CN104888885A - Cone sand making machine two-component rolling sand making cavity assembly and production method thereof - Google Patents

Cone sand making machine two-component rolling sand making cavity assembly and production method thereof Download PDF

Info

Publication number
CN104888885A
CN104888885A CN201510156249.6A CN201510156249A CN104888885A CN 104888885 A CN104888885 A CN 104888885A CN 201510156249 A CN201510156249 A CN 201510156249A CN 104888885 A CN104888885 A CN 104888885A
Authority
CN
China
Prior art keywords
wall
rolled mortar
crushing
mortar wall
zgmn13
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510156249.6A
Other languages
Chinese (zh)
Other versions
CN104888885B (en
Inventor
胡祖尧
胡建明
王永清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Shuangjin Machinery Group Co Ltd
Original Assignee
Zhejiang Shuangjin Machinery Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Shuangjin Machinery Group Co Ltd filed Critical Zhejiang Shuangjin Machinery Group Co Ltd
Priority to CN201510156249.6A priority Critical patent/CN104888885B/en
Publication of CN104888885A publication Critical patent/CN104888885A/en
Application granted granted Critical
Publication of CN104888885B publication Critical patent/CN104888885B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a cone sand making machine two-component rolling sand making cavity assembly and a production method thereof. According to the invention, the upper part of a rolling mortar wall is made of Mn13, a lower part of the rolling mortar wall is high-carbon chromium steel, an ringed groove is arranged at outer wall or inner wall of the lower part of the rolling mortar wall, and the ringed groove can form concave-convex fusion casting cooperation with a ringed groove on the inner wall or outer wall at upper part of the rolling mortar wall, the upper part of a crushing wall is made of Mn13, a lower part of the crushing wall is made of high-carbon chromium steel, a ringed groove is arranged at outer wall or inner wall of the lower part of the crushing wall, and the ringed groove can form concave-convex fusion cooperation with a ringed groove on the inner wall or outer wall at upper part of the crushing wall. The method has the following advantages that 1)during a sand making process, wear extent of the rolling mortar wall and the crushing wall is different by stone with different specification, defect that a groove is formed on the rolling sand making cavity so that sands can not be produced due to little wearing at upper part of the rolling mortar wall and the crushing wall as well as large wearing at lower part of the rolling mortar wall and the crushing wall can be solved; and 2)wear extent of Mn13 at upper part of the rolling mortar wall and the crushing wall generated during stone crushing is relatively consistent with the wear extent of the rolling sand making cavity at lower part of the high-carbon chromium steel rolling mortar wall.

Description

The two component of circular cone sand making machine rolls sand chamber assembly processed and preparation method
Technical field
The present invention relates to a kind of circular cone sand making machine and can meet wear-resisting requirement to rubble fragmentation in sand process processed, the two component of circular cone sand making machine that can meet again the wear-resisting requirement rolling sand processed rolls sand chamber assembly processed and preparation method, belongs to circular cone sand making machine component assembly and manufactures field.
Background technology
CN102350388A, title " cone sand making machine Special high-chromium rolled mortar wall assembly ", it comprises rolled mortar wall assembly, it is characterized in that: described rolled mortar wall material is high chromium white antifriction cast iron, and its chromium content is more than or equal to 9%, is equal to or less than 32%.Advantage: one is that rolled mortar wall anti-wear performance improves greatly, its wearability is about 5 times of current Mn13 rolled mortar wall, not only greatly extend service life, and the use cost of user reduces significantly: two is achieve the impact resistance that improve high chromium white antifriction cast iron rolled mortar wall by the structure of physics, the impulsive force of slowly-releasing suffered by high chromium white antifriction cast iron rolled mortar wall effectively, solves high chromium white antifriction cast iron rolled mortar wall and to be hit the defect of cracky.But, because circular cone sand making machine is crushed to the different duty of two kinds, sand system processed from building stones in the process of sand processed, its rolled mortar wall top is used for broken building stones, building stones to rolled mortar wall top formed be impact load and contact extruding, and that what building stones and rolled mortar wall were formed is is uncertain, be not that the impact extruded rubble of whole contact coordinates, thus relatively little to the state of wear on rolled mortar wall top; And rolled mortar wall bottom is for rolling sand portion processed, what broken little building stones and rolled mortar wall were formed contacts completely, the rolling of plyability, under the little brute force at rolled mortar wall and crushing wall of its broken gravelstone between rolled mortar wall and crushing wall rolls, to ward off the wearing and tearing of (also comprising crushing wall) very serious to rolling mortar for sandstone.If adopt homogenous material to make rolled mortar wall, no matter be manganese steel, or high-carbon chromium steel, because the building stones of different size are different to the wear extent of rolled mortar wall, result causes the situation that rolled mortar wall Upper wear is little, middle part wearing and tearing opposite upper parts is little and formation groove is worn and torn in bottom, causes rolled mortar wall to wear and tear and scraps.
