CN104230227B - A kind of decoration mortar and preparation method thereof - Google Patents

A kind of decoration mortar and preparation method thereof Download PDF

Info

Publication number
CN104230227B
CN104230227B CN201410420065.1A CN201410420065A CN104230227B CN 104230227 B CN104230227 B CN 104230227B CN 201410420065 A CN201410420065 A CN 201410420065A CN 104230227 B CN104230227 B CN 104230227B
Authority
CN
China
Prior art keywords
sodium
mortar
mixing
auxiliary agent
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410420065.1A
Other languages
Chinese (zh)
Other versions
CN104230227A (en
Inventor
孙峰
郑权
吕希萌
Original Assignee
筑隆建材科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
Application filed by 筑隆建材科技有限公司 filed Critical 筑隆建材科技有限公司
Priority to CN201410420065.1A priority Critical patent/CN104230227B/en
Publication of CN104230227A publication Critical patent/CN104230227A/en
Application granted granted Critical
Publication of CN104230227B publication Critical patent/CN104230227B/en
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=52219245&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN104230227(B) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of decoration mortar, be made up of the raw material of following weight part: calcium chloride 3-4, Tai-Ace S 150 2-3, flyash 60-70, sodium sulfate 3-4, alum powder 2-3, ironic hydroxide 10-15, vegetables oil 2-3, water are appropriate, auxiliary agent 20-25, cement 100-120, quartz sand 100-120, sodium lauryl sulphate 0.8-1.2, sodium abietate 1-1.4, carboxylic styrene butadiene latex 14-18, diatomite 40-50, sepiolite 30-40; Mortar good leveling property of the present invention, easy application, good endurance, containing diatomite, sepiolite, can purify air, not containing toxic substance, not efflorescence; The application of the invention auxiliary agent, improves the resistance to compression of mortar, folding strength, improves workability, sag resistance, thixotropy and anti-settling.

Description

A kind of decoration mortar and preparation method thereof
Technical field
The invention belongs to building material field, particularly a kind of decoration mortar and preparation method thereof.
Background technology
Mortar is common material for building, belongs to the indispensable material in building operation.Divide according to performance, mortar is divided into a variety of, has in conjunction with mortar, filleting mortar, thermal insulation mortar etc.; Masonry mortar, plastering mortar (comprising decoration mortar, waterproof mortar), adhesive mortar etc. are divided into by purposes.
The performance quality of current mortar differs, and affects use.Specifically the factor affecting mortar performance comprises the workability of fresh mortar, mobility, water-retentivity, is exactly the intensity of hardened mortar in addition.Need to study new mortar, make it have excellent application property and processibility, sag resistance, thixotropy, anti-settling, package stability, improve pumping and shear-thinning, also need to find new material, to improve its use properties and intensity, and reduce comprehensive cost.
Summary of the invention
The object of the present invention is to provide a kind of decoration mortar and preparation method thereof, this mortar good leveling property, easy application, good endurance, can purify air, not containing toxic substance, and not efflorescence.
Technical scheme of the present invention is as follows:
A kind of decoration mortar, is characterized in that being made up of the raw material of following weight part: calcium chloride 3-4, Tai-Ace S 150 2-3, flyash 60-70, sodium sulfate 3-4, alum powder 2-3, ironic hydroxide 10-15, vegetables oil 2-3, water are appropriate, auxiliary agent 20-25, cement 100-120, quartz sand 100-120, sodium lauryl sulphate 0.8-1.2, sodium abietate 1-1.4, carboxylic styrene butadiene latex 14-18, diatomite 40-50, sepiolite 30-40;
Described auxiliary agent is made up of the raw material of following weight part: attapulgite 2-3, wilkinite 2-3, steel fiber 6-7, urethane acrylate 4-5, E-12 epoxy resin 2-3, epoxy acrylate 3-4, peroxidized t-butyl perbenzoate 0.2-0.3, vinylbenzene 1-2, dipropylene glycol 3-4, TriMethylolPropane(TMP) 2-3, Calucium Silicate powder 3-4, mandarin oil 0.8-1.2, benzotriazole 0.6-0.9, trimeric cyanamide 1-2, 10-15% sodium hydroxide solution 6-8, sodium oleate 0.2-0.3, ammonium persulphate 0.1-0.2, water 17-20, preparation method is: attapulgite, wilkinite are put into calcining furnace, at 670-700 DEG C, calcine 3-4 hour, takes out, puts into 10-15% sodium hydroxide solution and be ground to 20-40 μm of slurry, and material pH value of sizing mixing is for neutral, and spraying dry obtains powder, by water, sodium oleate, urethane acrylate, E-12 epoxy resin, epoxy acrylate, vinylbenzene, dipropylene glycol, TriMethylolPropane(TMP) mixing, be heated to 60-70 DEG C, add peroxidized t-butyl perbenzoate, stirring reaction 20-30 minute, add described powder and other composition again, continue to be warming up to 80-90 DEG C, stirring reaction 50-60 minute, to obtain final product.
The preparation method of described decoration mortar, is characterized in that comprising the following steps:
(1) by diatomite, sepiolite, ironic hydroxide mixing, 140-180 order particle is ground into;
(2) by calcium chloride, Tai-Ace S 150, sodium sulfate, alum powder, sodium lauryl sulphate, sodium abietate, carboxylic styrene butadiene latex, water mixing, stir and obtain slurry;
(3) by auxiliary agent, flyash, vegetables oil mixing, dispersion grinding 20-30 minute, obtains mixture;
(4) mixing of materials other remaining components and (1) step, (2) step, (3) step obtained is even, and stirring reaction 10-15 minute, to obtain final product.
Beneficial effect of the present invention
Mortar good leveling property of the present invention, easy application, good endurance, containing diatomite, sepiolite, can purify air, not containing toxic substance, not efflorescence; The application of the invention auxiliary agent, improves the resistance to compression of mortar, folding strength, improves workability, sag resistance, thixotropy and anti-settling.
Embodiment
A kind of decoration mortar, is made up of the raw material of following weight part (kilogram): calcium chloride 3.5, Tai-Ace S 150 2.5, flyash 65, sodium sulfate 3.5, alum powder 2.5, ironic hydroxide 13, vegetables oil 2.5, water are appropriate, auxiliary agent 23, cement 110, quartz sand 110, sodium lauryl sulphate 1, sodium abietate 1.2, carboxylic styrene butadiene latex 16, diatomite 45, sepiolite 35;
Described auxiliary agent is made up of the raw material of following weight part (kilogram): attapulgite 2.5, wilkinite 2.5, steel fiber 6.5, urethane acrylate 4.5, E-12 epoxy resin 2.5, epoxy acrylate 3.5, peroxidized t-butyl perbenzoate 0.5, vinylbenzene 1.5, dipropylene glycol 3.5, TriMethylolPropane(TMP) 2.5, Calucium Silicate powder 3.5, mandarin oil 1, benzotriazole 0.8, trimeric cyanamide 1.5,3% sodium hydroxide solution 7, sodium oleate 0.3, ammonium persulphate 0.2, water 19; Preparation method is: attapulgite, wilkinite are put into calcining furnace, calcines 3.5 hours at 69 DEG C, takes out, puts into 13% sodium hydroxide solution and be ground to 30 μm of slurries, and material pH value of sizing mixing is for neutral, and spraying dry obtains powder; By water, sodium oleate, urethane acrylate, E-12 epoxy resin, epoxy acrylate, vinylbenzene, dipropylene glycol, TriMethylolPropane(TMP) mixing, be heated to 65 DEG C, add peroxidized t-butyl perbenzoate, stirring reaction 25 minutes, add described powder and other composition again, continue to be warming up to 85 DEG C, stirring reaction 55 minutes, to obtain final product.
The preparation method of described decoration mortar, comprises the following steps:
(1) by diatomite, sepiolite, ironic hydroxide mixing, 160 order particles are ground into;
(2) by calcium chloride, Tai-Ace S 150, sodium sulfate, alum powder, sodium lauryl sulphate, sodium abietate, carboxylic styrene butadiene latex, water mixing, stir and obtain slurry;
(3) by auxiliary agent, flyash, vegetables oil mixing, dispersion grinding 25 minutes, obtains mixture;
(4) mixing of materials other remaining components and (1) step, (2) step, (3) step obtained is even, and stirring reaction 13 minutes, to obtain final product.
Experimental data:
The ultimate compression strength of the mortar 28d of this embodiment is 42MPa, folding strength 12MPa, water-intake rate 2.1%.

