CN103788540A - Uvioresistant PVC (Polyvinyl Chloride) fastening plate for outdoor use - Google Patents

Uvioresistant PVC (Polyvinyl Chloride) fastening plate for outdoor use Download PDF

Info

Publication number
CN103788540A
CN103788540A CN201410014894.XA CN201410014894A CN103788540A CN 103788540 A CN103788540 A CN 103788540A CN 201410014894 A CN201410014894 A CN 201410014894A CN 103788540 A CN103788540 A CN 103788540A
Authority
CN
China
Prior art keywords
parts
raw material
fastening plate
pvc
uvioresistant
Prior art date
Application number
CN201410014894.XA
Other languages
Chinese (zh)
Inventor
胡其飞
Original Assignee
安庆市吉美装饰材料有限责任公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 安庆市吉美装饰材料有限责任公司 filed Critical 安庆市吉美装饰材料有限责任公司
Priority to CN201410014894.XA priority Critical patent/CN103788540A/en
Publication of CN103788540A publication Critical patent/CN103788540A/en

Abstract

The invention discloses an uvioresistant PVC (Polyvinyl Chloride) fastening plate for outdoor use. The uvioresistant PVC fastening plate for outdoor use comprises the following raw materials in parts by weight: 94-100 parts of PVC resin, 1-2 parts of dodecyl dimethyl benzyl ammonium oxide, 4-5 parts of calcium stearate, 1-2 parts of mannitol, 0.2-0.4 part of dioctyldilauryltin, 7-10 parts of nanocarbon powder, 0.6-1 part of polyvinylpyrrolidone, 2-5 parts of medical stone powder, 5-7 parts of polytetrafluoroethylene fiber, 2-3 parts of bisphenol A phosphate ester, 3-5 parts of triglycol dioctate, 1-2 parts of 2-hydroxy-4-methoxybenzophenone and 10-15 parts of modified accessory ingredient. The fastening plate is good in uvioresistant effect, long in sunlight-resisting time, excellent in temperature deformation resistance, especially applicable to outdoor buildings, long in service life and excellent in safety.

Description

A kind of outdoor uvioresistant pvc buckle

Technical field

The present invention relates generally to a kind of plate, relates in particular to a kind of outdoor uvioresistant pvc buckle.

Background technology

PVC cover plate ceiling material, is take polyvinyl chloride (PVC) RESINS as base-material, adds the auxiliary agents such as a certain amount of antiaging agent, properties-correcting agent, makes through techniques such as mixing, calendering, vacuum formings.This PVC cover plate ceiling is specially adapted to the ceiling decoration of kitchen, toilet, have that quality is light, moisture proof, heat-insulation and heat-preservation, nonflammable, not dust suction, easy to clean, can cover with paint, lacquer, colour wash, etc., easily install, the advantage such as price is low.

Summary of the invention

The object of the invention is exactly for a kind of outdoor uvioresistant pvc buckle is provided.

The present invention is achieved by the following technical solutions:

A kind of outdoor uvioresistant pvc buckle, it is made up of the raw material of following weight parts:

Pvc resin 94-100, dodecyl dimethyl benzyl ammonium oxide 1-2, calcium stearate 4-5, N.F,USP MANNITOL 1-2, Bis(lauroyloxy)dioctyltin 0.2-0.4, nano-carbon powder 7-10, polyvinylpyrrolidone 0.6-1, medical stone powder 2-5, polytetrafluoroethylene fiber 5-7, phosphorous acid dihydroxyphenyl propane ester 2-3, triethylene glycol two 2-ethylhexoate 3-5, ESCALOL 567 1-2, modified additive 10-15;

Described modified additive is made up of the raw material of following weight parts:

Polydicyclopentadiene 30-40, high boron lime borate 10-14, aluminium nitride 3-4, barium stearate 3-5, perfluoro butyl potassium sulfonate 0.4-1,1-hydroxyethyl-2-oil-based imidazoline 0.1-0.2, polypropylene adipate (PPA) 2-3;

Above-mentioned polydicyclopentadiene is heated to 20-30 minute at 200-220 ℃, discharging is cooling, add aluminium nitride, be uniformly mixed rear ball milling even, add barium stearate, polypropylene adipate (PPA), insulated and stirred 4-7 minute at 40-50 ℃, add the each raw material of residue, 100-200 rev/min of dispersed with stirring 3-5 minute is dry, cross 80-120 mesh sieve, obtain described modified additive.

