CN104278409B - A kind of preparation technology of yam-dyed jacquard fabric and the yam-dyed jacquard fabric that utilizes this technique to prepare - Google Patents

A kind of preparation technology of yam-dyed jacquard fabric and the yam-dyed jacquard fabric that utilizes this technique to prepare Download PDF

Info

Publication number
CN104278409B
CN104278409B CN201310701653.8A CN201310701653A CN104278409B CN 104278409 B CN104278409 B CN 104278409B CN 201310701653 A CN201310701653 A CN 201310701653A CN 104278409 B CN104278409 B CN 104278409B
Authority
CN
China
Prior art keywords
fabric
yam
temperature
technology
jacquard fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310701653.8A
Other languages
Chinese (zh)
Other versions
CN104278409A (en
Inventor
何芝萍
林参军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Ruiyijia Textile Technology Co., Ltd.
Original Assignee
何芝萍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 何芝萍 filed Critical 何芝萍
Priority to CN201310701653.8A priority Critical patent/CN104278409B/en
Publication of CN104278409A publication Critical patent/CN104278409A/en
Application granted granted Critical
Publication of CN104278409B publication Critical patent/CN104278409B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to weaving face fabric and fabricating technology field thereof, the yam-dyed jacquard fabric that is specifically related to a kind of preparation technology of yam-dyed jacquard fabric and utilizes this technique to prepare. This process using adopt mechanical type jacquard weave water-jet loom by warping, starching axle, weave and arrange and prepared a kind of yam-dyed jacquard fabric. This technique can effectively solve the variety of issue that current jacquard fabric adopts rapier loom or air-jet loom weaving to exist.

Description

A kind of preparation technology of yam-dyed jacquard fabric and the yam-dyed jacquard fabric that utilizes this technique to prepare
Technical field
The present invention relates to weaving face fabric and fabricating technology field thereof, the yam-dyed jacquard fabric that is specifically related to a kind of preparation technology of yam-dyed jacquard fabric and utilizes this technique to prepare.
Background technology
At present, existing jacquard fabric mostly adopts rapier loom or air-jet loom weaving, little by the woven jacquard fabric kind of water-jet loom. And, because water spray is weaved less energy consumption, the speed of a motor vehicle is fast, there is constantly relative advantage weaving same chemical fibre class jacquard fabric, be therefore also subject to gradually the attention of manufacturer. But jacquard fabric is in water spray weaving process, because workshop condition moisture is larger, electronic jacquard loom is easy to make moist break down in operation process, causes and stops platform. In weaving process, particularly in the time weaving highly dense yam-dyed jacquard fabric, if only adopt electronic jacquard machine, large owing to causing dress to make the friction of harness cord gapping of spring through close height, because Warp opening is larger more backward, harness cord return spring is easily weak after excessively stretching again, and it is slack-off that warp thread returns the speed of combining, cause the unintelligible or opening of opening to postpone, the easy injected water of warp thread thrusts.
Original liquid coloring polyster fibre, because its hygroscopicity is poor, modulus is high, very easily static, and keep fit poor-performing, irregularity is higher, if whole slurry technique are incorrect, easily causes warp thread fluffing, cracked ends frequent. And current colored woven fabric is not because needing dyed rear arrangement, the general mode that adopts the sizing of low temperature secondary after refining destarch, and softening agent in the time of sizing, pad and differ because fabric humidity causes on fabric when soft, fabric feeling is unstable, and when low-temperature shaped,, due to cloth cover humidity, the easy run-bake-needle fault of selvedge, affects and runs well.
Summary of the invention
The present invention, in order to address the above problem, provides a kind of preparation technology of yam-dyed jacquard fabric.
Another object of the present invention is for a kind of yam-dyed jacquard fabric that adopts above-mentioned technique to prepare is provided.
In order to reach foregoing invention object, the present invention by the following technical solutions:
A preparation technology for yam-dyed jacquard fabric, comprises the following steps:
A) warping: by through inspection after warp thread on sectional warper after lease reed leasing beaming pulping axle, when warping, rotating speed is 242-286 rev/min;
B) starching: by steps A) slurry axle carry out starching, when starching, controlling workshop temperature is 20 DEG C-25 DEG C, humidity is 70%-85%, after starching, controlling the rate of sizing is 8%-13%, oven dry rate is 98.6%-99.8%;
Starching the most important thing is two parameters, is respectively the rate of sizing and oven dry rate. The rate of sizing is to be directly proportional with the filling density of fabric, in order that ensure that warp thread in weaving process is wrapped by serous coat and reed that serous coat can be resistance to be lived certain number of times rubs, guarantees phozyly, does not entwine; Oven dry rate is that relevant with weather, different weather will do suitable adjustment, causes warp thread to entwine in order that eliminate static, and impact is normally weaved.
