CN103834270A - 一种净味清香紫外光固化木器漆及其制备方法 - Google Patents

一种净味清香紫外光固化木器漆及其制备方法 Download PDF

Info

Publication number
CN103834270A
CN103834270A CN201410075426.3A CN201410075426A CN103834270A CN 103834270 A CN103834270 A CN 103834270A CN 201410075426 A CN201410075426 A CN 201410075426A CN 103834270 A CN103834270 A CN 103834270A
Authority
CN
China
Prior art keywords
parts
acrylate
wood lacquer
minute
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410075426.3A
Other languages
English (en)
Inventor
汤广顺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Edison Automation Equipment Co Ltd
Original Assignee
Wuhu Edison Automation Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Edison Automation Equipment Co Ltd filed Critical Wuhu Edison Automation Equipment Co Ltd
Priority to CN201410075426.3A priority Critical patent/CN103834270A/zh
Publication of CN103834270A publication Critical patent/CN103834270A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种净味清香紫外光固化木器漆，其特征在于，由下列重量份的原料制备制成：环氧丙烯酸酯30-34、脂肪族聚氨酯丙烯酸酯20-23、双季戊四醇六丙烯酸酯9-12、聚乙二醇二甲基丙烯酸酯6-9、光引发剂11733-4、二缩三丙二醇二丙烯酸酯13-16、乙二醇而缩水甘油醚9-12、聚二甲基硅氧烷1-2、硅烷偶联剂KH5501-2、锆英粉3-4、白土3-4、柠檬精油1-2、助剂4-5；本发明添加柠檬精油使涂料具有清新的香味，安全无毒；添加助剂，流平性好，可形成均匀的涂层，遮盖能力好，固化速度快，制成的涂料附着力良好，耐磨耐污，适合木器使用。

Description

一种净味清香紫外光固化木器漆及其制备方法
技术领域
本发明涉及一种涂料及其制备方法，特别是一种净味清香紫外光固化木器漆及其制备方法。
背景技术
UV固化涂料已经成为较为成熟的技术，特别是随着人们环保意识的提高，生产和研究人员更加注意UV固化涂料的开发和应用。UV固化涂料是一种绿色环保型涂料，它完全符合“4E”原则，一般UV固化能耗为热固化的1/5，且UV固化涂料含挥发组分较少，污染小，最吸引研究人员和开发商的是UV固化涂料能减少原材料消耗，有利于降低经济成本。
目前的UV固化材料各种各样，但是还是不同程度的存在着一些问题，现有的UV固化涂料经光固化后收缩率大、产生收缩应力, 导致涂膜性脆、附着力和耐冲击力差、以及涂膜的柔韧性差和硬度低、不耐腐蚀、易黄变老化等缺点，这一系列问题都需要针对不同的用途继续改良，降低生产成本，扩大用途。
发明内容
本发明的目的是提供一种净味清香紫外光固化木器漆及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种净味清香紫外光固化木器漆，由下列重量份的原料制备制成：环氧丙烯酸酯30-34、脂肪族聚氨酯丙烯酸酯20-23、双季戊四醇六丙烯酸酯9-12、聚乙二醇二甲基丙烯酸酯6-9、光引发剂1173 3-4、二缩三丙二醇二丙烯酸酯13-16、乙二醇而缩水甘油醚9-12、聚二甲基硅氧烷1-2、硅烷偶联剂KH550 1-2、锆英粉3-4、白土3-4、柠檬精油1-2、助剂4-5；
所述助剂由下列重量份的原料制成：重晶石10-13、竹炭5-7、纳米二氧化硅5-7、环氧大豆油1-2、柠檬精油0.1-0.2、月桂酸甲基丙烯酸酯4-6、丙烯酸羟乙酯3-5、硅烷偶联剂KH560 2-3、甲基丙烯酸羟乙酯20-24；制备方法是将重晶石放入煅烧炉中在520-540℃下煅烧3-4小时，取出，与竹炭、纳米二氧化硅一起粉碎成50-100目的混合粉末；将其余剩余成分混合，加热至50-60℃，搅拌30-45分钟后加入混合粉末，保温研磨1-1.5小时，即得。
本发明所述一种净味清香紫外光固化木器漆，由以下具体步骤制成：
（1）将环氧丙烯酸酯、脂肪族聚氨酯丙烯酸酯、双季戊四醇六丙烯酸酯、聚乙二醇二甲基丙烯酸酯放入反应釜中搅拌，加热至75-85℃，搅拌15-20分钟；
（2）加入除光引发剂1173之外的其余剩余成分，继续搅拌反应30-40分钟，使之分散均匀；
（3）最后降温至45-55℃，加入光引发剂1173，搅拌反应20-25分钟，冷却后，研磨得到20-40μm浆料，即得。
本发明的有益效果是：本发明添加柠檬精油使涂料具有清新的香味，安全无毒；添加助剂，流平性好，可形成均匀的涂层，遮盖能力好，固化速度快，制成的涂料附着力良好，耐磨耐污，适合木器使用。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种净味清香紫外光固化木器漆，由下列重量份（公斤）的原料制备制成：环氧丙烯酸酯30、脂肪族聚氨酯丙烯酸酯20、双季戊四醇六丙烯酸酯9、聚乙二醇二甲基丙烯酸酯6、光引发剂1173 3、二缩三丙二醇二丙烯酸酯13、乙二醇而缩水甘油醚9、聚二甲基硅氧烷1、硅烷偶联剂KH550 1、锆英粉3、白土3、柠檬精油1、助剂4；
所述助剂由下列重量份（公斤）的原料制成：重晶石10、竹炭5、纳米二氧化硅5、环氧大豆油1、柠檬精油0.1、月桂酸甲基丙烯酸酯4、丙烯酸羟乙酯3、硅烷偶联剂KH560 2、甲基丙烯酸羟乙酯20；制备方法是将重晶石放入煅烧炉中在520-540℃下煅烧3-4小时，取出，与竹炭、纳米二氧化硅一起粉碎成50-100目的混合粉末；将其余剩余成分混合，加热至50-60℃，搅拌30-45分钟后加入混合粉末，保温研磨1-1.5小时，即得。
本发明所述一种净味清香紫外光固化木器漆，由以下具体步骤制成：
（1）将环氧丙烯酸酯、脂肪族聚氨酯丙烯酸酯、双季戊四醇六丙烯酸酯、聚乙二醇二甲基丙烯酸酯放入反应釜中搅拌，加热至75-85℃，搅拌15-20分钟；
（2）加入除光引发剂1173之外的其余剩余成分，继续搅拌反应30-40分钟，使之分散均匀；
（3）最后降温至45-55℃，加入光引发剂1173，搅拌反应20-25分钟，冷却后，研磨得到20-40μm浆料，即得。
该涂料可以采用滚涂、喷涂的施工方式进行施工。按以上方案制得的涂料涂装在木板上附着力都好于二级，耐75％乙醇24 小时以上，耐碱24小时以上、耐酸48小时以上，耐受零下40 度和40度的冷热循环10 次不发生开裂，耐15％食盐水60 小时以上，硬度可在2H 到3H 间调节，耐磨指数在4000转以上。