Summary of the invention
Purpose of design: avoid the weak point in background technology, design a kind of circular cone sand making machine and can meet wear-resisting requirement to rubble fragmentation in sand process processed, the two component of circular cone sand making machine that can meet again the wear-resisting requirement rolling sand processed rolls sand chamber assembly processed and preparation method.
Design: in order to realize above-mentioned purpose of design.The present invention is in structural design: 1, rolled mortar wall top is Mn13, rolled mortar wall bottom is the design of high-carbon chromium steel, is one of technical characteristic of the present invention.The object of such design is: Mn13 is opposing thump, one of optimal selection in the high-abrasive materials such as large pressure material wearing and tearing, it not only has the incomparable Work Hardening Characteristic of other high-abrasive material, and in greater impact load or compared with under the effect of large contacting stress, the top layer of its manganese steel steel plate Mn13 produces work hardening, case hardness rises to more than HB500 rapidly by HB200, and along with the wearing and tearing gradually of cementation zone, new work hardening layer can successively be formed, thus produce endlessly while high abrasion superficial layer, and Mn13 internal layer austenite still keeps good impact flexibility.The present invention utilizes this characteristic of Mn13 just, the top of rolled mortar wall (or middle part and top) is adopted Mn13, because rolled mortar wall top is for broken building stones, what building stones were formed rolled mortar wall top is impact load just, thus rolled mortar wall case-hardening can be made, hardness promotes rapidly, meets rolled mortar wall top to the hardness requirement of rubble and wear-resisting requirement, and high-carbon chromium steel can obtain the matrix of martensite or austenite or the two mixed type and the alloy carbide of chromium by high-alloying and heat treatment, this alloy carbide is the Me in hexaplanar, C, its hardness is up to HVl200-1600, it has much higher wearability than potassium steel, its wearability is the several times of Mn13, it also has good high temperature resistance and corrosion resistance concurrently simultaneously, the present invention utilizes the above-mentioned characteristic of high-carbon chromium steel to adopt it as the bottom moulding material of rolled mortar wall just, portion is rolled in stone roller sand process processed in the rolled mortar wall bottom that it not only solves background technology existence, its rate of wear is greater than the situation that the rolled mortar wall bottom wearing and tearing brought on rolled mortar wall top form groove, the wear extent of rolled mortar wall bottom is made to define optimum coupling with the wear extent on rolled mortar wall top, avoid rolled mortar wall Upper wear amount little, the generation of bottom wear damage situation, not only greatly extend the service life of rolled mortar wall, and while the use cost greatly reducing rolled mortar wall, reduce sand cost processed.2, using the outer wall of rolled mortar wall bottom or inwall annular groove section as rolled mortar wall top shaping mould bed die, and making the design being in the state of cooling beyond the annular groove Access Division in rolled mortar wall bottom, is technical characteristic two of the present invention.The object of such design is: mold counterdie outer wall or inwall have annular groove clamping shaping mould and the cross section of annular groove clamping shaping mould is inner large outer little because rolled mortar wall waters, and groove is along having tubaeform casting runner on annular groove, when it is as rolled mortar wall top shaping mould bed die, be cast to the annular groove that the rolled mortar wall top melting Mn13 watered in mold enters rolled mortar wall bottom and form fine and close concavo-convex snap-fit engagement, the rolled mortar wall of Mn13 and high-carbon chromium steel formation is obtained after cooling demoulding, rolled mortar wall bottom synchronous can be driven to rise when rising under the effect of rolled mortar wall top in external force, thus reach the size of Longkou (rolling chamber) between convenient adjustment rolled mortar wall and crushing wall.3, using outer wall in rolled mortar wall top or inwall annular groove section as rolled mortar wall bottom shaping mould bed die, and making the design being in the state of cooling beyond the annular groove Access Division in rolled mortar wall top, is technical characteristic three of the present invention.The object of such design is: owing to the outer wall on rolled mortar wall top or inwall having annular groove and the cross section of annular groove is inner large outer little, and groove is along having tubaeform casting runner on annular groove, when it is as rolled mortar wall bottom shaping mould bed die, be cast to the interior concavo-convex snap-fit engagement forming densification of annular groove that the rolled mortar wall bottom melting high-carbon chromium steel watered in mold enters rolled mortar wall top, the