动调温纤维面料的制作工艺。
为解决上述技术问题,本发明提供一种自动调温纤维面料的制作工艺,包括以下工艺步骤:
(1)选取相变材料,通过纳米技术,制得纳米级含有相变物质的微胶囊,
(2)选取竹炭纤维和天然棉纤维配制成纺丝溶液,
(3)将上述(1)相变物质的微胶囊,均匀分散在上述纺丝溶液中,得到相变物质混合溶液,
(4)对上述相变物质混合溶液进行纺丝,得到可调温纤维面料,
(5)对上述可调温纤维面料表面进行环氧树脂处理,得到自动调温纤维面料。
在本发明一个较佳实施例中,所述相变材料包括有机相变材料、无机相变材料和复合相变材料。
在本发明一个较佳实施例中,所述相变物质的微胶囊直接大小为1-10微米。
在本发明一个较佳实施例中,所述相变物质混合溶液竹炭纤维所占重量百分比为30%-40%,天然棉纤维所占重量百分比为40%-50%,所述相变物质的微胶囊所占重量百分比为5%-15%。
在本发明一个较佳实施例中,所述有机相变材料可选用脂肪烃、石蜡、脂肪酸和脂肪酸酯等。
本发明的有益效果是:本发明自动调温纤维面料的制作工艺操作简单,制得的面料使用范围广,对冷、热环境能自主调整,具有双向温度调节和舒适性的功能,可主动、智能的改变温度,且耐水洗,可反复循环使用。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
本发明实施例包括:
一种自动调温纤维面料的制作工艺,包括以下工艺步骤:
(1)选取相变材料,通过纳米技术,制得纳米级含有相变物质的微胶囊,
(2)选取竹炭纤维和天然棉纤维配制成纺丝溶液,
(3)将上述(1)相变物质的微胶囊,均匀分散在上述纺丝溶液中,得到相变物质混合溶液,
(4)对上述相变物质混合溶液进行纺丝,得到可调温纤维面料,
(5)对上述可调温纤维面料表面进行环氧树脂处理,得到自动调温纤维面料。
另外,所述相变材料包括有机相变材料、无机相变材料和复合相变材料。
另外,所述相变物质的微胶囊直接大小为1-10微米。
另外,所述相变物质混合溶液竹炭纤维所占重量百分比为30%-40%,天然棉纤维所占重量百分比为40%-50%,所述相变物质的微胶囊所占重量百分比为5%-15%,制得的面料手感柔顺、吸汗性强,且具有抗菌、防臭等功效。
另外,所述有机相变材料可选用脂肪烃、石蜡、脂肪酸和脂肪酸酯等,熔融热大,稳定性好,不易出现过冷和析出,织出的纺织品耐水洗。
区别于现有技术,本发明自动调温纤维面料的制作工艺操作简单,制得的面料对冷、热环境能自主调整,具有双向温度调节和舒适性的功能,可主动、智能的改变温度,且耐水洗,可反复循环使用。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (5)
1.一种自动调温纤维面料的制作工艺,其特征在于,包括以下工艺步骤:
(1)选取相变材料,通过纳米技术,制得纳米级含有相变物质的微胶囊,
(2)选取竹炭纤维和天然棉纤维配制成纺丝溶液,
(3)将上述(1)相变物质的微胶囊,均匀分散在上述纺丝溶液中,得到相变物质混合溶液,
(4)对上述相变物质混合溶液进行纺丝,得到可调温纤维面料,
(5)对上述可调温纤维面料表面进行环氧树脂处理,得到自动调温纤维面料。
2.根据权利要求1所述的自动调温纤维面料的制作工艺,其特征在于,所述相变材料包括有机相变材料、无机相变材料和复合相变材料。
3.根据权利要求1所述的自动调温纤维面料的制作工艺,其特征在于,所述相变物质的微胶囊直接大小为1-10微米。
4.根据权利要求1所述的自动调温纤维面料的制作工艺,其特征在于,所述相变物质混合溶液竹炭纤维所占重量百分比为30%-40%,天然棉纤维所占重量百分比为40%-50%,所述相变物质的微胶囊所占重量百分比为5%-15%。
5.根据权利要求2所述的自动调温纤维面料的制作工艺,其特征在于,所述有机相变材料可选用脂肪烃、石蜡、脂肪酸和脂肪酸酯等。