CN103979861A - Slag/ceramic factory waste composite lightweight partition plate and manufacturing method thereof - Google Patents

Slag/ceramic factory waste composite lightweight partition plate and manufacturing method thereof Download PDF

Info

Publication number
CN103979861A
CN103979861A CN201410135244.0A CN201410135244A CN103979861A CN 103979861 A CN103979861 A CN 103979861A CN 201410135244 A CN201410135244 A CN 201410135244A CN 103979861 A CN103979861 A CN 103979861A
Authority
CN
China
Prior art keywords
parts
slag
partition plate
powder
waste
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410135244.0A
Other languages
Chinese (zh)
Other versions
CN103979861B (en
Inventor
章功国
王泾文
段宗银
李纯金
陈超
王淑妍
张少伍
王晓芬
谢勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI JISITE INTELLIGENT EQUIPMENT CO., LTD.
Original Assignee
Maanshan Hengyi Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Maanshan Hengyi Machinery Manufacturing Co Ltd filed Critical Maanshan Hengyi Machinery Manufacturing Co Ltd
Priority to CN201410135244.0A priority Critical patent/CN103979861B/en
Publication of CN103979861A publication Critical patent/CN103979861A/en
Application granted granted Critical
Publication of CN103979861B publication Critical patent/CN103979861B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a slag/ceramic factory waste composite lightweight partition plate. The partition plate is characterized by being prepared from the following raw materials by weight: 20 to 25 parts of cement, 19 to 22 parts of slag, 11 to 14 parts of nanometer carbon, 14 to 17 parts of limestone, 6 to 8 parts of a polycarboxylate superplasticizer, 1.2 to 2.5 parts of ammonium persulfate, 2.4 to 4.2 parts of calcium oxide, 12 to 14 parts of a nylon fiber, 1 to 3 parts of honeysuckle flower extract, 10 to 13 parts of ceramic factory waste, 12 to 14 parts of shell, 13 to 16 parts of ceramsite, 3 to 6 parts of an auxiliary agent and a proper amount of water. The partition plate provided by the invention has the characteristics of sterilization and insect prevention performance, corrosion resistance, light weight, high strength, heat preservation, sound insulation, fire resistance, water resistance and the like; since the ceramic factory waste, the shell and the like are added into the raw materials, production cost is reduced, energy is conserved, and energy consumption is reduced; the prepared partition plate hardly cracks and has good practicality and wide prospects.

Description

A kind of slag/ceramics factory waste material composite light partition plate and preparation method thereof
 
Technical field
The present invention relates to building material field, be specifically related to a kind of slag/ceramics factory waste material composite light partition plate and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, a kind of novel energy-conserving walling material forming through the maintenance of frequency conversion steam pressurized, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, when installation, only sheet material need be erected, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but the shortcomings such as the light cellular partition board ultimate compression strength using is in the market low, tensile strength weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of slag/ceramics factory waste material composite light partition plate and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of slag/ceramics factory waste material composite light partition plate, it is characterized in that, made by the raw material of following weight part: cement 20-25, slag 19-22, nano-sized carbon 11-14, Wingdale 14-17, polycarboxylate dehydragent 6-8, ammonium persulphate 1.2-2.5, calcium oxide 2.4-4.2, nylon fiber 12-14, Flos Lonicerae extractive solution 1-3, the waste material 10-13 of ceramics factory, shell 12-14, haydite 13-16, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain in 3:2 ratio, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
The preparation method of described a kind of slag/ceramics factory waste material composite light partition plate, is characterized in that comprising the following steps:
(1) shell is sent in charring furnace, at 510-635 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form Flos Lonicerae extractive solution under condition to the powder of gained in air blast, makes it to mix;
(2) slag, Wingdale, ceramics factory's waste material are calcined at 605-850 DEG C after 3-6 hour and taken out, pulverize, extremely even with spraying gun sprinkling 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions, dipping 10-12 hour;
(3) step (1), (2) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: partition plate of the present invention has sterilization and insect prevention, anticorrosion, lightweight, intensity is high, insulation, sound insulation, fire prevention, the feature such as water-fast, the present invention simultaneously adds ceramics factory's waste material, shell etc. in starting material to, reduce production cost, save energy reduces energy consumption, make product not easy to crack, practicality is good, has a extensive future.
Embodiment
Described a kind of slag/ceramics factory waste material composite light partition plate, it is characterized in that, made by the raw material of following weight part: cement 20, slag 19, nano-sized carbon 11, Wingdale 14, polycarboxylate dehydragent 6, ammonium persulphate 1.2, calcium oxide 2.4, nylon fiber 12, Flos Lonicerae extractive solution 1, ceramics factory's waste material 10, shell 14, haydite 13, auxiliary agent 3, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5, titanium dioxide 5, lithium silicate 0.1, magnesium chloride 2, magnesium oxide 1, sodium tetraborate 0.02, Sodium hexametaphosphate 99 0.04, redispersable latex powder 0.24, molasses 0.6, SHP-50 polysiloxane powder hydrophober 1.2, Oenothera oil 0.02, dimethyl silicone oil 2.6, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain in 3:2 ratio, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
Making method comprises the following steps:
(1) shell is sent in charring furnace, at 510-635 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form Flos Lonicerae extractive solution under condition to the powder of gained in air blast, makes it to mix;
(2) slag, Wingdale, ceramics factory's waste material are calcined at 605-850 DEG C after 3-6 hour and taken out, pulverize, extremely even with spraying gun sprinkling 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions, dipping 10-12 hour;
(3) step (1), (2) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The technical indicator of processing the light cellular partition board obtaining by above-described embodiment is as follows:
(1) unit weight: 511kg/m 3;
(2) thermal conductivity (25 ± 2 DEG C of medial temperatures): 0.086W/ (mk);
(3) ultimate compression strength: 5.1Mpa.

Claims (2)

1. slag/ceramics factory waste material composite light partition plate, it is characterized in that, made by the raw material of following weight part: cement 20-25, slag 19-22, nano-sized carbon 11-14, Wingdale 14-17, polycarboxylate dehydragent 6-8, ammonium persulphate 1.2-2.5, calcium oxide 2.4-4.2, nylon fiber 12-14, Flos Lonicerae extractive solution 1-3, the waste material 10-13 of ceramics factory, shell 12-14, haydite 13-16, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain in 3:2 ratio, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
2. the making method of a kind of slag/ceramics factory according to claim 1 waste material composite light partition plate, is characterized in that comprising the following steps:
(1) shell is sent in charring furnace, at 510-635 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form Flos Lonicerae extractive solution under condition to the powder of gained in air blast, makes it to mix;
(2) slag, Wingdale, ceramics factory's waste material are calcined at 605-850 DEG C after 3-6 hour and taken out, pulverize, extremely even with spraying gun sprinkling 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions, dipping 10-12 hour;
(3) step (1), (2) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
CN201410135244.0A 2014-04-04 2014-04-04 A kind of slag/ceramics factory's waste material composite light partition plate and preparation method thereof Active CN103979861B (en)