Ink-jet advertisement consumptive material and production method
Technical field
The present invention relates to ink-jet advertisement consumptive material and production method.
Background technology
The making of ink-jet advertisement consumptive material in prior art; as shown in Figure 1; usually by PP coating synthetic paper 10(also referred to as directly dividing for the non-gum of PP, PP, PP consumptive material etc.) and cold lamination film 20 2 complete stand-alone products form; first need PP coating synthetic paper to be carried out air brushing during use and beat picture formation sprayed picture surface layer 30; after completing the picture of needs, cold lamination film 20 is used to carry out mounting film protection.Manufacturer is also that PP coating synthetic paper and cold lamination film are separated when delivering goods, and two products are completely independently.
The cold lamination film wherein adopted in said process; as shown in Figure 2; be generally release liners 3 and adopt with the protective layer 1 that polyvinyl chloride (PVC) hyaline membrane makes that pressure sensitive adhesive 2 is bonding to be formed; release liners is also known as silicone oil paper, separate paper; body paper is typically used or recycled paper is processed into through film due to release liners; surface is comparatively coarse; even if the silicone oil on the surface when film; still not reaching the requirement of high aloof from politics and material pursuits degree, there is comparatively obviously snowflake and cloudy surface defect in the cold lamination film product using release liners to produce usually.On the other hand, the release liners of this paper substrate is used also not meet national ecological forestry protection requirement.
Simultaneously due to the independence of PP coating synthetic paper and cold lamination film product in Conventional process, production technology is also separately carried out usually, and efficiency is lower.
Summary of the invention
The object of the invention is to the problem overcoming above-mentioned prior art, provide a kind of ink-jet advertisement consumptive material, it has integrated structure, can avoid use time again mount film, there is the advantage of high-resolution and high degree thoroughly simultaneously, avoid adopting traditional release liners, thus save forest resourceies.
Above-mentioned purpose is achieved through the following technical solutions:
Ink-jet advertisement consumptive material, comprise transparent protective layer, the below of described protective layer is provided with adhesive linkage, the below of described upper adhesive linkage is provided with silicon layer, the below of described upper silicon layer is provided with basic unit, the below of described upper basic unit is provided with lower silicon layer, and the below of described lower silicon layer is provided with lower adhesive linkage; The below of described lower adhesive linkage is provided with goes to a grassroots level, described in the below of going to a grassroots level be provided with ink-absorbed coated layer, described upper basic unit and described in go to a grassroots level and adopt plastic material respectively.
Further, described upper basic unit adopts PET built up membrane, described in go to a grassroots level and adopt PP synthetic paper or PEPA iridescent paper.
Further, described protective layer is polyvinyl chloride transparent film.
Further, described upper adhesive linkage and lower adhesive linkage are pressure sensitive adhesive.
Further, described ink-absorbed coated layer adopts polyvinyl alcohol synthesis ink-absorbed coated layer or solvent type acrylic resin synthesis ink-absorbed coated layer or water-borne acrylic resin to synthesize ink-absorbed coated layer.
There is provided the production method of this ink-jet advertisement consumptive material, it can avoid processing PP coating synthetic paper and cold lamination film respectively, and realize integrated production, production efficiency is higher simultaneously.
The production method of preparation ink-jet advertisement consumptive material as previously discussed, comprises the following steps:
S1: first, side of going to a grassroots level described in described ink-absorbed coated layer is uniformly coated on the dry glue thickness grammes per square metre of every square metre 3 grams to 80 grams, wherein said employing plastic material of going to a grassroots level;
S2: then carry out drying and processing by baking oven;
S3: both side surface silicone oil being uniformly coated on respectively described upper basic unit with the dry silicon consumption of every square metre 0.1 gram to 3.5 grams, silicon layer and lower silicon layer in formation, wherein said upper basic unit adopts plastic material;
S4: then carry out drying and processing by baking oven;
S5: the surface again pressure sensitive adhesive being evenly coated in the described lower silicon layer after S4 step process with the dry glue consumption of every square metre 8 grams to 40 grams, forms lower adhesive linkage;
S6: by the product that obtains through step S5 through oven for drying process;
S7: fit bonding with the lower adhesive linkage after step S6 process by going to a grassroots level described in after step S2 process;
S8: pressure sensitive adhesive is evenly coated in the described upper silicon layer surface after step S7 process with the dry glue consumption of every square metre 8 grams to 40 grams, and adhesive linkage in formation, fits bonding by described upper adhesive linkage with transparent protective layer.
