CN104817875A - Microcrystalline wax printing ink and preparation method thereof - Google Patents
Microcrystalline wax printing ink and preparation method thereof Download PDFInfo
- Publication number
- CN104817875A CN104817875A CN201510199334.0A CN201510199334A CN104817875A CN 104817875 A CN104817875 A CN 104817875A CN 201510199334 A CN201510199334 A CN 201510199334A CN 104817875 A CN104817875 A CN 104817875A
- Authority
- CN
- China
- Prior art keywords
- parts
- microcrystalline wax
- acrylic resin
- talcum powder
- printing ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a microcrystalline wax printing ink and a preparation method thereof, wherein the microcrystalline wax printing ink comprises, by weight, 25-50 parts of microcrystalline wax emulsion, 2-9 parts of anti-friction auxiliary agent, 10-25 parts of black carbon, 1-8 parts of water-soluble acrylic resin, 0.8-3 parts of phthalocyanine pigment, 11-23 parts of binder, 6-14 parts of cellulose, 1-4 parts of talcum powder and 21-27 parts of calcium carbonate. The microcrystalline wax printing ink disclosed by the invention is prepared by adopting the water-soluble acrylic resin, the microcrystalline wax emulsion and the talcum powder, so that the frequency of grinding procedures is reduced, and the production efficiency is improved; meanwhile, the microcrystalline wax emulsion is used, so that the adhesive force and the friction resistance of the printing ink are greatly improved, and the applicability is wider.
Description
Technical field
The present invention relates to a kind of Microcrystalline Wax ink and preparation method thereof.
Background technology
Ink is the important materials for printing, for the various printing such as books and periodicals, packaging.Along with social demand increases, ink kind and output is respective extension and growth also.Existing ink adopts the mineral dye such as silicon-dioxide, clay mostly.But after mineral dye mixes with binder, when carrying out grinding step, needing to increase grinding number of times could control fineness in acceptability limit, thus the energy of at substantial and working hour.Printing ink producing inefficiency.
Summary of the invention
It is good that technical problem to be solved by this invention is to provide a kind of wear resistance, and printing adaptability is good, strong adhesion, high gloss, Microcrystalline Wax ink applied widely.
For solving the problem, the present invention is achieved through the following technical solutions: a kind of Microcrystalline Wax ink, and this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 25-50 part, friction resistant auxiliary agent 2-9 part, black wood charcoal 10-25 part, water soluble acrylic resin 1-8 part, phthalein blue or green series pigments 0.8-3 part, binder 11-23 part, Mierocrystalline cellulose 6-14 part, talcum powder 1-4 part and calcium carbonate 21-27 part.
Another technical problem to be solved by this invention is to provide a kind of preparation method of Microcrystalline Wax ink,
The present invention is achieved through the following technical solutions: the preparation process of described Microcrystalline Wax ink is as follows:
1) stir in stirring tank after extracting Microcrystalline Wax emulsion 25-50 part, black wood charcoal 10-25 part, water soluble acrylic resin 1-8 part, phthalein blue or green series pigments 0.8-3 part, binder 11-23 part, talcum powder 1-4 part and the mixing of calcium carbonate 21-27 part by weight ratio;
2) mixture of extraction step 1, carries out grinding distribution;
3) mixture of extraction step 2, adds friction resistant auxiliary agent 2-9 part and Mierocrystalline cellulose 6-14 part is stirred, and whipping temp remains on 30 DEG C-60 DEG C, stirs and within 30 minutes, is Microcrystalline Wax ink finished product.
The beneficial effect of Microcrystalline Wax ink of the present invention is: adopt water soluble acrylic resin, Microcrystalline Wax emulsion and talcum powder time prepared by described Microcrystalline Wax ink, decrease the number of times of grinding step, enhance productivity; The use of Microcrystalline Wax emulsion simultaneously, allow the sticking power of ink and rub resistance greatly improve, suitability is also wider.
Embodiment
Following examples for illustration of the present invention, but are not used for limiting the scope of the invention.
Embodiment 1
A kind of Microcrystalline Wax ink of the present invention, this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 25 parts, friction resistant auxiliary agent 2 parts, black wood charcoal 10 parts, water soluble acrylic resin 1 part, phthalein blue or green series pigments 0.8 part, binder 11 parts, Mierocrystalline cellulose 6 parts, talcum powder 1 part and 21 parts, calcium carbonate.
