CN104030732B - 一种骨质瓷玲珑釉及用该釉制作骨质瓷玲珑产品的方法 - Google Patents

一种骨质瓷玲珑釉及用该釉制作骨质瓷玲珑产品的方法 Download PDF

Info

Publication number
CN104030732B
CN104030732B CN201410262706.5A CN201410262706A CN104030732B CN 104030732 B CN104030732 B CN 104030732B CN 201410262706 A CN201410262706 A CN 201410262706A CN 104030732 B CN104030732 B CN 104030732B
Authority
CN
China
Prior art keywords
glaze
bone china
parts
china
exquisite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410262706.5A
Other languages
English (en)
Other versions
CN104030732A (zh
Inventor
林道藩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chaozhou Yasen Ceramics Industry Co. Ltd.
Original Assignee
GUANGDONG SONGFA CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG SONGFA CERAMICS CO Ltd filed Critical GUANGDONG SONGFA CERAMICS CO Ltd
Priority to CN201410262706.5A priority Critical patent/CN104030732B/zh
Publication of CN104030732A publication Critical patent/CN104030732A/zh
Application granted granted Critical
Publication of CN104030732B publication Critical patent/CN104030732B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种骨质瓷玲珑釉,该釉料包括如下组分和重量配比份数:石英16~24份,粘土0~8份,钾长石28~38份,硼砂12~18份,硼酸0~7份,碳酸钡10~17份,碳酸锶0~5份,碳酸锂0~8份,氧化锌2-12份,氢氧化铝0~6份,滑石0~3份,方解石0~12份,硅酸锆0~1份,该釉料透光度好,玲珑剔透,晶莹如宝石,无乳浊现象;本发明还提供一种用该釉制作骨质瓷玲珑产品的方法,该方法可消除玻璃体中的残存气泡,同时使该釉与骨质瓷的膨胀系数匹配,提高产品的耐急冷急热能力,避免开裂问题。