rolled mortar wall of Mn13 and high-carbon chromium steel formation is obtained after cooling and demolding, rolled mortar wall bottom synchronous can be driven to rise when rising under the effect of rolled mortar wall top in external force, thus reach the size of Longkou (rolling chamber) between convenient adjustment rolled mortar wall and crushing wall.4, crushing wall top is Mn13, crushing wall bottom is the design of high-carbon chromium steel, is technical characteristic four of the present invention.The object of such design is: Mn13 is opposing thump, one of optimal selection in the high-abrasive materials such as large pressure material wearing and tearing, it not only has the incomparable Work Hardening Characteristic of other high-abrasive material, and in greater impact load or compared with under the effect of large contacting stress, the top layer of its manganese steel steel plate Mn13 produces work hardening, case hardness rises to more than HB500 rapidly by HB200, and along with the wearing and tearing gradually of cementation zone, new work hardening layer can successively be formed, thus produce endlessly while high abrasion superficial layer, and Mn13 internal layer austenite still keeps good impact flexibility.The present invention utilizes this characteristic of Mn13 just, the top of crushing wall (or middle part and top) is adopted Mn13, because crushing wall top is for broken building stones, what building stones were formed crushing wall top is impact load just, thus crushing wall case-hardening can be made, hardness promotes rapidly, meets crushing wall top to the hardness requirement of rubble and wear-resisting requirement, and high-carbon chromium steel can obtain the matrix of martensite or austenite or the two mixed type and the alloy carbide of chromium by high-alloying and heat treatment, this alloy carbide is the Me in hexaplanar, C, its hardness is up to HVl200-1600, it has much higher wearability than potassium steel, its wearability is the several times of Mn13, it also has good high temperature resistance and corrosion resistance concurrently simultaneously, the present invention utilizes the above-mentioned characteristic of high-carbon chromium steel to adopt it as the bottom moulding material of crushing wall just, portion is rolled in stone roller sand process processed in the crushing wall bottom that it not only solves background technology existence, its rate of wear is greater than the situation that the crushing wall bottom wearing and tearing brought on crushing wall top form groove, the wear extent of crushing wall bottom is made to define optimum coupling with the wear extent on crushing wall top, avoid crushing wall Upper wear amount little, the generation of bottom wear damage situation, not only greatly extend the service life of crushing wall, and while the use cost greatly reducing crushing wall, reduce sand cost processed.5, using the outer wall of crushing wall bottom or inwall annular groove section as crushing wall top shaping mould bed die, and making the design being in the state of cooling beyond the annular groove Access Division in crushing wall bottom, is technical characteristic five of the present invention.The object of such design is: mold counterdie outer wall or inwall have annular groove clamping shaping mould and the cross section of annular groove clamping shaping mould is inner large outer little because crushing wall waters, and groove is along having tubaeform casting runner on annular groove, when it is as crushing wall top shaping mould bed die, be cast to the annular groove that the crushing wall top melting Mn13 watered in mold enters crushing wall bottom and form fine and close concavo-convex snap-fit engagement, the crushing wall of Mn13 and high-carbon chromium steel formation is obtained after cooling demoulding, crushing wall bottom synchronous can be driven to rise when rising under the effect of crushing wall top in external force, thus reach the size of Longkou (rolling chamber) between convenient adjustment crushing wall and crushing wall.6, using outer wall in crushing wall top or inwall annular groove section as crushing wall bottom shaping mould bed die, and making the design being in the state of cooling beyond the annular groove Access Division in crushing wall top, is technical characteristic six of the present invention.The object of such design is: owing to the outer wall on crushing wall top or inwall having annular groove and the cross section of annular groove is inner large outer little, and groove is along having tubaeform casting runner on annular groove, when it is as crushing wall bottom shaping mould bed die, be cast to the interior concavo-convex snap-fit engagement forming densification of annular groove that the crushing wall bottom melting high-carbon chromium steel watered in mold enters crushing wall top, the crushing wall of Mn13 and high-carbon chromium steel formation is obtained after cooling and demolding, crushing wall bottom synchronous can be driven to rise when rising under the effect of crushing wall top in external force, thus reach the size of Longkou (rolling chamber) between convenient adjustment crushing wall and crushing wall.