Further, described upper basic unit adopts PET built up membrane, described in go to a grassroots level and adopt PP synthetic paper or PEPA iridescent paper.
Further, in step S2, step S4 and step S6, the temperature that baking oven carries out drying and processing is respectively 25 degrees Celsius to 160 degrees Celsius.
Further, in step S2, it is 15 meters to 200 meters per minute by the speed of baking oven; In step S4, it is 20 meters to 250 meters per minute by the speed of baking oven; In step S6, it is 20 meters to 150 meters per minute by the speed of baking oven.
Further, described ink-absorbed coated layer adopts polyvinyl alcohol synthesis ink-absorbed coated layer or solvent type acrylic resin synthesis ink-absorbed coated layer or water-borne acrylic resin to synthesize ink-absorbed coated layer.
Ink-jet advertisement consumptive material of the present invention and production method, this ink-jet advertisement consumptive material comprises transparent protective layer, the below of protective layer is provided with adhesive linkage, the below of upper adhesive linkage is provided with silicon layer, the below of upper silicon layer is provided with basic unit, the below of upper basic unit is provided with lower silicon layer, and the below of lower silicon layer is provided with lower adhesive linkage; The below of lower adhesive linkage is provided with goes to a grassroots level, and the below of going to a grassroots level is provided with ink-absorbed coated layer, upper basic unit and go to a grassroots level and adopt plastic material respectively.Ink-absorbed coated layer is first coated in the side drying and processing of going to a grassroots level by this production method; silicone oil is coated with in the both sides of upper basic unit; after drying and processing, below lower silicon layer, coat pressure sensitive adhesive again form lower adhesive linkage; again after drying and processing by lower adhesive linkage with go to a grassroots level bonding, then on passing through adhesive linkage bonding on silicon layer and protective layer.By replace traditional basic unit with material, the plastic material adopting smooth surface smooth the form be arranged to basic unit and gone to a grassroots level, thus make it have the advantage of high-resolution and high degree thoroughly, avoid simultaneously and adopt traditional release liners, save forest resourceies; Simultaneously it has integrated structure, thus again mounts film when avoiding use; This production method avoids and processes PP coating synthetic paper and cold lamination film respectively simultaneously, and achieve integrated production, production efficiency is higher.In addition Dual-layer form is set, also there is the advantage more easily peeling off goods.
Accompanying drawing explanation
Fig. 1 is the structural representation of ink-jet advertisement consumptive material in prior art;
Fig. 2 is the structural representation of cold lamination film in prior art;
Fig. 3 is the structural representation of ink-jet advertisement consumptive material of the present invention.
Detailed description of the invention
According to drawings and embodiments the present invention is described in further detail below.
As shown in Figure 3, a kind of ink-jet advertisement consumptive material described in the embodiment of the present invention, ink-jet advertisement consumptive material, comprise transparent protective layer 1, the below of protective layer 1 is provided with adhesive linkage 4, and the below of upper adhesive linkage 4 is provided with silicon layer 5, and the below of upper silicon layer 5 is provided with basic unit 6, the below of upper basic unit 6 is provided with lower silicon layer 7, and the below of lower silicon layer 7 is provided with lower adhesive linkage 8; The below of lower adhesive linkage 8 is provided with goes to a grassroots level 9, go to a grassroots level 9 below be provided with ink-absorbed coated layer 10, upper basic unit 6 and go to a grassroots level and 9 adopt plastic material respectively.
Upper basic unit 6 adopts PET built up membrane, go to a grassroots level 9 employing PP synthetic papers or PEPA iridescent paper.Upper adhesive linkage 4 and lower adhesive linkage 8 are pressure sensitive adhesive.
Basic unit adopts PP synthetic paper or PEPA iridescent paper or PET built up membrane.PP synthetic paper is generally formed with primary raw material mixing compactings such as natural stone-powders by acrylic resin, polyvinyl resin; PEPA iridescent paper is normally suppressed by the polyolefin resin of petroleum cracking again through being polymerized; PET is the abbreviation of PETG, and chemical formula is-OCH2-CH2OCOC6H4CO-, repeats no more.
