CN104446195A - Light cement brick and production method - Google Patents

Light cement brick and production method Download PDF

Info

Publication number
CN104446195A
CN104446195A CN201410668325.7A CN201410668325A CN104446195A CN 104446195 A CN104446195 A CN 104446195A CN 201410668325 A CN201410668325 A CN 201410668325A CN 104446195 A CN104446195 A CN 104446195A
Authority
CN
China
Prior art keywords
brick
cement
lime
light
yellow sand
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410668325.7A
Other languages
Chinese (zh)
Inventor
朱又良
Original Assignee
朱又良
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 朱又良 filed Critical 朱又良
Priority to CN201410668325.7A priority Critical patent/CN104446195A/en
Publication of CN104446195A publication Critical patent/CN104446195A/en
Pending legal-status Critical Current

Abstract

The invention relates to a light cement brick and a production method, and belongs to the production field of a brick for buildings. The existing ordinary brick produced in a traditional method is relatively light in weight and poor in heat insulation effect, and the existing equipment for producing a foam brick has defects such as high cost, complicated procedure and the like. The light cement brick consists of cement, yellow sand, lime and foam particles, wherein the weight percentages of the ingredients are as follows: 24 to 26 percent of cement, 60 to 65 percent of yellow sand, 10 to 16 percent of lime, and the volume ratio of the foam particles in the cement brick is 35 percent. According to the light cement brick, the lime and foam particles are added on the basis of the materials of the ordinary brick, the lime plays a role in absorbing the water, so that a damp-proof function to a house can be realized; and by adding the foam particles to the ordinary brick, not only can the weight of the brick be reduced, but also a heat insulation effect can be realized.