And axle C): by after slurry beam warp denting good starching and on machine and become beam of a loom, and to control workshop moisture temperature when axle be 22 DEG C-26 DEG C, humidity is 78%-86%; Controlling the Shore hardness of beam of a loom is 82-88, by and axle after the beam of a loom that obtains place more than 24 hours;
D) weave: the colored type designing is inputted on the water-jet loom that jacquard attachment is housed, weaved after required weft preparing is good and obtain fabric;
The key point of beam of a loom hardness is, hardness height, warp thread drawing-off is excessive, is easily to pull fluffing or cracked ends weaving, and hardness is low, and warp beam is reeled bad, between layer, easily intersects, and affects unwinding.
E) arrange: by first refining destarch of the fabric after weaving, then adopt the mode of shaping after secondary drying to dry, and auxiliary agent in the time drying for the second time; When refining, the speed of a motor vehicle is 47-63 rev/min, and when oven dry, temperature is controlled at 82-94 DEG C, and oven dry degree is 83-92%, and when sizing, temperature is 174-181 DEG C, and the speed of a motor vehicle is 68-82 rev/min.
As preferably, step D) be woven as: adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, before looming weaving, first the colored type designing is washed into plastics cardboard, be arranged on the water-jet loom that mechanical type jacquard attachment is housed, weave after required weft preparing is good and obtain fabric.
As preferably, step e) secondary drying is prebake and secondary drying, and the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C.
When secondary drying, be conducive to auxiliary agent, after drying for the first time on auxiliary agent can make auxiliary agent be penetrated into more equably in fabric, reach the object of feel homogeneous soft
As preferably, described warp thread is 108D colored terylene filament, and weft yarn is three kinds of 145D colored terylene filament.
As preferably, through close be 128/cm, filling density is 72/cm, weft yarn arrangement is 1:1:2, upper machine fabric width is 310cm, total warp thread radical is 39680, adopts upper and lower double ends axle, warp thread ratio is 3:2.
As preferably, step D) warp tension while weaving is 560Kg, the speed of a motor vehicle is 350rpm.
As preferably, step e) auxiliary agent be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: meter by weight, by decamethylcyclopentaandoxane 85-88 part, silane coupler 1-2 part, potassium hydroxide 0.5-1 part, normal butane 8-15 part and oxirane 2-4 part is the lower 1h of maintenance under 100-105 DEG C of continuous stirring, then temperature is brought up to 160 DEG C and kept 10-15min, then decompression distillation goes out solvent, continue to keep 2h at 80-90 DEG C, then add polyoxyethylene sorbitan monoleate 3-5 part, poly hydroxy ethyl acrylate 3-5 part, chloroacetic chloride 1-2 part, and to control pH be 5.8, temperature is 75-79 DEG C, constantly stir and continue 3h, then add barium sulfate 3-8 part, zinc chloride 3-5 part, after stirring, obtain amino-silicone oil softening agent.
Amido silicon oil is the fundamental component of using specially what textile soft finishing agent. It has best adsorptivity, compatibility and easy emulsibility. Use blender or homogenizer, amido silicon oil is easily emulsified into stable, transparent microemulsion by suitable surfactant. It can use separately, also can be combined into special soft finishing agent with other organosilicon or organic softening agent, is suitable for the soft finish of the various textiles of what. The ammonia value of amido silicon oil is between 0.2 ~ 1.2, and ammonia value is higher, and flexibility and slippery are better, but xanthochromia can be larger. Therefore, provide good softness, level and smooth, uniform feel for happy, and strengthen tearing strength and the wrinkle resistance of fabric and improve the elasticity of fabric, water-fastness and dry cleaning resistance. The application provides the component of above-mentioned auxiliary agent, solves easy xanthochromia that current amido silicon oil exists as third generation silicone softening agent, increases the defects such as fabric hydrophobicity, amino skewness. The easy emulsification of amido silicon oil of the present invention, can be made into stable microemulsion and is difficult for causing xanthochromia. Be applicable in the preparation technology of yam-dyed jacquard fabric of the present invention.
