CN104074330A - Undertread formed by compounding mortar cloth with anti-crack fiber nets - Google Patents

Undertread formed by compounding mortar cloth with anti-crack fiber nets Download PDF

Info

Publication number
CN104074330A
CN104074330A CN201410296066.XA CN201410296066A CN104074330A CN 104074330 A CN104074330 A CN 104074330A CN 201410296066 A CN201410296066 A CN 201410296066A CN 104074330 A CN104074330 A CN 104074330A
Authority
CN
China
Prior art keywords
cloth
mortar
fiber
crack fiber
crack
Prior art date
Application number
CN201410296066.XA
Other languages
Chinese (zh)
Other versions
CN104074330B (en
Inventor
王新
巢启
钟勤
Original Assignee
广西启利新材料科技股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 广西启利新材料科技股份有限公司 filed Critical 广西启利新材料科技股份有限公司
Priority to CN201410296066.XA priority Critical patent/CN104074330B/en
Publication of CN104074330A publication Critical patent/CN104074330A/en
Application granted granted Critical
Publication of CN104074330B publication Critical patent/CN104074330B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses an undertread formed by compounding mortar cloth with anti-crack fiber nets. A preparing method comprises the following steps that: (1) raw materials for forming composite slurry are mixed according to a proportion, and the mixture is uniformly stirred to obtain the composite slurry for standby; and (2) a layer of composite slurry is smeared on a layer of mortar cloth; a layer of anti-crack fiber net cloth in the same size is paved; press smearing or press rolling is carried out until the anti-crack fiber net cloth is recessed into the composite slurry; then, a layer of composite slurry is smeared, and the press smearing or the press rolling is carried out until the anti-crack fiber net cloth is soaked and coated by the composite slurry; or the steps are repeated on the basis, 1-2 pieces of anti-crack fiber net cloth are added again, and natural curing is carried out for 3 to 7 days to obtain the undertread formed by compounding the mortar cloth with the anti-crack fiber nets. In the step (2), 0.5 to 1.5kg/m<2> of composite slurry is used for carrying out pasting cladding with the mortar cloth when each layer of anti-crack fiber net is paved. The undertread has the advantages of softness, light weight, thin appearance, crack resistance, folding resistance, aging resistance, environment protection, durability and the like; the undertread is soft but rigid; the manufacturing procedure is simplified; the manufacturing cost is reduced; and the construction is simple.