Description

A kind of light cement brick and making method
Technical field
The invention belongs to brick for building and make field, especially relevant with a kind of light cement brick and making method.
Background technology
Brick is that architectural frequent needs apply to and requisite material, traditional brick making method is after cement, yellow sand and water being stirred by stirrer according to certain ratio, then brick press straight forming building site brick used is passed through, then place out of doors and can use for about 20 days, but the heavier mass of this common brick, effect of heat insulation is not good.Also many businessmans are had to develop a kind of cement foamed bricks at present, its manufacture craft is after yellow sand, cement, cinder etc. being stirred, then injected by cement blowing agent, by being shaped at container producer reflection method big gun, thus form the weight that foam class material alleviates brick, because the raw material volume after foaming is comparatively large, after having foamed, also need the common brick by cutting machine, brick cutting being formed building site.Foaming brick alleviates the quality of brick to a certain extent, and has moistureproof function.But the cost of the plant-scale equipment of foaming brick is far above the equipment of traditional mode of production brick, and needs to be cut by cutting machine, technique is also comparatively complicated, reduces the make efficiency of brick to a certain extent.
Summary of the invention
The object of the present invention is to provide a kind of light cement brick and making method, the invention solves the heavier mass of the common brick common brick head of existing traditional fabrication, effect of heat insulation be not good and the existing equipment cost making foaming brick is comparatively large, the defect such as complex procedures.
For this reason, the present invention is by the following technical solutions: a kind of light cement brick, it is characterized in that, described light cement brick is made up of cement, yellow sand, lime and foam particle, its weight proportion of composing is cement 24%-26%, yellow sand 60%-65%, lime 10%-16%, the shared volume of the foam particle in its composition cement brick is 35%.
A kind of light cement brick making method, is characterized in that, after first the mixing of cement, yellow sand, lime and foam particle being added water, is stirred, is then processed to form brick by brick press, then placed by brick and can use for about 20 days by stirrer.
Described cement weight optimum proportion is 25%.
Described yellow sand weight optimum proportion is 65%.
Described lime weight optimum proportion is 10%.
The diameter of described foam particle is 1-2 millimeter.
The optimum diameter of described foam particle is 2 millimeters, thus is conducive to the quality alleviating brick, and effectively plays heat insulation effect.
Use the present invention can reach following beneficial effect: the present invention by increasing lime and foam particle on the material of common brick, lime can play the effect of water suction, thus the effect that can play house protection against the tide, common brick adds foam particle, namely alleviate the quality of brick, thus serve heat insulation effect.
Embodiment
Embodiment 1: this light cement brick is made up of cement, yellow sand, lime and foam particle, its proportion of composing is cement 25%, yellow sand 65%, lime 10%, the shared volume of the foam particle in its composition cement brick is 35%, after first the mixing of cement, yellow sand, lime and foam particle being added water, is stirred by stirrer, then be processed to form brick by brick press, then brick placed and can use for about 20 days.
Embodiment 2: this light cement brick is made up of cement, yellow sand, lime and foam particle, its proportion of composing is cement 24%, yellow sand 65%, lime 11%, the shared volume of the foam particle in its composition cement brick is 35%, after first the mixing of cement, yellow sand, lime and foam particle being added water, is stirred by stirrer, then be processed to form brick by brick press, then brick placed and can use for about 20 days.
Embodiment 3: this light cement brick is made up of cement, yellow sand, lime and foam particle, its proportion of composing is cement 26%, yellow sand 60%, lime 14%, the shared volume of the foam particle in its composition cement brick is 35%, after first the mixing of cement, yellow sand, lime and foam particle being added water, is stirred by stirrer, then be processed to form brick by brick press, then brick placed and can use for about 20 days.
Embodiment 4: this light cement brick is made up of cement, yellow sand, lime and foam particle, its proportion of composing is cement 24%, yellow sand 60%, lime 16%, the shared volume of the foam particle in its composition cement brick is 35%, after first the mixing of cement, yellow sand, lime and foam particle being added water, is stirred by stirrer, then be processed to form brick by brick press, then brick placed and can use for about 20 days.
Because the weight of foam particle kicks the beam, foam particle weight accounts for overall content almost not to be had, and therefore can ignore the weight content per-cent of foam particle.
As preferably, the granular size of above-mentioned foam particle is diameter 1-2 millimeter, is preferably 2 millimeters, thus is conducive to the quality alleviating brick, and effectively play heat insulation effect.
The present invention by increasing lime and foam particle on the material of common brick, lime can play the effect of water suction, thus can play the effect to house protection against the tide, and common brick adds foam particle, namely alleviate the quality of brick, thus serve heat insulation effect.This lightweight brick is shown by practice, the wherein one side of brick is placed on stove and fires 5 minutes, the temperature of its other one side is still normal temperature, therefore the present invention has outstanding substantive distinguishing features and significant progress relative to existing common brick, and manufacture craft is simple, price due to foam particle is beneficial to yellow sand and cement, and therefore cost is less than common brick and foaming brick, is worth commercially promoting and using.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.

Claims (7)

1. a light cement brick, it is characterized in that: described light cement brick is made up of cement, yellow sand, lime and foam particle, its weight proportion of composing is cement 24%-26%, yellow sand 60%-65%, lime 10%-16%, the shared volume of the foam particle in its composition cement brick is 35%.
2. a light cement brick making method, is characterized in that: after first the mixing of cement, yellow sand, lime and foam particle being added water, stirred, be then processed to form brick by brick press by stirrer, then place and can use for about 20 days.
3. a kind of light cement brick according to claim 1, is characterized in that: described cement weight optimum proportion is 25%.
4. a kind of light cement brick according to claim 1, is characterized in that: described yellow sand weight optimum proportion is 65%.
5. a kind of light cement brick according to claim 1, is characterized in that: described lime weight optimum proportion is 10%.
6. a kind of light cement brick according to claim 1 or 5, is characterized in that: the diameter of described foam particle is 1-2 millimeter.
7. a kind of light cement brick according to claim 6, is characterized in that: the optimum diameter of described foam particle is 2 millimeters.
CN201410668325.7A 2014-11-19 2014-11-19 Light cement brick and production method Pending CN104446195A (en)