CN103896519A - 外墙复合保温砂浆 - Google Patents

外墙复合保温砂浆 Download PDF

Info

Publication number
CN103896519A
CN103896519A CN201210584453.4A CN201210584453A CN103896519A CN 103896519 A CN103896519 A CN 103896519A CN 201210584453 A CN201210584453 A CN 201210584453A CN 103896519 A CN103896519 A CN 103896519A
Authority
CN
China
Prior art keywords
parts
mortar
insulation mortar
cement
thermal insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210584453.4A
Other languages
English (en)
Inventor
陈昊
Original Assignee
陈昊
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陈昊 filed Critical 陈昊
Priority to CN201210584453.4A priority Critical patent/CN103896519A/zh
Publication of CN103896519A publication Critical patent/CN103896519A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种外墙复合保温砂浆,按重量百分比计,所述保温砂浆的各个组分的含量为:水泥60-80份、树脂型可再分散乳胶粉0.25-0.35份、冷水型聚乙烯醇0.6-0.9份、羟丙基甲基纤维素醚0.1-0.2份、引气剂0.01-0.03份、水玻璃0.06-0.1份、无机缓凝剂0.005-0.01份、聚苯颗粒8-13份、玻化微珠30-50份、混凝土防水剂0.2-0.5份。该发明的优点是具有较强的保温效果,施工结束后不易开鼓、脱落又能有效防水防火。

