CN104591740A - 一种耐冲击陶瓷材料及其制备方法 - Google Patents

一种耐冲击陶瓷材料及其制备方法 Download PDF

Info

Publication number
CN104591740A
CN104591740A CN201510013960.6A CN201510013960A CN104591740A CN 104591740 A CN104591740 A CN 104591740A CN 201510013960 A CN201510013960 A CN 201510013960A CN 104591740 A CN104591740 A CN 104591740A
Authority
CN
China
Prior art keywords
weight
shock
parts
stupalith
resistant
Prior art date
Application number
CN201510013960.6A
Other languages
English (en)
Inventor
陆全明
Original Assignee
吴江佳亿电子科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 吴江佳亿电子科技有限公司 filed Critical 吴江佳亿电子科技有限公司
Priority to CN201510013960.6A priority Critical patent/CN104591740A/zh
Publication of CN104591740A publication Critical patent/CN104591740A/zh

Abstract

本发明公开了一种耐冲击陶瓷材料及其制备方法,该耐冲击陶瓷材料,由包含以下重量份的组分制成:碳化硅88-93份、二硼化钛纤维5-12份、三氧化二锑5-7份、二苯基甲烷二异氰酸酯4-5份、聚乙烯醇2-3份、碳酸钡2-3份、三氧化钨2-3份、氧化铜0.5-1.5份、酒石酸0.5-1份和双(3,5-三级丁基-4-羟基苯基)硫醚0.05-0.9份。本发明还提供了一种耐冲击陶瓷材料的制备方法,该方法包括以下步骤:称取上述组分混合均匀,升温至500-700℃,保温1-2小时,超声10-15分钟,加入窑炉中1250-1300℃中烧结2-3h,冷却,得到耐冲击陶瓷材料。

Description

一种耐冲击陶瓷材料及其制备方法
技术领域
[0001] 本发明属于陶瓷材料领域,特别涉及一种耐冲击陶瓷材料及其制备方法。
[0002]
背景技术
[0003]陶瓷材料是用天然或合成化合物经过成形和高温烧结制成的一类无机非金属材 料。根据陶瓷材料的用途可以将陶瓷材料分为普通陶瓷材料和特种陶瓷材料。
[0004]陶瓷材料暗器性能又可分为高温陶瓷、超硬质陶瓷、高韧陶瓷、半导体陶瓷。电解 质陶瓷、磁性陶瓷、导电性陶瓷等。随着成分、结构和工艺的不断改进,新型陶瓷层出不穷。 因此制备得到的陶瓷材料也相应的具有特殊的力学、光、声、电、磁、热等性能,具有高熔点、 高硬度、高耐磨性、耐氧化等优点。
[0005]氮化硅高强度陶瓷以强度高著称,可用于制造燃气轮机的燃烧器、叶片、涡轮等。 氨化硅陶瓷可代替金属制造发动机的耐热部件,能大幅度提高工件温度,从而提高热效率, 降低燃料消耗,节约能源,减少发动机的体积和重量,而且又代替了如镍、铬、钠等重要金属 材料。
[0006]因此利用陶瓷的光学性能制造固体激光材料、光导纤维、光储存材料,以及陶瓷还 用作压电材料、磁性材料、基底材料等。都证实了陶瓷材料有着广阔的应用前景。
[0007]
发明内容
[0008]针对上述的需求,本发明特别提供了一种耐冲击陶瓷材料及其制备方法。
[0009]本发明的目的可以通过以下技术方案实现: 一种耐冲击陶瓷材料,由包含以下重量份的组分制成: 碳化硅 88-93份, 二硼化钛纤维 5-12份, 三氧化二锑5-7份, 二苯基甲烷二异氰酸酯 4-5份, 聚乙烯醇 2-3份, 碳酸钡 2-3份, 三氧化钨 2-3份, 氧化铜 0. 5-1. 5份, 酒石酸 0. 5-1份, 双(3, 5-三级丁基-4-羟基苯基)硫醚 0. 05-0. 9份。
[0010]所述二硼化钛纤维的直径为20-35纳米。
[0011]所述聚乙烯醇的平均分子量为7500-8000。
[0012] 所述组分还包括色粉0-0. 5重量份。
[0013] 一种耐冲击陶瓷材料的制备方法,该方法包括以下步骤: (1) 称取碳化硅88-93重量份、二硼化钛纤维5-12重量份、二苯基甲烷二异氰酸酯4-5 重量份、聚乙烯醇2-3重量份、酒石酸0. 5-1重量份和双(3, 5-三级丁基-4-羟基苯基)硫 醚0. 05-0. 9重量份,加入推进式搅拌机中,混合均匀; (2) 称取三氧化二锑5-7重量份、碳酸钡2-3重量份、三氧化钨2-3重量份、氧化铜 0. 5-1. 5重量份和色粉0-0. 5重量份,加入球磨机中充分球磨,升温至500-70(TC,保温1-2 小时; (3) 将步骤1的产物中加入步骤2的产物,超声10-15分钟,加入窑炉中1250-1300°C 中烧结2-3h,冷却,得到耐冲击陶瓷材料。
[0014] 步骤1中所述混合温度为80_100°C。
[0015] 本发明与现有技术相比,其有益效果为: (1)本发明制得的耐冲击陶瓷材料具有耐高温、耐高压性能,同时具有抗冲击性能好、 重量轻、抗拉强度高和寿命长的特点。
[0016] (2)本发明制得的耐冲击陶瓷材料在不同的使用环境中仍能保持良好的稳定性和 耐候性。
[0017] (3)本发明的耐冲击陶瓷材料,其制备方法简单,易于工业化生产。
具体实施方式
[0018] 以下结合实施例对本发明作进一步的说明。
[0019] 实施例1 (1) 称取碳化娃88kg、直径为20纳米的二硼化钛纤维5kg、二苯基甲烧二异氰酸酯4kg、 平均分子量为7500的聚乙烯醇2kg、酒石酸lkg和双(3, 5-三级丁基-4-羟基苯基)硫醚 0. 05kg,加入推进式搅拌机中,在80°C温度下混合均勻; (2) 称取三氧化二锑5kg、碳酸钡2kg、三氧化钨2kg和氧化铜lkg,加入球磨机中充分 球磨,升温至500°C,保温1小时; (3) 将步骤1的产物中加入步骤2的产物,超声10分钟,加入窑炉中1300°C中烧结2h, 冷却,得到耐冲击陶瓷材料。
[0020] 制得耐冲击陶瓷材料的性能测试结果如表1所示。
[0021] 实施例2 (1) 称取碳化硅93kg、直径为35纳米的二硼化钛纤维12kg、二苯基甲烷二异氰酸酯 5kg、平均分子量为8000的聚乙烯醇3kg、酒石酸0. 5kg和双(3, 5-三级丁基-4-羟基苯基) 硫醚0. 9kg,加入推进式搅拌机中,在95°C温度下混合均匀; (2) 称取三氧化二铺7kg、碳酸钡3kg、三氧化鹤2kg、氧化铜0. 5kg和日落黄0. 5kg,加 入球磨机中充分球磨,升温至600°C,保温2小时; (3) 将步骤1的产物中加入步骤2的产物,超声15分钟,加入窑炉中1250°C中烧结3h, 冷却,得到耐冲击陶瓷材料。
[0022] 制得耐冲击陶瓷材料的性能测试结果如表1所示。
[0023] 实施例3 (1)称取碳化硅90kg、直径为20纳米的二硼化钛纤维7kg、二苯基甲烷二异氰酸酯4kg、 平均分子量为7500的聚乙烯醇3kg、酒石酸0. 8kg和双(3, 5-三级丁基-4-羟基苯基)硫 醚0. 5kg,加入推进式搅拌机中,在90°C温度下混合均匀; (2) 称取三氧化二铺6kg、碳酸钡3kg、三氧化鹤3kg和氧化铜1. 5kg,加入球磨机中充 分球磨,升温至700°C,保温1小时; (3) 将步骤1的产物中加入步骤2的产物,超声12分钟,加入窑炉中1250°C中烧结2h, 冷却,得到耐冲击陶瓷材料。
[0024] 制得耐冲击陶瓷材料的性能测试结果如表1所示。
[0025] 实施例4 (1) 称取碳化娃92kg、直径为30纳米的二硼化钛纤维8kg、二苯基甲烧二异氰酸酯5kg、 平均分子量为7500的聚乙烯醇3kg、酒石酸lkg和双(3, 5-三级丁基-4-羟基苯基)硫醚 0. 6kg,加入推进式搅拌机中,在85°C温度下混合均勻; (2) 称取三氧化二锑5kg、碳酸钡2kg、三氧化钨2kg和氧化铜0. 5kg,加入球磨机中充 分球磨,升温至500°C,保温2小时; (3) 将步骤1的产物中加入步骤2的产物,超声15分钟,加入窑炉中1300°C中烧结2h,冷却,得到耐冲击陶瓷材料。
[0026] 制得耐冲击陶瓷材料的性能测试结果如表1所示。
[0027]表1
Figure CN104591740AD00051
本发明不限于这里的实施例,本领域技术人员根据本发明的揭示,不脱离本发明范畴 所做出的改进和修改都应该在本发明的保护范围之内。

