CN103952055B - Antifreeze and insulated coating and preparation method thereof - Google Patents

Antifreeze and insulated coating and preparation method thereof Download PDF

Info

Publication number
CN103952055B
CN103952055B CN201410166058.3A CN201410166058A CN103952055B CN 103952055 B CN103952055 B CN 103952055B CN 201410166058 A CN201410166058 A CN 201410166058A CN 103952055 B CN103952055 B CN 103952055B
Authority
CN
China
Prior art keywords
parts
coating
freeze proof
proof insulation
polypropylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410166058.3A
Other languages
Chinese (zh)
Other versions
CN103952055A (en
Inventor
王龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan city Delaide coating Co. Ltd.
Original Assignee
Dongguan City Delaide Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan City Delaide Coating Co Ltd filed Critical Dongguan City Delaide Coating Co Ltd
Priority to CN201410166058.3A priority Critical patent/CN103952055B/en
Publication of CN103952055A publication Critical patent/CN103952055A/en
Application granted granted Critical
Publication of CN103952055B publication Critical patent/CN103952055B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses an antifreeze and insulated coating and a preparation method thereof. The antifreeze and insulated coating is prepared from the following components in parts by weight: 19-29 parts of phenolic resin, 12-15 parts of tung oil, 5-8 parts of polypropylene, 8-13 parts of methylcyclopentane, 14-17 parts of glyceryl triacetate, 15-19 parts of ethylene glycol and 16-19 parts of water. The formula components of the coating are dissolved, agitated and sealed to obtain the antifreeze and insulated coating, and the prepared coating has excellent anti-frost property and thermal insulation properties, and can be applied to a low-temperature environment.