A yam-dyed jacquard fabric that adopts the preparation technology of yam-dyed jacquard fabric to prepare, in aggregates by warp thread and the weft yarn structure that interweaves, warp thread is 83-128D colored terylene filament, weft yarn is the coloured chemical-fibres filaments of 126-330D.
Compared with prior art, beneficial effect is in the present invention: the present invention, by adopting mechanical type jacquard weave water-jet loom, can effectively solve and cause greatly the reasons such as electronic jacquard loom electronic component damage to make the too high problem of device fails rate because of moisture; By adopting rational whole slurry technique to solve because drying the unreasonable problems such as the excessive drawing-off of warp thread, starching be bad of causing, reduce the generation of the unclear phenomenon such as not in time of warp thread fluffing, cracked ends, opening, effectively improve weaving efficiency and fabric quality; Be raw material by adopting coloured chemical-fibres filaments, avoided printing and dyeing link, reduced the use of resource and the discharge of discarded object, shortened production process time. Technique of the present invention is reasonable, advanced, raw material environmental protection, the advantages such as fabric has cloth cover exquisiteness, soft, drapability good, flower type third dimension is strong, level is obvious, color fastness is high, shading.
Detailed description of the invention
Below by specific embodiment, technical scheme of the present invention is further described to explanation.
If without specified otherwise, the raw material adopting in embodiments of the invention is the conventional raw material in this area, and the method adopting in embodiment is the conventional method of this area.
Embodiment 1:
A kind of yam-dyed jacquard fabric, adopts following technique to be prepared from:
A) warping: warp thread is 83D colored terylene filament, weft yarn is the coloured chemical-fibres filaments of 330D, by through inspection after warp thread on sectional warper after lease reed leasing beaming pulping axle, when warping, rotating speed is 242 revs/min; Through close be 128/cm, filling density is 72/cm, weft yarn arrangement is 1:1:2, upper machine fabric width is 310cm, total warp thread radical is 39680, adopts upper and lower double ends axle, warp thread ratio is 3:2.
B) starching: by steps A) slurry axle carry out starching, when starching, controlling workshop temperature is 25 DEG C, humidity is 70%, after starching, controlling the rate of sizing is 13%, oven dry rate is 98.6%;
And axle C): by after slurry beam warp denting good starching and on machine and become beam of a loom, and to control workshop moisture temperature when axle be 26 DEG C, humidity is 78%; Controlling the Shore hardness of beam of a loom is 88, by and axle after the beam of a loom that obtains place more than 24 hours;
D) weave: the colored type designing is inputted on the water-jet loom that jacquard attachment is housed, weaved after required weft preparing is good and obtain fabric; Adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, before looming weaving, first the colored type designing is washed into plastics cardboard, be arranged on the water-jet loom that mechanical type jacquard attachment is housed, weave after required weft preparing is good and obtain fabric; Warp tension is 560Kg, and the speed of a motor vehicle is 350rpm;
E) arrange: by first refining destarch of the fabric after weaving, then adopt the mode of shaping after secondary drying to dry, and auxiliary agent in the time drying for the second time; Secondary drying is prebake and secondary drying, and the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C; When refining, the speed of a motor vehicle is 47 revs/min, and when oven dry, temperature is controlled at 94 DEG C, and oven dry degree is 83%, and when sizing, temperature is 181 DEG C, and the speed of a motor vehicle is 68 revs/min.
Wherein, step e) the auxiliary agent using be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: meter by weight, by 85 parts of decamethylcyclopentaandoxane, 2 parts of silane couplers, 0.5 part, potassium hydroxide, 2 parts of lower 1h of maintenance under 105 DEG C of continuous stirrings of 15 parts of normal butanes and oxirane, then temperature is brought up to 160 DEG C and kept 10min, then decompression distillation goes out solvent, continue to keep 2h at 90 DEG C, then add 3 parts of polyoxyethylene sorbitan monoleates, 5 parts of poly hydroxy ethyl acrylates, 1 part of chloroacetic chloride, and to control pH be 5.8, temperature is 79 DEG C, constantly stir and continue 3h, then add 3 parts, barium sulfate, 5 parts of zinc chloride, after stirring, obtain amino-silicone oil softening agent.