Technical scheme 1: the two component of a kind of circular cone sand making machine rolls sand chamber processed assembly, rolled mortar wall top is Mn13, rolled mortar wall bottom is high-carbon chromium steel and rolled mortar wall bottom outer wall or inwall have annular groove and form concavo-convex founding with annular groove on rolled mortar wall upper inside wall or outer wall coordinate; Crushing wall top is Mn13, crushing wall bottom is high-carbon chromium steel and crushing wall bottom outer wall or inwall have annular groove and form concavo-convex founding with annular groove on crushing wall upper inside wall or outer wall coordinate.
Technical scheme 2: the two component of a kind of circular cone sand making machine rolls the manufacture method of sand chamber processed assembly, rolled mortar wall makes: (1) routinely fabrication techniques rolled mortar wall bottom waters mold and rolled mortar wall waters fluted shaping clamping mould on mold counterdie outer wall or inwall, mold counterdie is watered in the rolled mortar wall bottom made to be placed on dither platform, under the vibration of dither platform, melting high-carbon chromium steel is cast to rolled mortar wall bottom and waters mold, obtain rolled mortar wall bottom after cooling forming, then rolled mortar wall bottom is heat-treated; (2) using the groove Access Division of rolled mortar wall bottom as rolled mortar wall top shaping mould bed die, the state of cooling is in below the groove Access Division of rolled mortar wall bottom, then make rolled mortar wall top water mold and be placed on dither platform, what melting Mn13 is cast to rolled mortar wall top under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at rolled mortar wall top and rolled mortar wall bottom, and de-rear mold is heat-treated rolled mortar wall top; (3) machining apparatus is adopted to carry out finishing to the rolled mortar wall by Mn13 and high-carbon chromium steel cast molding; Crushing wall makes: (1) routinely fabrication techniques crushing wall bottom waters mold and crushing wall waters fluted shaping clamping mould on mold counterdie outer wall or inwall, mold counterdie is watered in the crushing wall bottom made to be placed on dither platform, under the vibration of dither platform, melting high-carbon chromium steel is cast to crushing wall bottom and waters mold, obtain crushing wall bottom after cooling forming, then crushing wall bottom is heat-treated; (2) using the groove Access Division of crushing wall bottom as crushing wall top shaping mould bed die, the state of cooling is in below the groove Access Division of crushing wall bottom, then make crushing wall top water mold and be placed on dither platform, what melting Mn13 is cast to crushing wall top under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at crushing wall top and crushing wall bottom, and de-rear mold is heat-treated crushing wall top; (3) machining apparatus is adopted to carry out finishing to the crushing wall by Mn13 and high-carbon chromium steel cast molding; Finally namely the assembling of rolled mortar wall and crushing wall is obtained circular cone sand making machine and roll sand chamber processed assembly.
