CN104760139B - 一种轻质保温砂浆生产工艺 - Google Patents

一种轻质保温砂浆生产工艺 Download PDF

Info

Publication number
CN104760139B
CN104760139B CN201410000147.0A CN201410000147A CN104760139B CN 104760139 B CN104760139 B CN 104760139B CN 201410000147 A CN201410000147 A CN 201410000147A CN 104760139 B CN104760139 B CN 104760139B
Authority
CN
China
Prior art keywords
light
blender
fiber
weight aggregate
production technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410000147.0A
Other languages
English (en)
Other versions
CN104760139A (zh
Inventor
王剑武
陆军
苑克江
高广永
韩子健
丁恩荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Building Material Municipal Architecture Design And Research Institute
Tianjin Wu Shuo Science And Technology Ltd
Original Assignee
Tianjin Building Material Municipal Architecture Design And Research Institute
Tianjin Wu Shuo Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Building Material Municipal Architecture Design And Research Institute, Tianjin Wu Shuo Science And Technology Ltd filed Critical Tianjin Building Material Municipal Architecture Design And Research Institute
Priority to CN201410000147.0A priority Critical patent/CN104760139B/zh
Publication of CN104760139A publication Critical patent/CN104760139A/zh
Application granted granted Critical
Publication of CN104760139B publication Critical patent/CN104760139B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种轻质保温砂浆生产工艺,它涉及建筑保温砂浆技术领域,它采用三级混合工艺,具体生产工艺为:首先选用双螺旋式搅拌机将各种添加剂与水泥按1:1‑3比例混合,这样可以使外加剂可初步均匀分散;然后将混合物输入二级搅拌机——强制式无重力搅拌机中,与水泥及纤维进行混合,分散多种功能纤维,为了纤维的均匀分散,搅拌时间应适当加长;最后将二次混合物输入三级搅拌机——轻集料专用搅拌机中,与轻集料进行混合;它能提高添加剂的混合均匀度;可使纤维充分混合均匀;专用搅拌机混合,既缩短轻集料的搅拌时间,减少轻集料的破损,又可使保温砂浆充分搅匀。

Description

一种轻质保温砂浆生产工艺
技术领域
[0001] 本发明涉及建筑保温砂浆技术领域,具体涉及一种轻质保温砂浆生产工艺。背景技术
[0002] 随着建筑保温砂浆的市场应用越来越大,对保温砂浆的质量要求越来越高,传统的保温砂浆生产设备,无论从生产质量上还是生产效率上,都很难满足要求。主要表现为常规的保温砂浆生产一般采用单一搅拌机按次投料的生产工艺。这种生产工艺的优点是投资少,缺点是产品稳定性差,效率较低,轻集料破损率高。
[0003] 由于轻集料在强力搅拌下很容易破碎,从而降低保温砂浆的保温性能。又由于保温砂浆中含有多种纤维,纤维在非强力分散下,分散不开形成小球,将严重影响砂浆的各项性能。又由于在保温砂浆中,有些外加剂含量极少,必须保证充足的搅拌时间,才能分散均匀。因此,传统保温砂浆的生产工艺,已不能适应现在保温砂浆的要求。必须寻找一种更适合的生产工艺来解决这个矛盾。发明内容
[0004] 本发明的目的是提供一种轻质保温砂浆生产工艺,它能提高添加剂的混合均匀度;可使纤维充分混合均匀;专用搅拌机混合,既缩短轻集料的搅拌时间,减少轻集料的破损,又可使保温砂浆充分搅匀。
[0005] 为了解决背景技术所存在的问题,本发明是采用以下技术方案:它采用三级混合工艺,具体生产工艺为:
[0006] (1)由于保温砂浆含有多种外加剂,且某些掺加量极少,因此保证产品的均匀度非常关键;首先选用双螺旋式搅拌机将各种添加剂与水泥按1:1-3比例混合,这样可以使外加剂可初步均匀分散;
[0007] (2)然后将混合物输入二级搅拌机一一强制式无重力搅拌机中,与水泥及纤维进行混合,分散多种功能纤维,为了纤维的均匀分散,搅拌时间应适当加长;
[0008] (3)最后将二次混合物输入三级搅拌机一一轻集料专用搅拌机中,与轻集料进行混合;在严格控制搅拌机低转速的同时,缩短搅拌时间。
[0009] 本发明主要用于以膨胀玻化微珠、珍珠岩等为轻集料,以水泥、石膏等为胶凝材料,以纤维及其他添加剂为辅料,按一定比例进行混合的干混材料的生产加工。
[0010] 本发明具有以下有益效果:[0〇11] A、提尚添加剂的混合均勾度;
[0012] B、可使纤维充分混合均匀;
[0013] C、专用搅拌机混合,既缩短轻集料的搅拌时间,减少轻集料的破损,又可使保温砂浆充分搅匀。
[0014] 具体实施方式:[〇〇15]本具体实施方式采用以下技术方案:它采用三级混合工艺,具体生产工艺为:
[0016] (1)由于保温砂浆含有多种外加剂,且某些掺加量极少,因此保证产品的均匀度非常关键;首先选用双螺旋式搅拌机将各种添加剂与水泥按1:1-3比例混合,这样可以使外加剂可初步均匀分散;
[0017] (2)然后将混合物输入二级搅拌机一一强制式无重力搅拌机中,与水泥及纤维进行混合,分散多种功能纤维,为了纤维的均匀分散,搅拌时间应适当加长;
[0018] (3)最后将二次混合物输入三级搅拌机一一轻集料专用搅拌机中,与轻集料进行混合;在严格控制搅拌机低转速的同时,缩短搅拌时间。
[0019] 本具体实施方式主要用于以膨胀玻化微珠、珍珠岩等为轻集料,以水泥、石膏等为胶凝材料,以纤维及其他添加剂为辅料,按一定比例进行混合的干混材料的生产加工。
[0020] 本具体实施方式具有以下有益效果:
[0021] A、提高添加剂的混合均匀度;[〇〇22] B、可使纤维充分混合均匀;
[0023] C、专用搅拌机混合,既缩短轻集料的搅拌时间,减少轻集料的破损,又可使保温砂浆充分搅匀。

Claims (1)

1.一种轻质保温砂浆生产工艺,其特征在于它采用三级混合工艺,具体生产工艺为:(1) 由于保温砂浆含有多种外加剂,且某些掺加量极少,因此保证产品的均匀度非常关 键;首先选用双螺旋式搅拌机将各种添加剂与水泥按1:1-3比例混合,这样可以使外加剂可 初步均匀分散;(2) 然后将混合物输入二级搅拌机一一强制式无重力搅拌机中,与水泥及纤维进行混 合,分散多种功能纤维,为了纤维的均匀分散,搅拌时间应适当加长;(3) 最后将二次混合物输入三级搅拌机一一轻集料专用搅拌机中,与轻集料进行混合; 在严格控制搅拌机低转速的同时,缩短搅拌时间。
CN201410000147.0A 2014-01-02 2014-01-02 一种轻质保温砂浆生产工艺 Expired - Fee Related CN104760139B (zh)