CN104058642B - 一种防冻加气砖 - Google Patents

一种防冻加气砖 Download PDF

Info

Publication number
CN104058642B
CN104058642B CN201410231242.1A CN201410231242A CN104058642B CN 104058642 B CN104058642 B CN 104058642B CN 201410231242 A CN201410231242 A CN 201410231242A CN 104058642 B CN104058642 B CN 104058642B
Authority
CN
China
Prior art keywords
sodium
antifreeze
aerated bricks
cement
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410231242.1A
Other languages
English (en)
Other versions
CN104058642A (zh
Inventor
张思坦
张绪庆
胡星
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU EAST CHINA GYPSUM Co Ltd
Original Assignee
BENGBU EAST CHINA GYPSUM Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU EAST CHINA GYPSUM Co Ltd filed Critical BENGBU EAST CHINA GYPSUM Co Ltd
Priority to CN201410231242.1A priority Critical patent/CN104058642B/zh
Publication of CN104058642A publication Critical patent/CN104058642A/zh
Application granted granted Critical
Publication of CN104058642B publication Critical patent/CN104058642B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种防冻加气砖，其是由下述重量份的原料制得：粉煤灰25-30、石膏8-9、氯化钠0.5-0.7，锌粉0.08-0.15、硅酸钠1-2，碳酸钠2-3，钠基膨润土4-6、水泥15-20，氯化镁0.4-0.8、河砂2-4、芒硝0.5-1、三聚磷酸钠1-3、泥炭土3-6、正硅酸钠1-2，蛭石粉3-5、助剂7-9；本发明提供的防冻加气砖具有防冻效果均匀、防冻度高的优点，硬度高，低容重，尤其适于低温施工。

Description

一种防冻加气砖
技术领域
本发明涉及加气砖领域，确切地说是一种防冻加气砖。
背景技术
加气砖，指的是通过高温蒸压设备工艺生产的加气混凝土砌块，现有加气砖品种单一，性能差，无法满足日益增加的市场需求。
发明内容
本发明的目的在于提供一种防冻加气砖。
上述目的通过以下方案实现：
一种防冻加气砖，其特征在于：其是由下述重量份的原料制得：
粉煤灰25-30、石膏8-9、氯化钠0.5-0.7，锌粉0.08-0.15、硅酸钠1-2，碳酸钠2-3，钠基膨润土4-6、水泥15-20，氯化镁0.4-0.8、河砂2-4、芒硝0.5-1、三聚磷酸钠1-3、泥炭土3-6、正硅酸钠1-2，蛭石粉3-5、助剂7-9；
所述的助剂由下述重量份的原料制得：铁矿尾渣5-8、黄土6-8、钢渣5-8、凹凸棒土15-18、明胶0.2-0.4，甘油三醋酸酯2.5-4、异构醇聚氧乙烯醚0.2-0.4、硅烷偶联剂KH7921-2、醋酸钠1-2、纳米二氧化硅1-2；
所述的助剂的制备方法为：
取黄土、铁矿尾渣、钢渣混匀后，破碎，所得粉料于920-960℃下于闪烧窑闪烧2-4秒，再取出冷却，与凹凸棒土、明胶、甘油三醋酸酯以及适量水混匀后，三辊研磨机研磨30-50分钟，取出加8-15%的氢氧化钠溶液调PH为8-8.5，再加入纳米二氧化硅，研磨浆料至400-500目后，再加盐酸溶液调为中性，喷雾干燥，所得粉末与其它剩余原料混合，混合均匀即得。
所述的一种防冻加气砖，其特征在于：
制备方法为：
（1）将除水泥、锌粉、河砂以外的其它原料混匀，加入适量水，在30-35℃下搅拌均匀后，再加入水泥、锌粉、河砂，搅拌8-20分钟，得混合水泥浆料；
（2）将混合水泥浆料浇筑入模成型，后在40-50℃下预养3-4小时，脱模，切割，蒸压养护后，即得。
本发明的有益效果为：本发明提供的防冻加气砖具有防冻效果均匀、防冻度高的优点，硬度高，低容重，尤其适于低温施工。
具体实施方式
一种防冻加气砖，其是由下述重量kg的原料制得：
粉煤灰27、石膏9、氯化钠0.7，锌粉0.15、硅酸钠1，碳酸钠2，钠基膨润土5、水泥15，氯化镁0.5、河砂3、芒硝0.6、三聚磷酸钠2、泥炭土5、正硅酸钠1，蛭石粉5、助剂9；
所述的助剂由下述重量kg的原料制得：铁矿尾渣8、黄土8、钢渣5、凹凸棒土15、明胶0.4，甘油三醋酸酯2.5、异构醇聚氧乙烯醚0.4、硅烷偶联剂KH7922、醋酸钠2、纳米二氧化硅2；
所述的助剂的制备方法为：
取黄土、铁矿尾渣、钢渣混匀后，破碎，所得粉料于940℃下于闪烧窑闪烧3秒，再取出冷却，与凹凸棒土、明胶、甘油三醋酸酯以及适量水混匀后，三辊研磨机研磨50分钟，取出加15%的氢氧化钠溶液调PH为8.5，再加入纳米二氧化硅，研磨浆料至500目后，再加盐酸溶液调为中性，喷雾干燥，所得粉末与其它剩余原料混合，混合均匀即得。
所述的一种防冻加气砖，
制备方法为：
（1）将除水泥、锌粉、河砂以外的其它原料混匀，加入适量水，在35℃下搅拌均匀后，再加入水泥、锌粉、河砂，搅拌10分钟，得混合水泥浆料；
（2）将混合水泥浆料浇筑入模成型，后在50℃下预养4小时，脱模，切割，蒸压养护后，即得。
本实施例所得加气砖的平均容重为630kg/m3,保温性能好,在砌块内部具有大量的气孔和微孔,因而有良好的保温隔热性能，平均值抗压强度为7.9MPa。

