CN104152698A - 钒氮合金废料的回收利用方法 - Google Patents

钒氮合金废料的回收利用方法 Download PDF

Info

Publication number
CN104152698A
CN104152698A CN201410381639.9A CN201410381639A CN104152698A CN 104152698 A CN104152698 A CN 104152698A CN 201410381639 A CN201410381639 A CN 201410381639A CN 104152698 A CN104152698 A CN 104152698A
Authority
CN
China
Prior art keywords
vanadium
waste
alloy waste
recycling
recoverying
Prior art date
Application number
CN201410381639.9A
Other languages
English (en)
Inventor
葛广凯
Original Assignee
南通汉瑞实业有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 南通汉瑞实业有限公司 filed Critical 南通汉瑞实业有限公司
Priority to CN201410381639.9A priority Critical patent/CN104152698A/zh
Publication of CN104152698A publication Critical patent/CN104152698A/zh

Abstract

本发明公开了一种那个钒氮合金废料的回收利用方法,包括以下步骤:收集钒氮合金废料后,焙烧3.5~4.5小时;向钒氮合金废料中缓慢加入浓度为2%的硫酸溶液,将钒溶解;取出溶解后的清液,放入药罐中,添加工业氢氧化钠溶液调节PH值至6.2~6.8;然后充氨,加压搅拌10~11小时,得白色沉淀,甩干机过滤得白色粉末,白色粉末与原料偏钒酸铵混合使用;废液循环使用数次,送至燃气炉上方蒸发锅内蒸发,蒸发后的固体废料回收处理;蒸发锅合成尾气回收集中供给燃气炉。本发明能够提高钒氮合金的利用率,经济环保,降低生产成本。

Description

钒氮合金废料的回收利用方法
技术领域
[0001] 本发明属于废料回收技术领域,具体涉及钒氮合金生产过程中的钒氮合金废料的 回收利用方法。
背景技术
[0002] 钒氮合金是一种新型合金添加剂,可以替代钒铁用于微合金化钢的生产,氮钒合 金添加于钢中能提高钢的强度、韧性、延展性及抗热疲劳性等综合机械性能,并使钢具有良 好的可焊性。氮钒合金可用于结构钢,工具钢,管道钢,钢筋及铸铁中。钒氮合金应用于高 强度低合金钢中可同时进行有效的钒、氮微合金化,促进钢中碳、钒、氮化合物的析出,更有 效的发挥沉降强化和细化晶粒作用。
[0003] 钒氮合金是由五氧化二钒、碳粉、活性剂等原材料制成的坯件,在常压、氮气氛保 护下,经1500〜180(TC高温状态下烧结,反应生成钒氮合金,在烧结过程中会有大量废料 产生,其纯度不能满足生产要求,又不能作为废弃物处理,为复合科学发展的要求需要对废 料进行回收利用。
发明内容
[0004] 本发明的目的在于针对现有技术中的不足,提供一种钒氮合金废料的回收利用方 法,操作简单,纯度高。
[0005] 为解决上述技术问题,本发明采用的技术方案为:钒氮合金废料的回收利用方法, 包括以下步骤: (1) 收集钒氮合金废料后,在带有蒸发锅的燃气炉内明火焙烧3. 5〜4. 5小时; (2) 向钒氮合金废料中缓慢加入浓度为2%的硫酸溶液,将钒溶解,钒达到200〜250g/ L后停止加入硫酸溶液; (3) 取出溶解后的清液,放入药罐中,添加工业氢氧化钠溶液调节PH值至6. 2〜6. 8 ; 然后用液氨瓶中的残液氨,缓慢充氨,加压搅拌10〜11小时,得白色沉淀,甩干机过滤得白 色粉末,白色粉末与原料偏钒酸铵混合使用; (4) 废液循环使用数次,送至燃气炉上方蒸发锅内蒸发,蒸发后的固体废料回收处理; (5) 蒸发锅合成尾气回收集中供给燃气炉。
[0006] 进一步的,所述步骤(1)中焙烧温度为800〜1000°C。
[0007] 进一步的,所述步骤(2)中,添加硫酸溶液进行搅拌,每隔5〜7min搅拌一次,直 至溶液终点浓度为220〜250g/L。
[0008] 进一步的,所述步骤(3 )中清液和液氨的体积比为5〜6:1。
[0009] 进一步的,所述步骤(3)中加压搅拌的压力为2〜3公斤。
[0010] 本发明的有益效果: 1、 本发明对钒氮合金进行回收再利用,提高了钒氮合金的利用率,降生产成本; 2、 本发明的工艺过程简单,回收过程绿色环保,不会对环境造成污染,操作简单; 3、本发明回收过程中固废循环套用,经济效益高。
具体实施方式
[0011] 下面结合具体实施例对本发明的技术方案作详细说明。
[0012] 本发明的一种钒氮合金废料的回收利用方法,包括以下步骤: (1) 收集钒氮合金废料后,在带有蒸发锅的燃气炉内明火焙烧3. 5〜4. 5小时; (2) 向钒氮合金废料中缓慢加入浓度为2%的硫酸溶液,将钒溶解,钒液浓度稳定后停 止加入硫酸溶液; (3) 取出溶解后的清液,放入药罐中,添加工业氢氧化钠溶液调节PH值至6. 2〜6. 8 ; 然后用液氨瓶中的残液氨,缓慢充氨,加压搅拌10〜11小时,得白色沉淀,甩干机过滤得白 色粉末,白色粉末与原料偏钒酸铵混合使用; (4) 废液循环使用数次,送至燃气炉上方蒸发锅内蒸发,蒸发后的固体废料回收处理; (5) 蒸发锅合成尾气回收集中供给燃气炉。
[0013] 实施例1 钒氮合金废料的回收利用方法:收集钒氮合金废料,在带有蒸发锅的燃气炉内明火焙 烧4小时;焙烧温度为900°C ;向钒氮合金废料中缓慢加入浓度为2%的硫酸溶液,将钒溶 解,每隔5min搅拌一次,直至溶液终点浓度为220g/L,停止加入硫酸溶液;取出清液,放入 药罐中,添加工业氢氧化钠溶液调节PH值至6. 2 ;然后用液氨瓶中的残液氨,缓慢充氨,清 液和液氨的体积比为5:1,加压搅拌10小时,压力为2公斤,得白色沉淀,甩干机过滤得白色 粉末,白色粉末与原料偏钒酸铵混合使用;废液循环使用数次,送至燃气炉上方蒸发锅内蒸 发,蒸发后的固体废料回收处理;蒸发锅合成尾气回收集中供给燃气炉。
[0014] 实施例2 钒氮合金废料的回收利用方法:收集钒氮合金废料,在带有蒸发锅的燃气炉内明火焙 烧4小时;焙烧温度为1000°C ;向钒氮合金废料中缓慢加入浓度为2%的硫酸溶液,将钒溶 解,每隔7min搅拌一次,直至溶液终点浓度为250g/L,停止加入硫酸溶液;取出清液,放入 药罐中,添加工业氢氧化钠溶液调节PH值至6. 5 ;然后用液氨瓶中的残液氨,缓慢充氨清液 和液氨的体积比为5. 2:1,加压搅拌10. 5小时,压力为2. 2公斤,得白色沉淀,甩干机过滤得 白色粉末,白色粉末与原料偏钒酸铵混合使用;废液循环使用数次,送至燃气炉上方蒸发锅 内蒸发,蒸发后的固体废料回收处理;蒸发锅合成尾气回收集中供给燃气炉。
[0015] 实施例3 钒氮合金废料的回收利用方法:收集钒氮合金废料,在带有蒸发锅的燃气炉内明火焙 烧4小时;焙烧温度为800°C;向钒氮合金废料中缓慢加入浓度为2%的硫酸溶液,将钒溶解, 每隔7min搅拌一次,直至溶液终点浓度为230g/L,停止加入硫酸溶液;取出清液,放入药罐 中,添加工业氢氧化钠溶液调节PH值至6. 8 ;然后用液氨瓶中的残液氨,缓慢充氨,清液和 液氨的体积比为5. 8:1,加压搅拌11小时,压力为2. 8公斤,得白色沉淀,甩干机过滤得白色 粉末,白色粉末与原料偏钒酸铵混合使用;废液循环使用数次,送至燃气炉上方蒸发锅内蒸 发,蒸发后的固体废料回收处理;蒸发锅合成尾气回收集中供给燃气炉。

