CN103787686B - 一种碳纤维复合球及其制备方法 - Google Patents
一种碳纤维复合球及其制备方法 Download PDFInfo
- Publication number
- CN103787686B CN103787686B CN201410037826.5A CN201410037826A CN103787686B CN 103787686 B CN103787686 B CN 103787686B CN 201410037826 A CN201410037826 A CN 201410037826A CN 103787686 B CN103787686 B CN 103787686B
- Authority
- CN
- China
- Prior art keywords
- carbon fiber
- ball
- preparation
- carbon
- round
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种碳纤维复合球及其制备方法。一种碳纤维复合球,由硬质碳纤维球和硬质碳纤维球表面覆盖的树脂炭层构成。一种碳纤维复合球的制备方法,由纤维破碎混合、滚圆造粒、二次滚圆造粒、固化、炭化和石墨化步骤制备而成。本发明具有以下特点:使短切碳纤维或磨碎碳纤维定型,方便运输和使用;高炭纤维含量成球,提供了发达的孔隙结构,可以被应用于吸附、保温、相变储能载体等方面,扩展了短切炭纤维的应用领域;其制备工艺相对简单,尤其是相对硬质碳纤维保温毡,更适合大规模连续化生产。
Description
技术领域
本发明涉及一种碳纤维复合球及其制备方法。
背景技术
碳纤维具有优良的力学性能、耐酸碱性能、抗高温性能以及优异的摩擦性能等,同时碳纤维也具有表面惰性、抗折和抗压强度低等缺点,尤其是采用短切碳纤维进行下游应用时,极易成团造成分散不均,也容易因其尖锐的断口造成对操作和使用人员的物理伤害。目前,随着碳纤维行业的蓬勃发展,短切和磨碎碳纤维作为低成本副产品得到了更为丰富的生产。
例如,高温工业炉的保温材料,采用粉末碳纤维直接填充,具有形状自由度大,可以根据消耗情况按需补充使用经济性好的特点,但是由于操作的不便和粉尘扬灰问题无法在工业炉中实际使用。
同时,碳纤维应用于保温、吸附等领域,一般以毡、布、纸、绳等产品形式而存在,但相关产品制备工序复杂,价格相对较高,一定程度上限制了其应用范围,以某种形式进行定型,并防止尖锐的碳纤维及其碎片飞散,则被更为广泛的应用领域所接受。
如专利申请号95108742.8,专利ZL 01130477.4采用碳纤维和其它纤维混杂增强制备了性能较好的盘式制动衬片,其混合工艺即采用混合设备直接混合碳纤维和其它物料,碳纤维的添加比例严重受制于其分散特性。文献“张西奎,等.炭纤维含量对摩擦材料性能的影响[J].机械工程材料,2003,27(7):49-51”对干法制备炭纤维摩擦材料中炭纤维含量作系列研究认为5%的含量比较合适,这是基于炭纤维含量增加后分散不均,摩擦系数偏低、高温欠稳定等现象而做出的选择。
发明内容
本发明的目的是提供一种碳纤维复合球及其制备方法,解决了现有技术中碳纤维复合球难分散易成团、易掉尖锐纤维、不便成型等技术难点。具有易成型、不掉渣、消除尖锐碳纤维碎片、易分散、密度和孔隙率可设计等优点,
为实现以上目的,本发明采用了以下技术方案:
一种碳纤维复合球,由碳纤维原料球和碳纤维原料球表面覆盖的树脂炭层构成。
所述碳纤维原料球直径为0.5-10mm,密度为0.1-0.7g/cm3;所述树脂炭层厚度为0.01-2mm。
上述一种碳纤维复合球的制备方法,其特征在于包括以下步骤:
(1)纤维破碎混合:100份长度3-10mm的短切碳纤维,添加0.1-20份树脂粉末和0.1-10份长度3-5mm有机纤维,破碎并混合,获得纤维长度小于3mm的破碎混合料;
(2)滚圆造粒:100份所述的破碎混合料,添加3-20份浓度5-30%的液体粘结剂,滚圆包覆成球,筛分,获得直径0.5-10mm的碳纤维原料球;