Claims (6)

1. 一种耐冲击陶瓷材料,其特征在于,由包含以下重量份的组分制成: 碳化硅 88-93份, 二硼化钛纤维 5-12份, 三氧化二锑5-7份, 二苯基甲烷二异氰酸酯 4-5份, 聚乙烯醇 2-3份, 碳酸钡 2-3份, 三氧化钨 2-3份, 氧化铜 0. 5-1. 5份, 酒石酸 0. 5-1份, 双(3, 5-三级丁基-4-羟基苯基)硫醚 0. 05-0. 9份。
2. 根据权利要求1所述的耐冲击陶瓷材料,其特征在于,所述二硼化钛纤维的直径为 20-35纳米。
3. 根据权利要求1所述的耐冲击陶瓷材料,其特征在于,所述聚乙烯醇的平均分子量 为 7500-8000。
4. 根据权利要求1所述的耐冲击陶瓷材料,其特征在于,所述组分还包括色粉0-0. 5重 量份。
5. -种耐冲击陶瓷材料的制备方法,其特征在于,该方法包括以下步骤: (1) 称取碳化硅88-93重量份、二硼化钛纤维5-12重量份、二苯基甲烷二异氰酸酯4-5 重量份、聚乙烯醇2-3重量份、酒石酸0. 5-1重量份和双(3, 5-三级丁基-4-羟基苯基)硫 醚0. 05-0. 9重量份,加入推进式搅拌机中,混合均匀; (2) 称取三氧化二锑5-7重量份、碳酸钡2-3重量份、三氧化钨2-3重量份、氧化铜 0. 5-1. 5重量份和色粉0-0. 5重量份,加入球磨机中充分球磨,升温至500-70(TC,保温1-2 小时; (3) 将步骤1的产物中加入步骤2的产物,超声10-15分钟,加入窑炉中1250-1300°C 中烧结2-3 h,冷却,得到耐冲击陶瓷材料。
6. 根据权利要求5所述的耐冲击陶瓷材料的制备方法,其特征在于,步骤1中所述混合 温度为80-KKTC。
CN201510013960.6A 2015-01-12 2015-01-12 一种耐冲击陶瓷材料及其制备方法 CN104591740A (zh)