CN104496417B - 高档骨质日用瓷 - Google Patents

高档骨质日用瓷 Download PDF

Info

Publication number
CN104496417B
CN104496417B CN201410735688.8A CN201410735688A CN104496417B CN 104496417 B CN104496417 B CN 104496417B CN 201410735688 A CN201410735688 A CN 201410735688A CN 104496417 B CN104496417 B CN 104496417B
Authority
CN
China
Prior art keywords
parts
grade
daily
sclerotin
household china
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410735688.8A
Other languages
English (en)
Other versions
CN104496417A (zh
Inventor
吴锐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Dahongying coating Co. Ltd.
Original Assignee
Nantong Dahongying Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Dahongying Coating Co Ltd filed Critical Nantong Dahongying Coating Co Ltd
Priority to CN201410735688.8A priority Critical patent/CN104496417B/zh
Publication of CN104496417A publication Critical patent/CN104496417A/zh
Application granted granted Critical
Publication of CN104496417B publication Critical patent/CN104496417B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高档骨质日用瓷,制作方法包括以下步骤:(1)按如下质量份数称取原材料:石英19~24份,斜长石10~16份,绿泥石3~6份,莫来石1~2份,骨粉35~43份,黑云母2~4份,CMC 0.2~0.5份,变石0.1~0.3份,将原材料按料:球:水=1:2:0.75入球磨湿磨10h,过300目筛筛余0.2%,除铁备用;(2)注浆:以25~30MPa的压力将泥浆注入模腔,0.5h后取出坯体烘干;(3)烧制:坯体入隧道窑烧制5~7h,温度范围为1300~1350℃,自然冷却,得到高档骨质日用瓷。所制得的高档骨质日用瓷其表面呈象牙色,精致高档,成品率达95%。