Description

The end tire that a kind of mortar cloth and anti-crack fiber net are compound
Technical field
The present invention relates to the compound end tire of a kind of mortar cloth and anti-crack fiber net, belong to architectural decoration field of new.
Background technology
Along with country puts more effort to the pressure of building energy conservation, and to more than 20 layers highrise building, or 60 meters of above raisings of assembling larger communal facility safety requirements intensity near visitors flowrate such as street, road, school, hospital, large-scale retail shop, style venues of height, traditional facing tile no longer generally uses.Along with socioeconomic development, the rising of price, constantly riseing of building operations cost, it is lower that each technician of building trade researchs and produces cost one after another, and construction cost is lower, performance is higher, safer building and ornament materials, therefore, outer wall decoration board arises at the historic moment, and the height accreditation that is subject to building industry, use amount is constantly expanding.
Cement mortar cloth, because its materials are thinner, can save space, and long service life, cold-resistant heat, anti-dry wet, anti-aging, ultraviolet ray and ozone are also had to certain opposing simultaneously, indeformable, durable in use, quality is softer, can be well install at curved surface, therefore it is the splendid selection of making tire at the bottom of outer wall decoration board.But, because its rigidity is bad, easily fold, cracking etc., this is to utilize it to make the large fatal shortcoming of dalle one.What the present invention studied is to utilize cement mortar cloth to make both soft, light books, cracking resistance again, tire at the bottom of the external wall of building dalle of anti-folding.
Summary of the invention
The object of this invention is to provide the compound end tire of a kind of mortar cloth and anti-crack fiber net, there is softness, light book, cracking resistance, anti-folding, anti-aging, environmental protection, the advantage such as durable in use, solve tire rigidity of the existing end bad, easily fold, the problem of cracking.
Foregoing invention object is achieved through the following technical solutions: the end tire that a kind of mortar cloth and anti-crack fiber net are compound, mainly prepare by following method:
(1) raw material of composition composite mortar is proportionally mixed, stir, obtain composite mortar for subsequent use;
(2) on one deck mortar cloth, smear one deck composite mortar, the onesize anti-crack fiber screen cloth of paving one deck, pressure is smeared or nip drum to anti-crack fiber screen cloth is absorbed in composite mortar, smearing one deck composite mortar presses and smears or nip drum to anti-crack fiber screen cloth is infiltrated coated by composite mortar again, or repeat on this basis above-mentioned steps, add again 1-2 and open anti-crack fiber screen cloth, within natural curing 3-7 days, obtain the compound end tire of mortar cloth and anti-crack fiber net;
In (2) described step, every paving one deck anti-crack fiber net carries out bonding coated with 0.5-1.5kg/ ㎡ composite mortar and mortar cloth;
Described mortar cloth is commercially available cement mortar cloth;
Described anti-crack fiber screen cloth refers to glass fiber reticular cloth or non-woven fabrics of synthetic fiber, and glass fiber reticular cloth refers to mainly weave with middle alkali or alkali-free glass fibre yarn, the glass fiber reticular cloth product applying through alkaline-resisting macromolecule emulsion; Non-woven fabrics of synthetic fiber refer to polyester fiber non-woven fabric or non-woven fabrics of synthetic fiber, geotextiles, long filament geotextiles wherein any one;
Described composite mortar is mainly made up of following weight parts raw material: cement 20-40 part, quartz sand 50-70 part, low temperature elasticity VAE emulsion or alkaline-resisting acrylic emulsion 5-20 part, cellulose ether 0.1-0.5 part, early strength admixture 0.05-0.2 part, PP fiber 0.1-0.5 part, wood fibre 0.1-0.3 part, water 18-40 part;
Described cement is the commercially available portland cement of No. 325, label or No. 425;
Described quartz sand is the clean quartz sands of 40 orders;
Described low temperature elasticity VAE emulsion, is the copolymer of ethylene/vinyl acetate, vinyl acetate/versatic acid ethylene copolymer, and acrylic acid copolymer etc., all using polyvinyl alcohol as protecting colloid, solid content is greater than 50%;
Described alkaline-resisting acrylic emulsion is commercially available alkaline-resisting acrylic emulsion;
Described cellulose ether is hydroxypropyl methylcellulose, methoxyl content 19.0-30.0%, hydroxypropyl content 4.0-12.0%, viscosity (22 DEG C, 2%) 4000~200000mPa.s;
Described early strength admixture is for the rapid solidification of cement, lubricated, early strong calcium formate;
Described PP fiber is the polypropylene bundle fiber of 0.1-2.0cm length;
Described wood fibre is the fibrous additive of natural fiber of having drawn from.
Take the present invention of above-mentioned measure, taking cement mortar cloth as base plate, strengthen screen cloth using glass fiber reticular cloth or non-woven fabrics of synthetic fiber as cracking resistance, the composite mortar of making taking cement mortar, emulsion, PP fiber, cellulose ether, wood fibre, early strength admixture etc. is as cementing agent, without mould directly on mortar cloth moulding obtain mortar cloth and the compound end tire of anti-crack fiber net, not only there is softness, light book, cracking resistance, anti-folding, anti-aging, environmental protection, the advantage such as durable in use, and soft and do not lack rigidity.In this end tire manufacturing process, without mould, simplify production process, reduced cost of manufacture.
Detailed description of the invention
embodiment 1
(1), by 20 parts of No. 425 cement, 58.8 parts of 40 order quartz sands, 20 parts of low temperature elasticity VAE emulsions, 0.5 part of hydroxypropyl methylcellulose, 0.2 part of early strength admixture, 0.5 part of mixing and stirring of 1mm polypropylene bundle fiber, the 24 parts of mediations that add water are stand-by to being suitable for batch slurry of scraping.
(2) paving one deck mortar cloth, at the onesize glass fiber reticular cloth of mortar reverse of the cloth paving one deck, smear the composite mortar of 0.6kg/ ㎡, by glass fiber reticular cloth press smear or nip drum to being absorbed in composite mortar,, within natural curing 3-7 days, obtain the compound end tire of mortar cloth and glass fiber net.
embodiment 2
(1), by 25 parts of No. 325 cement, 70 parts of 40 order quartz sands, 5 parts of alkaline-resisting acrylic emulsions, 0.1 part of hydroxypropyl methylcellulose, 0.05 part of early strength admixture, 0.3 part of mixing and stirring of wood fibre, the 40 parts of mediations that add water are stand-by to being suitable for batch slurry of scraping.
(2) paving one deck mortar cloth, at the onesize non-woven fabrics of synthetic fiber of mortar reverse of the cloth paving one deck, smear the composite mortar of 0.6kg/ ㎡, by non-woven fabrics of synthetic fiber press smear or nip drum to being absorbed in composite mortar, smear again one deck composite mortar, consumption is 1.0kg/ ㎡, and pressure is smeared or nip drum to non-woven fabrics of synthetic fiber is infiltrated and is coated by composite mortar, within natural curing 3-7 days, obtains the compound end tire of mortar cloth and non-woven fabrics of synthetic fiber.
embodiment 3
(1), by 30 parts of No. 425 cement, 60 parts of 40 order quartz sands, 9 parts of alkaline-resisting acrylic emulsions, 0.4 part of hydroxypropyl methylcellulose, 0.1 part of early strength admixture, 0.2 part of 10mm polypropylene bundle fiber, 0.3 part of mixing and stirring of wood fibre, the 18 parts of mediations that add water are stand-by to being suitable for batch slurry of scraping.
(2) paving one deck mortar cloth, at the onesize glass fiber reticular cloth of mortar reverse of the cloth paving one deck, smear the composite mortar of 0.6kg/ ㎡, by glass fiber reticular cloth press smear or nip drum to being absorbed in composite mortar, repeat on this basis this step, add 1-2 again and open glass fiber reticular cloth, the consumption of a glass fiber reticular cloth composite mortar of every paving is 1.2kg/ ㎡, within natural curing 3-7 days, obtains the compound end tire of mortar cloth and glass fiber net.
embodiment 4
(1), by 40 parts of No. 325 cement, 50 parts of 40 order quartz sands, 9.35 parts of VAE emulsions, 0.3 part of hydroxypropyl methylcellulose, 0.15 part of early strength admixture, 0.1 part of 20mm polypropylene bundle fiber, 0.1 part of mixing and stirring of wood fibre, the 27 parts of mediations that add water are stand-by to being suitable for batch slurry of scraping.
(2) paving one deck mortar cloth, at the onesize glass fiber reticular cloth of mortar reverse of the cloth paving one deck, smear the composite mortar of 0.6kg/ ㎡, by glass fiber reticular cloth press smear or nip drum to be absorbed in composite mortar and slurry by floating, smearing one deck composite mortar presses and smears or nip drum to non-woven fabrics of synthetic fiber is infiltrated coated by composite mortar again, repeat on this basis this step, add again 1-2 and open non-woven fabrics of synthetic fiber, the consumption of a glass fiber reticular cloth composite mortar of every paving is 1.5kg/ ㎡, within natural curing 3-7 days, obtains the compound end tire of mortar cloth and anti-crack fiber net.