Technical scheme 3: the two component of a kind of circular cone sand making machine rolls the manufacture method of sand chamber processed assembly, rolled mortar wall makes: (1) routinely fabrication techniques rolled mortar wall top waters mold and rolled mortar wall top is watered on the outer wall of mold or inwall and had the shaping clamping mould of annular groove, mold is watered on the rolled mortar wall top made to be placed on dither platform, under the vibration of dither platform, melting Mn13 is cast to rolled mortar wall top and waters mold, cooling and demolding obtains rolled mortar wall top, then heat-treats rolled mortar wall top; (2) using lower surface, rolled mortar wall top as rolled mortar wall bottom shaping mould bed die and rolled mortar wall top is in the state of cooling, then make rolled mortar wall bottom water mold and be placed on dither platform, what melting high-carbon chromium steel is cast to rolled mortar wall bottom under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at rolled mortar wall bottom and rolled mortar wall top, heat-treats after the demoulding to rolled mortar wall bottom; (3) namely obtain the two component of circular cone sand making machine after finishing being carried out to the rolled mortar wall by Mn13 and high-carbon chromium steel cast molding and roll sand chamber processed assembly; Crushing wall makes: (1) routinely fabrication techniques crushing wall top waters mold and crushing wall top is watered on the outer wall of mold or inwall and had the shaping clamping mould of annular groove, mold is watered on the crushing wall top made to be placed on dither platform, under the vibration of dither platform, melting Mn13 is cast to crushing wall top and waters mold, cooling and demolding obtains crushing wall top, then heat-treats crushing wall top; (2) using lower surface, crushing wall top as crushing wall bottom shaping mould bed die and crushing wall top is in the state of cooling, then make crushing wall bottom water mold and be placed on dither platform, what melting high-carbon chromium steel is cast to crushing wall bottom under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at crushing wall bottom and crushing wall top, heat-treats after the demoulding to crushing wall bottom; (3) two component circular cone sand making machine crushing wall is namely obtained after finishing being carried out to the crushing wall by Mn13 and high-carbon chromium steel cast molding; Finally namely the assembling of rolled mortar wall and crushing wall is obtained circular cone sand making machine and roll sand chamber processed assembly.
The present invention is compared with background technology, one is no matter fundamentally solve single (is manganese steel, or high-carbon chromium steel) material rolled mortar wall and crushing wall be in sand process processed, because the building stones of different size are different with the wear extent of crushing wall to rolled mortar wall, the rolled mortar wall caused and crushing wall Upper wear is little, bottom wearing and tearing are large and cause roll sand chamber processed shape formation groove and cannot the critical defect of sand processed; The wear extent that sand chamber processed is rolled in the wear extent that two is rolled mortar walls produces at broken building stones with the Mn13 on crushing wall top and high-carbon chromium steel rolled mortar wall bottom is relative consistent, thus sand chamber processed is rolled in stone roller sand process processed in the rolled mortar wall and the crushing wall bottom that fundamentally solve homogenous material, due to wear extent be greater than rolled mortar wall and crushing wall Upper wear amount cause the situation of groove, not only greatly extend the service life of rolled mortar wall and crushing wall, and while the use cost greatly reducing rolled mortar wall and crushing wall, reduce sand cost processed.
Accompanying drawing explanation
Fig. 1 is the structural representation that the two component of circular cone sand making machine rolls sand chamber processed assembly.
Fig. 2 is the structural representation that the two component of circular cone sand making machine rolls sand chamber processed assembly rolled mortar wall.
Fig. 3 is the structural representation that the two component of circular cone sand making machine rolls sand chamber processed assembly crushing wall.
Fig. 4 is the structural representation of homogenous material rolled mortar wall.
Fig. 5 is the structural representation of homogenous material crushing wall.
Detailed description of the invention
Embodiment 1: with reference to accompanying drawing 1-3.The two component of a kind of circular cone sand making machine rolls sand chamber processed assembly, and rolled mortar wall top 1 is Mn13, rolled mortar wall bottom 2 coordinates 3 for high-carbon chromium steel and rolled mortar wall bottom outer wall or inwall have annular groove and form concavo-convex founding with annular groove on rolled mortar wall upper inside wall or outer wall; Crushing wall top 5 is Mn13, crushing wall bottom 6 coordinates 4 for high-carbon chromium steel and crushing wall bottom outer wall or inwall have annular groove and form concavo-convex founding with annular groove on crushing wall upper inside wall or outer wall.On annular groove, groove is along having tubaeform casting runner.Mn13 rolled mortar wall height is greater than the height of high-carbon chromium steel rolled mortar wall; Mn13 crushing wall height is greater than the height of high-carbon chromium steel crushing wall.The material of Mn13 rolled mortar wall is ZGMn13-1, ZGMn13-2, ZGMn13-3, ZGMn13-4, ZGMn13-5; The material of Mn13 crushing wall is ZGMn13-1, ZGMn13-2, ZGMn13-3, ZGMn13-4, ZGMn13-5.High-carbon chromium steel rolled mortar wall material is Cr15 or Cr26; High-carbon chromium steel crushing wall material is Cr15 or Cr26.