Upper basic unit 6 or go to a grassroots level 9 thickness specification select can from 0.065mm to 0.25mm.Protective layer 1 is polyvinyl chloride transparent film 1.The thickness specification of protective layer 1 is optional selects 0.040mm to 0.25mm.Such as by customer demand, basic unit 6 can be selected and the 9 thickness 0.1mm that go to a grassroots level, protective layer 1 thickness 0.1mm.
Ink-absorbed coated layer 10 adopts polyvinyl alcohol to synthesize ink-absorbed coated layer 106 or solvent type acrylic resin synthesizes ink-absorbed coated layer 10 or water-borne acrylic resin synthesis ink-absorbed coated layer 10.Protective layer 1 is polyvinyl chloride transparent film.
Preparation, as the production method of above ink-jet advertisement consumptive material, comprises the following steps:
S1: first, is uniformly coated on the dry glue thickness grammes per square metre of every square metre 3 grams to 80 grams 9 sides of going to a grassroots level by ink-absorbed coated layer 10,9 employing plastic materials of wherein going to a grassroots level; S2: then carry out drying and processing by baking oven; S3: both side surface silicone oil being uniformly coated on respectively upper basic unit 6 with the dry silicon consumption of every square metre 0.1 gram to 3.5 grams, silicon layer 5 and lower silicon layer 7 in formation, wherein go up basic unit 6 and adopt plastic material; S4: then carry out drying and processing by baking oven; S5: the surface again pressure sensitive adhesive being evenly coated in the lower silicon layer 7 after S4 step process with the dry glue consumption of every square metre 8 grams to 40 grams, forms lower adhesive linkage 8; S6: by the product that obtains through step S5 through oven for drying process; S7: going to a grassroots level after step S2 process 9 is fitted bonding with the lower adhesive linkage 8 after step S6 process; S8: pressure sensitive adhesive is evenly coated in the surface of the upper silicon layer 5 after step S7 process with the dry glue consumption of every square metre 8 grams to 40 grams, and adhesive linkage 4 in formation, fits bonding by upper adhesive linkage 4 with transparent protective layer 1.
In step S2, step S4 and step S6, the temperature that baking oven carries out drying and processing is respectively 25 degrees Celsius to 160 degrees Celsius.In step S2, it is 15 meters to 200 meters per minute by the speed of baking oven; In step S4, it is 20 meters to 250 meters per minute by the speed of baking oven; In step S6, it is 20 meters to 150 meters per minute by the speed of baking oven.By the speed of baking oven and the temperature of baking oven generally corresponding, the higher required drying time of temperature is shorter, and the speed passed through is also faster.Such as, can adopt the speed of under 80 degrees Celsius 100 meters per minute in step S2; The speed of under 80 degrees Celsius 100 meters per minute can be adopted in step S4; The speed of under 80 degrees Celsius 90 meters per minute can be adopted in step S6.
This production method first ink-absorbed coated layer 10 is coated in go to a grassroots level 9 side and drying and processing; silicone oil is coated with in the both sides of upper basic unit 6; after drying and processing, below lower silicon layer 7, coat pressure sensitive adhesive again form lower adhesive linkage 8; again after drying and processing by lower adhesive linkage 8 with go to a grassroots level 9 bonding, then on passing through adhesive linkage 4 bonding on silicon layer 5 and protective layer 1.By replace traditional basic unit with material, adopt the smooth plastic material of smooth surface and be arranged to basic unit 6 and go to a grassroots level 9 form, thus make it have the advantage of high-resolution and high degree thoroughly, avoid simultaneously and adopt traditional release liners, save forest resourceies; Simultaneously it has integrated structure, thus again mounts film when avoiding use; This production method avoids and processes PP coating synthetic paper and cold lamination film respectively simultaneously, and achieve integrated production, production efficiency is higher.In addition Dual-layer form is set, also there is the advantage more easily peeling off goods.Meanwhile, in actual use, integrated structure effectively can reduce transport and storage cost about 50%.In addition Dual-layer form is set, also there is the advantage more easily peeling off goods.
The foregoing is only explanation embodiments of the present invention; be not limited to the present invention, for a person skilled in the art, within the spirit and principles in the present invention all; any amendment of doing, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.