CN104403372A - 干法超细重质碳酸钙的制备方法 - Google Patents

干法超细重质碳酸钙的制备方法 Download PDF

Info

Publication number
CN104403372A
CN104403372A CN201410745866.5A CN201410745866A CN104403372A CN 104403372 A CN104403372 A CN 104403372A CN 201410745866 A CN201410745866 A CN 201410745866A CN 104403372 A CN104403372 A CN 104403372A
Authority
CN
China
Prior art keywords
calcium carbonate
heavy calcium
parts
preparation
auxiliary agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410745866.5A
Other languages
English (en)
Inventor
廖煜明
李安平
廖文成
李�杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI LISHENG STONE INDUSTRY Co Ltd
Original Assignee
GUANGXI LISHENG STONE INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI LISHENG STONE INDUSTRY Co Ltd filed Critical GUANGXI LISHENG STONE INDUSTRY Co Ltd
Priority to CN201410745866.5A priority Critical patent/CN104403372A/zh
Publication of CN104403372A publication Critical patent/CN104403372A/zh
Pending legal-status Critical Current

Abstract

本发明的干法超细重质碳酸钙的制备方法，将重质碳酸钙粗粉加入研磨设备中，在85～95℃下，以重质碳酸钙粗粉的重量百分比计，加入10-12％的助剂，经高速研磨而制得粒径为0.1～10微米的改性超细碳酸钙粉；所述助剂，由聚丙烯酸钠2-3份，铝酸酯偶联剂2-3份，超细氢氧化镁2-3份，碳酸钠5-8份组成；具有设计科学合理，工艺简单，安全可靠性，易于控制，操作方便，适合大规模生产，生产成本低等优点。

Description

干法超细重质碳酸钙的制备方法
技术领域
本发明属于一种碳酸钙粉体的生产方法。
背景技术
目前,碳酸钙已广泛应用于造纸、塑料、塑料薄膜、化纤、橡胶、胶粘剂、密封剂、日用化工、化妆品、建材、涂料、油漆、油墨、油灰、封蜡、腻子、毡层包装、医药、食品(如口香糖、巧克力)、饲料中,其作用有:增加产品体积、降低成本,改善加工性能(如调节粘度、流变性能、硫化性能),提高尺寸稳定性,补强或半补强,提高印刷性能,提高物理性能(如耐热性、消光性、耐磨性、阻燃性、白度、光泽度)等。重质碳酸钙的生产工艺流程有两种。干法生产工艺流程:首先手选从采石场运来的方解石、石灰石、白垩、贝壳等,以除去脉石；然后用破碎机对石灰石进行粗破碎,再用雷蒙(摆式)磨粉碎得到细石灰石粉,最后用分级机对磨粉进行分级,符合粒度要求的粉末作为产品包装入库,否则返回磨粉机再次磨粉。湿法生产工艺流程:先将干法细粉制成悬浮液置于磨机内进一步粉碎,经脱水、干燥后便制得超细重质碳酸钙。
经中国公开专利检索，查到碳酸钙发明专利申请53件；没发现与本专利申请相同的方案。
发明内容
本发明的目的在于；提出一种干法超细重质碳酸钙的制备方法。
本发明的干法超细重质碳酸钙的制备方法，其特征在于：将重质碳酸钙粗粉加入研磨设备中，在85～95℃下，以重质碳酸钙粗粉的重量百分比计，加入10-12％的助剂，经高速研磨而制得粒径为0.1～10微米的改性超细碳酸钙粉；所述助剂，以重量计，由聚丙烯酸钠2-3份，铝酸酯偶联剂2-3份，超细氢氧化镁2-3份，碳酸钠5-8份组成。
本发明与现有技术相比其有益效果是：具有设计科学合理，工艺简单，安全可靠性，易于控制，操作方便，适合大规模生产，生产成本低等优点。
具体实施方式
下面结合实施例对本发明作进一步说明，但本发明的实施方式不限于此。
实施例1
本发明的干法超细重质碳酸钙的制备方法，其特征在于：将重质碳酸钙粗粉加入研磨设备中，在85～95℃下，以重质碳酸钙粗粉的重量百分比计，加入10-12％的助剂，经高速研磨而制得粒径为0.1～10微米的改性超细碳酸钙粉；所述助剂，以重量计，由聚丙烯酸钠2-3份，铝酸酯偶联剂2-3份，超细氢氧化镁2-3份，碳酸钠5-8份组成。
实施例1
本发明的干法超细重质碳酸钙的制备方法，其特征在于：将重质碳酸钙粗粉加入研磨设备中，在85～95℃下，以重质碳酸钙粗粉的重量百分比计，加入10-12％的助剂，经高速研磨而制得粒径为0.1～10微米的改性超细碳酸钙粉；所述助剂，以重量计，由聚丙烯酸钠2份，铝酸酯偶联剂3份，超细氢氧化镁2份，碳酸钠8份组成。
实施例1
本发明的干法超细重质碳酸钙的制备方法，其特征在于：将重质碳酸钙粗粉加入研磨设备中，在85～95℃下，以重质碳酸钙粗粉的重量百分比计，加入10-12％的助剂，经高速研磨而制得粒径为0.1～10微米的改性超细碳酸钙粉；所述助剂，以重量计，由聚丙烯酸钠3份，铝酸酯偶联剂2份，超细氢氧化镁3份，碳酸钠5份组成。
产品经客户使用，反应效果很好。

Claims (1)

1.一种干法超细重质碳酸钙的制备方法，其特征在于：将重质碳酸钙粗粉加入研磨设备中，在85～95℃下，以重质碳酸钙粗粉的重量百分比计，加入10-12％的助剂，经高速研磨而制得粒径为0.1～10微米的改性超细碳酸钙粉；所述助剂，以重量计，由聚丙烯酸钠2-3份，铝酸酯偶联剂2-3份，超细氢氧化镁2-3份，碳酸钠5-8份组成。
CN201410745866.5A 2014-12-08 2014-12-08 干法超细重质碳酸钙的制备方法 Pending CN104403372A (zh)