Embodiment 2:
A kind of yam-dyed jacquard fabric, adopts following technique to be prepared from:
A) warping: warp thread is 128D colored terylene filament, weft yarn is the coloured chemical-fibres filaments of 126D, by through inspection after warp thread on sectional warper after lease reed leasing beaming pulping axle, when warping, rotating speed is 286 revs/min; Through close be 128/cm, filling density is 72/cm, weft yarn arrangement is 1:1:2, upper machine fabric width is 310cm, total warp thread radical is 39680, adopts upper and lower double ends axle, warp thread ratio is 3:2.
B) starching: by steps A) slurry axle carry out starching, when starching, controlling workshop temperature is 20 DEG C, humidity is 85%, after starching, controlling the rate of sizing is 8%, oven dry rate is 99.8%;
And axle C): by after slurry beam warp denting good starching and on machine and become beam of a loom, and control workshop moisture temperature when axle and be 22 DEG C DEG C, humidity is 86%; Controlling the Shore hardness of beam of a loom is 82, by and axle after the beam of a loom that obtains place more than 24 hours;
D) weave: the colored type designing is inputted on the water-jet loom that jacquard attachment is housed, weaved after required weft preparing is good and obtain fabric; Adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, before looming weaving, first the colored type designing is washed into plastics cardboard, be arranged on the water-jet loom that mechanical type jacquard attachment is housed, weave after required weft preparing is good and obtain fabric; Warp tension is 560Kg, and the speed of a motor vehicle is 350rpm;
E) arrange: by first refining destarch of the fabric after weaving, then adopt the mode of shaping after secondary drying to dry, and auxiliary agent in the time drying for the second time; Secondary drying is prebake and secondary drying, and the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C; When refining, the speed of a motor vehicle is 63 revs/min, and when oven dry, temperature is controlled at 82 DEG C, and oven dry degree is 92%, and when sizing, temperature is 174 DEG C, and the speed of a motor vehicle is 82 revs/min.
Wherein, step e) the auxiliary agent using be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: meter by weight, by 88 parts of decamethylcyclopentaandoxane, 1 part of silane coupler, 1 part, potassium hydroxide, 4 parts of lower 1h of maintenance under 100 DEG C of continuous stirrings of 8 parts of normal butanes and oxirane, then temperature is brought up to 160 DEG C and kept 15min, then decompression distillation goes out solvent, continue to keep 2h at 80 DEG C, then add 5 parts of polyoxyethylene sorbitan monoleates, 3 parts of poly hydroxy ethyl acrylates, 2 parts of chloroacetic chlorides, and to control pH be 5.8, temperature is 75 DEG C, constantly stir and continue 3h, then add 8 parts, barium sulfate, 3 parts of zinc chloride, after stirring, obtain amino-silicone oil softening agent.
Embodiment 3:
A kind of yam-dyed jacquard fabric, adopts following technique to be prepared from:
A) warping: by through inspection after warp thread on sectional warper after lease reed leasing beaming pulping axle, when warping, rotating speed is 242-286 rev/min; Described warp thread is 108D colored terylene filament, and weft yarn is three kinds of 145D colored terylene filament, through close be 128/cm, filling density is 72/cm, and weft yarn arrangement is 1:1:2, and upper machine fabric width is 310cm, total warp thread radical is 39680, adopts upper and lower double ends axle, and warp thread ratio is 3:2.
B) starching: by steps A) slurry axle carry out starching, when starching, control workshop temperature and be 20 DEG C DEG C, humidity is 85%, after starching, controlling the rate of sizing is 10%, oven dry rate is 99.8%;
And axle C): by after slurry beam warp denting good starching and on machine and become beam of a loom, and control workshop moisture temperature when axle and be 22 DEG C DEG C, humidity is 81%; Controlling the Shore hardness of beam of a loom is 85, by and axle after the beam of a loom that obtains place more than 24 hours;
D) weave: the colored type designing is inputted on the water-jet loom that jacquard attachment is housed, weaved after required weft preparing is good and obtain fabric; Adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, before looming weaving, first the colored type designing is washed into plastics cardboard, be arranged on the water-jet loom that mechanical type jacquard attachment is housed, weave after required weft preparing is good and obtain fabric; Warp tension is 560Kg, and the speed of a motor vehicle is 350rpm;
E) arrange: by first refining destarch of the fabric after weaving, then adopt the mode of shaping after secondary drying to dry, and auxiliary agent in the time drying for the second time; Secondary drying is prebake and secondary drying, and the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C; When refining, the speed of a motor vehicle is 56 revs/min, and when oven dry, temperature is controlled at 90 DEG C, and oven dry degree is 85%, and when sizing, temperature is 180 DEG C, and the speed of a motor vehicle is 72 revs/min.