Claims (1)

1. the compound end tire of mortar cloth and anti-crack fiber net, is characterized in that tire of the described end mainly prepared by following method:
(1) raw material of composition composite mortar is proportionally mixed, stir, obtain composite mortar for subsequent use;
(2) on one deck mortar cloth, smear one deck composite mortar, the onesize anti-crack fiber screen cloth of paving one deck, pressure is smeared or nip drum to anti-crack fiber screen cloth is absorbed in composite mortar, smearing one deck composite mortar presses and smears or nip drum to anti-crack fiber screen cloth is infiltrated coated by composite mortar again, or repeat on this basis above-mentioned steps, add again 1-2 and open anti-crack fiber screen cloth, within natural curing 3-7 days, obtain the compound end tire of mortar cloth and anti-crack fiber net;
In (2) described step, every paving one deck anti-crack fiber net carries out bonding coated with 0.5-1.5kg/ ㎡ composite mortar and mortar cloth;
Described mortar cloth is commercially available cement mortar cloth;
Described anti-crack fiber screen cloth refers to glass fiber reticular cloth or non-woven fabrics of synthetic fiber, and glass fiber reticular cloth refers to mainly weave with middle alkali or alkali-free glass fibre yarn, the glass fiber reticular cloth product applying through alkaline-resisting macromolecule emulsion; Non-woven fabrics of synthetic fiber refer to polyester fiber non-woven fabric or non-woven fabrics of synthetic fiber, geotextiles, long filament geotextiles wherein any one;
Described composite mortar is mainly made up of following weight parts raw material: cement 20-40 part, quartz sand 50-70 part, low temperature elasticity VAE emulsion or alkaline-resisting acrylic emulsion 5-20 part, cellulose ether 0.1-0.5 part, early strength admixture 0.05-0.2 part, PP fiber 0.1-0.5 part, wood fibre 0.1-0.3 part, water 18-40 part;
Described cement is the commercially available portland cement of No. 325, label or No. 425;
Described quartz sand is the clean quartz sands of 40 orders;
Described low temperature elasticity VAE emulsion, is the copolymer of ethylene/vinyl acetate, vinyl acetate/versatic acid ethylene copolymer, and acrylic acid copolymer etc., all using polyvinyl alcohol as protecting colloid, solid content is greater than 50%;
Described alkaline-resisting acrylic emulsion is commercially available alkaline-resisting acrylic emulsion;
Described cellulose ether is hydroxypropyl methylcellulose, methoxyl content 19.0-30.0%, hydroxypropyl content 4.0-12.0%, viscosity (22 DEG C, 2%) 4000~200000mPa.s;
Described early strength admixture is for the rapid solidification of cement, lubricated, early strong calcium formate;
Described PP fiber is the polypropylene bundle fiber of 0.1-2.0cm length;
Described wood fibre is the fibrous additive of natural fiber of having drawn from.
CN201410296066.XA 2014-06-27 2014-06-27 The end tire of a kind of mortar cloth and anti-crack fiber net compound Active CN104074330B (en)