(3)二次滚圆造粒:将所述的100份碳纤维原料球,均匀喷洒5-50份浓度5-30%的热固性树脂,热固性树脂吸附完全后,再依此加入0.1-20份200目以下沥青粉和0.1-20份200目以下微细碳粉,滚圆并筛除多余粉末,获得碳纤维二次加工原料球;
(4)固化:将碳纤维二次加工原料球置于100℃-300℃空气气氛中固化2-10hr,获得碳纤维固化球;
(5)炭化:将碳纤维固化球置于600-1100℃氮气气氛中炭化1-180min,获得碳纤维炭化球;
(6)石墨化:将碳纤维炭化球置于1500-2200℃氩气气氛中石墨化1-60min,获得碳纤维复合球。
步骤(1)所述的树脂粉末是200目以下丁腈橡胶粉末、酚醛树脂粉末或沥青粉末的一种或多种混合。
步骤(1)所述的有机纤维是预氧化纤维、聚乙烯醇纤维或粘胶纤维的一种或多种混合。有机纤维的加入对辅助成球、辅助粘结和控制密度具有非常好的效果,优选聚乙烯醇纤维。
步骤(2)所述的液体粘结剂是酚醛树脂乳液或溶液、环氧树脂乳液或溶液、聚乙烯醇水溶液或聚丙烯酰胺水溶液的一种或多种混合液。优选聚丙烯酰胺水溶液。
步骤(3)所述的热固性树脂是环氧树脂、酚醛树脂、糠醛树脂的一种或多种混合物;所述的微细碳粉为炭黑、石墨粉、鳞片石墨、磨碎碳纤维、石墨烯、碳纳米管中的一种或多种混合物;所述的沥青粉软化点高于200℃。
步骤(1)中,超过3mm的纤维易成团,不利于后续工艺,炭纤维的长度及其长度分布对最终碳纤维复合球的直径大小和密度等参数有着至关重要的影响,这也是不便直接采用一定长度短切碳纤维直接进行下一步工序的原因。
实现以上工艺所用设备可以是多种形式市售定型设备,无需专门开发。
与现有工艺和产品相比,本发明所具有以下有益效果:
(1)使短切碳纤维或磨碎碳纤维定型,方便运输和使用。
(2)高炭纤维含量成球,提供了发达的孔隙结构,可以被应用于吸附、保温、相变储能载体等方面,扩展了短切炭纤维的应用领域。
(3)其制备工艺相对简单,尤其是相对硬质碳纤维保温毡,更适合大规模连续化生产。
本发明基于低成本化和实用性,解决短切碳纤维在复合材料中的分散,解决碳纤维吸附材料在使用过程中的掉渣问题,并更有效的扩大短切碳纤维的应用,获得一种可以更方便使用且更经济的复合材料。
这种新型碳纤维成型复合球具有非常广泛的应用空间,除可直接应用于不定形高温保温料、水质净化生物膜、相变储能材料载体,还可通过进一步活化应用于吸附领域,也可作为增强材料进一步的复合制成复合材料,尤其是作为刹车片的摩擦颗粒。
附图说明
图1为本发明实施例示意图。
1-树脂炭层,2-碳纤维原料球。
具体实施方式
下面,结合本发明实施例,对本发明作进一步说明。
实施例一:
(1)纤维破碎混合:100份长度为3mm的短切碳纤维,添加10份软化点280℃沥青粉末,7份长度3mm的聚乙烯醇纤维,破碎并混合,获得纤维长度0.06-1.5mm的破碎混合料;
(2)滚圆造粒:取100份破碎混合料,添加10份浓度5%的液体粘结剂,滚圆包覆成球,筛分,获得直径1.7-2.36mm碳纤维原料球;
(3)二次滚圆造粒:取100份碳纤维原料球,均匀喷洒20份浓度15%的热固性树脂,热固性树脂吸附完全后,再依此加入5份200目沥青粉和10份200目焦粉,滚圆并筛除多余粉末,获得碳纤维二次加工原料球;
(4)固化:220℃空气气氛中固化2hr;
(5)炭化:850℃氮气气氛中炭化30min;
(6)石墨化:2200℃氩气气氛中石墨化30min。
获得表面包覆树脂炭层1为0.2-0.3mm厚,直径1.5-2mm的碳纤维复合球,密度0.16g/cm3。
采用以上碳纤维复合球,直接填充于直径1m的高温炉隔热层,填充厚度为60mm,填充密度为0.13g/cm3,测得1500℃对应导热系数为0.43W/M/K。
实施例二:
(1)纤维破碎混合:100份10mm短切碳纤维,添加10份丁腈橡胶粉末,7份10mm预氧化纤维,破碎并混合,获得纤维长度0.08-2.7mm的破碎混合料;
(2)滚圆造粒:取100份破碎混合料,添加20份浓度10%的液体粘结剂,滚圆包覆成球,筛分,获得直径2-3.35mm碳纤维原料球;
(3)二次滚圆造粒:取100份碳纤维原料球,均匀喷洒45份浓度20%的热固性树脂,热固性树脂吸附完全后,再依此加入10份200目沥青粉,加入15份炭黑,滚圆并筛除多余粉末;
