CN104726650A - T10钢机用丝锥水—空—水淬火热处理工艺 - Google Patents

T10钢机用丝锥水—空—水淬火热处理工艺 Download PDF

Info

Publication number
CN104726650A
CN104726650A CN201510187179.0A CN201510187179A CN104726650A CN 104726650 A CN104726650 A CN 104726650A CN 201510187179 A CN201510187179 A CN 201510187179A CN 104726650 A CN104726650 A CN 104726650A
Authority
CN
China
Prior art keywords
water
screw taps
machines
heat treatment
air
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510187179.0A
Other languages
English (en)
Inventor
郑卫刚
尹佳成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan University of Technology WUT
Original Assignee
Wuhan University of Technology WUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University of Technology WUT filed Critical Wuhan University of Technology WUT
Priority to CN201510187179.0A priority Critical patent/CN104726650A/zh
Publication of CN104726650A publication Critical patent/CN104726650A/zh
Pending legal-status Critical Current

Abstract

本发明涉及T10钢机用丝锥水—空—水淬火热处理工艺,包括有以下步骤:1)将机用丝锥加热,保温,使其奥氏体化;2)然后放入水介质中淬火冷却;3)将机用丝锥从水中取出,置于空气中冷却;4)然后放入水介质中冷却至室温;5)再将机用丝锥转入回火炉进行回火热处理;6)最后将机用丝锥空冷到室温。使用本工艺与传统工艺相比具有以下优点:1)具有无油烟,无火灾,不伤害操作人员身体健康,同时介质成本低,经济效益高;2)处理后的机用丝锥完全达到国际使用标准,使用本工艺机用丝锥的表面硬度可达61HRC以上,芯部硬度可达50HRC以上,韧性和使用寿命比常规热处理时加强,同时变形和开裂现象大大减少。

Description

Tl O钢机用丝锥水一空一水淬火热处理工艺
技术领域
[0001] 本发明涉及一种高碳钢刀具淬火热处理工艺,特别涉及一种TlO钢机用丝锥水一空一水淬火热处理工艺。
背景技术
[0002] 传统热处理工艺中,有些步骤是使用油进行淬火,但是采用油淬时存在不足,由于淬火时产生大量的油烟,使环境受到污染,同时使用油淬会使工件达不到相应的硬度和使用要求。
[0003] 如果采用一种绿色淬火热处理方法,如水一空一水淬火工艺,既可以保证在生产过程中不污染环境,保护工人的身体健康,同时可以使钢材的组织和力学性能可以达到要求,直接产生经济效益,这是非常有益的。
发明内容
[0004] 本发明的目的在于提供一种TlO钢机用丝锥水一空一水淬火热处理工艺,可以解决传统淬火工艺产生的缺陷,在生产过程中不生成油烟,从而减少环境污染,改善由于油淬时,工件淬透性不足的缺点,增加硬度,改善其组织性能和使用性能。
[0005] 为了实现上述目的,本发明采用以下技术方案:T10钢机用丝锥水一空一水淬火热处理工艺,包括有以下步骤:
[0006] I)将机用丝锥加热到770〜800°C,保温2〜3小时,使其奥氏体化;
[0007] 2)然后放入水介质中淬火冷却3〜6秒;
[0008] 3)将机用丝锥从水中取出,置于空气中冷却10〜20秒;
[0009] 4)然后放入水介质中冷却至室温;
[0010] 5)再将机用丝锥转入180〜200°C的回火炉进行回火热处理;
[0011] 6)最后将机用丝锥空冷到室温。
[0012] 按上述方案,所述的机用丝锥直径范围为Φ6〜8mm。
[0013]按上述方案,所述的 TlO 钢含有 C:0.95%〜1.04%,Si ^ 0.35%, Mn ^ 0.40%,P 彡 0.035%, S 彡 0.030%。
[0014] 在机用丝锥的热处理工艺过程中,不采用传统的油淬工艺方法,而是使用水一空一水淬火工艺,使工件组织中得到下贝氏体与条马氏体束交割分布的复相组织,以及少量残余奥氏体等二次析出相的综合作用,这有利于改善材料的韧性和阻止微裂纹的产生与扩展,进而提高钢件的力学性能和组织性能。
[0015] 使用本工艺与传统工艺相比具有以下优点:
[0016] I)使用水一空一水淬火,与传统的油淬工艺对比,具有无油烟,无火灾,不伤害操作人员身体健康,同时介质成本低,经济效益高;
[0017] 2)本工艺采用水一空一水淬火工艺,相对于传统工艺比较,处理后的机用丝锥完全达到国际使用标准,使用本工艺机用丝锥的表面硬度可达61HRC以上,芯部硬度可达 50HRC以上,韧性和使用寿命比常规热处理时加强,同时变形和开裂现象大大减少。
具体实施方式
[0018] 下面结合具体实施例对本发明进行详细说明。
[0019] 实施例1
[0020]直径 Φ6ιήπι TlO 钢机用丝锥,含有 C:1.01%,Si:0.33%, Mn:0.35%, P:0.030%,S:0.030% ;
[0021] I)将机用丝锥加热到780°C,保温2小时,使其奥氏体化;
[0022] 2)将机用丝锥放入水介质中淬火冷却6秒;
[0023] 3)将机用丝锥从水中取出,置于空气中冷却11秒;
[0024] 4)将机用丝锥放入水介质中冷却至室温;
[0025] 5)将机用丝锥转入200 °C的回火炉进行回火热处理3.5小时;
[0026] 6)将机用丝锥空冷到室温;
[0027] 经检测,其表面硬度达63HRC,芯部硬度可达53HRC,韧性和使用寿命比常规热处理时加强,同时变形和开裂现象大大减少。
[0028] 实施例2
[0029]直径 Φ6ιήπι TlO 钢机用丝锥,含有 C:1.01%,Si:0.33%, Mn:0.35%, P:0.030%,S:0.030% ;
[0030] I)将机用丝锥加热到800°C,保温2小时,使其奥氏体化;
[0031] 2)将机用丝锥放入水介质中淬火冷却5秒;
[0032] 3)将机用丝锥从水中取出,置于空气中冷却10秒;
[0033] 4)将机用丝锥放入水介质中冷却至30°C ;
[0034] 5)将机用丝锥转入180°C的回火炉进行回火热处理3小时;
[0035] 6)将机用丝锥空冷到室温;
[0036] 经检测,其表面硬度达62HRC,芯部硬度可达51HRC,韧性和使用寿命比常规热处理时加强,同时变形和开裂现象大大减少。

Claims (3)

1.TlO钢机用丝锥水一空一水淬火热处理工艺,包括有以下步骤: 1)将机用丝锥加热到770〜800°C,保温2〜3小时,使其奥氏体化; 2)然后放入水介质中淬火冷却3〜6秒; 3)将机用丝锥从水中取出,置于空气中冷却10〜20秒; 4)然后放入水介质中冷却至室温; 5)再将机用丝锥转入180〜200°C的回火炉进行回火热处理; 6)最后将机用丝锥空冷到室温。
2.按权利要求1所述的TlO钢机用丝锥水一空一水淬火热处理工艺,其特征在于所述的机用丝锥直径范围为Φ6〜8mm。
3.按权利要求1所述的TlO钢机用丝锥水一空一水淬火热处理工艺,其特征在于所述的 TlO 钢含有 C:0.95%〜1.04%, Si 彡 0.35%,Mn 彡 0.40%,P 彡 0.035%,S 彡 0.030%。
CN201510187179.0A 2015-04-20 2015-04-20 T10钢机用丝锥水—空—水淬火热处理工艺 Pending CN104726650A (zh)