CN104131291B - 一种复合金属抛光液及其制备方法 - Google Patents

一种复合金属抛光液及其制备方法 Download PDF

Info

Publication number
CN104131291B
CN104131291B CN201410308864.XA CN201410308864A CN104131291B CN 104131291 B CN104131291 B CN 104131291B CN 201410308864 A CN201410308864 A CN 201410308864A CN 104131291 B CN104131291 B CN 104131291B
Authority
CN
China
Prior art keywords
auxiliary agent
polishing fluid
mixing
polishing
slowly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410308864.XA
Other languages
English (en)
Other versions
CN104131291A (zh
Inventor
肖宪书
文庆华
张俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Original Assignee
BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU CITY GAOHUA ELECTRONIC Co Ltd filed Critical BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Priority to CN201410308864.XA priority Critical patent/CN104131291B/zh
Publication of CN104131291A publication Critical patent/CN104131291A/zh
Application granted granted Critical
Publication of CN104131291B publication Critical patent/CN104131291B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种复合金属抛光液,其特征在于,由下列重量份的原料制成:氧化铈11-13、氧化石墨烯2-4、菜籽油7-9、辛酸亚锡1-2、聚氧乙烯失水山梨醇脂肪酸酯4-6、聚氧乙烯蓖麻油3-5、尿素4-6、柠檬酸2-4、乳化硅油4-6、助剂5-7、去离子水300;本发明制取的混合抛光液,安全无毒,配方合理,通过添加表面活性剂与磨料相配合,不仅可以提高抛光效果,而且可以优先吸附,形成长期易清洗的物理吸附表面,添加助剂,具有良好的分散、润滑、成膜性,在工件表面就形成一个阻隔空气层,防止空气对金属表面的腐蚀;本发明抛光液能满足各产品、零部件的抛光处理要求,提高了抛光效率高、清洗效果、表面精度等。

Description

一种复合金属抛光液及其制备方法
技术领域
[0001] 本发明涉及表面处理技术领域,特别是一种复合金属抛光液及其制备方法。
背景技术
[0002] 金属表面的处理有许多种方法和手段,如电镀、电泳、化学处理、表面抛光等。化学抛光是一种特殊条件下的化学腐蚀,它是通过控制金属选择性的溶解而使金属表面达到整平和光亮的金属加工过程,一直受到人们的重视,但是,要想钢铁基体达到全面的光亮效果及保持清晰的文字和图案,这给化学抛光工艺提出了更高要求,其中就包括化学抛光液。金属器具加工成形后表面通常会附着一层油污或其它化学制剂,器具使用一段时间后由使用环境的腐蚀,在表面会产生锈迹,为了美观和延长使用寿命,常用专用的金属清洗剂或抛光剂来清理表面的污物,但现有抛光剂产品存在返锈快、可适用金属种类窄、清洗不彻底、抛光性能较弱,容易产生气味、抛光后表面挂灰、抛光后容易生锈,抛光液容易腐败等问题,本发明即对该混合抛光液的技术改进。
发明内容
[0003] 本发明的目的是提供一种复合金属抛光液及其制备方法。
[0004] 为了实现本发明的目的,本发明通过以下方案实施:
[0005] —种复合金属抛光液,由下列重量份的原料制成:氧化铈11-13、氧化石墨烯2-4、菜籽油7-9、辛酸亚锡1-2、聚氧乙烯失水山梨醇脂肪酸酯4-6、聚氧乙烯蓖麻油3-5、尿素4-6、梓檬酸2-4、乳化娃油4-6、助剂5-7、去离子水300 ;
[0006] 所述助剂由以下重量份的原料制成:三氧化二铝4-6、纳米二氧化钛5-7、硅酸钠1-2、丙二醇甲醚醋酸酯3-4、十二碳醇酯2-3、丙烯酸甲酯2-4、交联羧甲基纤维素钠2_3、乳化剂BP4-5、水50-54 ;制备方法是首先将三氧化二铝、纳米二氧化钛、交联羧甲基纤维素钠、乳化剂BP加入一半量的水中,研磨1-2小时,然后缓慢加入其余剩余成分,缓慢加热至70°C -80°C,在300-500转/分条件下搅拌反应30-50分钟,冷却至室温即得。
[0007] 本发明所述一种复合金属抛光液,由以下具体步骤制成:
[0008] (1)将氧化铈、氧化石墨烯、聚氧乙烯失水山梨醇脂肪酸酯混合均匀,加入适量的去离子水,加热至30°C -35°C,研磨25-35分钟,得到混合A料;
[0009] (2)将除助剂之外的其余剩余成分加入到反应釜中,搅拌混合均匀,缓慢加热至35。。-45。。,保温1-1.5小时,得到混合B料;
[0010] (3)将保温的混合B料边搅拌边缓慢加入到混合A料中,充分搅拌后加入助剂,继续搅拌20-30分钟,冷却至室温即得。
[0011] 本发明的优异效果是:本发明制取的混合抛光液,安全无毒,配方合理,通过添加表面活性剂与磨料相配合,不仅可以提高抛光效果,而且可以优先吸附,形成长期易清洗的物理吸附表面,添加助剂,具有良好的分散、润滑、成膜性,在工件表面就形成一个阻隔空气层,防止空气对金属表面的腐蚀;本发明抛光液能满足各产品、零部件的抛光处理要求,提高了抛光效率高、清洗效果、表面精度等。
具体实施方式
[0012] 下面通过具体实例对本发明进行详细说明。
[0013] —种复合金属抛光液,由下列重量份(公斤)的原料制成:氧化铈11、氧化石墨烯2、菜籽油7、辛酸亚锡1、聚氧乙烯失水山梨醇脂肪酸酯4、聚氧乙烯蓖麻油3、尿素4、柠檬酸2、乳化硅油4、助剂5、去离子水300 ;
[0014] 所述助剂由以下重量份(公斤)的原料制成:三氧化二铝4、纳米二氧化钛5、硅酸钠1、丙二醇甲醚醋酸酯3、十二碳醇酯2、丙烯酸甲酯2、交联羧甲基纤维素钠2、乳化剂BP4、水50 ;制备方法是首先将三氧化二铝、纳米二氧化钛、交联羧甲基纤维素钠、乳化剂BP加入一半量的水中,研磨1-2小时,然后缓慢加入其余剩余成分,缓慢加热至70°C -80°C,在300-500转/分条件下搅拌反应30-50分钟,冷却至室温即得。
[0015] 本发明所述一种复合金属抛光液,由以下具体步骤制成:
[0016] (1)将氧化铈、氧化石墨烯、聚氧乙烯失水山梨醇脂肪酸酯混合均匀,加入适量的去离子水,加热至30°C -35°C,研磨25-35分钟,得到混合A料;
[0017] (2)将除助剂之外的其余剩余成分加入到反应釜中,搅拌混合均匀,缓慢加热至35。。-45。。,保温1-1.5小时,得到混合B料;
[0018] (3)将保温的混合B料边搅拌边缓慢加入到混合A料中,充分搅拌后加入助剂,继续搅拌20-30分钟,冷却至室温即得。
[0019] 实验检测结果:肉眼观察各工件的表面,工件表面外观均匀、无异色或有轻微色差、且无雪花;采用微型光泽仪A-4430(德国BYK公司)测试各抛光工件表面的光泽度,光泽度为47Gu。

