CN104592271A - Cadmium isophthalate anthracene cyclo-bis(triazolyl) complex used as potential fluorescent material and preparation method of cadmium isophthalate anthracene cyclo-bis(triazolyl) complex - Google Patents
Cadmium isophthalate anthracene cyclo-bis(triazolyl) complex used as potential fluorescent material and preparation method of cadmium isophthalate anthracene cyclo-bis(triazolyl) complex Download PDFInfo
- Publication number
- CN104592271A CN104592271A CN201510088170.4A CN201510088170A CN104592271A CN 104592271 A CN104592271 A CN 104592271A CN 201510088170 A CN201510088170 A CN 201510088170A CN 104592271 A CN104592271 A CN 104592271A
- Authority
- CN
- China
- Prior art keywords
- triazole
- anthracene
- ipa
- phthalic acid
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cadmium isophthalate anthracene cyclo-bis(triazolyl) complex {[Cd(ipa)(L)].2DMF.3H2O} (1), the structural unit of which is as shown in the figure 1. The invention further discloses a preparation method of {[Cd(ipa)(L)].2DMF.3H2O} (1) (L is equal to 1-[9-(1H-1,2,4-triazole-1-yl)anthracene-10-yl]-1H-1,2,4-triazole, ipa is equal to isophthalic acid, and DMF is equal to N,N'-dimethyl formamide), wherein the preparation method adopts a normal temperature volatilization method and comprises the following steps: placing Cd(NO3)2.(6H2O), isophthalic acid and L into a mixed solvent of DMF and water, stirring for half an hour, filtering to obtain a filtrate, and volatilizing the filtrate at normal temperature for one week, so as to obtain a yellow rod-like crystal suitable for X-ray single crystal diffraction. The invention further discloses application of the cadmium isophthalate anthracene cyclo-bis(triazolyl) complex used as a potential fluorescent material.
Description
The present invention obtains state natural sciences fund general project (21471113), young top-notch personnel's support plan, Tianjin Education Commission general project (20140506), Tianjin Normal University Middl-age and youth faculty Academic innovations advance planning item (52XC1401), the subsidy of Tianjin State Scientific and Technological Commission general project (11JCYBJC03600) and Tianjin innovation team of institution of higher education training plan (TD12-5038).
Technical field
The invention belongs to organic and Inorganic synthese technical field, relate to and state two triazole m-phthalic acid cadmium complex { [Cd (ipa) (the L)] 2DMF3H of anthracene nucleus
2o} (
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) preparation method and application as potential fluorescent material.
Background technology
1,2,4-triazole and derivative thereof have the coordination feature of pyrazoles and imidazoles concurrently, are the bridgingligands that coordination ability is stronger, have synthesized at present and have characterized a large amount of monokaryons, multinuclear and multidimensional compound.These parts can with 1, nitrogen-atoms on 2 and metallic ion coordination form N1, N2-bridging pattern, for 4 unsubstituted 1,2,4-triazole derivative is by 2, nitrogen-atoms on 4 forms N2, N4-bridging pattern, this N2, N4-bridging pattern is with the N1 of imidazoles in metalloenzyme, and N3-bridging mode class seemingly.Special purpose for triazole class compounds also shows in the design of molecular device, and the metal complexes that synthesis has different dimension has been the vital step of device.
The present invention selects Cd (NO
3)
26H
2o, ipa and L filter stir half an hour in the mixed solvent of DMF and water after, and filtrate normal temperature obtains yellow rhabdolith { [Cd (ipa) (L)] 2DMF3H of applicable X-ray single crystal diffraction after volatilizing one week
2o} (
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide).This title complex also can be used as potential fluorescent material aspect and is applied.
Summary of the invention
Another object of the present invention is to provide a kind of anthracene nucleus two triazole m-phthalic acid cadmium complex { [Cd (ipa) (L)] 2DMF3H
2o}
n(
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) monocrystalline and preparation method thereof.
Current inventor provides following technical scheme for this reason:
Two triazole m-phthalic acid cadmium complex { [Cd (ipa) (the L)] 2DMF3H of anthracene nucleus
2o} (
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) structural motif as shown in Figure 1.
