CN104072194B - 保温层粉刷石膏 - Google Patents

保温层粉刷石膏 Download PDF

Info

Publication number
CN104072194B
CN104072194B CN201410303561.9A CN201410303561A CN104072194B CN 104072194 B CN104072194 B CN 104072194B CN 201410303561 A CN201410303561 A CN 201410303561A CN 104072194 B CN104072194 B CN 104072194B
Authority
CN
China
Prior art keywords
insulation layer
thermal insulation
gypsum
flyash
layer brushing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410303561.9A
Other languages
English (en)
Other versions
CN104072194A (zh
Inventor
孙红芳
杨庆兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHONGKUANG LUCHENG GYPSUM EX BASE
Original Assignee
孙红芳
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 孙红芳 filed Critical 孙红芳
Priority to CN201410303561.9A priority Critical patent/CN104072194B/zh
Publication of CN104072194A publication Critical patent/CN104072194A/zh
Application granted granted Critical
Publication of CN104072194B publication Critical patent/CN104072194B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种保温层粉刷石膏,属于建筑材料,解决水泥生产能耗高,用作建筑施工材料时,使用量大,会减少使用面积的问题。保温层粉刷石膏,原料包括下列重量份的各组分:半水石膏粉30-70、无水石膏粉10-30、粉煤灰1-20、石英砂1-10、珍珠岩1-5、聚乙烯醇PVA0.1-3、羧甲基纤维素CMC0.1-3、甲基纤维素MC0.1-0.5、柠檬酸0.1-2、K12发泡剂0.1-3,制作时,将上述各组分粉碎研磨后混合搅拌10-60分钟或者进行二次搅拌即得。本发明能耗低,制备方法简单,产品安全无害,应用范围广。

