CN104278409A - Preparation process for yarn-dyed jacquard fabric and yarn-dyed jacquard fabric prepared by process - Google Patents

Preparation process for yarn-dyed jacquard fabric and yarn-dyed jacquard fabric prepared by process Download PDF

Info

Publication number
CN104278409A
CN104278409A CN201310701653.8A CN201310701653A CN104278409A CN 104278409 A CN104278409 A CN 104278409A CN 201310701653 A CN201310701653 A CN 201310701653A CN 104278409 A CN104278409 A CN 104278409A
Authority
CN
China
Prior art keywords
fabric
yam
temperature
weaving
jacquard fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310701653.8A
Other languages
Chinese (zh)
Other versions
CN104278409B (en
Inventor
何芝萍
林参军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Ruiyijia Textile Technology Co., Ltd.
Original Assignee
何芝萍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 何芝萍 filed Critical 何芝萍
Priority to CN201310701653.8A priority Critical patent/CN104278409B/en
Publication of CN104278409A publication Critical patent/CN104278409A/en
Application granted granted Critical
Publication of CN104278409B publication Critical patent/CN104278409B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to the technical field of a textile fabric and a preparation process thereof, in particular to a preparation process for a yarn-dyed jacquard fabric and the yarn-dyed jacquard fabric prepared by the process. According to the process, the yarn-dyed jacquard fabric is prepared by adopting a mechanical jacquard water-jet loom through beaming, sizing, warp re-beaming, weaving and finishing. Various existing problems caused by the fact that the jacquard fabric is woven by adopting a rapier loom or an air-jet loom at present can be effectively solved by the process.

