CN104311042A - Kr脱硫搅拌桨用耐火浇注料 - Google Patents

Kr脱硫搅拌桨用耐火浇注料 Download PDF

Info

Publication number
CN104311042A
CN104311042A CN201410488865.7A CN201410488865A CN104311042A CN 104311042 A CN104311042 A CN 104311042A CN 201410488865 A CN201410488865 A CN 201410488865A CN 104311042 A CN104311042 A CN 104311042A
Authority
CN
China
Prior art keywords
granularity
temperature
electrofused mullite
powder
basic components
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410488865.7A
Other languages
English (en)
Other versions
CN104311042B (zh
Inventor
庄国兴
姚文卫
何银荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU BAOLI REFRACTORY CO Ltd
Original Assignee
SUZHOU BAOLI REFRACTORY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU BAOLI REFRACTORY CO Ltd filed Critical SUZHOU BAOLI REFRACTORY CO Ltd
Priority to CN201410488865.7A priority Critical patent/CN104311042B/zh
Publication of CN104311042A publication Critical patent/CN104311042A/zh
Application granted granted Critical
Publication of CN104311042B publication Critical patent/CN104311042B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种KR脱硫搅拌桨用耐火浇注料,当气温大于30℃时,因采用纯酸钙水泥为结合剂,并加有SiO2微粉,用三聚磷酸钠和六偏磷酸钠复合加入分散效果较好,而柠檬酸的加入不但有减水效果也有一定的缓凝作用,可供一般振动施工的浇注料,保证施工体在浇注料的初凝时间内完成;当气温在20~30℃时,此气温比较适合浇注料的施工,除继续沿用三聚磷酸钠和六偏磷酸钠复合分散剂,加入三聚氰胺具有更好的减水效果,施工性能明显得到提高;当气温小于20℃时,此气温段内引入金属铝粉,金属铝粉的加入与水混合后发生放热反应,使料温升高促进超微粉凝聚结合的发展,从而得到浇注体的强度,缩短整体养护时间。

Description

KR脱硫搅拌桨用耐火浇注料
技术领域
[0001] 本发明涉及一种KR脱硫搅拌桨用耐火浇注料。
背景技术
[0002] 在炼钢过程中,铁水在进入转炉、电炉冶炼钢前,进行炉外预处理脱硫,可提高钢材质量及扩大钢产品的品种、加快钢铁企业生产节奏、提高生产效率、降低炼钢成本等。迄今为止,铁水脱硫预处理主要采用KR搅拌脱硫方式。在KR搅拌脱硫过程中,将搅拌桨插入铁水液面下一定深度进行旋转,强烈搅动铁水,使铁水与脱硫剂反应,达到脱硫效果。