Description

A kind of coating of freeze proof insulation and preparation method thereof
Technical field
The present invention relates to a kind of coating and preparation method thereof, more particularly to a kind of freeze proof insulation Coating and preparation method thereof.
Background technology
In the environment of the area of some colds and low temperature, coating is on the surface being applied to body of wall Afterwards, due to due to weather, in the environment of coating can be in low temperature for a long time, the performance of coating Can have a greater change, reduce the stability of coating.Under cryogenic conditions, due to coating Constituent there is no frost resistance, therefore will produce the change of coating form, have impact on painting The use of material.Conventional body of wall has generally gone through isothermal holding, and materials for wall possesses certain guarantor Warm nature, if coating also has good heat-insulating property, can improve the guarantor of building further Warm nature energy, reduces the energy loss of building.
Content of the invention
Technical problem to be solved:The low temperature resistant poor-performing of common coating for wall surface, when long Between be in coating under low-temperature condition and can ftracture, and poor the asking of heat-insulating property of the coating of routine Topic.
Technical scheme:The invention discloses a kind of coating of freeze proof insulation and preparation method thereof, resist The coating freezing insulation is made up of according to weight ratio following component:Phenolic resin be 19~29 parts, Tung oil is 12~15 parts, polypropylene is 5~8 parts, methyl cyclopentane is 8~13 parts, three second Acid glyceride is 14~17 parts, ethylene glycol is 15~19 parts, water is 16~19 parts.
A kind of preparation method of the coating of freeze proof insulation, comprises the following steps:(1) phenolic resin is taken to be 19~29 parts, tung oil be 12~15 parts, polypropylene be 5~8 parts, by phenolic aldehyde tree after heating Fat, tung oil, polypropylene are uniformly dissolved;(2) add methyl cyclopentane be 8~13 parts, three Acetin is 14~17 parts, ethylene glycol is 15~19 parts, is dissolved again, dissolving After stir;(3) be eventually adding water be 16~19 parts, be stirred again, stir to Mixture mixes, and the coating liquid mixing is carried out sealing preserve, prepares anti- Freeze the coating of insulation.
The phenolic resin adding in a kind of preparation process of coating of freeze proof insulation is preferably 29 Part.
The polypropylene adding in a kind of preparation process of coating of freeze proof insulation is preferably 5 parts.
The glyceryl triacetate adding in a kind of preparation process of coating of freeze proof insulation is preferably 14~17 parts.
Beneficial effect:It is prepared by the method for the present invention the coating obtaining and there is good freexing tolerance energy And heat-insulating property, after depositing 60 days at -40 DEG C to -20 DEG C, coating stateless changes, tool There is preferable freexing tolerance energy.Determine the heat insulating coefficient of the coating of the present invention, the coating of the present invention Thermal conductivity factor be 0.039~0.044W/ (m K), there is preferable heat insulation effect.
Specific embodiment
Embodiment 1
A kind of preparation method of the coating of freeze proof insulation, comprises the following steps:(1) take phenolic aldehyde tree Fat be 29kg, tung oil be 15kg, polypropylene be 5kg, after heating by phenolic resin, tung oil, Polypropylene is uniformly dissolved;(2) adding methyl cyclopentane is that 13kg, glyceryl triacetate are 14kg, ethylene glycol are 15kg, are dissolved again, stir after dissolving;(3) last Addition water is 19kg, is stirred again, stirs and mix to mixture, will mix all Even coating liquid carries out sealing preserve, prepares the coating of freeze proof insulation.
Embodiment 2
A kind of preparation method of the coating of freeze proof insulation, comprises the following steps:(1) take phenolic aldehyde tree Fat be 19kg, tung oil be 12kg, polypropylene be 7kg, after heating by phenolic resin, tung oil, Polypropylene is uniformly dissolved;(2) adding methyl cyclopentane is that 8kg, glyceryl triacetate are 15kg, ethylene glycol are 19kg, are dissolved again, stir after dissolving;(3) last Addition water is 16kg, is stirred again, stirs and mix to mixture, will mix all Even coating liquid carries out sealing preserve, prepares the coating of freeze proof insulation.
Embodiment 3
A kind of preparation method of the coating of freeze proof insulation, comprises the following steps:(1) take phenolic aldehyde tree Fat be 24kg, tung oil be 13kg, polypropylene be 8kg, after heating by phenolic resin, tung oil, Polypropylene is uniformly dissolved;(2) adding methyl cyclopentane is that 11kg, glyceryl triacetate are 17kg, ethylene glycol are 17kg, are dissolved again, stir after dissolving;(3) last Addition water is 17kg, is stirred again, stirs and mix to mixture, will mix all Even coating liquid carries out sealing preserve, prepares the coating of freeze proof insulation.
After preparing coating, determine embodiment 1, embodiment 2, the coating of embodiment 3 anti- Freeze performance and heat-insulating property.The coating of embodiment 1, embodiment 2, embodiment 3 is existed respectively - 40 DEG C, -30 DEG C, deposit 60 days at -20 DEG C, observe the state change of coating.In addition survey again Determine to determine embodiment 1, embodiment 2, the thermal conductivity factor of the coating of embodiment 3, measured Experimental data as follows.
After placed 60 days at low temperature, coating itself does not change it was demonstrated that this The coating that bright preparation method prepares has preferable cryoprotective effects, in addition, the present invention Coating also has relatively low thermal conductivity factor, improves the heat insulation effect of coating, in sum, this The coating of invention is with a wide range of applications at low ambient temperatures.

Claims (3)

1. a kind of coating of freeze proof insulation is it is characterised in that the coating of freeze proof insulation is by following one-tenth Divide according to weight than composition:Phenolic resin be 19~29 parts, tung oil be 12~15 parts, poly- third Alkene is 5~8 parts, methyl cyclopentane is 8~13 parts, glyceryl triacetate is 14~17 parts, Ethylene glycol is 15~19 parts, water is 16~19 parts;
The preparation method of the described coating of a kind of freeze proof insulation, comprises the following steps:(1) take Phenolic resin is 19~29 parts, tung oil is 12~15 parts, polypropylene is 5~8 parts, heating Afterwards phenolic resin, tung oil, polypropylene are uniformly dissolved;(2) add methyl cyclopentane be 8~ 13 parts, glyceryl triacetate be 14~17 parts, ethylene glycol be 15~19 parts, carry out again Dissolving, stirs after dissolving;(3) it is eventually adding water and is 16~19 parts, stirred again Mix, stir and mix to mixture, the coating liquid mixing is carried out sealing preserve, Prepare the coating of freeze proof insulation.
2. a kind of coating of freeze proof insulation according to claim 1 is it is characterised in that make The phenolic resin adding during standby is 29 parts.
3. a kind of coating of freeze proof insulation according to claim 1 is it is characterised in that make The polypropylene adding during standby is 5 parts.
CN201410166058.3A 2014-04-23 2014-04-23 Antifreeze and insulated coating and preparation method thereof Expired - Fee Related CN103952055B (en)