The present invention further discloses two triazole m-phthalic acid cadmium complex { [Cd (ipa) (the L)] 2DMF3H of anthracene nucleus
2o} (
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) monocrystalline, it is characterized in that this single crystal structure adopts APEX II CCD single crystal diffractometer, use through graphite monochromatised Mok alpha-ray (λ=0.71073)) be incident radiation, with
ω-2
θscan mode collects point diffraction, obtains unit cell parameters, utilize SHELXL-97 direct method to solve single crystal data from difference Fourier electron density map through least-squares refinement:
Table 1. title complex
1crystallographic data
two triazole m-phthalic acid cadmium complex { [Cd (ipa) (the L)] 2DMF3H of anthracene nucleus of the present invention
2o}
n(
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) preparation method of monocrystalline, its feature is at employing " normal temperature volatilization method ", i.e. Cd (NO
3)
26H
2o, m-phthalic acid and L filter stir half an hour in the mixed solvent of DMF and water after, and filtrate normal temperature volatilizees one week to prepare this title complex
the present invention's preferred example:
The preparation of 1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole (L)
" one kettle way " is adopted at polar solvent, by 9,10-dibromoanthracene, 1H-1,2,4-triazole, salt of wormwood and cupric oxide react preparation in a heated condition; Wherein 9,10-dibromoanthracenes: 1H-1,2,4-triazole: salt of wormwood: the mol ratio of cupric oxide is 2:10-15:30:1;
The present invention is 9,10-dibromoanthracenes preferably: 1H-1,2,4-triazole: salt of wormwood: the mol ratio of cupric oxide is 2:10-15:30:1; Temperature of reaction 100 DEG C, 48 hours reaction times.In polar solvent, adopt " one kettle way ", by 9,10-dibromoanthracene, 1H-1,2,4-triazole, this organic compound prepared in a heated condition by salt of wormwood and cupric oxide;
Another preferred embodiment of the present invention
L (0.1 mmol), m-phthalic acid (0.1 mmol) and Cd (NO
3)
26H
2o (0.2 mmo) produces a small amount of yellow mercury oxide stir half an hour in 10 mL water and 6 mL DMF mixed solvents after, and after filtration, filtrate is in yellow.Normal temperature has the yellow bulk crystals of applicable X-ray single crystal diffraction after volatilizing one week.Productive rate: 35%.Ultimate analysis (C
32h
36cdN
8o
9) theoretical value (%): C, 48.71; H, 4.60; N, 14.20.Measured value: C, 48.77; H, 4.64; N, 14.29.
The present invention further discloses two triazole m-phthalic acid cadmium complex { [Cd (ipa) (the L)] 2DMF3H of anthracene nucleus
2o} (
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) can be used as potential fluorescent material aspect and applied.
Two triazole m-phthalic acid cadmium complex { [Cd (ipa) (the L)] 2DMF3H of a kind of anthracene nucleus disclosed by the invention
2o} (
1) advantage and disadvantage that has of (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) monocrystalline is:
(1) operation is simple and easy to do.
(2) reaction yield is high, and the purity of products obtained therefrom is high.
(3) { [Cd (ipa) (the L)] 2DMF3H prepared by the present invention
2o}
n(
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) production cost is low, and method is easy, is applicable to scale operation.
Accompanying drawing explanation
Fig. 1: title complex
1crystalline structure primitive figure;
Fig. 2: title complex
1two-dimensional layered structure figure.
Embodiment
Below in conjunction with embodiment, the present invention is described further, and embodiment is only indicative, never means that it limits the scope of the invention by any way.All raw materials are such as: anthracene nucleus etc. are all buy from chemical reagents corporation both domestic and external, through continuing to purify but directly use.Raw materials used 9,10-dibromoanthracenes, 1H-1,2,4-triazole, salt of wormwood, cupric oxide etc. all have commercially available.
Embodiment 1
9,10-dibromoanthracene: 1H-1,2,4-triazole: salt of wormwood: the mol ratio of cupric oxide is 2:10-15:30:1
CuO (0.0398 mg is added respectively in 50 mL, tri-mouthfuls of round-bottomed flasks that magneton, reflux exchanger and thermometer are housed, 0.5 mmol), salt of wormwood (2.0731 g, 15 mmol), triazole (0.345 mg, 5 mmol), 9,10-dibromoanthracene (0.3360 g, 1 mmol), 20 mL DMF.Start and be stirred in 100
oc, reacts 24 hours.After reaction terminates, reaction solution is down to room temperature, filter, filtrate adds 100 mL water, separates out and precipitates in a large number, suction filtration, collects filter cake, 1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole (L), yield 60%.
Embodiment 2
1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole (0.1 mmol), m-phthalic acid (0.1 mmol) and Cd (NO
3)
26H
2o (0.2 mmo) produces a small amount of yellow mercury oxide stir half an hour in 10 mL water and 6 mL DMF mixed solvents after, and after filtration, filtrate is in yellow.Normal temperature has the yellow bulk crystals of applicable X-ray single crystal diffraction after volatilizing one week.Productive rate: 35%.Ultimate analysis (C
32h
36cdN
8o
9) theoretical value (%): C, 48.71; H, 4.60; N, 14.20.Measured value: C, 48.77; H, 4.64; N, 14.29.Embodiment 3
Crystal structure determination adopts APEX II CCD single crystal diffractometer, use through graphite monochromatised Mok alpha-ray (λ=0.71073) be incident radiation, with
ω-2
θscan mode collects point diffraction, obtains unit cell parameters, utilize software to solve crystalline structure from difference Fourier electron density map through least-squares refinement, and through Lorentz lorentz and polarizing effect correction.All H atom are synthesized by difference Fourier and are determined through desirable position calculation.Detailed axonometry data are in table 1.Structural motif is shown in Fig. 1, and two-dimensional layered structure is shown in Fig. 2.