Description

A kind of preparation technology of yam-dyed jacquard fabric and the yam-dyed jacquard fabric utilizing this technique to prepare
Technical field
The present invention relates to weaving face fabric and fabricating technology field thereof, the preparation technology being specifically related to a kind of yam-dyed jacquard fabric and the yam-dyed jacquard fabric utilizing this technique to prepare.
Background technology
At present, existing jacquard fabric mostly adopts Rapier looms or air-jet loom weaving, little by water jet looms woven jacquard fabric kind.And, because water-jet weaving less energy consumption, the speed of a motor vehicle are fast, there is relative advantage constantly weaving same chemical fibre class jacquard fabric, be therefore also subject to the attention of manufacturer gradually.But jacquard fabric is in water-jet weaving process, and because workshop condition moisture is comparatively large, electronic jacquard loom is easy to make moist break down in operation process, causes and stops platform.In weaving process, particularly when weaving highly dense yam-dyed jacquard fabric, if only adopt electronic jacquard machine, large owing to causing dress to make the friction of harness cord gapping of spring through close height, again because Warp opening is larger more backward, easily weak after harness cord return spring excessive tensile, warp thread returns to combine and slows, cause the unintelligible or opening of opening to postpone, the easy injected water of warp thread thrusts.
Original liquid coloring polyster fibre, because its hygroscopicity is poor, modulus is high, very easily electrostatic, and keeps fit poor-performing, and irregularity is higher, if whole slurry technique is incorrect, easily causes that warp thread fluffs, cracked ends is frequent.And current colored woven fabric is not because needing dyed Final finishing, the general mode adopting low temperature secondary to shape after refining destarch, and shape time on softener, differ owing to padding when fabric moisture causes soft on fabric, fabric feeling is unstable, and because cloth cover is moist time low-temperature shaped, the easy run-bake-needle fault of selvedge, impact runs well.
Summary of the invention
The present invention, in order to solve the problem, provides a kind of preparation technology of yam-dyed jacquard fabric.
Another object of the present invention is to provide a kind of yam-dyed jacquard fabric adopting above-mentioned technique to prepare.
In order to reach foregoing invention object, the present invention by the following technical solutions:
A preparation technology for yam-dyed jacquard fabric, comprises the following steps:
A) warping: by through inspection after warp thread on Sectional warping machines after lease reed leasing beaming pulping axle, during warping, rotating speed is 242-286 rev/min;
B) starching: by steps A) slurry axle carry out starching, controlling workshop temperature during starching is 20 DEG C-25 DEG C, and humidity is 70%-85%, and controlling the rate of sizing after starching is 8%-13%, and oven dry rate is 98.6%-99.8%;
Starching the most important thing is two parameters, is the rate of sizing and oven dry rate respectively.The rate of sizing is directly proportional with the filling density of fabric, in order that ensure warp thread in weaving process wrapped by serous coat and serous coat can resistance to live the reed of certain number of times rub, guarantee phozy, do not entwine; Oven dry rate is relevant with weather, and different weathers will do suitable adjustment, and cause warp thread to entwine in order that eliminate electrostatic, impact is normally weaved.
And axle C): by after slurry beam warp denting good for starching and on machine, become beam of a loom, and to control workshop moisture temperature during axle be 22 DEG C-26 DEG C, and humidity is 78%-86%; Controlling the Shore hardness of beam of a loom is 82-88, by and the beam of a loom obtained after axle places more than 24 hours;
D) weave: the flower pattern input designed on the water jet looms that jacquard attachment is housed, carry out weaving obtaining fabric after required weft preparing is good;
The key point of beam of a loom hardness is, hardness is high, and warp thread drawing-off is excessive, and be easily pull fluffing or cracked ends weaving, hardness is low, and warp beam winding is bad, easily intersects, affect unwinding between layer.
E) arrange: by the fabric first refining destarch after weaving, the mode of shaping after then adopting secondary drying is dried, and when second time is dried on auxiliary agent; During refining, the speed of a motor vehicle is 47-63 rev/min, and during oven dry, temperature controls at 82-94 DEG C, and oven dry degree is 83-92%, and during sizing, temperature is 174-181 DEG C, and the speed of a motor vehicle is 68-82 rev/min.
As preferably, step D) be woven as: adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, first the flower pattern designed is washed into plastics cardboard before looming weaving, be arranged on mechanical type jacquard attachment is housed water jet looms on, carry out weaving obtaining fabric after required weft preparing is good.
As preferably, step e) secondary drying is prebake and secondary drying, the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C.
Be conducive to auxiliary agent during secondary drying, on after first time dries, auxiliary agent can make auxiliary agent penetrate into more equably in fabric, reaches the object of feel homogeneous soft
As preferably, described warp thread is 108D colored terylene filament, and weft yarn is three kinds of 145D colored terylene filament.
As preferably, through close be 128/cm, filling density is 72/cm, and weft yarn arrangement is 1:1:2, and upper machine fabric width is 310cm, and total warp thread radical is 39680, adopts upper and lower double-beam, and warp thread ratio is 3:2.
As preferably, step D) warp tension when weaving is 560Kg, the speed of a motor vehicle is 350rpm.
As preferably, step e) auxiliary agent be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: count by weight, by decamethylcyclopentaandoxane 85-88 part, silane coupler 1-2 part, potassium hydroxide 0.5-1 part, normal butane 8-15 part and oxirane 2-4 part constantly stir at 100-105 DEG C under under keep 1h, then temperature is brought up to 160 DEG C and keep 10-15min, then decompression distillation goes out solvent, continue to keep 2h at 80-90 DEG C, then polyoxyethylene sorbitan monoleate 3-5 part is added, poly hydroxy ethyl acrylate 3-5 part, chloroacetic chloride 1-2 part, and control pH is 5.8, temperature is 75-79 DEG C, continuous stirring continues 3h, then barium sulfate 3-8 part is added, zinc chloride 3-5 part, amino-silicone oil softening agent is obtained after stirring.
Amido silicon oil is the fundamental component using what textiles soft finishing agent specially.It has best adsorptivity, compatibility and easy emulsibility.Use blender or homogenizer, amido silicon oil is easily become stable, transparent microemulsion by suitable surfactant emulsifies.It can be used alone, and also can be combined into special soft finishing agent with other organosilicon or organic softener, be suitable for the soft finish of the various textiles of what.The ammonia value of amido silicon oil is between 0.2 ~ 1.2, and ammonia value is higher, flexibility and slippery better, but xanthochromia can be larger.Therefore, provide excellent softness, level and smooth, uniform feel for happy, and strengthen the tearing strength of fabric and wrinkle resistance and improve the elasticity of fabric, water-fastness and dry cleaning resistance.The application provides the component of above-mentioned auxiliary agent, solves the defect such as easy xanthochromia, increase fabric hydrophobicity, amino skewness that current amido silicon oil exists as third generation silicone softening agent.The easy emulsification of amido silicon oil of the present invention, can be made into stable microemulsion and not easily causes xanthochromia.Be applicable in the preparation technology of yam-dyed jacquard fabric of the present invention.
Adopt a yam-dyed jacquard fabric prepared by the preparation technology of yam-dyed jacquard fabric, by warp thread and weft yarns structure in aggregates, warp thread is 83-128D colored terylene filament, and weft yarn is the coloured chemical-fibres filaments of 126-330D.
Compared with prior art, beneficial effect is in the present invention: the present invention, by adopting mechanical type water jet jacquard loom, effectively can solve the problem causing greatly the reasons such as electronic jacquard loom electronic component damage to make device fails rate too high because of moisture; By adopting rational whole slurry and technique solves because drying the unreasonable problem such as cause the excessive drawing-off of warp thread, starching bad, decreasing the generation of the unclear phenomenon such as not in time of warp thread fluffing, cracked ends, opening, effectively improve weaving efficiency and fabric quality; By adopting coloured chemical-fibres filaments to be raw material, avoiding printing and dyeing link, decreasing the use of resource and the discharge of discarded object, shorten production process time.Present invention process is reasonable, advanced, raw material environmental protection, the advantages such as fabric has cloth cover exquisiteness, soft, drapability good, flower pattern third dimension is strong, level is obvious, COLOR FASTNESS is high, shading.
Detailed description of the invention
Below by specific embodiment, explanation is further described to technical scheme of the present invention.
If without specified otherwise, the raw material adopted in embodiments of the invention is the conventional raw material in this area, and the method adopted in embodiment, is the conventional method of this area.
embodiment 1:
A kind of yam-dyed jacquard fabric, adopts following technique to be prepared from:
A) warping: warp thread is 83D colored terylene filament, weft yarn is the coloured chemical-fibres filaments of 330D, by through inspection after warp thread on Sectional warping machines after lease reed leasing beaming pulping axle, during warping, rotating speed is 242 revs/min; Through close be 128/cm, filling density is 72/cm, and weft yarn arrangement is 1:1:2, and upper machine fabric width is 310cm, and total warp thread radical is 39680, adopts upper and lower double-beam, and warp thread ratio is 3:2.
B) starching: by steps A) slurry axle carry out starching, controlling workshop temperature during starching is 25 DEG C, and humidity is 70%, and controlling the rate of sizing after starching is 13%, and oven dry rate is 98.6%;
And axle C): by after slurry beam warp denting good for starching and on machine, become beam of a loom, and to control workshop moisture temperature during axle be 26 DEG C, and humidity is 78%; Controlling the Shore hardness of beam of a loom is 88, by and the beam of a loom obtained after axle places more than 24 hours;
D) weave: the flower pattern input designed on the water jet looms that jacquard attachment is housed, carry out weaving obtaining fabric after required weft preparing is good; Adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, first the flower pattern designed is washed into plastics cardboard before looming weaving, be arranged on mechanical type jacquard attachment is housed water jet looms on, carry out weaving obtaining fabric after required weft preparing is good; Warp tension is 560Kg, and the speed of a motor vehicle is 350rpm;
E) arrange: by the fabric first refining destarch after weaving, the mode of shaping after then adopting secondary drying is dried, and when second time is dried on auxiliary agent; Secondary drying is prebake and secondary drying, and the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C; During refining, the speed of a motor vehicle is 47 revs/min, and during oven dry, temperature controls at 94 DEG C, and oven dry degree is 83%, and during sizing, temperature is 181 DEG C, and the speed of a motor vehicle is 68 revs/min.
 