Embodiment 2: on the basis of embodiment 1, the two component of a kind of circular cone sand making machine rolls the manufacture method of sand chamber processed assembly, rolled mortar wall makes: (1) routinely fabrication techniques rolled mortar wall bottom waters mold and rolled mortar wall waters fluted shaping clamping mould on mold counterdie outer wall or inwall, mold counterdie is watered in the rolled mortar wall bottom made to be placed on dither platform, under the vibration of dither platform, melting high-carbon chromium steel is cast to rolled mortar wall bottom and waters mold, obtain rolled mortar wall bottom after cooling forming, then rolled mortar wall bottom is heat-treated; (2) using the groove Access Division of rolled mortar wall bottom as rolled mortar wall top shaping mould bed die, the state of cooling is in below the groove Access Division of rolled mortar wall bottom, then make rolled mortar wall top water mold and be placed on dither platform, what melting Mn13 is cast to rolled mortar wall top under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at rolled mortar wall top and rolled mortar wall bottom, and de-rear mold is heat-treated rolled mortar wall top; (3) machining apparatus is adopted to carry out finishing to the rolled mortar wall by Mn13 and high-carbon chromium steel cast molding; Crushing wall makes: (1) routinely fabrication techniques crushing wall bottom waters mold and crushing wall waters fluted shaping clamping mould on mold counterdie outer wall or inwall, mold counterdie is watered in the crushing wall bottom made to be placed on dither platform, under the vibration of dither platform, melting high-carbon chromium steel is cast to crushing wall bottom and waters mold, obtain crushing wall bottom after cooling forming, then crushing wall bottom is heat-treated; (2) using the groove Access Division of crushing wall bottom as crushing wall top shaping mould bed die, the state of cooling is in below the groove Access Division of crushing wall bottom, then make crushing wall top water mold and be placed on dither platform, what melting Mn13 is cast to crushing wall top under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at crushing wall top and crushing wall bottom, and de-rear mold is heat-treated crushing wall top; (3) machining apparatus is adopted to carry out finishing to the crushing wall by Mn13 and high-carbon chromium steel cast molding; Finally namely the assembling of rolled mortar wall and crushing wall is obtained circular cone sand making machine and roll sand chamber processed assembly.
Embodiment 2: on the basis of embodiment 1, the two component of a kind of circular cone sand making machine rolls the manufacture method of sand chamber processed assembly, rolled mortar wall makes: (1) routinely fabrication techniques rolled mortar wall top waters mold and rolled mortar wall top is watered on the outer wall of mold or inwall and had the shaping clamping mould of annular groove, mold is watered on the rolled mortar wall top made to be placed on dither platform, under the vibration of dither platform, melting Mn13 is cast to rolled mortar wall top and waters mold, cooling and demolding obtains rolled mortar wall top, then heat-treats rolled mortar wall top; (2) using lower surface, rolled mortar wall top as rolled mortar wall bottom shaping mould bed die and rolled mortar wall top is in the state of cooling, then make rolled mortar wall bottom water mold and be placed on dither platform, what melting high-carbon chromium steel is cast to rolled mortar wall bottom under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at rolled mortar wall bottom and rolled mortar wall top, heat-treats after the demoulding to rolled mortar wall bottom; (3) namely obtain the two component of circular cone sand making machine after finishing being carried out to the rolled mortar wall by Mn13 and high-carbon chromium steel cast molding and roll sand chamber processed assembly; Crushing wall makes: (1) routinely fabrication techniques crushing wall top waters mold and crushing wall top is watered on the outer wall of mold or inwall and had the shaping clamping mould of annular groove, mold is watered on the crushing wall top made to be placed on dither platform, under the vibration of dither platform, melting Mn13 is cast to crushing wall top and waters mold, cooling and demolding obtains crushing wall top, then heat-treats crushing wall top; (2) using lower surface, crushing wall top as crushing wall bottom shaping mould bed die and crushing wall top is in the state of cooling, then make crushing wall bottom water mold and be placed on dither platform, what melting high-carbon chromium steel is cast to crushing wall bottom under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at crushing wall bottom and crushing wall top, heat-treats after the demoulding to crushing wall bottom; (3) two component circular cone sand making machine crushing wall is namely obtained after finishing being carried out to the crushing wall by Mn13 and high-carbon chromium steel cast molding; Finally namely the assembling of rolled mortar wall and crushing wall is obtained circular cone sand making machine and roll sand chamber processed assembly.