[0003] 搅拌桨的生产过程一般由金属搅拌芯的制作、浇注成型、养护与烘烤等工序组成,每一道工序质量都将影响搅拌头的最终使用性能。而浇注成型工序是制作搅拌桨的重中之重,不同的施工气温对连续生产有着不同的影响,一般情况下以10〜30°C为宜。另外,搅拌桨的浇注成型一般采用吊挂式浇注成型方式,由于搅拌桨的金属搅拌芯具有一定的重量,所以搅拌桨浇注成型后必须采取绝对静止养护的方式进行养护,先进行模内养护,再进行模外养护,养护温度要求在20〜30°C为宜,此条件下一般模内养护2〜3d,然后脱模养护3〜7d,整个养护期应保持在5〜10d,当气温在10〜20°C时则整个养护期应延长至10〜15d,当气温低于10°C时,则更应延长整个养护时间,或相应采取保温措施,这样整个生产周期将被延长,有时无法保证正常生产,进而影响供货时间。而当气温大于30°C时,由于温度较高,浇注料凝固加快,影响浇注。
发明内容
[0004] 为解决上述问题,本发明的目的在于提供一种KR脱硫搅拌桨用耐火浇注料,可适宜不同气温条件,保证在不同气温条件下连续生产,提高生产效率。
[0005] 为了达到以上目的,本发明采用的技术方案是:一种KR脱硫搅拌桨用耐火浇注料,它包括基础组分和外加剂,所述的基础组分按照质量百分比为:粒度8彡d < 5mm的电熔莫来石19〜23%、粒度5 < d < 3mm的电熔莫来石18〜22%、粒度3 < d < Imm的电熔莫来石6〜10%、粒度I < d < Omm的电熔莫来石8〜12%、粒度d < 0.088mm的电熔莫来石2〜4%、粒度I < d < (tom的焦宝石5〜8%、粒度d < 0.108謹的蓝晶石3〜6%、粒度d彡0.088mm的特矾细粉6〜10%、粒度d彡0.044mm的白刚玉粉2〜5%、粒度d彡0.044mm的碳化硅粉2〜4%、纯铝酸钙水泥3〜6%、S12微粉2〜5%、a -Al2O3微粉7〜10% ;
当气温大于30°C时,所述的外加剂包括以基础组分质量为基准的:钢纤维2〜3%、防爆纤维0.1〜0.2%、三聚磷酸钠0.05〜0.15%、六偏磷酸钠0.15〜0.30%、柠檬酸0.01〜0.05% ;
当气温为20〜30°C时,所述的外加剂包括以基础组分质量为基准的:钢纤维2〜3%、防爆纤维0.1〜0.2%、三聚磷酸钠0.05〜0.15%、六偏磷酸钠0.15〜0.30%、三聚氰胺0.10 〜0.25% ;
当气温小于20°C时,所述的外加剂包括以基础组分质量为基准的:钢纤维2〜3%、防爆纤维0.1〜0.2%、三聚磷酸钠0.05〜0.15%、六偏磷酸钠0.15〜0.30%、粒度d彡0.108mm的金属铝粉0.04〜0.10%、三聚氰胺0.10〜0.25%。
[0006] 通过采用上述技术方案,本发明KR脱硫搅拌桨用耐火浇注料,当气温大于30°C时,因采用纯酸钙水泥为结合剂,并加有S12微粉,用三聚磷酸钠和六偏磷酸钠复合加入分散效果较好,而柠檬酸的加入不但有减水效果也有一定的缓凝作用,可供一般振动施工的浇注料,保证施工体在浇注料的初凝时间内完成;当气温在20〜30°C时,此气温比较适合浇注料的施工,除继续沿用三聚磷酸钠和六偏磷酸钠复合分散剂,加入三聚氰胺具有更好的减水效果,施工性能明显得到提高;当气温小于20°C时,此气温段内引入金属铝粉,金属铝粉的加入与水混合后发生放热反应,使料温升高促进超微粉凝聚结合的发展,从而得到浇注体的强度,缩短整体养护时间。
具体实施方式
[0007] 下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
[0008] 本技术领域技术人员可以理解,除非另外定义,这里使用的所有术语(包括技术术语和科学术语)具有与本发明所属领域中的普通技术人员的一般理解相同的意义。还应该理解的是,诸如通用字典中定义的那些术语应该被理解为具有与现有技术的上下文中的意义一致的意义,并且除非像这里一样定义,不会用理想化或过于正式的含义来解释。