Description

一种骨质瓷玲珑釉及用该釉制作骨质瓷玲珑产品的方法
技术领域
[0001]本发明涉及一种骨质瓷玲珑釉及用该釉制作骨质瓷玲珑产品的方法。
背景技术
[0002]玲珑瓷起始于北朝末年至隋初,唐、宋、元未见,至明永乐年间景德镇窑有甜白釉玲珑烧造,此后复现于清乾隆期,然而数量很少,至于永乐年间的玲珑瓷流传极少,很不易见。
[0003]玲珑瓷器的产生源于产品缺陷。在宋代景德镇瓷器中有一种叫熏炉的产品,炉盖采用镂空装饰,在烧成过程中,由于釉料的高温流动性好,加之烧成温度往往控制不严,常使窑内温度过高,从而使釉料熔融后流动而将炉盖上的孔洞填平,出窑后对光一照,光亮透明。这种偶然的产品缺陷却使工匠们大受启发,终于在明代永乐年间成功烧制出晶莹剔透的玲珑瓷器。
[0004]晶莹、幽雅的玲珑瓷采纳了镂雕艺术之妙法,具有精巧致密,素雅清新的特点,夕卜国人称其为“嵌玻璃的瓷器”;玲珑瓷又称“米花”,日本人称为“米通”,西方人把它叫做“嵌玻璃的瓷器”。玲珑瓷以其玲珑剔透、幽静雅致、精巧细腻、朴素大方的艺术特色,给人以清新明快之感,为人们所推崇备至,数百年来一直誉满中外。
[0005]但是如果将传统的玲珑釉料用于骨质瓷上,骨质瓷玲珑产品孔洞玻璃体中的残存气泡难以消除,易出现乳浊现象;且由于传统玲珑釉与骨质瓷的膨胀系数不匹配,使用过程中耐热冲击性能差,易产生裂纹缺陷。
发明内容
[0006]本发明的目的在于提供一种骨质瓷玲珑釉及用该釉制作骨质瓷玲珑产品的方法,以解决上述技术中存在的问题和缺陷。
[0007]为达到上述目的,本发明采用以下技术方案:
[0008] —种骨质瓷玲珑釉,包括如下组分和重量配比份数:石英16〜24份,粘土 O〜8份,钾长石28〜38份,硼砂12〜18份,硼酸O〜7份,碳酸钡6〜17份,碳酸锁O〜5份,碳酸锂O〜8份,氧化锌2-12份,氢氧化铝O〜6份,滑石O〜3份,方解石O〜12份,硅酸锆O〜I份。
[0009]本发明还提供一种用骨质瓷玲珑釉制作骨质瓷玲珑产品的方法,其方法步骤为:
[0010] S1:按所述骨质瓷玲珑釉的原料及配比称取所需原料并搅拌均匀,在1330-1350°c熔成熔块,水淬好的熔块放入球磨机内,以总质量为基准,加入质量百分比为25-28%的水,湿球磨48小时,细度万孔筛余< 0.1%,加入0.1%黄原胶,0.3%糖稀,再研磨2小时通过200-250目筛后备用;
[0011 ] S2:骨瓷坯体经过修坯后,在550_750°C素烧,粘贴已按设计镂空好的塑料膜,用喷砂机喷砂打孔,在1250-1270°C素烧成瓷,经过抛光机抛光,素瓷烘干后用备好的釉料封堵孔洞,再次烘干,经650-750°C烧成后喷骨瓷熔块釉;
[0012] S3:喷好釉的骨质瓷,烘干后入窑,升温到800°C,保温30分钟,再以I〜2°C/min速率升温至1120〜1180°C温度范围内烧成,保温30分钟,自然冷却到室温。
[0013]硅酸锆在骨质瓷玲珑产品中,主要以氧化锆产生作用,氧化锌、氧化锆可提高玻璃体的弹性,提高玻璃体透明度;碳酸锂在骨质瓷玲珑产品中,主要以氧化锂产生作用,氧化锂对玻璃体的膨胀系数的调节起着很重要的作用,调节膨胀系数使之与骨瓷坯体膨胀系数匹配,解决玲珑制品在使用过程中的裂纹缺陷的发生,同时提高玲珑釉的耐热冲击性能,提高产品的耐急冷急热能力;碳酸钡、碳酸锶在骨质瓷玲珑产品中,主要以氧化钡、氧化锶产生作用,氧化钡、氧化锶可提高玻璃的透光度,提高玻璃体的折射,提高玻璃体的弹性,有很好的助熔效果;滑石在骨质瓷玲珑产品中,主要以氧化镁产生作用,氧化镁在助熔的基础上,可提高玻璃体强度,增加玻璃体粘度,确保孔中的玻璃体不会流出,同时降低玻璃体膨胀系数;氧化铝由氢氧化铝和长石带入,可调整玻璃体的高温粘度,较高的高温粘度,有益于玲珑釉制品的生产。
[0014]与现有技术相比,本发明具有以下有益效果:
[0015] 1.提高玻璃体的弹性、强度与透明度,增加玻璃体粘度,确保孔中的玻璃体在烧成过程中不会流出,有益于玲珑釉制品的生产;
[0016] 2.调整玲珑釉的始熔温度,消除玻璃体中的残存气泡;
[0017] 3.调整玲珑釉的膨胀系数,使之与骨质瓷的膨胀系数匹配,提高产品耐急冷急热能力,避免开裂问题。
具体实施方式
[0018]下面结合具体实施方式对本发明作进一步的说明。
[0019] 实施例1
[0020]本实施例公开了一种骨质瓷玲珑釉,包括如下组分和重量配比份数:石英20.5份,钾长石34份,硼砂18份,碳酸钡11份,碳酸锶4.5份,碳酸锂2份,氧化锌2份,氢氧化铝4.5份,滑石3份,硅酸锆0.5份。
[0021 ]取上述原料搅拌均匀,在1340°C熔成熔块,水淬好的熔块放入球磨机内,以总质量为基准,加入质量百分比为26%的水,湿球磨48小时,细度万孔筛余0.08%,加入0.1%黄原胶,0.3%糖稀,再研磨2小时通过200目筛后备用;骨瓷坯体经过修坯后,在650°C素烧,粘贴已按设计镂空好的塑料膜,用喷砂机喷砂打孔,在1260°C素烧成瓷,经过抛光机抛光,素瓷烘干后用备好的釉料封堵孔洞,再次烘干,经700°C烧成后喷骨瓷熔块釉;喷好釉的骨质瓷,烘干后入窑,升温到800°C,保温30分钟,再以l°C/min速率升温至1150°C温度范围内烧成,保温30分钟,自然冷却到室温。
[0022]本实施例制备的骨质瓷玲珑产品,通过180_20°C水热交换一次不裂,达到了日用瓷的质量要求。
[0023] 实施例2
[0024]本实施例公开了一种骨质瓷玲珑釉,包括如下组分和重量配比份数:石英16份,钾长石28份,硼砂17份,碳酸钡6份,碳酸锶3份,碳酸锂4份,氧化锌6份,氢氧化铝5份,滑石3份,硅酸锆I份,方解石12份。
[0025]取上述原料及配比称取所需原料并搅拌均匀,在1350°C熔成熔块,水淬好的熔块放入球磨机内,以总质量为基准,加入质量百分比为28%的水,湿球磨48小时,细度万孔筛余0.05%,加入0.1%黄原胶,0.3%糖稀,再研磨2小时通过250目筛后备用;骨瓷坯体经过修坯后,在750°C素烧,粘贴已按设计镂空好的塑料膜,用喷砂机喷砂打孔,在1270°C素烧成瓷,经过抛光机抛光,素瓷烘干后用备好的釉料封堵孔洞,再次烘干,经750°C烧成后喷骨瓷熔块釉;喷好釉的骨质瓷,烘干后入窑,升温到800°C,保温30分钟,再以2°C/min速率升温至1120温度范围内烧成,保温30分钟,自然冷却到室温。
[0026]本实施例制备的骨质瓷玲珑产品,透光度好,玲珑剔透,晶莹如宝石,无乳浊现象。