It is to be understood that: although above-described embodiment to be contrasted detailed text description to mentality of designing of the present invention; but these text descriptions; just the simple text of mentality of designing of the present invention is described; instead of the restriction to mentality of designing of the present invention; any do not exceed mentality of designing of the present invention combination, increase or amendment, all fall within the scope of protection of the present invention.

Claims (13)

1. the two component of circular cone sand making machine rolls a sand chamber processed assembly, it is characterized in that: rolled mortar wall top is Mn13, rolled mortar wall bottom is high-carbon chromium steel and rolled mortar wall bottom outer wall or inwall have annular groove and form concavo-convex founding with annular groove on rolled mortar wall upper inside wall or outer wall coordinate; Crushing wall top is Mn13, crushing wall bottom is high-carbon chromium steel and crushing wall bottom outer wall or inwall have annular groove and form concavo-convex founding with annular groove on crushing wall upper inside wall or outer wall coordinate.
2. the two component of circular cone sand making machine according to claim 1 rolls sand chamber processed assembly, it is characterized in that: on annular groove, groove is along having tubaeform casting runner.
3. the two component of circular cone sand making machine according to claim 1 rolls sand chamber processed assembly, it is characterized in that: Mn13 rolled mortar wall height is greater than the height of high-carbon chromium steel rolled mortar wall; Mn13 crushing wall height is greater than the height of high-carbon chromium steel crushing wall.
4. the two component of circular cone sand making machine according to claim 1 rolls sand chamber processed assembly, it is characterized in that: the material of Mn13 rolled mortar wall is ZGMn13-1, ZGMn13-2, ZGMn13-3, ZGMn13-4, ZGMn13-5; The material of Mn13 crushing wall is ZGMn13-1, ZGMn13-2, ZGMn13-3, ZGMn13-4, ZGMn13-5.
5. the two component of circular cone sand making machine according to claim 1 rolls sand chamber processed assembly, it is characterized in that: high-carbon chromium steel rolled mortar wall material is Cr15 or Cr26; High-carbon chromium steel crushing wall material is Cr15 or Cr26.
6. the two component of circular cone sand making machine rolls a manufacture method for sand chamber processed assembly, it is characterized in that:
Rolled mortar wall makes: (1) routinely fabrication techniques rolled mortar wall bottom waters mold and rolled mortar wall waters fluted shaping clamping mould on mold counterdie outer wall or inwall, mold counterdie is watered in the rolled mortar wall bottom made to be placed on dither platform, under the vibration of dither platform, melting high-carbon chromium steel is cast to rolled mortar wall bottom and waters mold, obtain rolled mortar wall bottom after cooling forming, then rolled mortar wall bottom is heat-treated; (2) using the groove Access Division of rolled mortar wall bottom as rolled mortar wall top shaping mould bed die, the state of cooling is in below the groove Access Division of rolled mortar wall bottom, then make rolled mortar wall top water mold and be placed on dither platform, what melting Mn13 is cast to rolled mortar wall top under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at rolled mortar wall top and rolled mortar wall bottom, and de-rear mold is heat-treated rolled mortar wall top; (3) machining apparatus is adopted to carry out finishing to the rolled mortar wall by Mn13 and high-carbon chromium steel cast molding;
Crushing wall makes: (1) routinely fabrication techniques crushing wall bottom waters mold and crushing wall waters fluted shaping clamping mould on mold counterdie outer wall or inwall, mold counterdie is watered in the crushing wall bottom made to be placed on dither platform, under the vibration of dither platform, melting high-carbon chromium steel is cast to crushing wall bottom and waters mold, obtain crushing wall bottom after cooling forming, then crushing wall bottom is heat-treated; (2) using the groove Access Division of crushing wall bottom as crushing wall top shaping mould bed die, the state of cooling is in below the groove Access Division of crushing wall bottom, then make crushing wall top water mold and be placed on dither platform, what melting Mn13 is cast to crushing wall top under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at crushing wall top and crushing wall bottom, and de-rear mold is heat-treated crushing wall top; (3) machining apparatus is adopted to carry out finishing to the crushing wall by Mn13 and high-carbon chromium steel cast molding;
Finally namely the assembling of rolled mortar wall and crushing wall is obtained circular cone sand making machine and roll sand chamber processed assembly.
7. the two component of circular cone sand making machine according to claim 6 rolls the manufacture method of sand chamber processed assembly, it is characterized in that: Mn13 rolled mortar wall height is greater than the height of high-carbon chromium steel rolled mortar wall; Mn13 crushing wall height is greater than the height of high-carbon chromium steel crushing wall.