Claims (5)

1. 钒氮合金废料的回收利用方法,其特征在于:包括以下步骤: (1) 收集钒氮合金废料后,在带有蒸发锅的燃气炉内明火焙烧3. 5〜4. 5小时; (2) 向钒氮合金废料中缓慢加入浓度为2%的硫酸溶液,将钒溶解,钒达到200〜250g/ L后停止加入硫酸溶液; (3) 取出溶解后的清液,放入药罐中,添加工业氢氧化钠溶液调节PH值至6. 2〜6. 8 ; 然后用液氨瓶中的残液氨,缓慢充氨,加压搅拌10〜11小时,得白色沉淀,甩干机过滤得白 色粉末,白色粉末与原料偏钒酸铵混合使用; (4) 废液循环使用数次,送至燃气炉上方蒸发锅内蒸发,蒸发后的固体废料回收处理; (5) 蒸发锅合成尾气回收集中供给燃气炉。
2. 根据权利要求1所述的钒氮合金废料的回收利用方法,其特征在于:所述步骤(1)中 焙烧温度为800〜1000°C。
3. 根据权利要求1所述的钒氮合金废料的回收利用方法,其特征在于:所述步骤(2) 中,添加硫酸溶液进行搅拌,每隔5〜7min搅拌一次,直至溶液终点浓度为220〜250g/L。
4. 根据权利要求1所述的钒氮合金废料的回收利用方法,其特征在于:所述步骤(3) 中清液和液氨的体积比为5〜6:1。
5. 根据权利要求1所述的钒氮合金废料的回收利用方法,其特征在于:所述步骤(3) 中加压搅拌的压力为2〜3公斤。
CN201410381639.9A 2014-08-06 2014-08-06 钒氮合金废料的回收利用方法 CN104152698A (zh)