[0009] 本发明KR脱硫搅拌桨用耐火浇注料,包括基础组分和外加剂。基础组分包括主原料、基质部分以及结合剂。主原料为电熔莫来石各级配,基质部份为焦宝石、蓝晶石、特矾细粉、白刚玉细粉、碳化硅,结合剂为纯铝酸钙水泥、硅微粉、a -Al2O3微粉,外加剂根据不同的气温由耐热钢纤维、防爆纤维、金属铝粉、三聚磷酸钠、六偏磷酸钠、三聚氰胺、柠檬酸中的几种组合而成。下面将要描述的电熔莫来石的根据粒度所进行的分类是按照本领域的公知标准,其中粒度I < d < 0_的电熔莫来石和粒度d < 0.088mm的电熔莫来石虽然在粒度范围内有重合,但是是行业内公认的两种不同的电熔莫来石,其中粒度I < d<0mm的电熔莫来石为颗粒状,粒度d < 0.088mm的电熔莫来石为细粉状。
[0010] 实施例一
当气温大于30°C时,基础组分包括:粒度8彡d < 5mm的电熔莫来石10.5kg、粒度5彡d
< 3mm的电熔莫来石10kg、粒度3 < d < Imm的电熔莫来石4kg、粒度I < d < Omm的电熔莫来石4.5 kg、粒度d彡0.088mm的电熔莫来石1.5 kg、粒度I彡d < Omm的焦宝石3 kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特矾细粉4 kg、粒度d彡0.044mm的白刚玉粉1.5kg、粒度d < 0.044mm的碳化硅粉1.5 kg、纯铝酸钙水泥2 kg、S12微粉1.5kg、a -Al2O3 微粉 4 kg ;
外加剂包括以基础组分质量为基准的:钢纤维1.25 kg、防爆纤维0.075 kg、三聚磷酸钠0.06 kg、六偏磷酸钠0.1 kg、柠檬酸0.015 kg。
[0011] 因采用纯酸钙水泥为结合剂,并加有S12微粉,用三聚磷酸钠和六偏磷酸钠复合加入分散效果较好,而柠檬酸的加入不但有减水效果也有一定的缓凝作用,可供一般振动施工的浇注料,保证施工体在浇注料的初凝时间内完成。
[0012] 当气温为20〜30°C时,基础组分包括:粒度8彡d < 5mm的电熔莫来石10.5kg、粒度5彡d < 3mm的电熔莫来石10kg、粒度3彡d < Imm的电熔莫来石4kg、粒度I ( d
< Omm的电熔莫来石4.5 kg、粒度d < 0.088mm的电熔莫来石1.5 kg、粒度I < d < Omm的焦宝石3 kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特帆细粉4 kg、粒度d < 0.044mm的白刚玉粉1.5kg、粒度d < 0.044mm的碳化硅粉1.5 kg、纯铝酸钙水泥2kg、S12 微粉 1.5 kg、a -Al2O3 微粉 4 kg ;
外加剂包括以基础组分质量为基准的:钢纤维1.25kg、防爆纤维0.075 kg、三聚磷酸钠0.025 kg、六偏磷酸钠0.075 kg、三聚氰胺0.075 kg。
[0013] 此气温段比较适合浇注料的施工,除继续沿用三聚磷酸钠和六偏磷酸钠复合分散齐U,加入三聚氰胺具有更好的减水效果,施工性能明显得到提高。
[0014] 当气温小于20°C时,基础组分包括:粒度8彡d < 5mm的电熔莫来石10.5kg、粒度5 ^ d < 3mm的电熔莫来石10kg、粒度3 < d < Imm的电熔莫来石4kg、粒度I < d < Omm的电熔莫来石4.5 kg、粒度d彡0.088mm的电熔莫来石1.5 kg、粒度I彡d < Omm的焦宝石3kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特矾细粉4 kg、粒度d彡0.044mm的白刚玉粉1.5kg、粒度0.044mm的碳化硅粉1.5 kg、纯铝酸钙水泥2 kg、Si02微粉1.5kg、a -Al2O3 微粉 4 kg ;
外加剂包括以基础组分质量为基准的:钢纤维1.25kg、防爆纤维0.075 kg、三聚磷酸钠0.025 kg、六偏磷酸钠0.075 kg、粒度d<0.108mm的金属铝粉0.025 kg、三聚氰胺0.05
kg ο