Wherein, step e) the auxiliary agent used be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: count by weight, by decamethylcyclopentaandoxane 85 parts, silane coupler 2 parts, 0.5 part, potassium hydroxide, 1h is kept under under normal butane 15 parts and 2 parts, oxirane constantly stir at 105 DEG C, then temperature is brought up to 160 DEG C and keep 10min, then decompression distillation goes out solvent, continue to keep 2h at 90 DEG C, then polyoxyethylene sorbitan monoleate 3 parts is added, poly hydroxy ethyl acrylate 5 parts, chloroacetic chloride 1 part, and control pH is 5.8, temperature is 79 DEG C, continuous stirring continues 3h, then 3 parts, barium sulfate is added, zinc chloride 5 parts, amino-silicone oil softening agent is obtained after stirring.
embodiment 2:
A kind of yam-dyed jacquard fabric, adopts following technique to be prepared from:
A) warping: warp thread is 128D colored terylene filament, weft yarn is the coloured chemical-fibres filaments of 126D, by through inspection after warp thread on Sectional warping machines after lease reed leasing beaming pulping axle, during warping, rotating speed is 286 revs/min; Through close be 128/cm, filling density is 72/cm, and weft yarn arrangement is 1:1:2, and upper machine fabric width is 310cm, and total warp thread radical is 39680, adopts upper and lower double-beam, and warp thread ratio is 3:2.
B) starching: by steps A) slurry axle carry out starching, controlling workshop temperature during starching is 20 DEG C, and humidity is 85%, and controlling the rate of sizing after starching is 8%, and oven dry rate is 99.8%;
And axle C): by after slurry beam warp denting good for starching and on machine, become beam of a loom, and control workshop moisture temperature during axle and be 22 DEG C DEG C, humidity is 86%; Controlling the Shore hardness of beam of a loom is 82, by and the beam of a loom obtained after axle places more than 24 hours;
D) weave: the flower pattern input designed on the water jet looms that jacquard attachment is housed, carry out weaving obtaining fabric after required weft preparing is good; Adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, first the flower pattern designed is washed into plastics cardboard before looming weaving, be arranged on mechanical type jacquard attachment is housed water jet looms on, carry out weaving obtaining fabric after required weft preparing is good; Warp tension is 560Kg, and the speed of a motor vehicle is 350rpm;
E) arrange: by the fabric first refining destarch after weaving, the mode of shaping after then adopting secondary drying is dried, and when second time is dried on auxiliary agent; Secondary drying is prebake and secondary drying, and the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C; During refining, the speed of a motor vehicle is 63 revs/min, and during oven dry, temperature controls at 82 DEG C, and oven dry degree is 92%, and during sizing, temperature is 174 DEG C, and the speed of a motor vehicle is 82 revs/min.
 
