CN104151784A - 纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料 - Google Patents

纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料 Download PDF

Info

Publication number
CN104151784A
CN104151784A CN201310178109.XA CN201310178109A CN104151784A CN 104151784 A CN104151784 A CN 104151784A CN 201310178109 A CN201310178109 A CN 201310178109A CN 104151784 A CN104151784 A CN 104151784A
Authority
CN
China
Prior art keywords
polybutylene terephthalate
alloy composite
parts
strengthens
carbon nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310178109.XA
Other languages
English (en)
Inventor
沈军明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU SHINE PLASTIC INDUSTRY Co Ltd
Original Assignee
CHANGSHU SHINE PLASTIC INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU SHINE PLASTIC INDUSTRY Co Ltd filed Critical CHANGSHU SHINE PLASTIC INDUSTRY Co Ltd
Priority to CN201310178109.XA priority Critical patent/CN104151784A/zh
Publication of CN104151784A publication Critical patent/CN104151784A/zh
Pending legal-status Critical Current

Abstract

一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：聚对苯二甲酸丁二醇酯43.2～48.5份；增韧剂9.4～16.3份；烯烃树脂6.1～12.6份；相容剂4.3~7.4份；抗氧剂0.4~0.9份；纤维粉9.3~14.2份；碳纤维7.5~15.7份；炭黑0.7~1.3份。经测试具有如下性能指标：拉伸强度155～175MPa，弯曲强度216～235MPa,缺口冲击强度65～78j/m；由于碳纤维含量低，因而具有经济上的廉价性。

Description

纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料。
背景技术
聚对苯二甲酸丁二醇酯（PBT）是一种热塑性塑料，广泛用做民用或工业用材料，具有耐热性、耐候性、耐药性、光泽好的特点。纳米碳纤维具有高模量，高强度，广泛用于高强、耐热的航天航空等部件。中国专利公开号CN102311616A公开了一种碳纤维增强的聚酯材料，其中使用较多的碳纤维，导致材料成本高昂，难以被普通民用行业所采用，并且由于该材料在阻燃方面比较欠缺，从而在一定程度上限制了其应用范围的扩展，因此有必要加以合理改进。
发明内容
本发明的任务在于提供一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，该材料具有低的碳纤维添加量，高强度，并且阻燃效果好的特点。
本发明的任务是这样来完成的，一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其是由以下重量份数的原料组成：
在本发明的一个实施例中，所述的聚对苯二甲酸丁二醇酯为熔点在230℃的聚对苯二甲酸丁二醇酯。
在本发明的另一个实施例中，所述的增韧剂为氢化的苯乙烯-丁二烯-苯乙烯共聚物。
在本发明的又一个实施例中，所述的烯烃树脂为熔点在150℃的共聚聚丙烯树脂。
在本发明的再一个实施例中，所述的相容剂为马来酸酐接枝的聚丙烯树脂。
在本发明的还有一个实施例中，所述的抗氧剂为2,5-二特丁基对苯二酚。
在本发明的更而一个实施例中，所述的纤维粉为磨碎的玻璃纤维粉，长度为120～150微米。
在本发明的进而一个实施例中，所述的碳纤维为纳米碳纤维，长度为50～120微米。
在本发明的又更而一个实施例中，所述的炭黑为槽法生产的炭黑。
本发明提供的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料经测试具有如下性能指标：拉伸强度155～175MPa，弯曲强度216～235MPa,缺口冲击强度65～78j/m；由于碳纤维含量低，因而具有经济上的廉价性。
具体实施方式
实施例1：
实施例2：
实施例3：
实施例4：
由上述实施例1至4得到的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料经测试具有如下技术效果：
测试项目 实施例1 实施例2 实施例3 实施例4
拉伸强度MPa 156 162 168 175
弯曲强度MPa 216 223 229 234
缺口冲击强度j/m 65.6 69.4 73.5 77.8

Claims (9)

1.一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于其是由以下重量份数的原料组成：
                  聚对苯二甲酸丁二醇酯         43.2～48.5份；
             增韧剂                   9.4～16.3份；
           烯烃树脂                   6.1～12.6份；
           相容剂                     4.3~7.4份；
           抗氧剂                     0.4~0.9份；
           纤维粉                     9.3~14.2份；
          碳纤维                      7.5~15.7份；
            炭黑                      0.7~1.3份。
2.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的聚对苯二甲酸丁二醇酯为熔点在230℃的聚对苯二甲酸丁二醇酯。
3.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的增韧剂为氢化的苯乙烯-丁二烯-苯乙烯共聚物。
4.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的烯烃树脂为熔点在150℃的共聚聚丙烯树脂。
5.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的相容剂为马来酸酐接枝的聚丙烯树脂。
6.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的抗氧剂为2,5-二特丁基对苯二酚。
7.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的纤维粉为磨碎的玻璃纤维粉，长度为120～150微米。
8.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的碳纤维为纳米碳纤维，长度为50～120微米。
9.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的炭黑为槽法生产的炭黑。
CN201310178109.XA 2013-05-14 2013-05-14 纳米碳纤维增强的聚对苯二甲酸丁二醇酯合金复合材料 Pending CN104151784A (zh)