CN104628334A - 一种防冻效果优秀的免蒸免烧空心砖及其制备方法 - Google Patents

一种防冻效果优秀的免蒸免烧空心砖及其制备方法 Download PDF

Info

Publication number
CN104628334A
CN104628334A CN201510025089.1A CN201510025089A CN104628334A CN 104628334 A CN104628334 A CN 104628334A CN 201510025089 A CN201510025089 A CN 201510025089A CN 104628334 A CN104628334 A CN 104628334A
Authority
CN
China
Prior art keywords
parts
brick
water
portland cement
slag
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510025089.1A
Other languages
English (en)
Inventor
黄国栋
刘树林
王其红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gao Xin Building Materials Co Ltd Of Huoqiu County
Original Assignee
Gao Xin Building Materials Co Ltd Of Huoqiu County
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Gao Xin Building Materials Co Ltd Of Huoqiu County filed Critical Gao Xin Building Materials Co Ltd Of Huoqiu County
Priority to CN201510025089.1A priority Critical patent/CN104628334A/zh
Publication of CN104628334A publication Critical patent/CN104628334A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防冻效果优秀的免蒸免烧空心砖,其特征在于,由下列重量份的原料制备制成:普通硅酸盐水泥10-12、粉煤灰30-35、建筑砖渣18-22、废玻璃骨料14-16、蜂窝煤渣5-7、针状硅灰石6-8、尿素0.05-0.1、丙二醇0.1-0.2、甲基纤维素2-3、增效剂15-18、水适量;本发明通过添加尿素、丙二醇等成分以及添加温水进行搅拌等配方与工艺的改进,使得制成的产品具有优秀的抗冻效果;添加特殊工艺制成的增效剂,具有质轻、强度大、防水、保温、抗菌防霉的特点;本发明采用免蒸免烧工艺,节能环保,工艺简单,便于操作,制成的空心砖抗冻、抗压、防震、防水、保温。

Description

一种防冻效果优秀的免蒸免烧空心砖及其制备方法
技术领域
[0001] 本发明涉及建筑材料领域,特别是一种防冻效果优秀的免蒸免烧空心砖及其制备方法。
背景技术
[0002] 混凝土空心砖有质轻、防火、隔音、保温、抗渗、抗震、耐久等几大特点,而且无污染、节能降耗、正是当代所需要的绿色的环保建材,已经成为当代新型墙材中的一个重要组成部分,有广阔的发展空间和发展前景。但是混凝土空心砖到了冬季就会出现沙粒松散,抗压强度降低,容易造成坍塌,是混凝土空心砖致命的弱点。
[0003] 本发明这对这一问题,通过合理配方,添加尿素、丙二醇等防冻剂,并在工艺中添加温水搅拌混凝土,通过这种配方的改进以及工艺的小改进,使得生产出来的产品具有良好的抗冻性,即使在冬天生产也能达到一定抗压强度。本发明添加粉煤灰、建筑砖澄、废玻璃骨料等废弃物经过粉碎后添加到产品的制造中,配合添加特殊工艺制成的增效剂,具有质轻、强度大、防水、保温、抗菌防霉的特点,增强了产品的综合性能。本发明采用免蒸免烧工艺,解决了工艺复杂、浪费能源、污染环境的问题,值得大面积推广使用。
发明内容
[0004] 本发明的目的是提供一种防冻效果优秀的免蒸免烧空心砖及其制备方法。
[0005] 为了实现本发明的目的,本发明通过以下方案实施:
一种防冻效果优秀的免蒸免烧空心砖,由下列重量份的原料制备制成:普通硅酸盐水泥10-12、粉煤灰30-35、建筑砖渣18-22、废玻璃骨料14-16、蜂窝煤渣5_7、针状硅灰石6-8、尿素0.05-0.1、丙二醇0.1-0.2、甲基纤维素2_3、增效剂15-18、水适量;
所述增效剂由以下重量份的原料制备而成:硬脂酸钙1-2、聚乙烯醇缩甲醛胶黏剂1-1.5、普通水泥4-6、聚苯泡沫颗粒3-5、苎麻纤维10-12、棕榈皮9_11、玉米芯13-15、落叶5-7、竹炭3-5、可再分散乳胶粉2-3、聚乙烯吡咯烷酮1-2、水15-20 ;制备方法如下:首先将苎麻纤维、棕榈皮、玉米芯、落叶、竹炭在50-60 0C条件下烘干后与聚苯泡沫颗粒混合粉碎成180-200目混合粉末,然后将可再分散乳胶粉、聚乙烯吡咯烷酮加入2-3倍量的水,搅拌均匀后加入混合粉末,再放入挤出机中造粒,最后将普通水泥以及其余剩余成分制成混合浆料,将浆料喷洒在颗粒表面,自然风干硬化即得增效剂。
[0006] 本发明所述一种防冻效果优秀的免蒸免烧空心砖,由以下具体步骤制成:
(O将建筑砖渣、废玻璃骨料、蜂窝煤渣、针状硅灰石混合后粉碎成80-100目的粉末,然后加入溶于3-4倍量水的甲基纤维素、尿素、丙二醇,混合搅拌10-15分钟后加入除普通硅酸盐水泥、增效剂之外的其余剩余成分,继续加水搅拌成混合浆料;
(2)将普通硅酸盐水泥、增效剂加入30°C -40°C的温水搅拌均匀,然后与步骤(I)中混合浆料混合搅拌8-10分钟,然后倒入制砖机模具中进行压制成型,在30°C _50°C养护10-24小时,最后脱模,将成型后的产品放在室温下保湿养护28即得到本发明砖块。
[0007] 本发明的有益效果是:本发明通过添加尿素、丙二醇等成分以及添加温水进行搅拌等配方与工艺的改进,使得制成的产品具有优秀的抗冻效果;添加特殊工艺制成的增效剂,具有质轻、强度大、防水、保温、抗菌防霉的特点;本发明采用免蒸免烧工艺,节能环保,工艺简单,便于操作,制成的空心砖抗冻、抗压、防震、防水、保温。
具体实施方案
[0008] 下面通过具体实例对本发明进行详细说明。
[0009] 一种防冻效果优秀的免蒸免烧空心砖,由下列重量份(公斤)的原料制备制成:普通硅酸盐水泥10、粉煤灰30、建筑砖渣18、废玻璃骨料14、蜂窝煤渣5、针状硅灰石6、尿素
0.05、丙二醇0.1、甲基纤维素2、增效剂15、水适量;
所述增效剂由以下重量份(公斤)的原料制备而成:硬脂酸钙1、聚乙烯醇缩甲醛胶黏剂
1、普通水泥4、聚苯泡沫颗粒3、苎麻纤维10、棕榈皮9、玉米芯13、落叶5、竹炭3、可再分散乳胶粉2、聚乙烯吡咯烷酮1、水15 ;制备方法如下:首先将苎麻纤维、棕榈皮、玉米芯、落叶、竹炭在50-60°C条件下烘干后与聚苯泡沫颗粒混合粉碎成180-200目混合粉末,然后将可再分散乳胶粉、聚乙烯吡咯烷酮加入2-3倍量的水,搅拌均匀后加入混合粉末,再放入挤出机中造粒,最后将普通水泥以及其余剩余成分制成混合浆料,将浆料喷洒在颗粒表面,自然风干硬化即得增效剂。
[0010] 本发明所述一种防冻效果优秀的免蒸免烧空心砖,由以下具体步骤制成:
(O将建筑砖渣、废玻璃骨料、蜂窝煤渣、针状硅灰石混合后粉碎成80-100目的粉末,然后加入溶于3-4倍量水的甲基纤维素、尿素、丙二醇,混合搅拌10-15分钟后加入除普通硅酸盐水泥、增效剂之外的其余剩余成分,继续加水搅拌成混合浆料;
(2)将普通硅酸盐水泥、增效剂加入30°C -40°C的温水搅拌均匀,然后与步骤(I)中混合浆料混合搅拌8-10分钟,然后倒入制砖机模具中进行压制成型,在30°C _50°C养护10-24小时,最后脱模,将成型后的产品放在室温下保湿养护28即得到本发明砖块。
[0011] 经各种试验测定,本发明空心砖的各项性能为:孔隙率为44.6%,导热系数为0.07W/ (m.K),抗压强度为 14.1Mpa0