[0015] 此气温段内引入金属铝粉,金属铝粉的加入与水混合后发生放热反应,使料温升高促进超微粉凝聚结合的发展,从而得到浇注体的强度,缩短整体养护时间,但在加金属铝粉时需注意,若金属铝粉加入量太多,铝粉与水反应激烈产生大量氢气,来不及排除时,将使浇注体发生裂缝或疏松,起到相反的作用。
[0016] 实施例二
当气温大于30°C时,基础组分包括:粒度8 < d < 5mm的电熔莫来石10kg、粒度5 ( d
< 3mm的电熔莫来石9.5 kg、粒度3 < d < Imm的电熔莫来石4 kg、粒度I < d < Omm的电熔莫来石5 kg、粒度d彡0.088mm的电熔莫来石1.5 kg、粒度I彡d < Omm的焦宝石3 kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特矾细粉4 kg、粒度d彡0.044mm的白刚玉粉1.5 kg、粒度d < 0.044mm的碳化硅粉1.5 kg、纯铝酸钙水泥2.5 kg、S12微粉 1.5 kg、a -Al2O3 微粉 4 kg ;
外加剂包括以基础组分质量为基准的:钢纤维1.25 kg、防爆纤维0.1 kg、三聚磷酸钠0.05 kg、六偏磷酸钠0.075 kg、柠檬酸0.025 kg;
当气温为20〜30°C时,基础组分包括:粒度8彡d < 5mm的电熔莫来石10kg、粒度5 ^ d < 3mm的电熔莫来石9.5 kg、粒度3 < d < Imm的电熔莫来石4 kg、粒度I < d < Omm的电熔莫来石5 kg、粒度d彡0.088mm的电熔莫来石1.5 kg、粒度I彡d < Omm的焦宝石3kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特矾细粉4 kg、粒度d彡0.044mm的白刚玉粉1.5 kg、粒度d < 0.044mm的碳化硅粉1.5 kg、纯铝酸钙水泥2.5 kg、S12微粉 1.5 kg、a -Al2O3 微粉 4 kg ;
外加剂包括以基础组分质量为基准的:钢纤维1.25 kg、防爆纤维0.05 kg、三聚磷酸钠0.025 kg、六偏磷酸钠0.075 kg、三聚氰胺0.1 kg ; 当气温小于20°C时,基础组分包括:粒度8 < d < 5mm的电熔莫来石10kg、粒度5彡d
< 3mm的电熔莫来石9.5 kg、粒度3 < d < Imm的电熔莫来石4 kg、粒度I < d < Omm的电熔莫来石5 kg、粒度d彡0.088mm的电熔莫来石1.5 kg、粒度I彡d < Omm的焦宝石3 kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特矾细粉4 kg、粒度d彡0.044mm的白刚玉粉1.5 kg、粒度d < 0.044mm的碳化硅粉1.5 kg、纯铝酸钙水泥2.5 kg、S12微粉 1.5 kg、a -Al2O3 微粉 4 kg ;
钢纤维1.25 kg、防爆纤维0.05 kg、三聚磷酸钠0.025 kg、六偏磷酸钠0.075 kg、粒度d ^ 0.108mm的金属铝粉0.035kg、三聚氰胺0.065kg。
[0017] 实施例三
当气温大于30°C时,基础组分包括:粒度8彡d < 5mm的电熔莫来石10.5kg、粒度5 ^ d < 3mm的电熔莫来石10 kg、粒度3彡d < Imm的电熔莫来石3.75 kg、粒度I ( d
< Omm的电熔莫来石5 kg、粒度d < 0.088mm的电熔莫来石1.25 kg、粒度I < d < Omm的焦宝石3 kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特矾细粉3.5 kg、粒度
0.044mm的白刚玉粉1.5 kg、粒度d < 0.044mm的碳化硅粉I kg、纯铝酸钙水泥2.25kg、S12 微粉 1.75 kg、a -Al2O3 微粉 4.5 kg ;
