CN104893864A - Paint surface oxidation layer cleaning agent - Google Patents

Abstract

The invention relates to a paint surface oxidation layer cleaning agent including the components in parts by mass: 10-20 parts of turpentine oil, 10-25 parts of methyl silicone oil, 5-10 parts of stannous chloride, 15-20 parts of sodium gluconate, 3-10 parts of dicumyl peroxide, 10-20 parts of volcanic mud and 5-10 parts of over-alkaline earth. The paint surface oxidation layer cleaning agent has no need of polishing, only needs simple cleaning, can easily remove a paint surface oxidation layer, restores a shining paint surface, can be produced on large scale, is low in manufacturing cost, can more effectively protect the paint surface, and is used more at ease.

Description

A kind of lacquer painting zone of oxidation clean-out system

Technical field

The present invention relates to a kind of automobile processing and manufacturing field, specifically, the present invention relates to a kind of lacquer painting zone of oxidation clean-out system.

Background technology

In the process that vehicle travels, car surface is in very harsh operating conditions: high temperature, at a high speed, many dirt, the road surface of jolting etc., thus cause the injury to lacquer painting, cause lacquer painting to send out crow, have zone of oxidation, have rust spot.If select traditional polishing, namely car paint is ground off one deck, have injury to lacquer painting, five polishings just can grind off lacquer painting bright layer.

Summary of the invention

For above shortcomings in prior art, technical problem to be solved by this invention is to provide a kind of effective lacquer painting zone of oxidation clean-out system.

The technical solution adopted for the present invention to solve the technical problems is: provide a kind of lacquer painting zone of oxidation clean-out system, comprise turps, methyl-silicone oil, tin protochloride, Sunmorl N 60S, dicumyl peroxide, volcanic mud and mistake alkaline earth, the mass fraction of each component is: turps 10-20, methyl-silicone oil 10-25, tin protochloride 5-10, Sunmorl N 60S 15-20, dicumyl peroxide 3-10, volcanic mud 10-20 and mistake alkaline earth 5-10.

As preferably, each constituent mass number of described glazing clean-out system is: turps 20, methyl-silicone oil 15, tin protochloride 6, Sunmorl N 60S 15, dicumyl peroxide 8, volcanic mud 10 and cross alkaline earth 8.

As preferably, a kind of step preparing above-mentioned lacquer painting zone of oxidation clean-out system is as follows:

(1), by the turps of the quality component provided in content of the present invention, methyl-silicone oil stir, standing 1 hour for subsequent use;

(2), the basis of step (1) adds the tin protochloride of provided quality component, Sunmorl N 60S, dicumyl peroxide, volcanic mud and crosses alkaline earth, control temperature stirs under the state of 50-60 DEG C;

(3) seal up for safekeeping under the mixture normal temperature, above-mentioned two steps drawn.

Lacquer painting zone of oxidation clean-out system of the present invention, without the need to polishing, only needs simple cleaning, just can easily remove lacquer painting zone of oxidation, reduces bright lacquer painting; Can produce on a large scale, and cheap for manufacturing cost, the more effective protection lacquer painting of energy, use is felt more relieved.

Embodiment

A kind of lacquer painting zone of oxidation clean-out system provided by the invention, comprise turps, methyl-silicone oil, tin protochloride, Sunmorl N 60S, dicumyl peroxide, volcanic mud and mistake alkaline earth, the mass fraction of each component is: turps 10-20, methyl-silicone oil 10-25, tin protochloride 5-10, Sunmorl N 60S 15-20, dicumyl peroxide 3-10, volcanic mud 10-20 and mistake alkaline earth 5-10.

As preferably, each constituent mass number of described glazing clean-out system is: turps 20, methyl-silicone oil 15, tin protochloride 6, Sunmorl N 60S 15, dicumyl peroxide 8, volcanic mud 10 and cross alkaline earth 8.

As preferably, a kind of step preparing above-mentioned lacquer painting zone of oxidation clean-out system is as follows:

(1), by the turps of the quality component provided in content of the present invention, methyl-silicone oil stir, standing 1 hour for subsequent use;

(2), the basis of step (1) adds the tin protochloride of provided quality component, Sunmorl N 60S, dicumyl peroxide, volcanic mud and crosses alkaline earth, control temperature stirs under the state of 50-60 DEG C;

(3) seal up for safekeeping under the mixture normal temperature, above-mentioned two steps drawn.

Claims (3)

1. a lacquer painting zone of oxidation clean-out system, it is characterized in that: comprise turps, methyl-silicone oil, tin protochloride, Sunmorl N 60S, dicumyl peroxide, volcanic mud and mistake alkaline earth, the mass fraction of each component is: turps 10-20, methyl-silicone oil 10-25, tin protochloride 5-10, Sunmorl N 60S 15-20, dicumyl peroxide 3-10, volcanic mud 10-20 and mistake alkaline earth 5-10.

2. lacquer painting zone of oxidation clean-out system according to claim 1, is characterized in that: each constituent mass number of described glazing clean-out system is: turps 20, methyl-silicone oil 15, tin protochloride 6, Sunmorl N 60S 15, dicumyl peroxide 8, volcanic mud 10 and mistake alkaline earth 8.

3. the step preparing above-mentioned lacquer painting zone of oxidation clean-out system is as follows:

(1), by the turps of the quality component provided in content of the present invention, methyl-silicone oil stir, standing 1 hour for subsequent use;

(2), the basis of step (1) adds the tin protochloride of provided quality component, Sunmorl N 60S, dicumyl peroxide, volcanic mud and crosses alkaline earth, control temperature stirs under the state of 50-60 DEG C;

(3) seal up for safekeeping under the mixture normal temperature, above-mentioned two steps drawn.