(4)固化:200℃空气气氛中固化4hr;
(5)炭化:800℃氮气气氛中炭化30min;
(6)石墨化:2200℃氩气气氛中石墨化30min。
获得表面包覆树脂炭层1为0.5-0.7mm厚,直径2-3.6mm的碳纤维复合球,密度0.33g/cm3。
采用10%浓度的热塑性酚醛树脂溶液均匀喷洒在所制得的碳纤维复合球表面,喷洒量控制在30ml/kg,然后与混合好的刹车片粉体纤维按12:100的质量比混合均匀。热压成型,与涂有粘结剂的钢背一起采用桑塔纳2000专用模具冲压,上模具温度为165℃,下模具温度为170℃,成型压力20MPa,成型时间60s/mm,脱模,经200℃4hr热处理,缓慢冷却,再经适当打磨(1.5mm厚)、喷涂,所得小型轿车刹车片经定速摩擦实验检验合格。
实施例三:
(1)纤维破碎混合:100份长度为10mm的短切碳纤维,添加2份酚醛树脂粉末,10份长度3mm的聚乙烯醇纤维,破碎并混合,获得纤维长度0.05-3mm的破碎混合料;
(2)滚圆造粒:取100份破碎混合料,添加10份浓度5%的液体粘结剂,滚圆包覆成球,筛分,获得直径2.5-3.5mm碳纤维原料球;
(3)二次滚圆造粒:取10份碳纤维原料球,均匀喷洒2份浓度5%的热固性树脂,树脂吸附完全后,再依此加入0.3份200目软化点200℃沥青粉和0.5份200目石墨粉,滚圆并筛除多余粉末。
(4)固化:220℃空气气氛中固化2hr;
(5)炭化:800℃氮气气氛中炭化30min;
(6)石墨化:2200℃氩气气氛中石墨化30min。
获得表面包覆树脂炭层1为0.1mm厚,直径2.5-3mm的碳纤维复合球,密度0.17g/cm3。
将石墨化后的碳纤维复合球于950℃水蒸气中活化10min,获得比表面积>2500m2/g,微孔平均直径1.85nm的超高比表面积活性碳纤维球。
Claims (8)
1.一种碳纤维复合球的制备方法,其特征在于包括以下步骤:
(1)纤维破碎混合:100份长度3-10mm的短切碳纤维,添加0.1-20份树脂粉末和0.1-10份长度3-5mm有机纤维,破碎并混合,获得纤维长度小于3mm的破碎混合料;
(2)滚圆造粒:100份所述的破碎混合料,添加3-20份浓度5-30%的液体粘结剂,滚圆包覆成球,筛分,获得直径0.5-10mm的碳纤维原料球;
(3)二次滚圆造粒:将所述的100份碳纤维原料球,均匀喷洒5-50份浓度5-30%的热固性树脂,热固性树脂吸附完全后,再依此加入0.1-20份200目以下沥青粉和0.1-20份200目以下微细碳粉,滚圆并筛除多余粉末,获得碳纤维二次加工原料球;
(4)固化:将碳纤维二次加工原料球置于100℃-300℃空气气氛中固化2-10hr,获得碳纤维固化球;
(5)炭化:将碳纤维固化球置于600-1100℃氮气气氛中炭化1-180min,获得碳纤维炭化球;
(6)石墨化:将碳纤维炭化球置于1500-2200℃氩气气氛中石墨化1-60min,获得碳纤维复合球。
2.根据权利要求1所述的一种碳纤维复合球的制备方法,其特征在于:步骤(1)所述的树脂粉末是200目以下丁腈橡胶粉末、酚醛树脂粉末或沥青粉末的一种或多种混合。
3.根据权利要求1所述的一种碳纤维复合球的制备方法,其特征在于:步骤(1)所述的有机纤维是预氧化纤维、聚乙烯醇纤维或粘胶纤维的一种或多种混合。
4.根据权利要求1所述的一种碳纤维复合球的制备方法,其特征在于:步骤(2)所述的液体粘结剂是酚醛树脂乳液或溶液、环氧树脂乳液或溶液、聚乙烯醇水溶液或聚丙烯酰胺水溶液的一种或多种混合液。
5.根据权利要求4所述的一种碳纤维复合球的制备方法,其特征在于:步骤(2)所述的液体粘结剂是聚丙烯酰胺水溶液。
6.根据权利要求1所述的一种碳纤维复合球的制备方法,其特征在于:步骤(3)所述的热固性树脂是环氧树脂、酚醛树脂、糠醛树脂的一种或多种混合物。
7.根据权利要求1所述的一种碳纤维复合球的制备方法,其特征在于:步骤(3)所述的微细碳粉为炭黑、石墨粉、鳞片石墨、磨碎碳纤维、石墨烯、碳纳米管中的一种或多种混合物。
8.根据权利要求1所述的一种碳纤维复合球的制备方法,其特征在于:步骤(3)所述的沥青粉软化点高于200℃。