Claims (2)

1.一种防冻效果优秀的免蒸免烧空心砖,其特征在于,由下列重量份的原料制备制成:普通硅酸盐水泥10-12、粉煤灰30-35、建筑砖渣18-22、废玻璃骨料14-16、蜂窝煤渣5-7、针状硅灰石6-8、尿素0.05-0.1、丙二醇0.1-0.2、甲基纤维素2_3、增效剂15-18、水适量; 所述增效剂由以下重量份的原料制备而成:硬脂酸钙1-2、聚乙烯醇缩甲醛胶黏剂1-1.5、普通水泥4-6、聚苯泡沫颗粒3-5、苎麻纤维10-12、棕榈皮9_11、玉米芯13-15、落叶5-7、竹炭3-5、可再分散乳胶粉2-3、聚乙烯吡咯烷酮1-2、水15-20 ;制备方法如下:首先将苎麻纤维、棕榈皮、玉米芯、落叶、竹炭在50-60 0C条件下烘干后与聚苯泡沫颗粒混合粉碎成180-200目混合粉末,然后将可再分散乳胶粉、聚乙烯吡咯烷酮加入2-3倍量的水,搅拌均匀后加入混合粉末,再放入挤出机中造粒,最后将普通水泥以及其余剩余成分制成混合浆料,将浆料喷洒在颗粒表面,自然风干硬化即得增效剂。
2.根据权利要求1所述一种防冻效果优秀的免蒸免烧空心砖,其特征在于,由以下具体步骤制成: (O将建筑砖渣、废玻璃骨料、蜂窝煤渣、针状硅灰石混合后粉碎成80-100目的粉末,然后加入溶于3-4倍量水的甲基纤维素、尿素、丙二醇,混合搅拌10-15分钟后加入除普通硅酸盐水泥、增效剂之外的其余剩余成分,继续加水搅拌成混合浆料; (2)将普通硅酸盐水泥、增效剂加入30°C -40°C的温水搅拌均匀,然后与步骤(I)中混合浆料混合搅拌8-10分钟,然后倒入制砖机模具中进行压制成型,在30°C _50°C养护10-24小时,最后脱模,将成型后的产品放在室温下保湿养护28即得到本发明砖块。
CN201510025089.1A 2015-01-19 2015-01-19 一种防冻效果优秀的免蒸免烧空心砖及其制备方法 Pending CN104628334A (zh)