Wherein, step e) the auxiliary agent used be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: count by weight, by decamethylcyclopentaandoxane 88 parts, silane coupler 1 part, 1 part, potassium hydroxide, 1h is kept under under normal butane 8 parts and 4 parts, oxirane constantly stir at 100 DEG C, then temperature is brought up to 160 DEG C and keep 15min, then decompression distillation goes out solvent, continue to keep 2h at 80 DEG C, then polyoxyethylene sorbitan monoleate 5 parts is added, poly hydroxy ethyl acrylate 3 parts, chloroacetic chloride 2 parts, and control pH is 5.8, temperature is 75 DEG C, continuous stirring continues 3h, then 8 parts, barium sulfate is added, zinc chloride 3 parts, amino-silicone oil softening agent is obtained after stirring.
 
embodiment 3:
A kind of yam-dyed jacquard fabric, adopts following technique to be prepared from:
A) warping: by through inspection after warp thread on Sectional warping machines after lease reed leasing beaming pulping axle, during warping, rotating speed is 242-286 rev/min; Described warp thread is 108D colored terylene filament, and weft yarn is three kinds of 145D colored terylene filament, through close be 128/cm, filling density is 72/cm, and weft yarn arrangement is 1:1:2, and upper machine fabric width is 310cm, total warp thread radical is 39680, adopts upper and lower double-beam, and warp thread ratio is 3:2.
B) starching: by steps A) slurry axle carry out starching, control workshop temperature during starching and be 20 DEG C DEG C, humidity is 85%, and controlling the rate of sizing after starching is 10%, and oven dry rate is 99.8%;
And axle C): by after slurry beam warp denting good for starching and on machine, become beam of a loom, and control workshop moisture temperature during axle and be 22 DEG C DEG C, humidity is 81%; Controlling the Shore hardness of beam of a loom is 85, by and the beam of a loom obtained after axle places more than 24 hours;
D) weave: the flower pattern input designed on the water jet looms that jacquard attachment is housed, carry out weaving obtaining fabric after required weft preparing is good; Adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, first the flower pattern designed is washed into plastics cardboard before looming weaving, be arranged on mechanical type jacquard attachment is housed water jet looms on, carry out weaving obtaining fabric after required weft preparing is good; Warp tension is 560Kg, and the speed of a motor vehicle is 350rpm;
E) arrange: by the fabric first refining destarch after weaving, the mode of shaping after then adopting secondary drying is dried, and when second time is dried on auxiliary agent; Secondary drying is prebake and secondary drying, and the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C; During refining, the speed of a motor vehicle is 56 revs/min, and during oven dry, temperature controls at 90 DEG C, and oven dry degree is 85%, and during sizing, temperature is 180 DEG C, and the speed of a motor vehicle is 72 revs/min.
 