Claims (1)

1.一种骨质瓷玲珑釉,其特征在于,其原料组分和重量配比份数为:石英16〜24份,粘土 O〜8份,钾长石28〜38份,硼砂12〜18份,硼酸O〜7份,碳酸钡6〜17份,碳酸锁O〜5份,碳酸锂O〜8份,氧化锌2-12份,氢氧化铝O〜6份,滑石O〜3份,方解石O〜12份,硅酸锆O〜I份; 用上述骨质瓷玲珑釉制作骨质瓷玲珑产品的方法步骤为: S1:按所述骨质瓷玲珑釉的原料及配比称取所需原料并搅拌均匀,在1330-1350°c熔成熔块,水淬好的熔块放入球磨机内,以总质量为基准,加入质量百分比为25-28%的水,湿球磨48小时,细度万孔筛余< 0.1%,再加入0.1%黄原胶,0.3%糖稀,再研磨2小时通过200-250目筛后备用; S2:骨瓷坯体经过修坯后,在550-750°C素烧,粘贴已镂空好的塑料膜,用喷砂机喷砂打孔,在1250-1270°C素烧成瓷,经过抛光机抛光,素瓷烘干后用备好的釉料封堵孔洞,再次烘干,经650-750°C烧成后喷骨瓷熔块釉; S3:喷好釉的骨质瓷,烘干后入窑,升温到800°C,保温30分钟,再以I〜2°C/min速率升温至1120〜1180°C温度范围内烧成,保温30分钟,然后自然冷却到室温。
CN201410262706.5A 2014-06-13 2014-06-13 一种骨质瓷玲珑釉及用该釉制作骨质瓷玲珑产品的方法 Expired - Fee Related CN104030732B (zh)