Claims (2)

1. a decoration mortar, is characterized in that being made up of the raw material of following weight part: calcium chloride 3-4, Tai-Ace S 150 2-3, flyash 60-70, sodium sulfate 3-4, alum powder 2-3, ironic hydroxide 10-15, vegetables oil 2-3, water are appropriate, auxiliary agent 20-25, cement 100-120, quartz sand 100-120, sodium lauryl sulphate 0.8-1.2, sodium abietate 1-1.4, carboxylic styrene butadiene latex 14-18, diatomite 40-50, sepiolite 30-40;
Described auxiliary agent is made up of the raw material of following weight ratio example: attapulgite 2-3, wilkinite 2-3, steel fiber 6-7, urethane acrylate 4-5, E-12 epoxy resin 2-3, epoxy acrylate 3-4, peroxidized t-butyl perbenzoate 0.2-0.3, vinylbenzene 1-2, dipropylene glycol 3-4, TriMethylolPropane(TMP) 2-3, Calucium Silicate powder 3-4, mandarin oil 0.8-1.2, benzotriazole 0.6-0.9, trimeric cyanamide 1-2, 10-15% sodium hydroxide solution 6-8, sodium oleate 0.2-0.3, ammonium persulphate 0.1-0.2, water 17-20, preparation method is: attapulgite, wilkinite are put into calcining furnace, at 670-700 DEG C, calcine 3-4 hour, takes out, puts into 10-15% sodium hydroxide solution and be ground to 20-40 μm of slurry, and adjust slurry pH value to be neutral, spraying dry obtains powder, by water, sodium oleate, urethane acrylate, E-12 epoxy resin, epoxy acrylate, vinylbenzene, dipropylene glycol, TriMethylolPropane(TMP) mixing, be heated to 60-70 DEG C, add peroxidized t-butyl perbenzoate, stirring reaction 20-30 minute, add described powder and other composition again, continue to be warming up to 80-90 DEG C, stirring reaction 50-60 minute, to obtain final product.
2. the preparation method of decoration mortar according to claim 1, is characterized in that comprising the following steps:
(1) by diatomite, sepiolite, ironic hydroxide mixing, 140-180 order particle is ground into;
(2) by calcium chloride, Tai-Ace S 150, sodium sulfate, alum powder, sodium lauryl sulphate, sodium abietate, carboxylic styrene butadiene latex, water mixing, stir and obtain slurry;
(3) by auxiliary agent, flyash, vegetables oil mixing, dispersion grinding 20-30 minute, obtains mixture;
(4) mixing of materials other remaining components and (1) step, (2) step, (3) step obtained is even, and stirring reaction 10-15 minute, to obtain final product.
CN201410420065.1A 2014-08-25 2014-08-25 A kind of decoration mortar and preparation method thereof Expired - Fee Related CN104230227B (en)