Wherein, step e) the auxiliary agent used be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: count by weight, by decamethylcyclopentaandoxane 86 parts, silane coupler 2 parts, 0.5 part, potassium hydroxide, 1h is kept under under normal butane 10 parts and 3 parts, oxirane constantly stir at 100 DEG C, then temperature is brought up to 160 DEG C and keep 15min, then decompression distillation goes out solvent, continue to keep 2h at 80 DEG C, then polyoxyethylene sorbitan monoleate 3 parts is added, poly hydroxy ethyl acrylate 5 parts, chloroacetic chloride 1 part, and control pH is 5.8, temperature is 75 DEG C, continuous stirring continues 3h, then 8 parts, barium sulfate is added, zinc chloride 3 parts, amino-silicone oil softening agent is obtained after stirring.

Claims (8)

1. a preparation technology for yam-dyed jacquard fabric, is characterized in that, comprises the following steps:
A) warping: by through inspection after warp thread on Sectional warping machines after lease reed leasing beaming pulping axle, during warping, rotating speed is 242-286 rev/min;
B) starching: by steps A) slurry axle carry out starching, controlling workshop temperature during starching is 20 DEG C-25 DEG C, and humidity is 70%-85%, and controlling the rate of sizing after starching is 8%-13%, and oven dry rate is 98.6%-99.8%;
And axle C): by after slurry beam warp denting good for starching and on machine, become beam of a loom, and to control workshop moisture temperature during axle be 22 DEG C-26 DEG C, and humidity is 78%-86%; Controlling the Shore hardness of beam of a loom is 82-88, by and the beam of a loom obtained after axle places more than 24 hours;
D) weave: the flower pattern input designed on the water jet looms that jacquard attachment is housed, carry out weaving obtaining fabric after required weft preparing is good;
E) arrange: by the fabric first refining destarch after weaving, the mode of shaping after then adopting secondary drying is dried, and when second time is dried on auxiliary agent; During refining, the speed of a motor vehicle is 47-63 rev/min, and during oven dry, temperature controls at 82-94 DEG C, and oven dry degree is 83-92%, and during sizing, temperature is 174-181 DEG C, and the speed of a motor vehicle is 68-82 rev/min.
2. the manufacturing technique of a kind of yam-dyed jacquard fabric according to claim 1, it is characterized in that, step D) be woven as: adopt mechanical type jacquard attachment at the front and posterior composite anti-blocking weaving mode of mechanical type dobby machine device, first the flower pattern designed is washed into plastics cardboard before looming weaving, be arranged on mechanical type jacquard attachment is housed water jet looms on, carry out weaving obtaining fabric after required weft preparing is good.
3. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, is characterized in that, step e) secondary drying is prebake and secondary drying, the bake out temperature of prebake is 80 DEG C, and oven dry degree is 90%, and the bake out temperature of secondary drying is 85 DEG C.
4. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, is characterized in that, described warp thread is 108D colored terylene filament, and weft yarn is three kinds of 145D colored terylene filament.
5. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, is characterized in that, described through close be 128/cm, filling density is 72/cm, and weft yarn arrangement is 1:1:2, and upper machine fabric width is 310cm, total warp thread radical is 39680, adopts upper and lower double-beam, and warp thread ratio is 3:2.
6. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, is characterized in that, step D) warp tension when weaving is 560Kg, the speed of a motor vehicle is 350rpm.
7. the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1, it is characterized in that, step e) auxiliary agent be amino-silicone oil softening agent, described amino-silicone oil softening agent is prepared from by following steps: count by weight, by decamethylcyclopentaandoxane 85-88 part, silane coupler 1-2 part, potassium hydroxide 0.5-1 part, normal butane 8-15 part and oxirane 2-4 part constantly stir at 100-105 DEG C under under keep 1h, then temperature is brought up to 160 DEG C and keep 10-15min, then decompression distillation goes out solvent, continue to keep 2h at 80-90 DEG C, then polyoxyethylene sorbitan monoleate 3-5 part is added, poly hydroxy ethyl acrylate 3-5 part, chloroacetic chloride 1-2 part, and control pH is 5.8, temperature is 75-79 DEG C, continuous stirring continues 3h, then barium sulfate 3-8 part is added, zinc chloride 3-5 part, amino-silicone oil softening agent is obtained after stirring.
8. the yam-dyed jacquard fabric adopting the preparation technology of a kind of yam-dyed jacquard fabric according to claim 1 to prepare, it is characterized in that, by warp thread and weft yarns structure in aggregates, warp thread is 83-128D colored terylene filament, and weft yarn is the coloured chemical-fibres filaments of 126-330D.
CN201310701653.8A 2013-12-19 2013-12-19 A kind of preparation technology of yam-dyed jacquard fabric and the yam-dyed jacquard fabric that utilizes this technique to prepare Active CN104278409B (en)