Claims (2)

1.一种防冻加气砖，其特征在于：其是由下述重量份的原料制得：粉煤灰25-30、石膏8-9、氯化钠0.5-0.7、锌粉0.08-0.15、硅酸钠1-2、碳酸钠2-3、钠基膨润土4-6、水泥15-20、氯化镁0.4-0.8、河砂2-4、芒硝0.5-1、三聚磷酸钠1-3、泥炭土3-6、正硅酸钠1-2、蛭石粉3-5、助剂7-9；所述的助剂由下述重量份的原料制得：铁矿尾渣5-8、黄土6-8、钢渣5-8、凹凸棒土15-18、明胶0.2-0.4、甘油三醋酸酯2.5-4、异构醇聚氧乙烯醚0.2-0.4、硅烷偶联剂KH7921-2、醋酸钠1-2、纳米二氧化硅1-2；所述的助剂的制备方法为：取黄土、铁矿尾渣、钢渣混匀后，破碎，所得粉料于920-960℃下于闪烧窑闪烧2-4秒，再取出冷却，与凹凸棒土、明胶、甘油三醋酸酯以及适量水混匀后，三辊研磨机研磨30-50分钟，取出加8-15%的氢氧化钠溶液调pH为8-8.5，再加入纳米二氧化硅，研磨浆料至400-500目后，再加盐酸溶液调为中性，喷雾干燥，所得粉末与其它剩余原料混合，混合均匀即得。
2.根据权利要求1所述的一种防冻加气砖，其特征在于：制备方法为：（1）将除水泥、锌粉、河砂以外的其它原料混匀，加入适量水，在30-35℃下搅拌均匀后，再加入水泥、锌粉、河砂，搅拌8-20分钟，得混合水泥浆料；（2）将混合水泥浆料浇筑入模成型，后在40-50℃下预养3-4小时，脱模，切割，蒸压养护后，即得。
CN201410231242.1A 2014-05-29 2014-05-29 一种防冻加气砖 Expired - Fee Related CN104058642B (zh)