Description

高档骨质日用瓷
技术领域
[0001 ]本发明涉及日用陶瓷材料领域,更具体地,涉及一种高档骨质日用瓷。
背景技术
[0002]骨质瓷因其造型独特、简洁明快,质地洁白而细腻,长期以来一直是各国贵族用瓷,是唯一世界上公认的高档瓷种,距今已有300多年的历史。因其“薄如纸、透如镜、声如磬、白如玉”,瓷质细腻通透,器型美观典雅,彩面润泽光亮,花面多姿多彩的特点,成就了它洁白的质地和华贵的造型,兼有使用和艺术的双重价值,历史上是宫廷专用品和贵族收藏之珍品,是权力和地位的象征,受到不少买家的青睐,号称“瓷器之王”。骨质瓷在经过一代代名匠之手后,逐渐成为世界陶瓷珍品。骨质瓷用料考究,制作精细,标准严格,它的规整度、洁白度、透明度、热稳定性等诸项指标均要求极高。由于高档骨质瓷工艺复杂,制作较普通日用瓷困难,其生产技术难以普及。
发明内容
[0003]本发明的目的是提供一种高档骨质日用瓷,其表面呈象牙色,精致高档。
[0004]本发明目的通过以下技术方案予以实现:
[0005]提供一种高档骨质日用瓷,制作方法包括以下步骤:
[0006] (I)按如下质量份数称取原材料:石英19〜24份,斜长石10〜16份,绿泥石3〜6份,莫来石I〜2份,骨粉35〜43份,黑云母2〜4份,CMC 0.2〜0.5份,变石0.1〜0.3份,将原材料按料:球:水=1:2:0.75入球磨湿磨1h,过300目筛筛余0.2%,除铁备用;
[0007] (2)注浆:以25〜30MPa的压力将泥浆注入模腔,0.5h后取出坯体烘干;
[0008] (3)烧制:坯体入隧道窑烧制5〜7h,自然冷却,得到高档骨质日用瓷。
[0009]优选地,步骤(I)中的原材料由以下重量分数的各组分组成:石英21份,斜长石14份,绿泥石5份,莫来石I份,骨粉39份,黑云母3份,CMC 0.4份,变石0.1份。
[0010] 优选地,步骤(3 )中的烧制温度范围为1300〜1350°C。
[0011 ]与现有技术相比,本发明具有以下有益效果:
[0012]本发明提供了一种高档骨质日用瓷,其表面呈象牙色,精致高档,成品率达95%。
具体实施方式
[0013]下面结合具体实施例对本发明作进一步的说明。
[0014] 实施例1
[0015]本实施例公开了一种高档骨日用质瓷餐具,制作方法包括以下步骤:
[0016] (I)按如下质量份数称取原材料:石英21份,斜长石14份,绿泥石5份,莫来石I份,骨粉39份,黑云母3份,CMC 0.4份,变石0.1份,将原材料按料:球:水=1:2:0.75入球磨湿磨1h,过300目筛筛余0.2%,除铁备用;
[0017] (2)注浆:以25MPa的压力将泥浆注入模腔,0.5h后取出坯体烘干;
[0018] (3)烧制:坯体入隧道窑烧制5h,温度范围为1300°C,自然冷却,得到高档骨质日用
bL.0
[0019] 实施例2
[0020]本实施例公开了一种高档骨质日用瓷餐具,制作方法包括以下步骤:
[0021] (I)按如下质量份数称取原材料:石英19份,斜长石10份,绿泥石3份,莫来石2份,骨粉35份,黑云母2份,CMC 0.2份,变石0.3份,将原材料按料:球:水=1:2:0.75入球磨湿磨1h,过300目筛筛余0.2%,除铁备用;
[0022] (2)注浆:以30MPa的压力将泥浆注入模腔,0.5h后取出坯体烘干;
[0023] (3)烧制:坯体入隧道窑烧制7h,温度范围为1350°C,自然冷却,得到高档骨质日用
bL.0
[0024] 实施例3
[0025]本实施例公开了一种高档骨质日用瓷茶具,制作方法包括以下步骤:
[0026] (I)按如下质量份数称取原材料:石英24份,斜长石16份,绿泥石6份,莫来石I份,骨粉43份,黑云母4份,CMC 0.5份,变石0.1份,将原材料按料:球:水=1:2:0.75入球磨湿磨1h,过300目筛筛余0.2%,除铁备用;
[0027] (2)注浆:以28MPa的压力将泥浆注入模腔,0.5h后取出坯体烘干;
[0028] (3)烧制:坯体入隧道窑烧制6h,温度范围为1320°C,自然冷却,得到高档骨质日用
bL.0
[0029] 实施例4
[0030]本实施例公开了一种高档骨质日用瓷咖啡具,制作方法包括以下步骤:
[0031] (I)按如下质量份数称取原材料:石英21份,斜长石12份,绿泥石4份,莫来石1.8份,骨粉38份,黑云母3.5份,CMC 0.3份,变石0.2份,将原材料按料:球:水=1:2:0.75入球磨湿磨1h,过300目筛筛余0.2%,除铁备用;
[0032] (2)注浆:以27MPa的压力将泥浆注入模腔,0.5h后取出坯体烘干;
[0033] (3)烧制:坯体入隧道窑烧制5h,温度范围为1330°C,自然冷却,得到高档骨质日用
bL.0

Claims (3)

1.一种高档骨质日用瓷,其特征在于,所述高档骨质日用瓷的制作方法包括以下步骤: (1)按如下质量份数称取原材料:石英19〜24份,斜长石10〜16份,绿泥石3〜6份,莫来石1〜2份,骨粉35〜43份,黑云母2〜4份,CMC 0.2〜0.5份,变石0.1〜0.3份,将原材料按料:球:水=1:2:0.75入球磨湿磨1h,过300目筛筛余0.2%,除铁备用; (2)注浆:以25〜30MPa的压力将泥浆注入模腔,0.5h后取出坯体烘干; (3)烧制:坯体入隧道窑烧制5〜7h,自然冷却,得到高档骨质日用瓷。
2.根据权利要求1所述的高档骨质日用瓷,其特征在于,步骤(I)中的原材料由以下重量份数的各组分组成:石英21份,斜长石14份,绿泥石5份,莫来石I份,骨粉39份,黑云母3份,CMC 0.4份,变石0.1份。
3.根据权利要求1所述高档骨质日用瓷,其特征在于,步骤(3)中的烧制温度范围为.1300 〜1350。。。
CN201410735688.8A 2014-12-08 2014-12-08 高档骨质日用瓷 Active CN104496417B (zh)