The preparation process of described Microcrystalline Wax ink is as follows:
1) stir in stirring tank after extracting Microcrystalline Wax emulsion 25 parts, black wood charcoal 10 parts, water soluble acrylic resin 1 part, blue or green series pigments 0.8 part, binder 11 parts, talcum powder 1 part and 21 parts, the calcium carbonate mixing of phthalein by weight ratio;
2) mixture of extraction step 1, carries out grinding distribution;
3) mixture of extraction step 2, adds friction resistant auxiliary agent 2 parts and Mierocrystalline cellulose 6 parts stirs, and whipping temp remains on 30 DEG C-60 DEG C, stirs and within 30 minutes, is Microcrystalline Wax ink finished product.
Embodiment 2
Its difference from Example 1 is, this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 50 parts, friction resistant auxiliary agent 9 parts, black wood charcoal 25 parts, water soluble acrylic resin 8 parts, phthalein blue or green series pigments 3 parts, binder 23 parts, Mierocrystalline cellulose 14 parts, talcum powder 4 parts and 27 parts, calcium carbonate.
Embodiment 3
Its difference from Example 1 is, this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 44 parts, friction resistant auxiliary agent 5 parts, black wood charcoal 16 parts, water soluble acrylic resin 4 parts, phthalein blue or green series pigments 2 parts, binder 17 parts, Mierocrystalline cellulose 10 parts, talcum powder 2 parts and 25 parts, calcium carbonate.
Embodiment 4
Its difference from Example 1 is, this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 30 parts, friction resistant auxiliary agent 3 parts, black wood charcoal 12 parts, water soluble acrylic resin 2 parts, phthalein blue or green series pigments 1.2 parts, binder 14 parts, Mierocrystalline cellulose 8 parts, talcum powder 2 parts and 22 parts, calcium carbonate.
Embodiment 5
Its difference from Example 1 is, this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 47 parts, friction resistant auxiliary agent 7 parts, black wood charcoal 23 parts, water soluble acrylic resin 7 parts, phthalein blue or green series pigments 2.5 parts, binder 21 parts, Mierocrystalline cellulose 13 parts, talcum powder 3 parts and 26 parts, calcium carbonate.
Embodiment 6
Its difference from Example 1 is, this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 33 parts, friction resistant auxiliary agent 4 parts, black wood charcoal 18 parts, water soluble acrylic resin 5.5 parts, phthalein blue or green series pigments 1.8 parts, binder 16 parts, Mierocrystalline cellulose 11 parts, talcum powder 2.8 parts and 24 parts, calcium carbonate.
Embodiment 7
Its difference from Example 1 is, this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 27 parts, friction resistant auxiliary agent 4 parts, black wood charcoal 15 parts, water soluble acrylic resin 5 parts, phthalein blue or green series pigments 1 part, binder 15 parts, Mierocrystalline cellulose 10 parts, talcum powder 1.5 parts and 25 parts, calcium carbonate.
Embodiment 8
Its difference from Example 1 is, this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 41 parts, friction resistant auxiliary agent 7.5 parts, black wood charcoal 20 parts, water soluble acrylic resin 5 parts, phthalein blue or green series pigments 2.5 parts, binder 20 parts, Mierocrystalline cellulose 11 parts, talcum powder 3 parts and 22 parts, calcium carbonate.
The present invention is not limited to above-mentioned preferred forms, anyone other any or akin products identical with the present invention drawn under enlightenment of the present invention, all drops within protection scope of the present invention.
Claims (2)
1. a Microcrystalline Wax ink, is characterized in that: this Microcrystalline Wax ink is made up of following weight composition: Microcrystalline Wax emulsion 25-50 part, friction resistant auxiliary agent 2-9 part, black wood charcoal 10-25 part, water soluble acrylic resin 1-8 part, phthalein blue or green series pigments 0.8-3 part, binder 11-23 part, Mierocrystalline cellulose 6-14 part, talcum powder 1-4 part and calcium carbonate 21-27 part.
2. prepare a preparation method for Microcrystalline Wax ink according to claim 1, it is characterized in that: the method comprises the following steps:
1) stir in stirring tank after extracting Microcrystalline Wax emulsion 25-50 part, black wood charcoal 10-25 part, water soluble acrylic resin 1-8 part, phthalein blue or green series pigments 0.8-3 part, binder 11-23 part, talcum powder 1-4 part and the mixing of calcium carbonate 21-27 part by weight ratio;
2) mixture of extraction step 1, carries out grinding distribution;
3) mixture of extraction step 2, adds friction resistant auxiliary agent 2-9 part and Mierocrystalline cellulose 6-14 part is stirred, and whipping temp remains on 30 DEG C-60 DEG C, stirs and within 30 minutes, is Microcrystalline Wax ink finished product.