Description

保温层粉刷石膏
技术领域
[0001] 本发明属于建筑材料,具体涉及一种适用建筑主体完工后内外墙体保温墙材,具体涉及一种保温层粉刷石膏。
背景技术
[0002]目前,在建筑行业一般都用水泥砂浆做墙体材料,施工时,在砖墙上抹上一层厚厚水泥砂浆,来保证墙面的平整。据统计,2013年我国水泥产量24.2亿吨/年,相当于其它国家的总和还多,在取缔了实心粘土砖后,水泥从2003年至2013年十年期间增长
[0003] 了 17亿吨。但是,水泥是高温煅烧材料,需要在温度为1400多度时煅烧而成,所以生产水泥的能耗很大。
[0004] 石膏的煅烧温度为200度左右,相比水泥的1400多度的生产温度,生产成本和能耗更低;而且水泥在用作建筑施工材料时,需要在墙体上抹上厚厚的一层,会在一定程度上缩小建筑的使用面积;此外,石膏本身就是一种很好的胶凝材料,具有保温,隔热,环保,会呼吸等功能,而水泥质感厚重,会给人压抑的感觉。
[0005]因此,为了降低水泥在建筑施工材料中的使用量,同时实现降低能耗的目的,本发明提供了一种石膏保温材料。
发明内容
[0006] 本发明是为了解决水泥生产能耗高,用作建筑施工材料时,使用量大,会减少使用面积的问题,而提供了保温层粉刷石膏。
[0007] 本发明是通过以下技术方案实现的:
[0008] 保温层粉刷石膏,原料包括下列重量份的各组分:
[0009] 半水石膏粉30-70 无水石膏粉10-30
[0010] 粉煤灰1-20 石英砂1-10
[0011] 珍珠岩1-5 聚乙烯醇PVA0.1-3
[0012] 羧甲基纤维素CMC0.1-3 甲基纤维素MC0.1-0.5
[0013]柠檬酸 0.1-2 K12 发泡剂 0.1-3,
[0014] 制作时,将上述各组分粉碎研磨后混合搅拌10-60分钟或者进行二次搅拌即得。
[0015] 进一步地,上述保温层粉刷石膏,原料包括下列重量份的各组分:
[0016] 半水石膏粉40 无水石膏粉20
[0017] 粉煤灰15 石英砂5
[0018] 珍珠岩3 聚乙烯醇PVA0.5
[0019] 羧甲基纤维素CMC2 甲基纤维素MC 0.5
[0020] 柠檬酸1 K12发泡剂0.8。
[0021] 所述的粉煤灰为低品位粉煤灰,研磨至粒度为0.3-3mm,比表面积为350_500m2/Kg,其中3丨02的质量百分比为38-45%,CaO的质量百分比为48_50%。
[0022] 在本发明原料中,半水石膏粉和无水石膏粉属于不燃材料,半水石膏粉2小时抗折强度是5.0-6.0 MPa, 2小时抗压强度是15-18 MPa,凝结膨胀率< 2%,吸水率为30%,石膏本身具有保温、防火、质轻、绝缘、易加工、呼吸功能、装饰性好的特点;无水石膏粉是立式窑炉中经过高温煅烧制得的一种动物食用添加剂,对人体身体百利而无一害,在添加上述重量份的情况下,不仅可以起到缓凝时间,同时还可以起到对人身体健康的作用;再加入石英砂,粉煤灰作填充及保水剂,另外增加了发泡剂及珍珠岩轻质材料,使保温层粉刷石膏粉质量轻,保温效果显著,石英砂其主要矿物成分是Si02占99% 2,密度为2.65,熔点1750°C,相对比重为2.21,莫氏硬度为7.0,容重1.75/m3,具有的耐高温、热膨胀系数小、高度绝缘、耐腐蚀的优点;K12发泡剂,其中主要成分是十二烷基硫酸钠,产品为白色或淡黄色粉状,溶于水,对碱水和硬水不敏感,具有优异的发泡力,并且成本低,毒害小,其生物降解度> 92%。
[0023] 为了验证本发明产品的性能,分别测定了产品的抗折强度、抗压强度、拉伸粘结强度和保水率,其中抗折强度是1.5-2.5 MPa,2小时抗压强度是2.5-3.5 MPa,拉伸粘结强度^ 0.3KN/m,保水率多60%,凝结时间在初凝在1小时,终凝时间低于8小时。
[0024] 与现有技术相比,本发明具有以下优点:
[0025] (1)石膏的生产温度低,可极大的降低能耗,保护环境;
[0026] (2)制备方法简单,易于操作推广;
[0027] (3)产品的应用范围广,使用时只要加水搅拌即可施工,不需要添加任何添加剂,施工简单;
[0028] (4)产品本身不含有不利于人体的成分,安全无害。
具体实施方式
[0029] 实施例1
[0030] 保温层粉刷石膏,包括半水石膏粉30Kg、无水石膏粉10 Kg、粉煤灰20Kg、石英砂8 Kg、珍珠岩2Kg、聚乙烯醇PVA3 Kg、羧甲基纤维素CMC3 Kg、甲基纤维素MC0.1 Kg、柠檬酸1.3Kg、K12发泡剂2 Kg,搅拌均匀即可。
[0031] 实施例2
[0032] 保温层粉刷石膏,包括半水石膏粉50Kg、无水石膏粉15 Kg、粉煤灰lKg、石英砂lKg、珍珠岩5Kg、聚乙烯醇PVA0.1 Kg、羧甲基纤维素CMC0.1 Kg、甲基纤维素MC0.3 Kg、柠檬酸2Kg、K12发泡剂0.1 Kg,搅拌均匀即可。
[0033] 实施例3
[0034] 保温层粉刷石膏,包括半水石膏粉70Kg、无水石膏粉30 Kg、粉煤灰10Kg、石英砂10Kg、珍珠岩lKg、聚乙烯醇PVA1 Kg、羧甲基纤维素CMC1 Kg、甲基纤维素MC0.4 Kg、柠檬酸
0.lKg、K12发泡剂3 Kg,搅拌均匀即可。
[0035] 实施例4
[0036] 保温层粉刷石膏,包括半水石膏粉40Kg、无水石膏粉20 Kg、粉煤灰15Kg、石英砂5Kg、珍珠岩3Kg、聚乙烯醇PVA0.5Kg、羧甲基纤维素CMC2 Kg、甲基纤维素MC0.5 Kg、柠檬酸lKg、K12发泡剂0.8 Kg,搅拌均匀即可。

Claims (1)

1.一种保温层粉刷石膏,其特征在于,原料包括下列重量份的各组分: 半水石膏粉40 无水石膏粉20 粉煤灰15 石英砂5 珍珠岩3 聚乙烯醇PVA0.5 羧甲基纤维素CMC2 甲基纤维素MC 0.5 柠檬酸1 K12发泡剂0.8 ; 其中所述的粉煤灰为低品位粉煤灰,研磨至粒度为0.3-3mm,比表面积为350_500m2/Kg,其中3丨02的质量百分比为38-45%,CaO的质量百分比为48-50% ; 制作时,将上述各组分粉碎研磨后混合搅拌10-60分钟即得。
CN201410303561.9A 2014-06-30 2014-06-30 保温层粉刷石膏 Active CN104072194B (zh)