外加剂包括以基础组分质量为基准的:钢纤维1.235kg、防爆纤维0.085kg、三聚磷酸钠0.035kg、六偏磷酸钠0.125kg、柠檬酸0.02kg ;
当气温为20〜30°C时,基础组分包括:粒度8彡d < 5mm的电熔莫来石10.5kg、粒度5 ^ d < 3mm的电熔莫来石10 kg、粒度3彡d < Imm的电熔莫来石3.75 kg、粒度I ( d
< Omm的电熔莫来石5 kg、粒度d < 0.088mm的电熔莫来石1.25 kg、粒度I < d < Omm的焦宝石3 kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特矾细粉3.5 kg、粒度
0.044mm的白刚玉粉1.5 kg、粒度d < 0.044mm的碳化硅粉I kg、纯铝酸钙水泥2.25kg、S12 微粉 1.75 kg、a -Al2O3 微粉 4.5 kg ;
外加剂包括以基础组分质量为基准的:钢纤维1.2kg、防爆纤维0.1kg、三聚磷酸钠0.05kg、六偏磷酸钠0.1kg、三聚氰胺0.05kg ;
当气温小于20°C时,基础组分包括:粒度8彡d < 5mm的电熔莫来石10.5kg、粒度5 ^ d < 3mm的电熔莫来石10 kg、粒度3彡d < Imm的电熔莫来石3.75 kg、粒度I ( d
< Omm的电熔莫来石5 kg、粒度d < 0.088mm的电熔莫来石1.25 kg、粒度I < d < Omm的焦宝石3 kg、粒度d彡0.108mm的蓝晶石2 kg、粒度d彡0.088mm的特矾细粉3.5 kg、粒度
0.044mm的白刚玉粉1.5 kg、粒度d < 0.044mm的碳化硅粉I kg、纯铝酸钙水泥2.25kg、S12 微粉 1.75 kg、a -Al2O3 微粉 4.5 kg ;
外加剂包括以基础组分质量为基准的:钢纤维1.1kg、防爆纤维0.07kg、三聚磷酸钠
0.1kg、六偏磷酸钠0.1kg、粒度d < 0.108mm的金属招粉0.03kg、三聚氰胺0.1kg。
[0018] 上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。

Claims (1)

1.一种KR脱硫搅拌桨用耐火浇注料,其特征在于:它包括基础组分和外加剂,所述的基础组分按照质量百分比为:粒度8彡d < 5mm的电熔莫来石19〜23%、粒度5彡d < 3mm的电熔莫来石18〜22%、粒度3 < d < Imm的电熔莫来石6〜10%、粒度I < d < Omm的电熔莫来石8〜12%、粒度d < 0.088mm的电熔莫来石2〜4%、粒度I < d < Omm的焦宝石.5〜8%、粒度d < 0.108mm的蓝晶石3〜6%、粒度d < 0.088mm的特帆细粉6〜10%、粒度d彡0.044mm的白刚玉粉2〜5%、粒度d彡0.044mm的碳化硅粉2〜4%、纯铝酸钙水泥3〜.6%、S12 微粉 2 〜5%、a -Al2O3 微粉 7 〜10% ; 当气温大于30°C时,所述的外加剂包括以基础组分质量为基准的:钢纤维2〜3%、防爆纤维0.1〜0.2%、三聚磷酸钠0.05〜0.15%、六偏磷酸钠0.15〜0.30%、柠檬酸0.01〜.0.05% ; 当气温为20〜30°C时,所述的外加剂包括以基础组分质量为基准的:钢纤维2〜3%、防爆纤维0.1〜0.2%、三聚磷酸钠0.05〜0.15%、六偏磷酸钠0.15〜0.30%、三聚氰胺.0.10 〜0.25% ; 当气温小于20°C时,所述的外加剂包括以基础组分质量为基准的:钢纤维2〜3%、防爆纤维0.1〜0.2%、三聚磷酸钠0.05〜0.15%、六偏磷酸钠0.15〜0.30%、粒度d彡0.108mm的金属铝粉0.04〜0.10%、三聚氰胺0.10〜0.25%。
CN201410488865.7A 2014-09-23 2014-09-23 Kr脱硫搅拌桨用耐火浇注料 Active CN104311042B (zh)