Wherein, step e) the auxiliary agent using be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: meter by weight, by 86 parts of decamethylcyclopentaandoxane, 2 parts of silane couplers, 0.5 part, potassium hydroxide, 3 parts of lower 1h of maintenance under 100 DEG C of continuous stirrings of 10 parts of normal butanes and oxirane, then temperature is brought up to 160 DEG C and kept 15min, then decompression distillation goes out solvent, continue to keep 2h at 80 DEG C, then add 3 parts of polyoxyethylene sorbitan monoleates, 5 parts of poly hydroxy ethyl acrylates, 1 part of chloroacetic chloride, and to control pH be 5.8, temperature is 75 DEG C, constantly stir and continue 3h, then add 8 parts, barium sulfate, 3 parts of zinc chloride, after stirring, obtain amino-silicone oil softening agent.

Claims (7)

1. a preparation technology for yam-dyed jacquard fabric, is characterized in that, comprises the following steps:
A) warping: by through inspection after warp thread on sectional warper after lease reed leasing beaming pulping axle, when warping, rotating speed is 242-286 rev/min;
B) starching: by steps A) slurry axle carry out starching, when starching, controlling workshop temperature is 20 DEG C-25 DEG C, humidity is 70%-85%, after starching, controlling the rate of sizing is 8%-13%, oven dry rate is 98.6%-99.8%;
And axle C): by after slurry beam warp denting good starching and on machine and become beam of a loom, and to control workshop moisture temperature when axle be 22 DEG C-26 DEG C, humidity is 78%-86%; Controlling the Shore hardness of beam of a loom is 82-88, by and axle after the beam of a loom that obtains place more than 24 hours;
D) weave: the colored type designing is inputted on the water-jet loom that jacquard attachment is housed, weaved after required weft preparing is good and obtain fabric;
E) arrange: by first refining destarch of the fabric after weaving, then adopt the mode of shaping after secondary drying to dry, and auxiliary agent in the time drying for the second time; When refining, the speed of a motor vehicle is 47-63 rev/min, and oven dry degree is 83-92%, and when sizing, temperature is 174-181 DEG C, and the speed of a motor vehicle is 68-82 rev/min; Secondary drying is prebake and secondary drying, and the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C.
2. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, it is characterized in that, step D) be woven as: adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, before looming weaving, first the colored type designing is washed into plastics cardboard, be arranged on the water-jet loom that mechanical type jacquard attachment is housed, weave after required weft preparing is good and obtain fabric.
3. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, is characterized in that, described warp thread is 108D colored terylene filament, and weft yarn is three kinds of 145D colored terylene filament.
4. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, is characterized in that, through close be 128/cm, filling density is 72/cm, and weft yarn arrangement is 1:1:2, and upper machine fabric width is 310cm, total warp thread radical is 39680, adopts upper and lower double ends axle, and warp thread ratio is 3:2.
5. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, is characterized in that, step D) warp tension while weaving is 560Kg, the speed of a motor vehicle is 350rpm.
6. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, it is characterized in that, step e) auxiliary agent be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: meter by weight, by decamethylcyclopentaandoxane 85-88 part, silane coupler 1-2 part, potassium hydroxide 0.5-1 part, normal butane 8-15 part and oxirane 2-4 part constantly keep 1h under stirring at 100-105 DEG C, then temperature is brought up to 160 DEG C and kept 10-15min, then decompression distillation goes out solvent, continue to keep 2h at 80-90 DEG C, then add polyoxyethylene sorbitan monoleate 3-5 part, poly hydroxy ethyl acrylate 3-5 part, chloroacetic chloride 1-2 part, and to control pH be 5.8, temperature is 75-79 DEG C, constantly stir and continue 3h, then add barium sulfate 3-8 part, zinc chloride 3-5 part, after stirring, obtain amino-silicone oil softening agent.
7. a yam-dyed jacquard fabric that adopts the preparation technology of a kind of yam-dyed jacquard fabric claimed in claim 1 to prepare, it is characterized in that, in aggregates by warp thread and the weft yarn structure that interweaves, warp thread is 83-128D colored terylene filament, and weft yarn is the coloured chemical-fibres filaments of 126-330D.
CN201310701653.8A 2013-12-19 2013-12-19 A kind of preparation technology of yam-dyed jacquard fabric and the yam-dyed jacquard fabric that utilizes this technique to prepare Active CN104278409B (en)