Description

外墙复合保温砂浆
技术领域
[0001] 本发明涉及一种建筑材料,特别涉及一种外墙保温砂浆。
背景技术
[0002]目前国内、外建筑墙体保温一般采用板材或者构件保温隔热材料,价格高、施工技术难度大、抗冲击能力差,但保温效果好,适应寒冷地区;目前还存在另一种保温材料,即胶粉聚苯颗粒外墙外保温体系,该保温体系由界面层、保温隔热层、抗裂防护层组成,起保温隔热、防护的作用。现有技术中的胶粉聚苯颗粒外墙外保温体系的各层都存在水泥,但是由于水泥是水硬性材料,与水化合物形成水泥石,一般需28天才能达到设计强度,过早脱水,水化停止,强度即不再上升,含水泥材料是用水拌和的塑性材料,体积随着水分的蒸发而收缩,在收缩过程中,含水泥材料若还没有强度或强度很低,收缩应力大于材料的抗张力,收缩量就会表现为比较集中的大裂缝,而且存在由于温度变化导致膨胀、收缩而产生裂缝的问题;其次现有技术的胶粉聚苯颗粒外墙外保温体系的抗渗、防水能力较差,而如果抗渗、防水性能差,被雨雪淋湿或在潮湿空气环境中容易受潮,比如在我国华东地区等空气湿度高的地区,从而在保温隔热层的空隙中形成水汽,热能就会通过水汽传导,削弱保温隔热层的保温节能效果;另外,现有的胶粉聚苯颗粒外墙外保温体系具有刚性的特点,因而容易造成因温度应力或其他外力产生的冲击、膨胀或收缩等脆性破坏;再次,现有的胶粉聚苯颗粒外墙外保温体系具有粘结强度低,抗冲击、抗压强度低的缺点,并且在夏热冬冷地区由于温差效应,在界面层容易产生局部的空鼓、脱落等现象。
[0003] 中国专利CN201010167784.9公开了一种具有多晶体保温砂浆的保温系统,包括以下组分:水泥、可再分散 乳胶粉、冷水型聚乙烯醇、羟丙基甲基纤维素醚、引气剂、水玻璃、无机缓凝剂和聚苯颗粒。与现有技术相比,该技术方案具有以下优点:1、改善无机胶凝材料渗透握裹力不足的缺陷;使整个保温系统的粘结、抗压强度显著提高。2、改善材料施工性能,提高系统保温效果。3、改善施工性能、增强产品后期强度。4、使系统的防水功能得以改善;并使各种多晶体砂浆性刚性变为柔性,提高保温系统的抗冲击、抗折、抗拉伸、收缩等应变能力。5、改善材料抗折、抗拉伸能力提高系统的物理抗裂性能。但是,其功能还稍显单一,其保温功能仍不够明显,防水防火功能不佳,对施工条件有较多的限制,难于广泛推广。
发明内容
[0004] 本发明是为了克服上述不足,提供一种具有较强的保温效果,施工结束后不易开鼓、脱落又能有效防水防火的复合保温砂浆。
[0005] 为了解决上述技术问题,本发明通过以下技术方案予以实现:一种外墙复合保温砂浆,按重量百分比计,所述保温砂浆的各个组分的含量为:水泥60-80份、树脂型可再分散乳胶粉0.25-0.35份、冷水型聚乙烯醇0.6-0.9份、羟丙基甲基纤维素醚0.1-0.2份、弓丨气剂0.01-0.03份、水玻璃0.06-0.1份、无机缓凝剂0.005-0.01份、聚苯颗粒8_13份、玻化微珠30-50份、混凝土防水剂0.2-0.5份。[0006] 本发明的最优选方案是:按重量百分比计,所述保温砂浆的各个组分的含量为:水泥65份、树脂型可再分散乳胶粉0.32份、冷水型聚乙烯醇0.85份、羟丙基甲基纤维素醚
0.18份、引气剂0.025份、水玻璃0.08份、无机缓凝剂0.008份、聚苯颗粒12份、玻化微珠32份、混凝土防水剂0.24份。
[0007]本发明通过树脂型可在再分散胶粉与水泥等发生胶凝反应,生成新的胶凝物,新的胶凝物具有较强的可持续性保持和平衡水气的能力,可保持砂浆后期粘结强度的稳定和不断增长其强度,能平衡砂浆中的水汽含量,防止渗漏水和墙体水气聚集、结露,有效控制和降低水泥的干缩性,增加塑性,防止出项包聚、空鼓、脱落。新的胶凝物可渗入玻化微珠浅表空腔毛细孔内,对玻化微珠进行包覆,连接各颗粒形成强度较高,比较致密的,稳定性更好的保温隔热层,提高玻化微珠的抗压强度,耐水性,降低吸水性,同时达到防火的目的。本发明中加入的羟丙基甲基纤维素醚是一种高吸水性、高保水性的多链高分子聚合物,其在砂浆搅拌中2-3分钟内迅速起糊形成高粘稠性的膜,能有效的阻止砂浆的分层离析、泌水,改善各种浆料的施工性能;也可使砂浆充分保持水份,让水泥充分水化并有效的得到养护,提高砂浆成型后的强度;羟丙基甲基纤维素醚起糊后,使砂浆内大量的引入微气泡。这样,因冻融循环导致砂浆膨胀收缩而破坏的游离水,可进入这些微气泡中,从而降低早期冻融破坏;另外,因温度变化而产生的膨胀、收缩应力向微气泡扩散得到有效的缓冲,从而减少裂缝的产生;引气剂为有机活性激活材料,能提高系统保温效果,并起到改善材料施工性能的作用。
具体实施方式
[0008] 下面通过实施例对本发明做进一步说明:
实施例1:称取水泥60KG、树脂型可再分散乳胶粉0.25KG、冷水型聚乙烯醇0.6KG、羟丙基甲基纤维素醚0.1KG、引气剂0.01KG、水玻璃0.06KG、无机缓凝剂0.005KG、聚苯颗粒8KG、玻化微珠30 KG、混凝土防水剂0.2KG,按常规保温砂浆生产工艺进行生产,即得。常温常压下,加水搅拌至适当稠度,用于墙体。
[0009] 实施例2:称取水泥80KG、树脂型可再分散乳胶粉0.35KG、冷水型聚乙烯醇0.9KG、羟丙基甲基纤维素醚0.2KG、引气剂0.03KG、水玻璃0.1KG、无机缓凝剂0.01KG、聚苯颗粒13KG、玻化微珠50 KG、混凝土防水剂0.5 KG,按常规保温砂浆生产工艺进行生产,即得。常温常压下,加水搅拌至适当稠度,用于墙体。
[0010] 需要指出的是,上述实施例虽对本发明作了比较详细的文字描述,但这些文字描述只是对本发明设计思路的简单描述,而不是对本发明思路的限制。任何不超过本发明设计思路的组合、增加或修改,均落入本发明的保护范围内。

Claims (2)

1.一种外墙复合保温砂浆,其特征在于按重量百分比计,所述保温砂浆的各个组分的含量为:水泥60-80份、树脂型可再分散乳胶粉0.25-0.35份、冷水型聚乙烯醇0.6-0.9份、羟丙基甲基纤维素醚0.1-0.2份、引气剂0.01-0.03份、水玻璃0.06-0.1份、无机缓凝剂.0.005-0.01份、聚苯颗粒8-13份、玻化微珠30-50份、混凝土防水剂0.2-0.5份。
2.根据权利要求1所述的外墙复合保温砂浆,其特征在于按重量百分比计,所述保温砂浆的各个组分的含量为:水泥65份、树脂型可再分散乳胶粉0.32份、冷水型聚乙烯醇.0.85份、羟丙基甲基纤维素醚0.18份、引气剂0.025份、水玻璃0.08份、无机缓凝剂0.008份、聚苯颗粒12份、玻化 微珠32份、混凝土防水剂0.24份。
CN201210584453.4A 2012-12-30 2012-12-30 外墙复合保温砂浆 Pending CN103896519A (zh)