Table 1. title complex
1crystallographic data
Embodiment 4
The concrete instance that dyestuff or luminous agent use
Method: PARSTAT 2273 electrochemical workstation of differentiated pulse volt-ampere (DPV) the curve negotiating Princeton Applied Research Laboratory development of dye solution is measured.The DPV test of solution adopts three-electrode system, and glass-carbon electrode is working electrode, and supporting electrode is platinum plate electrode, homemade Ag/AgNO
3electrode is reference electrode; Electrolytic solution is the acetonitrile solution of 0.1molL-1TBAP.Reduce reversible point to for interior mark with Oxidation of Ferrocene, obtains the correction value between test system and standard hydrogen electrode system.
Monochromatic incident light photoelectric transformation efficiency (IPCE) describes the photoelectric transformation efficiency of DSCs under monochromatic ray effect, is transfer to the electronic number of external circuit and the ratio of incident light subnumber.During measurement, use 500 W xenon lamps as light source, the monochromatic ray of incident light under the multifunctional assembled grating spectrograph of WDS-5 type obtains different wave length λ; Monochromatic light exposure, in the light anode of battery, reads current value I by Keithley2400 digital sourcemeter.Monochromatic good fortune illumination is measured by USB4000 plug-and-play Miniature optical linear light spectrometer.
Step: in order to definitely understand dyestuff at TiO
2adsorptive capacity on film, by dye sensitization TiO
2(geometric area is about 1 cm to nanometer crystal film
2) be immersed in 10 mL 0.01 molL
-1sodium hydroxide methanol solution in spend the night, treat that the absorbancy of attached mensuration solution separated completely by dyestuff.Wash one's face and rinse one's mouth according to absorbancy and molar absorptivity and can calculate the adsorptive capacity of dyestuff on unit surface nanometer crystal film.The adsorptive capacity of this title complex is 1.4 × 10
-4mol/cm
2.
Result: compared with the methanol solution of dyestuff, dyestuff is at TiO
2absorption spectrum on film all obviously broadens and red shift.This shows that dye molecule is at TiO
2define the J-aggregate of first also tail.From the principle of work of DSCs, the spectrum broadening that dye aggregation causes and red shift are very favourable for the widening of photoelectric response scope of dyestuff.But meanwhile, dye aggregation cognition reduces its electron injection efficiency greatly, thus causes the degraded performance of DSCs.So, in dye solution, usually add coadsorbent to suppress the gathering of dyestuff.This title complex is in methanol solution and at TiO
2the fluorometric investigation of the purple solution on membrane electrode adopts 2.5 × 10
-5the methanol solution of mol/L, maximum emission wavelength is positioned at 535 nm.
After the preferred embodiment described in detail, be familiar with this technology personage can be well understood to, do not departing under above-mentioned claim and spirit and can carry out various change and amendment, all above embodiment is done according to technical spirit of the present invention any simple modification, equivalent variations and modification, all belong to the scope of technical solution of the present invention.And the present invention is not also by the restriction of example embodiment in specification sheets.
Claims (4)
1. two triazole m-phthalic acid cadmium complex { [Cd (ipa) (L)] 2DMF3H of anthracene nucleus
2o} (
1) structural motif as shown in Figure 1:
L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide.
2. the monocrystalline of the two triazole m-phthalic acid cadmium complex of anthracene nucleus described in claim 1, it is characterized in that this single crystal structure adopts APEX II CCD single crystal diffractometer, use through graphite monochromatised Mok alpha-ray (λ=0.71073) be incident radiation, with
ω-2
θscan mode collects point diffraction, obtains unit cell parameters, utilize software to solve single crystal data from difference Fourier electron density map through least-squares refinement:
Table 1. title complex
1crystallographic data
。
3. two triazole m-phthalic acid cadmium complex { [Cd (ipa) (L)] 2DMF3H of anthracene nucleus described in claim 1
2o}
n(
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) preparation method, it is characterized in that it be adopt " normal temperature volatilization method ", i.e. Cd (NO
3)
26H
2o, ipa and L filter, to prepare this title complex after filtrate normal temperature volatilizees one week stir half an hour in the mixed solvent of DMF and water after
L ipa。
4. two triazole m-phthalic acid cadmium complex { [Cd (ipa) (L)] 2DMF3H of anthracene nucleus described in claim 1
2o} (
1) (L=1-[9-(1H-1,2,4-triazole-1-base) anthracene-10-base]-1H-1,2,4-triazole, ipa=m-phthalic acid, DMF=N, N'-dimethyl formamide) as the application of potential fluorescent material aspect.