CN104210193B - A kind of antifog film - Google Patents
A kind of antifog film Download PDFInfo
- Publication number
- CN104210193B CN104210193B CN201410428239.9A CN201410428239A CN104210193B CN 104210193 B CN104210193 B CN 104210193B CN 201410428239 A CN201410428239 A CN 201410428239A CN 104210193 B CN104210193 B CN 104210193B
- Authority
- CN
- China
- Prior art keywords
- layer
- resistance
- fog
- composite
- photosphere
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of antifog film, relate to packaging material field, including resistance to photosphere, anti-fog layer, sandwich layer and protective layer, described sandwich layer is arranged over anti-fog layer, described resistance to photosphere is the composite of PBT and PC, described anti-fog layer is arranged over resistance to photosphere, described anti-fog layer is the composite of BMA and EA material, it is provided with protective layer below described sandwich layer, described sandwich layer is PA material, described protective layer is HDPE material, there is the preventing atomization performance of excellence, preferably glossiness, there is preferable acid and alkali-resistance simultaneously, anticorrosive, resistance to ag(e)ing, it is suitable for packaging fresh fruit, vegetables etc., it it is nontoxic environment-friendlymembrane membrane.
Description
Technical field
The present invention relates to packaging material field, particularly relate to a kind of food packaging antifog film.
Background technology
Antifog film be a kind of prevent steam film surface formed fogging and affect the merit of transparency
Can property film.Such as bag, glue-free composite membrane etc. remain in that the build-in attribute of BOPP film；
Such as keep the high grade of transparency, there is splendid added property and illustrative, and keep the highest strong
Degree, does not affect transport, stores and use, as public in China Application No. CN 203267424 U
Having opened a kind of antifog film, including pet base material, described pet base material is arranged over anti-fog layer, should
Anti-fog layer is arranged over diaphragm, and adhesive-layer is passed through with release in the lower section of the most described pet base material
Paper is bonding, the antifog film Main Auto vehicle window of this technology, rearview mirror, high-grade hotel glass with
And Domestic glass is first-class, the heat of major part solar energy can be reflected back in hot summer,
Play holding indoor temperature and will not raise too much, reduce room conditioning load, thus reach energy-conservation
Purpose, it addition, the antifog film illustrated its one side be tough and tensile PET base material, one side be viscous
Glue-line, this adhesive-layer has good bonding force, if eyeglass is not with the one side of eyeglass japanning
Carefully being staved, fragment will be glued without falling down, and is so possible to prevent to be scattered
Glass people and other article may be caused damage, but the antifog film of this technology is the most preferably
Glossiness, simultaneously the most not there is preferable acid and alkali-resistance, anticorrosive, resistance to ag(e)ing, be unsuitable for
The food such as packaging fresh water fruits and vegetables.
Summary of the invention
It is an object of the invention to provide a kind of antifog film, upper with solve prior art causes
State multinomial defect.
A kind of antifog film, including resistance to photosphere, anti-fog layer, sandwich layer and protective layer, on described sandwich layer
Side is provided with anti-fog layer, and described anti-fog layer is arranged over resistance to photosphere, is provided with protection below described sandwich layer
Layer, the thickness of described protective layer is 0.8-1 μm.
Preferably, described resistance to photosphere is the composite of PBT and PC, and mass ratio is 1:1.2-1.5.
Preferably, described sandwich layer is PA material, and thickness is 15-20 μm.
Preferably, described anti-fog layer is the composite of BMA and EA material, and mass ratio is 1.3-
1.7:1。
Preferably, described protective layer is HDPE material.
It is an advantage of the current invention that: antifog film has the preventing atomization performance of excellence, preferable gloss
Degree, has preferable acid and alkali-resistance, anticorrosive, resistance to ag(e)ing simultaneously, and resistance to photosphere is PBT and PC
Composite, the composite of PBT and PC has heat-resist, resistance to optical good, tool
Have excellent wear-resisting, chemical resistance, sandwich layer is PA material, and thickness is 15-20 μm,
PA material has preferable tensile property, low cost, and light transmittance is high, tear-proof, resistance to deformation
Modulus is big, and anti-fog layer is the composite of BMA and EA material, BMA and EA material
It is good that composite has anti-fog performance, Heat stability is good, and protective layer is HDPE material, HDPE
Material has the most anti-aging, uvioresistant, meanwhile, also has good chemical stability,
Resistance to height, low temperature, the chemical solution such as acid and alkali resistance, salt, it is suitable for packaging fresh water fruits and vegetables
Deng, it is nontoxic environment-friendlymembrane membrane.