Claims (2)

1.一种复合金属抛光液,其特征在于,由下列重量份的原料制成:氧化铈11-13、氧化石墨烯2-4、菜籽油7-9、辛酸亚锡1-2、聚氧乙烯失水山梨醇脂肪酸酯4-6、聚氧乙烯蓖麻油3_5、尿素4-6、梓檬酸2-4、乳化娃油4-6、助剂5_7、去离子水300 ;所述助剂由以下重量份的原料制成:三氧化二铝4-6、纳米二氧化钛5-7、硅酸钠1-2、丙二醇甲醚醋酸酯3-4、十二碳醇酯2-3、丙烯酸甲酯2-4、交联羧甲基纤维素钠2-3、乳化剂BP4-5、水50-54 ;制备方法是首先将三氧化二铝、纳米二氧化钛、交联羧甲基纤维素钠、乳化剂BP加入一半量的水中,研磨1-2小时,然后缓慢加入其余剩余成分,缓慢加热至70°C -80°C,在300-500转/分条件下搅拌反应30-50分钟,冷却至室温即得。
2.根据权利要求1所述一种复合金属抛光液,其特征在于,由以下具体步骤制成: (1)将氧化铈、氧化石墨烯、聚氧乙烯失水山梨醇脂肪酸酯混合均匀,加入适量的去离子水,加热至30°C -35°C,研磨25-35分钟,得到混合A料; (2)将除助剂之外的其余剩余成分加入到反应釜中,搅拌混合均匀,缓慢加热至35。。-45。。,保温1-1.5小时,得到混合B料; (3)将保温的混合B料边搅拌边缓慢加入到混合A料中,充分搅拌后加入助剂,继续搅拌20-30分钟,冷却至室温即得。
CN201410308864.XA 2014-07-01 2014-07-01 一种复合金属抛光液及其制备方法 Expired - Fee Related CN104131291B (zh)