A preparation method for outdoor uvioresistant pvc buckle, comprises the following steps:

Each raw material is mixed to rear extrusion moulding, obtain described outdoor uvioresistant pvc buckle.

Advantage of the present invention is:

Buckle of the present invention has good uvioresistant effect, sun-resistant of long duration, and temperature-change resistance is good, is specially adapted to outdoor building use, long service life, and security is good.

Embodiment

Embodiment 1

A kind of outdoor uvioresistant pvc buckle, it by following weight parts (kilogram) raw material form:

Pvc resin 100, dodecyl dimethyl benzyl ammonium oxide 2, calcium stearate 5, N.F,USP MANNITOL 2, Bis(lauroyloxy)dioctyltin 0.4, nano-carbon powder 10, polyvinylpyrrolidone 0.6, medical stone powder 2, polytetrafluoroethylene fiber 7, phosphorous acid dihydroxyphenyl propane ester 3, triethylene glycol two 2-ethylhexoates 3, ESCALOL 567 1, modified additive 15;

Described modified additive is made up of the raw material of following weight parts:

Polydicyclopentadiene 40, high boron lime borate 14, aluminium nitride 4, barium stearate 5, perfluoro butyl potassium sulfonate 0.4,1-hydroxyethyl-2-oil-based imidazoline 0.2, polypropylene adipate (PPA) 2;

Above-mentioned polydicyclopentadiene is heated 30 minutes at 220 ℃, discharging is cooling, add aluminium nitride, be uniformly mixed rear ball milling even, add barium stearate, polypropylene adipate (PPA), insulated and stirred 4 minutes at 50 ℃, add the each raw material of residue, 200 revs/min of dispersed with stirring 5 minutes, dry, cross 120 mesh sieves, obtain described modified additive.

A preparation method for outdoor uvioresistant pvc buckle, comprises the following steps:

Above-mentioned each raw material is mixed to rear extrusion moulding, obtain described outdoor uvioresistant pvc buckle.

MOR: 24.9MPa;

Shao Er hardness (a): >=55;

Falling ball impact test at low temperature crack-free.

Claims (2)

1. an outdoor uvioresistant pvc buckle, is characterized in that what it was made up of the raw material of following weight parts:
Pvc resin 94-100, dodecyl dimethyl benzyl ammonium oxide 1-2, calcium stearate 4-5, N.F,USP MANNITOL 1-2, Bis(lauroyloxy)dioctyltin 0.2-0.4, nano-carbon powder 7-10, polyvinylpyrrolidone 0.6-1, medical stone powder 2-5, polytetrafluoroethylene fiber 5-7, phosphorous acid dihydroxyphenyl propane ester 2-3, triethylene glycol two 2-ethylhexoate 3-5, ESCALOL 567 1-2, modified additive 10-15;
Described modified additive is made up of the raw material of following weight parts:
Polydicyclopentadiene 30-40, high boron lime borate 10-14, aluminium nitride 3-4, barium stearate 3-5, perfluoro butyl potassium sulfonate 0.4-1,1-hydroxyethyl-2-oil-based imidazoline 0.1-0.2, polypropylene adipate (PPA) 2-3;
Above-mentioned polydicyclopentadiene is heated to 20-30 minute at 200-220 ℃, discharging is cooling, add aluminium nitride, be uniformly mixed rear ball milling even, add barium stearate, polypropylene adipate (PPA), insulated and stirred 4-7 minute at 40-50 ℃, add the each raw material of residue, 100-200 rev/min of dispersed with stirring 3-5 minute is dry, cross 80-120 mesh sieve, obtain described modified additive.
2. a preparation method for outdoor uvioresistant pvc buckle as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned each raw material is mixed, mix rear extrusion moulding, obtain described outdoor uvioresistant pvc buckle.
CN201410014894.XA 2014-01-14 2014-01-14 Uvioresistant PVC (Polyvinyl Chloride) fastening plate for outdoor use CN103788540A (en)