Accompanying drawing explanation
Fig. 1 is the structural representation of a kind of antifog film of the present invention.
Fig. 2 is the side view of a kind of antifog film of the present invention.
Wherein: the resistance to photosphere of 1-, 2-anti-fog layer, 3-sandwich layer, 4-protective layer.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be prone to bright with effect
White understanding, below in conjunction with detailed description of the invention, is expanded on further the present invention.
As depicted in figs. 1 and 2, a kind of antifog film, including resistance to photosphere 1, anti-fog layer 2, sandwich layer 3
With protective layer 4, described sandwich layer 3 is arranged over anti-fog layer 2, and described anti-fog layer 2 is arranged over fast light
Layer 1, is provided with protective layer 4 below described sandwich layer 3, the thickness of described protective layer 4 is 0.8-1 μm,
Antifog film have excellence preventing atomization performance, preferable glossiness, have simultaneously preferable acid and alkali-resistance,
Anticorrosive, resistance to ag(e)ing, resistance to photosphere 1 is the composite of PBT and PC, PBT and PC answers
Condensation material has heat-resist, resistance to optical good, has excellent wear-resisting, chemical resistance,
Sandwich layer 3 is PA material, and thickness is 15-20 μm, and PA material has preferable tensile property, one-tenth
This is low, and light transmittance is high, and tear-proof, resistance to deformation modulus are big, and anti-fog layer 2 is BMA and EA material
Composite, it is good that the composite of BMA and EA material has anti-fog performance, heat endurance
Good, protective layer 4 is HDPE material, and HDPE material has the most anti-aging, uvioresistant,
Meanwhile, also there is good chemical stability, resistance to height, low temperature, the chemistry such as acid and alkali resistance, salt
Solution, is suitable for packaging fresh water fruits and vegetables etc., is nontoxic environment-friendlymembrane membrane.
It should be noted that the composite that described resistance to photosphere 1 is PBT and PC, mass ratio is
The composite of 1:1.2-1.5, PBT and PC has heat-resist, resistance to optical good, has
Excellent is wear-resisting, chemical resistance, and described sandwich layer 3 is PA material, and thickness is 15-20 μm,
PA material has preferable tensile property, low cost, and light transmittance is high, tear-proof, resistance to deformation
Modulus is big.
Additionally, the composite that described anti-fog layer 2 is BMA and EA material, mass ratio is
It is good that the composite of 1.3-1.7:1, BMA and EA material has anti-fog performance, Heat stability is good,
Described protective layer 4 is HDPE material, and HDPE material has the most anti-aging, uvioresistant,
Meanwhile, also there is good chemical stability, resistance to height, low temperature, the chemistry such as acid and alkali resistance, salt
Solution.
Based on above-mentioned, antifog film have excellence preventing atomization performance, preferable glossiness, simultaneously
Having preferable acid and alkali-resistance, anticorrosive, resistance to ag(e)ing, resistance to photosphere 1 is the composite wood of PBT and PC
Material, the composite of PBT and PC has heat-resist, resistance to optical good, has excellent resistance to
Mill, chemical resistance, sandwich layer 3 is PA material, and thickness is 15-20 μm, and PA material has
Preferably tensile property, low cost, light transmittance is high, and tear-proof, resistance to deformation modulus are big, antifog
Layer 2 is the composite of BMA and EA material, and the composite of BMA and EA material has anti-
Mist performance is good, Heat stability is good, and protective layer 4 is HDPE material, and HDPE material has preferably
Anti-aging, uvioresistant, meanwhile, also there is good chemical stability, resistance to height, low temperature,
The chemical solution such as acid and alkali resistance, salt, is suitable for packaging fresh water fruits and vegetables etc., is nontoxic
Environment-friendlymembrane membrane.
As known by the technical knowledge, the present invention can be by other essence without departing from its spirit or necessary special
The embodiment levied realizes.Therefore, embodiment disclosed above, for each side,
All it is merely illustrative, is not only.All within the scope of the present invention or be equal to this
Change in the range of invention is all included in the invention.
Claims (1)
1. an antifog film, including resistance to photosphere, anti-fog layer, sandwich layer and protective layer, its feature
Being, described sandwich layer is arranged over anti-fog layer, and described anti-fog layer is arranged over resistance to photosphere, described
Being provided with protective layer below sandwich layer, the thickness of described protective layer is 0.8-1 μm, and resistance to photosphere is PBT
With the composite of PC, mass ratio is 1:1.2-1.5, and sandwich layer is PA material, and thickness is 15-20
μm, anti-fog layer is the composite of BMA and EA material, and mass ratio is 1.3-1.7:1, protects
Sheath is HDPE material.