Claims (2)

1.一种净味清香紫外光固化木器漆，其特征在于，由下列重量份的原料制备制成：环氧丙烯酸酯30-34、脂肪族聚氨酯丙烯酸酯20-23、双季戊四醇六丙烯酸酯9-12、聚乙二醇二甲基丙烯酸酯6-9、光引发剂1173 3-4、二缩三丙二醇二丙烯酸酯13-16、乙二醇而缩水甘油醚9-12、聚二甲基硅氧烷1-2、硅烷偶联剂KH550 1-2、锆英粉3-4、白土3-4、柠檬精油1-2、助剂4-5；
所述助剂由下列重量份的原料制成：重晶石10-13、竹炭5-7、纳米二氧化硅5-7、环氧大豆油1-2、柠檬精油0.1-0.2、月桂酸甲基丙烯酸酯4-6、丙烯酸羟乙酯3-5、硅烷偶联剂KH560 2-3、甲基丙烯酸羟乙酯20-24；制备方法是将重晶石放入煅烧炉中在520-540℃下煅烧3-4小时，取出，与竹炭、纳米二氧化硅一起粉碎成50-100目的混合粉末；将其余剩余成分混合，加热至50-60℃，搅拌30-45分钟后加入混合粉末，保温研磨1-1.5小时，即得。
2.根据权利要求1所述一种净味清香紫外光固化木器漆，其特征在于，由以下具体步骤制成：
（1）将环氧丙烯酸酯、脂肪族聚氨酯丙烯酸酯、双季戊四醇六丙烯酸酯、聚乙二醇二甲基丙烯酸酯放入反应釜中搅拌，加热至75-85℃，搅拌15-20分钟；
（2）加入除光引发剂1173之外的其余剩余成分，继续搅拌反应30-40分钟，使之分散均匀；
（3）最后降温至45-55℃，加入光引发剂1173，搅拌反应20-25分钟，冷却后，研磨得到20-40μm浆料，即得。
CN201410075426.3A 2014-03-04 2014-03-04 一种净味清香紫外光固化木器漆及其制备方法 Pending CN103834270A (zh)