8. the two component of circular cone sand making machine according to claim 6 rolls the manufacture method of sand chamber processed assembly, it is characterized in that: the material of Mn13 rolled mortar wall is ZGMn13-1, ZGMn13-2, ZGMn13-3, ZGMn13-4, ZGMn13-5; The material of Mn13 crushing wall is ZGMn13-1, ZGMn13-2, ZGMn13-3, ZGMn13-4, ZGMn13-5.
9. the two component of circular cone sand making machine according to claim 6 rolls the manufacture method of sand chamber processed assembly, it is characterized in that: high-carbon chromium steel rolled mortar wall material is Cr15 or Cr26; High-carbon chromium steel crushing wall material is Cr15 or Cr26.
10. the two component of circular cone sand making machine rolls a manufacture method for sand chamber processed assembly, it is characterized in that:
Rolled mortar wall makes: (1) routinely fabrication techniques rolled mortar wall top waters mold and rolled mortar wall top is watered on the outer wall of mold or inwall and had the shaping clamping mould of annular groove, mold is watered on the rolled mortar wall top made to be placed on dither platform, under the vibration of dither platform, melting Mn13 is cast to rolled mortar wall top and waters mold, cooling and demolding obtains rolled mortar wall top, then heat-treats rolled mortar wall top; (2) using lower surface, rolled mortar wall top as rolled mortar wall bottom shaping mould bed die and rolled mortar wall top is in the state of cooling, then make rolled mortar wall bottom water mold and be placed on dither platform, what melting high-carbon chromium steel is cast to rolled mortar wall bottom under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at rolled mortar wall bottom and rolled mortar wall top, heat-treats after the demoulding to rolled mortar wall bottom; (3) namely obtain the two component of circular cone sand making machine after finishing being carried out to the rolled mortar wall by Mn13 and high-carbon chromium steel cast molding and roll sand chamber processed assembly;
Crushing wall makes: (1) routinely fabrication techniques crushing wall top waters mold and crushing wall top is watered on the outer wall of mold or inwall and had the shaping clamping mould of annular groove, mold is watered on the crushing wall top made to be placed on dither platform, under the vibration of dither platform, melting Mn13 is cast to crushing wall top and waters mold, cooling and demolding obtains crushing wall top, then heat-treats crushing wall top; (2) using lower surface, crushing wall top as crushing wall bottom shaping mould bed die and crushing wall top is in the state of cooling, then make crushing wall bottom water mold and be placed on dither platform, what melting high-carbon chromium steel is cast to crushing wall bottom under the vibration of dither platform waters in mold, after cooling forming, concavo-convex snap-fit engagement is formed at crushing wall bottom and crushing wall top, heat-treats after the demoulding to crushing wall bottom; (3) two component circular cone sand making machine crushing wall is namely obtained after finishing being carried out to the crushing wall by Mn13 and high-carbon chromium steel cast molding;
Finally namely the assembling of rolled mortar wall and crushing wall is obtained circular cone sand making machine and roll sand chamber processed assembly.
The two component of 11. circular cone sand making machines according to claim 10 rolls the manufacture method of sand chamber processed assembly, it is characterized in that: Mn13 rolled mortar wall height is greater than the height of high-carbon chromium steel rolled mortar wall; Mn13 crushing wall height is greater than the height of high-carbon chromium steel crushing wall.
The two component of 12. circular cone sand making machines according to claim 10 rolls the manufacture method of sand chamber processed assembly, it is characterized in that: the material of Mn13 rolled mortar wall is ZGMn13-1, ZGMn13-2, ZGMn13-3, ZGMn13-4, ZGMn13-5; The material of Mn13 crushing wall is ZGMn13-1, ZGMn13-2, ZGMn13-3, ZGMn13-4, ZGMn13-5.
The two component of 13. circular cone sand making machines according to claim 10 rolls the manufacture method of sand chamber processed assembly, it is characterized in that: high-carbon chromium steel rolled mortar wall material is Cr15 or Cr26; High-carbon chromium steel crushing wall material is Cr15 or Cr26.
CN201510156249.6A 2015-04-03 2015-04-03 Circular cone sand making machine two-component rolls sand chamber assembly processed and production method Active CN104888885B (en)