CN103936371A - 一种含有陶瓷纤维的不易开裂的粉煤灰砖 - Google Patents
一种含有陶瓷纤维的不易开裂的粉煤灰砖 Download PDFInfo
- Publication number
- CN103936371A CN103936371A CN201410118575.3A CN201410118575A CN103936371A CN 103936371 A CN103936371 A CN 103936371A CN 201410118575 A CN201410118575 A CN 201410118575A CN 103936371 A CN103936371 A CN 103936371A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic fiber
- hour
- fly ash
- flyash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种含有陶瓷纤维的不易开裂的粉煤灰砖,其是由下述重量份的原料制得:甲基纤维素1-2、粉煤灰10-12,陶粒5-7、石膏10-12、六钛酸钾晶须1-2、铝酸钙水泥8-12、煤矸石粉2-5、环烷酸镁1-2,食盐1-2,陶瓷纤维2-4、葡萄糖酸钠0.1-0.2,填充料5-8。本发明强度高,不易开裂,使用寿命长。
Description
技术领域
本发明涉及加气砖领域,确切地说是一种含有陶瓷纤维的不易开裂的粉煤灰砖。
背景技术
陶瓷纤维是一种纤维状轻质耐火材料,具有重量轻、耐高温、热稳定性好、导热率低、比热小及耐机械震动等优点,因而在机械、冶金、化工、石油、陶瓷、玻璃、电子等行业都得到了广泛的应用。
发明内容
本发明的目的在于提供一种含有陶瓷纤维的不易开裂的粉煤灰砖。
上述目的通过以下方案实现:
一种含有陶瓷纤维的不易开裂的粉煤灰砖,其特征在于:其是由下述重量份的原料制得:甲基纤维素1-2、粉煤灰10-12,陶粒5-7、石膏10-12、六钛酸钾晶须1-2、铝酸钙水泥8-12、煤矸石粉2-5、环烷酸镁1-2,食盐1-2,陶瓷纤维2-4、葡萄糖酸钠0.1-0.2,填充料5-8;
填充料由下列重量份的原料制成:硅藻土18-22、煤矸石粉5-8,萤石矿渣粉5-8,氮化铝粉末2-4、硬脂酸钙1-2,脂肪醇聚氧乙烯醚1-2,硅烷偶联剂KH560 1-2,氯化石蜡2-4,苯基缩水甘油醚1-2,3-氨丙基三甲氧基硅烷2-3、二缩三丙二醇二丙烯酸酯2-3、柠檬酸1-2;
填充料的制备方法是将硅藻土、煤矸石粉混匀,再放入浓度为10-15%的乙酸溶液中,浸泡8-10小时,取出去离子水洗涤烘干,放入煅烧炉中在600-700℃下煅烧2-3小时,冷却,放入10-12%氢氧化钠溶液中浸泡5-7小时,过滤取出,去离子水洗涤,烘干,再与其它剩余原料混合均匀后,即得。
所述的一种含有陶瓷纤维的不易开裂的粉煤灰砖,其特征在于:
制备方法为:
(1)将铝酸钙水泥、粉煤灰、煤矸石粉、石膏按重量份混匀,再加入适量水,于100-200转/分下搅拌20-30分钟,再与其余原料混匀,再加入适量水,浇筑入模成型,后在40-50℃下预养3-5小时,脱模,切割,得砌块坯;
(2)将砌块坯放入反应釜中蒸压养护14-16小时,入库成品即得。
本发明的有益效果为:本发明强度高,不易开裂,使用寿命长。
具体实施方式
一种含有陶瓷纤维的不易开裂的粉煤灰砖,其是由下述重量kg的原料制得:甲基纤维素2、粉煤灰12,陶粒5、石膏12、六钛酸钾晶须1、铝酸钙水泥12、煤矸石粉5、环烷酸镁2,食盐1,陶瓷纤维4、葡萄糖酸钠0.2,填充料8;
填充料由下列重量份的原料制成:硅藻土22、煤矸石粉8,萤石矿渣粉5,氮化铝粉末4、硬脂酸钙1,脂肪醇聚氧乙烯醚2,硅烷偶联剂KH560 2,氯化石蜡2,苯基缩水甘油醚2,3-氨丙基三甲氧基硅烷3、二缩三丙二醇二丙烯酸酯3、柠檬酸1;
填充料的制备方法是将硅藻土、煤矸石粉混匀,再放入浓度为15%的乙酸溶液中,浸泡10小时,取出去离子水洗涤烘干,放入煅烧炉中在680℃下煅烧3小时,冷却,放入10%氢氧化钠溶液中浸泡7小时,过滤取出,去离子水洗涤,烘干,再与其它剩余原料混合均匀后,即得。
所述的一种含有陶瓷纤维的不易开裂的粉煤灰砖,
制备方法为:
(1)将铝酸钙水泥、粉煤灰、煤矸石粉、石膏按重量份混匀,再加入适量水,于100转/分下搅拌20分钟,再与其余原料混匀,再加入适量水,浇筑入模成型,后在40℃下预养5小时,脱模,切割,得砌块坯;
(2)将砌块坯放入反应釜中蒸压养护16小时,入库成品即得。
本实施例加气砖的平均容重为550kg/m3,保温性能好,平均值抗压强度为9.4MPa。
Claims (2)
1.一种含有陶瓷纤维的不易开裂的粉煤灰砖,其特征在于:其是由下述重量份的原料制得:甲基纤维素1-2、粉煤灰10-12,陶粒5-7、石膏10-12、六钛酸钾晶须1-2、铝酸钙水泥8-12、煤矸石粉2-5、环烷酸镁1-2,食盐1-2,陶瓷纤维2-4、葡萄糖酸钠0.1-0.2,填充料5-8;
填充料由下列重量份的原料制成:硅藻土18-22、煤矸石粉5-8,萤石矿渣粉5-8,氮化铝粉末2-4、硬脂酸钙1-2,脂肪醇聚氧乙烯醚1-2,硅烷偶联剂KH560 1-2,氯化石蜡2-4,苯基缩水甘油醚1-2,3-氨丙基三甲氧基硅烷2-3、二缩三丙二醇二丙烯酸酯2-3、柠檬酸1-2;
填充料的制备方法是将硅藻土、煤矸石粉混匀,再放入浓度为10-15%的乙酸溶液中,浸泡8-10小时,取出去离子水洗涤烘干,放入煅烧炉中在600-700℃下煅烧2-3小时,冷却,放入10-12%氢氧化钠溶液中浸泡5-7小时,过滤取出,去离子水洗涤,烘干,再与其它剩余原料混合均匀后,即得。
2.根据权利要求1所述的一种含有陶瓷纤维的不易开裂的粉煤灰砖,其特征在于:
制备方法为:
(1)将铝酸钙水泥、粉煤灰、煤矸石粉、石膏按重量份混匀,再加入适量水,于100-200转/分下搅拌20-30分钟,再与其余原料混匀,再加入适量水,浇筑入模成型,后在40-50℃下预养3-5小时,脱模,切割,得砌块坯;
(2)将砌块坯放入反应釜中蒸压养护14-16小时,入库成品即得。