CN103992116A - Blue and white color porcelain preparation method - Google Patents

Blue and white color porcelain preparation method Download PDF

Info

Publication number
CN103992116A
CN103992116A CN201410139969.7A CN201410139969A CN103992116A CN 103992116 A CN103992116 A CN 103992116A CN 201410139969 A CN201410139969 A CN 201410139969A CN 103992116 A CN103992116 A CN 103992116A
Authority
CN
China
Prior art keywords
blue
kiln
glaze
billet
white
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410139969.7A
Other languages
Chinese (zh)
Inventor
蔡胜兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Blue And White Fang Ci Industry Limited-Liability Co
Original Assignee
Anhui Blue And White Fang Ci Industry Limited-Liability Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Blue And White Fang Ci Industry Limited-Liability Co filed Critical Anhui Blue And White Fang Ci Industry Limited-Liability Co
Priority to CN201410139969.7A priority Critical patent/CN103992116A/en
Publication of CN103992116A publication Critical patent/CN103992116A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a blue and white color porcelain preparation method, wherein the blue and white color porcelain is prepared by carrying out billet material preparing, molding, firing, colored drawing and other processing processes. The preparation method sequentially comprises: preparing a billet material and a glaze material, carrying out rolling pressing molding on a rolled and pressed mud cake in a gypsum mold, placing the mold billet into a chain type drying agent or baking chamber to dry, drying the green billet after separating the mold and the billet, taking out the green billet after achieving a certain strength, finishing the billet, loading the qualified green billet into a kiln car boron plate or gate bowl, carrying biscuit firing in a biscuit firing kiln tunnel, burning by using natural gas, carrying out biscuit finishing and polishing water washing after discharging out from the kiln, drying, carrying out glaze spraying on the biscuit porcelain in a manual or automatic glaze applying production line manner, drying, loading into a glaze firing tunnel kiln to carry out glaze firing, carrying out manual applique, colored drawing and gold inlaying on the qualified white porcelain, drying, placing into a natural gas open-flame burning roller channel decorating kiln to fire, and discharging out from the kiln to obtain the color porcelain. The blue and white color porcelain preparation method has the following advantages that: the industrial production efficiency is increased, the product appearance is beautiful, the duration time, the degree and the temperature of heating can be well controlled, the finished product quality is increased and the like.

Description

A kind of blue and white faience preparation method
Technical field
The present invention relates to the preparation of bule and white porcelain, relate in particular to a kind of blue and white faience preparation method.
Background technology
At present, bule and white porcelain is as the symbol of Chinese porcelain culture, though its figure in ancient times or the modern times all leave enduring impression, thereby because the different quality differences that can have influence on bule and white porcelain of the method for complete processing, the quality of blue and white colorant is because of itself component difference and thereby glaze colours is different forms various bule and white porcelain, because its temperature that adopts high temperature oxidation flame to burn is very high, thus sometimes can not well control the duration and degree of heating, thus affect the quality of bule and white porcelain.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, the object of this invention is to provide a kind of blue and white faience preparation method.
The present invention takes following technical scheme to realize: a kind of preparation method of blue and white faience, it is by preparing blank, moulding, burning till with complete processings such as colored drawings and make, there are successively following steps, first prepare blank and glaze, the mud cake of roll forming is carried out in plaster mould to roll forming, mould base is entered in chain type siccative or drying room and is dried: after the separation of mould base, blue or green base is dried again, reach after some strength and take out and carry out repaired biscuit; Qualified blue or green base is packed in kiln car boron plate or lock alms bowl, in biscuiting tunnel furnace, carry out biscuiting, adopt combustion of natural gas, after kiln discharge, carry out element and repair with polishing and wash, after dry, bique is carried out to artificial or automatic glazing line glaze spraying, after being again dried, pack glaze fired tunnel kiln into and carry out glaze firing; By qualified ceramic whiteware manually applique, paint coloured silk and be inlaid with gold after, enter Tian Ran Qi Ming flame burning Roller-hearth decoration firing kiln after dry and carry out grilling, after kiln discharge, become faience; Described moulding is divided into roll forming and two kinds of methods of injection forming; The combustion system Wei Ming flame formula perfect combustion of described employing Sweet natural gas; Described qualified blue or green base once fills burning with lock alms bowl and support in roller kiln.
The present invention has following beneficial effect in sum: the preparation method of bule and white porcelain of the present invention has and fires the advantages such as pattern simple, beautiful in colour, that make bule and white porcelain is more attractive in appearance.
Embodiment
According to flow process accompanying drawing, be described further below: a kind of preparation method of blue and white faience, it is by preparing blank, moulding, burning till with complete processings such as colored drawings and make, there are successively following steps, first prepare blank and glaze, the mud cake of roll forming is carried out in plaster mould to roll forming, mould base is entered in chain type siccative or drying room and is dried: after the separation of mould base, blue or green base is dried again, reach after some strength and take out and carry out repaired biscuit; Qualified blue or green base is packed in kiln car boron plate or lock alms bowl, in biscuiting tunnel furnace, carry out biscuiting, adopt combustion of natural gas, after kiln discharge, carry out element and repair with polishing and wash, after dry, bique is carried out to artificial or automatic glazing line glaze spraying, after being again dried, pack glaze fired tunnel kiln into and carry out glaze firing; By qualified ceramic whiteware manually applique, paint coloured silk and be inlaid with gold after, enter Tian Ran Qi Ming flame burning Roller-hearth decoration firing kiln after dry and carry out grilling, after kiln discharge, become faience; Described moulding is divided into roll forming and two kinds of methods of injection forming; The combustion system Wei Ming flame formula perfect combustion of described employing Sweet natural gas; Described qualified blue or green base once fills burning with lock alms bowl and support in roller kiln.
The above is the embodiment of the present invention, and the equivalence of doing according to structure, feature and principle described in the present patent application scope therefore all changes or modifies, and is included in patent claim of the present invention.

Claims (4)

1. the preparation method of a blue and white faience, it is by preparing blank, moulding, burning till with complete processings such as colored drawings and make, it is characterized in that: have successively following steps, first prepare blank and glaze, the mud cake of roll forming is carried out in plaster mould to roll forming, mould base is entered in chain type siccative or drying room and is dried: after the separation of mould base, blue or green base is dried again, reach after some strength and take out and carry out repaired biscuit; Qualified blue or green base is packed in kiln car boron plate or lock alms bowl, in biscuiting tunnel furnace, carry out biscuiting, adopt combustion of natural gas, after kiln discharge, carry out element and repair with polishing and wash, after dry, bique is carried out to artificial or automatic glazing line glaze spraying, after being again dried, pack glaze fired tunnel kiln into and carry out glaze firing; By qualified ceramic whiteware manually applique, paint coloured silk and be inlaid with gold after, enter Tian Ran Qi Ming flame burning Roller-hearth decoration firing kiln after dry and carry out grilling, after kiln discharge, become faience.
2. a kind of blue and white faience preparation method according to claim 1, is characterized in that: described moulding is divided into roll forming and two kinds of methods of injection forming.
3. a kind of blue and white faience preparation method according to claim 1, is characterized in that: the combustion system Wei Ming flame formula perfect combustion of described employing Sweet natural gas.
4. a kind of blue and white faience preparation method according to claim 1, is characterized in that: described qualified blue or green base once fills burning with lock alms bowl and support in roller kiln.
CN201410139969.7A 2014-04-09 2014-04-09 Blue and white color porcelain preparation method Pending CN103992116A (en)